Abstract: The charge-coupled devices used in electron microscopy are coated with a scintillating crystal that gives rise to a severe modulation transfer function (MTF). Exact knowledge of the MTF is imperative for a good correspondence between image simulation and experiment. We present a practical method to measure the MTF above the Nyquist frequency from the beam blocker's shadow image. The image processing has been fully automated and the program is made public. The method is successfully tested on three cameras with various beam blocker shapes.

Abstract: Conventional glass-ionomer cements (GICs) are popular restorative materials, but their use is limited by their relatively low mechanical strength. This paper reports an attempt to improve these materials by incorporation of 10 wt% of three different types of nanoparticles, aluminum oxide, zirconium oxide, and titanium dioxide, into two commercial GICs (ChemFil((R)) Rock and EQUIA (TM) Fil). The results indicate that the nanoparticles readily dispersed into the cement matrix by hand mixing and reduced the porosity of set cements by filling the empty spaces between the glass particles. Both cements showed no significant difference in compressive strength with added alumina, and ChemFil((R)) Rock also showed no significant difference with zirconia. By contrast, ChemFil((R)) Rock showed significantly higher compressive strength with added titania, and EQUIA (TM) Fil showed significantly higher compressive strength with both zirconia and titania. Fewer air voids were observed in all nanoparticle-containing cements and this, in turn, reduced the development of cracks within the matrix of the cements. These changes in microstructure provide a likely reason for the observed increases in compressive strength, and overall the addition of nanoparticles appears to be a promising strategy for improving the physical properties of GICs.

Abstract: Electron energy loss spectra in conjunction with near-edge fine structures of purely stoichiometric niobium monoxide (NbO) and niobium pentoxide (Nb2O5) reference materials were recorded. The structures of the niobium oxide reference materials were checked by selected area electron diffraction to ensure a proper assignment of the fine structures. NbO and Nb2O5 show clearly different energy loss near-edge fine structures of the Nb-M-4,M-5 and -M-2,M-3 edges and of the O-K edge, reflecting the specific local environments of the ionized atoms. To distinguish the two oxides in a quantitative manner, the intensities under the Nb-M-4,M-5 as well as Nb-M-2,M-3 edges and the O-K edge were measured and their ratios calculated. k-factors were also derived from these measurements.

Abstract: Focused ion beam specimen preparation has been used for NiTi samples and SrTiO(3)/SrRuO(3) multilayers with prevention of surface amorphization and Ga implantation by a 2-kV cleaning procedure. Transmission electron microscopy techniques show that the samples are of high quality with a controlled thickness over large scales. Furthermore, preferential thinning effects in multicompounds are avoided, which is important when analytical transmission electron microscopy measurements need to be interpreted in a quantitative manner. The results are compared to similar measurements acquired for samples obtained using conventional preparation techniques such as electropolishing for alloys and ion milling for oxides.