“The darkening of copper- or lead-based pigments explained by a structural modification of natural orpiment : a spectroscopic and electrochemical study”. Vermeulen M, Sanyova J, Janssens K, Nuyts G, De Meyer S, De Wael K, Journal of analytical atomic spectrometry 32, 1331 (2017). http://doi.org/10.1039/C7JA00047B
Abstract: A combined Raman and electrochemical study of natural orpiment (As2S3), an arsenic sulfide pigment, was used to assess the quick formation of oxidized species such as arsenic oxide (As2O3) upon exposing the pigment to 405 nm or 532 nm monochromatic light while simultaneously recording the Raman spectra of the exposed sample. During this process, a distortion of the main band at 355 cm−1, associated with the stretching of the AsS3/2 pyramids of natural orpiment, was observed as well as an increased intensity of the 359 cm−1 band, corresponding to covalent AsAs bonds in natural orpiment. The distortion was accompanied by an overall decrease of the global Raman signal for natural orpiment, which could be explained by a loss in the crystal structure. The same phenomena were recorded in reference natural orpiment model paint samples stored for a long time together with verdigris (Cu(OH)2·(CH3COO)2·5H2O) and minium (Pb3O4) paints, the latter two appearing darkened on their sides closest to the orpiment sample as well as in several historical samples containing natural orpiment mixed with various blue pigments. By SEM-EDX and XRPD analysis, respectively on loose material and cast thin-sections of model paint samples, the darkening was identified as dark sulfide species such as chalcocite (Cu2S) and galena (PbS), suggesting the release of volatile sulfide or related species by the natural orpiment paint. XANES analyses of paint samples presenting AsAs bond increase indicated the presence of sulfur species most likely identified as organosulfur compounds formed upon the AsAs bond formation and explained the darkening of the Cu- and Pb-based pigments. To the best of our knowledge, this article reports for the first time the light-induced formation of AsAs bonds in natural orpiment used as an artists' pigment and objectively demonstrates the incompatibility between orpiment and (arsenic) sulfide-sensitive pigments.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 10
DOI: 10.1039/C7JA00047B
|
|
|
“Indoor environmental quality index for conservation environments : the importance of including particulate matter”. Marchetti A, Pilehvar S, 't Hart L, Leyva Pernia D, Voet O, Anaf W, Nuyts G, Otten E, Demeyer S, Schalm O, De Wael K, Building and environment 126, 132 (2017). http://doi.org/10.1016/J.BUILDENV.2017.09.022
Abstract: It is commonly known that the conservation state of works of arts exhibited inside museums is strongly influenced by the indoor environmental quality (IEQ). Heritage institutions traditionally record and evaluate their IEQ by monitoring temperature, relative humidity, and -more rarely-light. However, smart use of technology enables monitoring other parameters that give a more complete insight in environmental air aggressiveness. One of this parameters is particulate matter (PM) and especially its concentration, size distribution and chemical composition. In this work, we present a selection of data sets which were obtained in a measuring campaign performed in the War Heritage Institute in Brussels, Belgium. A continuous monitoring of PM concentration with a light scattering based particle counter was performed. In addition the daily mass concentration and size distribution of airborne PM was monitored by means of Harvard impactors. The chemical composition of sampled PM was inferred from the results of XRF and IC analysis. The insights from these datasets are combined with the results of traditional environmental monitoring (temperature, relative humidity and light intensity), and assessed against the recommended guidelines for conservation environments. By using an integrated approach based on the calculation of an IEQ-index, we present a straightforward methodology to evaluate and visualize the IEQ including also continuous PM monitoring. It is clear from the results of this study how including PM in IEQ analysis allows to identify potential risks for museum collections that remain invisible when only traditional parameters are considered.
