“Microstructural investigation of IASCC crack tips extracted from thimble tube O-ring specimens”. Penders AG, Konstantinovic MJ, Yang T, Bosch R-w, Schryvers D, Somville F, Journal of nuclear materials 565, 153727 (2022). http://doi.org/10.1016/J.JNUCMAT.2022.153727
Abstract: The microstructural features of intergranular irradiation-assisted stress corrosion crack tips from a redeemed neutron-irradiated flux thimble tube (60 dpa) have been investigated using focused-ion beam analysis and (scanning) transmission electron microscopy. The current work presents a close examination of the deformation field and oxide assembly associated with intergranular cracking, in addition to the analysis of radiation-induced segregation at leading grain boundaries. Evidence of stress induced martensitic transformation extending from the crack tips is presented. Intergranular crack arrest is demonstrated on the account of the external tensile stress orientation, and as a consequence of MnS inclusion particles segregating close to the fractured grain boundary. Exclusive observations of grain boundary oxidation prior to the cracking are presented, which is in full-agreement with the internal oxidation model.(c) 2022 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.1
DOI: 10.1016/J.JNUCMAT.2022.153727
|
“On the formation of antiphase boundaries in Fe₄Al₁₃, intermetallics during a high temperature treatment”. Ding L, Sapanathan T, Schryvers D, Simar A, Idrissi H, Scripta materialia 215, 114726 (2022). http://doi.org/10.1016/J.SCRIPTAMAT.2022.114726
Abstract: In this paper, we report atomic scale observations and formation mechanisms of a high-density of antiphase boundaries (APBs) within an ultra-fine-grained Fe4Al13 intermetallic layer at an Al/steel interface after a heat treatment at 596 degrees C. The results reveal that the APBs are formed by nucleation and the glide of partial dislocations with Burgers vector of b/3[010] (b = 12.47 angstrom). The intensive activation of APBs locally transforms the Fe4Al13 structure from the quasicrystal approximant structure to a quasicrystal. Very few stacking faults and nanotwins are observed indicating that the formation of planar defects is mainly driven by this transformation. This new insight on the formation of high density of APBs could possibly lead to an improvement in toughness by increasing the strength/ductility balance of this intermetallic.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6
DOI: 10.1016/J.SCRIPTAMAT.2022.114726
|
“Characterization of IASCC crack tips extracted from neutron-irradiated flux thimble tube specimens in view of a probabilistic fracture model”. Penders AG, Konstantinović, MJ, Van Renterghem W, Bosch R-W, Schryvers D, Somville F, Journal of nuclear materials 571, 154015 (2022). http://doi.org/10.1016/J.JNUCMAT.2022.154015
Abstract: This study reports the properties of irradiation assisted stress corrosion crack tips extracted by means of focused-ion beam from 60 to 80 dpa neutron-irradiated O-ring specimens tested under straining conditions under a pressurized-water reactor environment. Various crack tip morphologies and surrounding deformation features were analyzed as a function of applied stress, surface oxidation state and loading form – constant versus cyclic. All investigated cracks exhibit grain boundary oxidation in front of the crack tip, with the extent of oxidation being proportional to applied stress. These findings clearly demonstrate that, under the subcritical crack propagation regime, the grain boundary oxide grows faster than the crack. On the other hand, crack tips appertaining to specimens with removed oxide layer at the outer surface show comparatively less oxidation at the crack tip, which could indicate towards crack initiation from regions that exemplify lower stress, such as the O-ring inner surface. Cyclic loading is found to have a more pronounced effect on the crack tip microstructure, demonstrating increased deformation twinning and -martensitic transformation, which signifies towards an increased susceptibility to intergranular failure. Still, the extent of crack tip grain boundary oxidation in this case agrees well with expected values for maximum stress applied during cyclic loading. All results are interpreted based on the probabilistic subcritical crack propagation mechanism and provide strong support to a stress-driven internal oxidation model.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.1
DOI: 10.1016/J.JNUCMAT.2022.154015
|
“Discovery of core-shell quasicrystalline particles”. Yang T, Kong Y, Du Y, Li K, Schryvers D, Scripta materialia 222, 115040 (2023). http://doi.org/10.1016/J.SCRIPTAMAT.2022.115040
Abstract: Submicron-sized quasicrystalline particles were obtained in an Al-Zn-Mg-Cu alloy produced by traditional melting. These particles consist of an Al-Fe-Ni core and a Mg-Cu-Zn shell and were found to be stable and embedded randomly in the Al matrix. The diffraction patterns of these core-shell particles reveal a decagonal core and an icosahedral shell with, respectively, ten- and five-fold axes aligned. High resolution scanning transmission electron microscopy of the Mg-Cu-Zn shell confirms the five-fold symmetry atomic arrangement and the icosahedral structure. It can therefore be concluded that Fe and Ni impurities play an important role in mediating the formation of such an unusual ternary core-shell quasicrystalline particle. These findings provide some novel insights in the formation of quasicrystals in traditional industrial Al alloys.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6
DOI: 10.1016/J.SCRIPTAMAT.2022.115040
|
“Application of atmospheric plasma-jets for the conservation of cultural heritage”. Grieten E, Storme P, Caen J, Schalm O, Schryvers D, (2015)
Keywords: P3 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Antwerp Cultural Heritage Sciences (ARCHES)
|
“Quasicrystalline clusters transformed from C14-MgZn₂, nanoprecipitates in Al alloys”. Yang T, Kong Y, Li K, Lu Q, Wang Y, Du Y, Schryvers D, Materials characterization 199, 112772 (2023). http://doi.org/10.1016/J.MATCHAR.2023.112772
Abstract: Ultrafine faulty C14-MgZn2 Laves phase precipitates containing quasicrystalline clusters and demonstrating the formation of binary quasicrystalline precipitates with Penrose-like random-tiling were observed in the over-aged FCC matrix of a commercial 7N01 Al-Zn-Mg alloy, using high angle annular dark field scanning transmission electron microscopy. The evolution from C14-Laves phase to quasicrystalline clusters is illustrated, and five-fold symmetry can be found in both real and reciprocal spaces. Our findings reveal the possibility of quasicrystalline formation from Laves phase in a highly plastic metal matrix like Al and demonstrate the structural relationship between Laves phase and quasicrystals.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.7
DOI: 10.1016/J.MATCHAR.2023.112772
|