Keywords: A1 Journal article; Engineering sciences. Technology; Antwerp Systems and software Modelling (AnSyMo); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 4.053
Times cited: 10
DOI: 10.1016/J.BUILDENV.2017.09.022
|
|
|
“Combined computed nanotomography and nanoscopic x-ray fluorescence imaging of cobalt nanoparticles in caenorhabditis elegans”. Cagno S, Brede DA, Nuyts G, Vanmeert F, Pacureanu A, Tucoulou R, Cloetens P, Falkenberg G, Janssens K, Salbu B, Lind OC, Analytical chemistry 89, 11435 (2017). http://doi.org/10.1021/ACS.ANALCHEM.7B02554
Abstract: Synchrotron radiation phase-contrast computed nanotomography (nano-CT) and two-and three-dimensional (2D and 3D) nanoscopic X-ray fluorescence (nano-XRF) were used to investigate the internal distribution of engineered-cobalt nanoparticles (Co NPs) in exposed individuals of the nematode Caenorhabditis elegans. Whole-nematodes and selected tissues and organs were 3D-rendered: anatomical 3D renderings with 50 nm voxel size enabled the visualization of spherical nanoparticle aggregates. with size tip to 200 nm within intact C. elegans. A 20 X 37 nm(2) high-brilliance beam was employed to obtain XRF elemental distribution maps of entire nematodes or anatomical details such as embryos, which could be compared with the CT data, These maps showed Co NPs to be predominantly present within the intestine and the epithelium, and they were not colocalized with Zn granules found in the lysosonie-containing vesicles or Fe agglomerates in the intestine. Iterated XRF scanning of a specimen at 0 degrees and 90 degrees angles suggested that NP aggregates were translocated into tissues outside of the intestinal lumen. Virtual-slicing by means of 2D XRF tomography, combined with holotomography, indicated presumable presence of individual NP aggregates inside the uterus and within embryos.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 13
DOI: 10.1021/ACS.ANALCHEM.7B02554
|
|
|
“Role of coating-metallic support interaction in the properties of electrosynthesized Rh-based structured catalysts”. Benito P, de Nolf W, Nuyts G, Janssens K, et al, ACS catalysis 4, 3779 (2014). http://doi.org/10.1021/CS501079K
Abstract: Rh-structured catalysts for the catalytic partial oxidation of CH4 to syngas were prepared by electrosynthesis of Rh-containing hydrotalcite-type (HT) compounds on FeCrAlloy foams followed by calcination at 900 degrees C. During the calcination the simultaneous decomposition of the layered HT structure and formation of the protective FeCrAlloy outer shell in alumina occurred. Here, we studied the role of the coating-metallic support interaction in the properties of the catalysts after calcination, H-2 reduction, and catalytic tests, by a combination of electron (FEG-SEM/EDS) and synchrotron X-ray (XRF/XRPD and XRF/XANES) microscopic techniques. The characterization of crystalline phases in the metallic support and coating and distribution of Rh active species was carried out on several samples prepared by modifying the Rh content in the electrolytic solution (Rh/Mg/Al = 11.0/70.0/19.0, 5.0/70.0/25.0, 0/70.0/30.0 atomic ratio). A sample was also prepared with no aluminum in the electrolytic solution (Rh/Mg/Al = 13.6/86.4/0.0 atomic ratio) and calcined at 550 and 900 degrees C. The interaction between the elements of the metallic support and the catalytic coating increased the film adhesion during the thermal treatment and catalytic tests and modified the catalyst crystalline phases. A chemical reaction between Al corning from the foam and Mg in the coating occurred during calcination at high temperature leading to the formation of spinel phases in which rhodium is solved, together with some Rh2O3 and Rh. The metallic support was oxidized forming the corundum scale and chromium oxides, moreover t-Al2O3 was identified. For the Rh11.0Mg70.0Al19.0 catalyst the inclusion of Rh in the spinel phase decreased its reducibility in the H-2 pretreatment. The reduction continued during catalytic tests by feeding diluted CH4/O-2/He gas mixtures, evidenced by the catalyst activation. While under concentrated gas mixtures the deactivation occurred, probably by oxidation.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 10.614
Times cited: 13
DOI: 10.1021/CS501079K
|
|
|
“Improvement in the coating homogeneity in electrosynthesized Rh structured catalysts for the partial oxidation of methane”. Benito P, Monti M, de Nolf W, Nuyts G, Janssens K, et al, Catalysis today 246, 154 (2015). http://doi.org/10.1016/J.CATTOD.2014.10.003
Abstract: The precipitation of Rh/Mg/Al and Rh/Al hydroxides on the surface of FeCrAlloy foams by a base electrogeneration method was investigated to improve the properties of the deposited film (homogeneity and composition) and therefore the performances of the structured catalysts, obtained by calcination, in the Catalytic Partial Oxidation of CH4 to syngas. The work focussed on decreasing current gradients within open-cell foam cylinders by increasing the number of electrical contacts from 1 to 3 points to promote a more homogeneous precipitation of the hydroxides. Electrochemical and catalytic tests as well as SEM/EDS and mu-XRFIXRD analyses allowed to correlate the effect of the number of electrical contact points with materials properties. Lastly, syntheses were performed on Pt plates to study the effect of the electrical behaviour and shape of the support on the composition of the film. A more homogeneous coating of the foam surface was achieved by adopting a configuration with 3 contact points since the reduction of nitrates and water molecules that generates the basic media in the vicinity of the support was enhanced. Layer thicknesses up to 5-15 mu m were deposited; however, the sequential precipitation of a film with composition closer to the expected one and a layer enriched in Al and Rh (outer layer) was not avoided. The improvement in the coating gave rise to enhanced performances for a sample prepared at -1.1 V for 3000 s. Contrarily, the low adherence of the outer layer in a sample prepared at -1.2 V for 2000 s during both calcination and catalytic tests may be responsible of the unexpected decrease in catalytic performances. The same sequential precipitation was observed by performing the syntheses on Pt plates, showing that the electrical nature the support did not play a key role on this phenomenon. (C) 2014 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.636
Times cited: 14
DOI: 10.1016/J.CATTOD.2014.10.003
|
|
|
“Stable Rh particles in hydrotalcite-derived catalysts coated on FeCrAlloy foams by electrosynthesis”. Benito P, Nuyts G, Monti M, de Nolf W, Fornasari G, Janssens K, Scavetta E, Vaccari A, Applied catalysis : B : environmental 179, 321 (2015). http://doi.org/10.1016/J.APCATB.2015.05.035
Abstract: Rh-based structured catalysts for the Catalytic Partial Oxidation of CH4 to syngas were prepared by electrosynthesis of Rh/Mg/Al hydrotalcite-type compounds on FeCrAlloy foams and calcination. The effects of Rh content, total metal concentration, and partial replacement of Mg2+ by Ni2+ in the electrolytic solution on coating thickness, Rh speciation, metallic particle size, and catalytic activity were investigated by SEM/EDS, mu-XRF/XANES and tests under diluted and concentrated reaction conditions. The amount of Rh species, present as Mg (RhxAl1-x)(2)O-4, depended on the thickness of the electrosynthesised layer as well as the Rh particle size and dispersion. Smaller and more dispersed particles were obtained by decreasing the Rh concentration in the electrolytic solution from Rh/Mg/Al=11/70/19 to 5/70/25 and 2/70/28 atomic ratio% (a.r.%) and in thinner rather than thicker layers. Despite the improvement in metallic particles features, the CH4 conversion was negatively affected by the low amount of active sites in the coating, the high metal support interaction and possibly the oxidation of metallic particles and carbon formation. A larger amount of solid containing well dispersed Rh particles was deposited by increasing the total metal concentration from 0.03 M to 0.06 M with the Rh/Mg/Al=5/70/25 a.r.%, and the catalytic performances were enhanced. The partial replacement of Mg2+ by Ni2+ gave rise to a very active bimetallic Rh/Ni catalyst, CH4 conversion and selectivity to syngas were above 90%, however, it slightly deactivated with time-on-stream. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 9.446
Times cited: 14
DOI: 10.1016/J.APCATB.2015.05.035
|
|
|
“A XANES study of chromophores : the case of black glass”. Ceglia A, Nuyts G, Cagno S, Meulebroeck W, Baert K, Cosyns P, Nys K, Thienpont H, Janssens K, Terryn H, Analytical methods 6, 2662 (2014). http://doi.org/10.1039/C3AY42029A
Abstract: We studied the Fe K-edge X-ray absorption near edge (XANES) spectra of several Roman black glass fragments in order to determine the Fe3+/ΣFe ratio of these materials. The selected archaeological glass samples cover the period 1st5th century AD in nine different sites of the North Western provinces of the Roman Empire. The fragments belong to two different compositional groups demonstrating a diachronic evolution: early Roman HMG (High Magnesia Glass) and Roman Imperial LMG (Low Magnesia Glass). The first group contains natural Fe levels (below 2 wt% as Fe2O3), while the LMG has concentrations above 5 wt%. This difference is also reflected by Fe3+/ΣFe values. Low iron glass was produced under strongly reducing conditions in order to obtain the black colour, with average Fe3+/ΣFe values ≈ 0.17. LMG glass is somewhat more oxidised (Fe3+/ΣFe ≈ 0.40.5). While HMG glass required active control of the furnace environment, LMG was made under ambient atmosphere and its higher oxidation degree is mainly determined by the chemistry of the raw glass.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.9
Times cited: 14
DOI: 10.1039/C3AY42029A
|
|
|
“Selectivity in ligand functionalization of photocatalytic metal oxide nanoparticles for phase transfer and self‐assembly applications”. Borah R, Ninakanti R, Nuyts G, Peeters H, Pedrazo-Tardajos A, Nuti S, Vande Velde C, De Wael K, Lenaerts S, Bals S, Verbruggen S, Chemistry-A European Journal , chem.202100029 (2021). http://doi.org/10.1002/CHEM.202100029
Abstract: Functionalization of photocatalytic metal oxide nanoparticles of TiO 2 , ZnO, WO 3 and CuO with amine‐terminated (oleylamine) and thiol‐terminated (1‐dodecanethiol) alkyl chained ligands was studied under ambient conditions. A high selectivity was observed in the binding specificity of a ligand towards nanoparticles of these different oxides. It was observed that oleylamine binds stably to only TiO 2 and WO 3 , while 1‐dodecanethiol binds stably only to ZnO and CuO. Similarly, polar to non‐polar solvent phase transfer of TiO 2 and WO 3 nanoparticles could be achieved by using oleylamine, but not by 1‐dodecanethiol, while the contrary holds for ZnO and CuO. The surface chemistry of ligand functionalized nanoparticles was probed by ATR‐FTIR spectroscopy, that enabled to elucidate the occupation of the ligands at the active sites. The photo‐stability of the ligands on the nanoparticle surface was determined by the photocatalytic self‐cleaning properties of the material. While TiO 2 and WO 3 degrade the ligands within 24 hours under both UV and visible light, ligands on ZnO and CuO remain unaffected. The gathered insights are also highly relevant from an application point of view. As an example, since the ligand functionalized nanoparticles are hydrophobic in nature, they can thus be self‐assembled at the air‐water interface, for obtaining nanoparticle films with demonstrated photocatalytic as well as anti‐fogging properties.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Sustainable Energy, Air and Water Technology (DuEL); Intelligence in PRocesses, Advanced Catalysts and Solvents (iPRACS)
Impact Factor: 5.317
Times cited: 15
DOI: 10.1002/CHEM.202100029
|
|
|
“Evaluation of manganese-bodies removal in historical stained glass windows via SR-\mu-XANES/XRF and SR-\mu-CT”. Cagno S, Nuyts G, Bugani S, De Vis K, Schalm O, Caen J, Helfen L, Cotte M, Reischig P, Janssens K, Journal of analytical atomic spectrometry 26, 2442 (2011). http://doi.org/10.1039/C1JA10204D
Abstract: The speed and effectiveness of a conservation treatment used for stained glass windows have been investigated. Dark-coloured Mn-rich stains can be found in the alteration layer of ancient glass artefacts and cause the surface to turn brown/black: this phenomenon is known as Mn-browning or Mn-staining. While in glass manganese is present in the +II or +III oxidation states, in the Mn-rich bodies, manganese is in a higher oxidation state (+IV). In restoration practice, mildly reducing solutions are employed to eliminate the dark colour and restore the clear appearance of the glass. In this paper the effectiveness and side effects of the use of hydroxylamine hydrochloride for this purpose are assessed. Archaeological fragments of stained glass windows, dated to the 14th century and originating from Sidney Sussex College, Cambridge (UK), were examined by means of synchrotron radiation (SR) based microscopic X-ray Absorption Near-Edge Spectroscopy (μ-XANES) and microscopic X-Ray Fluorescence (μ-XRF) and with high resolution computed absorption tomography (μ-CT) before, during and after the treatment. The monitoring of the glass fragments during the treatment allows us to better understand the manner in which the process unfolds and its kinetics. The results obtained reveal that the hydroxylamine hydrochloride treatment is effective, but also that it has a number of unwanted side effects. These findings are useful for optimizing the time and other modalities of the Mn-reducing treatment as well as minimizing its unwanted results.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 17
DOI: 10.1039/C1JA10204D
|
|
|
“Iron speciation in soda-lime-silica glass: a comparison of XANES and UV-vis-NIR spectroscopy”. Ceglia A, Nuyts G, Meulebroeck W, Cagno S, Silvestri A, Zoleo A, Nys K, Janssens K, Thienpont H, Terryn H, Journal of analytical atomic spectrometry 30, 1552 (2015). http://doi.org/10.1039/C5JA00046G
Abstract: Scientific analyses of ancient glasses have been carried out for many years using elemental chemical analysis. However, it is known that the control of the redox conditions in the glass melt has a strong implication on the final hue of glass because it affects Fe2+/SFe. Therefore an increasing number of studies on the redox conditions have been published in recent years by means of synchrotron based Xray absorption spectroscopy. This is a technique which is not easily accessible and requires dedicated facilities. In this paper we describe an alternative approach by means of optical absorption spectroscopy. We synthesised 10 soda-lime-silica glasses with known redox conditions and iron concentration to calibrate the absorption at 1100 nm as a function of Fe2+ concentration. The linear extinction coefficient was also determined. These glasses were also studied by means of X-ray Absorption Near Edge Structure (XANES) spectroscopy. Electron paramagnetic resonance spectroscopy was additionally used as an ancillary method to verify the quality of our data. Furthermore 28 samples from real archaeological samples were analysed by XANES and optical spectroscopy as a case study. The Fe2+/SFe values obtained were compared and demonstrated that the two techniques were in good agreement with each other. Optical spectroscopy can be applied in situ with moderate sample preparation to determine the concentration of Fe2+. To investigate the redox conditions, especially as a first screening approach, this methodology is an important tool to take into consideration before applying more sophisticated techniques such as XANES, which is more elaborate and requires high-tech resources.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 20
DOI: 10.1039/C5JA00046G
|
|
|
“Visualization of As(III) and As(V) distributions in degraded paint micro-samples from Baroque- and Rococo-era paintings”. Vermeulen M, Nuyts G, Sanyova J, Vila A, Buti D, Suuronen J-P, Janssens K, Journal of analytical atomic spectrometry 31, 1913 (2016). http://doi.org/10.1039/C6JA00134C
Abstract: Orpiment and realgar, both arsenic sulfide pigments respectively used for their vivid yellow and red-orange hues, are two of many artists' pigments that appear not to be stable upon light exposure, quickly degrading to arsenic trioxide and arsenate. This often results in whitening or transparency in the painted surfaces. While conventional techniques such as microscopic Raman (mu-RS) and microscopic Fourier transform infrared (mu-FTIR) spectroscopies can allow a quick and relatively easy identification of the orpiment, realgar, artificial arsenic sulfide glass and, to some extent, arsenic oxide, the identification and visualization of distributions of the degradation products – and especially arsenate compounds – in the paint micro-samples is generally more challenging. This challenge is due to the rather unfavorable limit of detection and low spectral resolution of such conventional spectroscopic techniques. This restricts the conclusions that can be drawn regarding the conservation state of valuable works of art. In this paper, we present how synchrotron radiation (SR) based techniques can overcome this challenge while working on painting cross-sections taken from a 17th-century painting by the Flemish artist Daniel Seghers (oil on canvas, Statens Museum for Kunst, Denmark) and an 18th-century French Chinoiserie (private collection, France). SR micro-X-ray fluorescence (m-XRF) mapping analysis performed on a visually degraded orpiment-containing paint stratigraphy reveals that arsenic is distributed throughout the entire cross-section, while X-ray absorption near edge structure (mu-XANES) demonstrated that the arsenic is present in both arsenite (As-III) and arsenate (As-V) forms. The latter compound(s), despite being barely identifiable by means of FTIR, were not only located at the surface of large and partially altered grains of arsenic sulfide but also spread throughout the entire paint stratigraphy. Their presence and distribution are attributed either to the complete degradation of smaller arsenic sulfide grains or to migration of the arsenates within the paint layer away from their original location of formation. The combination of mu-XRF and mu-XANES was very useful for the characterization of the advanced degradation state of the arsenic-containing pigments in paint systems; this type of information could not be obtained by means of conventional spectroscopic methods of microanalysis.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 20
DOI: 10.1039/C6JA00134C
|
|
|
“Room-temperature study of iron gall ink impregnated paper degradation under various oxygen and humidity conditions : time-dependent monitoring by viscosity and X-ray absorption near-edge spectrometry measurements”. Rouchon V, Duranton M, Burgaud C, Pellizzi E, Lavédrine B, Janssens K, de Nolf W, Nuyts G, Vanmeert F, Hellemans K, Analytical chemistry 83, 2589 (2011). http://doi.org/10.1021/AC1029242
Abstract: Many western manuscripts were written using iron gall inks. These inks can damage the paper via two major mechanisms: (a) acid hydrolysis, enhanced by humidity, and (b) oxidative depolymerization provoked by the presence of oxygen and free iron(II) ions. The degradation of unsized Whatman paper impregnated with different combinations of iron sulfate, gallic acid, and gum arabic was studied at room temperature in order to assess the relative importance of each mechanism. The samples were stored in various environments including a dry and/or an oxygen-free atmosphere. The cellulose depolymerization was monitored by viscometry and related to changes in the oxidation state of iron, determined by X-ray absorption near-edge spectrometry. The results indicate that residual amounts of oxygen (less than 0.1%) promote cellulose depolymerization, whereas the level of relative humidity has no impact. The cellulose depolymerization also appears closely correlated to oxidative mechanisms. Regarding the oxidation of iron, it only occurs in the simultaneous presence of oxygen and moisture, suggesting the occurrence of rustlike oxidative mechanisms. Finally, the presence of gallic acid has a strong influence, which is only partially explained by its capacity to reduce iron(III) to iron(II).
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 28
DOI: 10.1021/AC1029242
|
|
|
“Non-invasive and non-destructive examination of artistic pigments, paints, and paintings by means of X-Ray methods”. Janssens K, van der Snickt G, Vanmeert F, Legrand S, Nuyts G, Alfeld M, Monico L, Anaf W, de Nolf W, Vermeulen M, Verbeeck J, De Wael K, Topics in Current Chemistry 374, 81 (2016). http://doi.org/10.1007/S41061-016-0079-2
Abstract: Recent studies are concisely reviewed, in which X-ray beams of (sub)micrometre to millimetre dimensions have been used for non-destructive analysis and characterization of pigments, minute paint samples, and/or entire paintings from the seventeenth to the early twentieth century painters. The overview presented encompasses the use of laboratory and synchrotron radiation-based instrumentation and deals with the use of several variants of X-ray fluorescence (XRF) as a method of elemental analysis and imaging, as well as with the combined use of X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Microscopic XRF is a variant of the method that is well suited to visualize the elemental distribution of key elements, mostly metals, present in paint multi-layers, on the length scale from 1 to 100 μm inside micro-samples taken from paintings. In the context of the characterization of artists pigments subjected to natural degradation, the use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that have taken place. However, at synchrotron facilities, combinations of μ-XRF with related methods such as μ-XAS and μ-XRD have proven themselves to be very suitable for such studies. Their use is often combined with microscopic Fourier transform infra-red spectroscopy and/or Raman microscopy since these methods deliver complementary information of high molecular specificity at more or less the same length scale as the X-ray microprobe techniques. Since microscopic investigation of a relatively limited number of minute paint samples, taken from a given work of art, may not yield representative information about the entire artefact, several methods for macroscopic, non-invasive imaging have recently been developed. Those based on XRF scanning and full-field hyperspectral imaging appear very promising; some recent published results are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.033
Times cited: 50
DOI: 10.1007/S41061-016-0079-2
|
|
|
“Plasmonic gold-embedded TiO2 thin films as photocatalytic self-cleaning coatings”. Peeters H, Keulemans M, Nuyts G, Vanmeert F, Li C, Minjauw M, Detavernier C, Bals S, Lenaerts S, Verbruggen SW, Applied Catalysis B-Environmental 267, 118654 (2020). http://doi.org/10.1016/j.apcatb.2020.118654
Abstract: Transparent photocatalytic TiO2 thin films hold great potential in the development of self-cleaning glass sur-
faces, but suffer from a poor visible light response that hinders the application under actual sunlight. To alleviate this problem, the photocatalytic film can be modified with plasmonic nanoparticles that interact very effectively with visible light. Since the plasmonic effect is strongly concentrated in the near surroundings of the nano- particle surface, an approach is presented to embed the plasmonic nanostructures in the TiO2 matrix itself, rather than deposit them loosely on the surface. This way the interaction interface is maximised and the plasmonic effect can be fully exploited. In this study, pre-fabricated gold nanoparticles are made compatible with the organic medium of a TiO2 sol-gel coating suspension, resulting in a one-pot coating suspension. After spin coating, homogeneous, smooth, highly transparent and photoactive gold-embedded anatase thin films are ob- tained.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 22.1
Times cited: 57
DOI: 10.1016/j.apcatb.2020.118654
|
|