“Stable polyoxometalate insertion within the mesoporous metal organic framework MIL-100(Fe)”. Canioni R, Roch-Marchal C, Sécheresse F, Horcajada P, Serre C, Hardi-Dan M, Férey G, Grenèche J-M, Lefebvre F, Chang J-S, Hwang Y-K, Lebedev O, Turner S, Van Tendeloo G, Journal of materials chemistry 21, 1226 (2011). http://doi.org/10.1039/c0jm02381g
Abstract: Successful encapsulation of polyoxometalate (POM) within the framework of a mesoporous iron trimesate MIL-100(Fe) sample has been achieved by direct hydrothermal synthesis in the absence of fluorine. XRPD, 31P MAS NMR, IR, EELS, TEM and 57Fe Mössbauer spectrometry corroborate the insertion of POM within the cavities of the MOF. The experimental Mo/Fe ratio is 0.95, in agreement with the maximum theoretical amount of POM loaded within the pores of MIL-100(Fe), based on steric hindrance considerations. The POM-MIL-100(Fe) sample exhibits a pore volume of 0.373 cm3 g−1 and a BET surface area close to 1000 m2 g−1, indicating that small gas molecules can easily diffuse inside the cavities despite the presence of heavy phosphomolybdates. These latter contribute to the decrease in the overall surface area, due to the increase in molar weight, by 65%. Moreover, the resulting Keggin containing MIL-100(Fe) solid is stable in aqueous solution with no POM leaching even after more than 2 months. In addition, no exchange of the Keggin anions by tetrabutylammonium perchlorate in organic media has been observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 158
DOI: 10.1039/c0jm02381g
|
“Pd-zeolites as heterogeneous catalysts in heck chemistry”. Dams M, Drijkoningen L, Pauwels B, Van Tendeloo G, de Vos DE, Jacobs PA, Journal of catalysis 209, 225 (2002). http://doi.org/10.1006/jcat.2002.3630
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 157
DOI: 10.1006/jcat.2002.3630
|
“Zn-Al layered double hydroxides: synthesis, characterization and photocatalytic application”. Seftel EM, Popovici E, Mertens M, de Witte K, Van Tendeloo G, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 113, 296 (2008). http://doi.org/10.1016/j.micromeso.2007.11.029
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 154
DOI: 10.1016/j.micromeso.2007.11.029
|
“Tailoring ZnSe-CdSe colloidal quantum dots via cation exchange : from core/shell to alloy nanocrystals”. Groeneveld E, Witteman L, Lefferts M, Ke X, Bals S, Van Tendeloo G, de Mello Donega C, ACS nano 7, 7913 (2013). http://doi.org/10.1021/nn402931y
Abstract: We report a study of Zn2+ by Cd2+ cation exchange (CE) in colloidal ZnSe nanocrystals (NCs). Our results reveal that CE in ZnSe NCs is a thermally activated isotropic process. The CE efficiency (i.e., fraction of Cd2+ ions originally in solution, Cdsol, that is incorporated in the ZnSe NC) increases with temperature and depends also on the Cdsol/ZnSe ratio. Interestingly, the reaction temperature can be used as a sensitive parameter to tailor both the composition and the elemental distribution profile of the product (Zn,Cd)Se NCs. At 150 °C ZnSe/CdSe core/shell hetero-NCs (HNCs) are obtained, while higher temperatures (200 and 220 °C) produce (Zn1xCdx)Se gradient alloy NCs, with increasingly smoother gradients as the temperature increases, until homogeneous alloy NCs are obtained at T ≥ 240 °C. Remarkably, sequential heating (150 °C followed by 220 °C) leads to ZnSe/CdSe core/shell HNCs with thicker shells, rather than (Zn1xCdx)Se gradient alloy NCs. Thermal treatment at 250 °C converts the ZnSe/CdSe core/shell HNCs into (Zn1xCdx)Se homogeneous alloy NCs, while preserving the NC shape. A mechanism for the cation exchange in ZnSe NCs is proposed, in which fast CE takes place at the NC surface, and is followed by relatively slower thermally activated solid-state cation diffusion, which is mediated by Frenkel defects. The findings presented here demonstrate that cation exchange in colloidal ZnSe NCs provides a very sensitive tool to tailor the nature and localization regime of the electron and hole wave functions and the optoelectronic properties of colloidal ZnSeCdSe NCs.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 153
DOI: 10.1021/nn402931y
|
“Direct observation of ferrielectricity at ferroelastic domain boundaries in CaTiO3 by electron microscopy”. Van Aert S, Turner S, Delville R, Schryvers D, Van Tendeloo G, Salje EKH, Advanced materials 24, 523 (2012). http://doi.org/10.1002/adma.201103717
Abstract: High-resolution aberration-corrected transmission electron microscopy aided by statistical parameter estimation theory is used to quantify localized displacements at a (110) twin boundary in orthorhombic CaTiO3. The displacements are 36 pm for the Ti atoms and confined to a thin layer. This is the first direct observation of the generation of ferroelectricity by interfaces inside this material which opens the door for domain boundary engineering.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 150
DOI: 10.1002/adma.201103717
|
“Cu(OH)2 nanowires, CuO nanowires and CuO nanobelts”. Du GH, Van Tendeloo G, Chemical physics letters 393, 64 (2004). http://doi.org/10.1016/j.cplett.2004.06.017
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 145
DOI: 10.1016/j.cplett.2004.06.017
|
“Polyethylene glycol conjugated polymeric nanocapsules for targeted delivery of quercetin to folate-expressing cancer cells in vitro and in vivo”. El-Gogary RI, Rubio N, Wang JTW, Al-Jamal WT, Bourgognon M, Kafa H, Naeem M, Klippstein R, Abbate V, Leroux F, Bals S, Van Tendeloo G, Kamel AO, Awad GAS, Mortada ND, Al-Jamal KT;, ACS nano 8, 1384 (2014). http://doi.org/10.1021/nn405155b
Abstract: In this work we describe the formulation and characterization of chemically modified polymeric nanocapsules incorporating the anticancer drug, quercetin, for the passive and active targeting to tumors. Folic acid was conjugated to poly(lactide-co-glycolide) (PLGA) polymer to facilitate active targeting to cancer cells. Two different methods for the conjugation of PLGA to folic acid were employed utilizing polyethylene glycol (PEG) as a spacer. Characterization of the conjugates was performed using FTIR and H-1 NMR studies. The PEG and folk acid content was independent of the conjugation methodology employed. PEGylation has shown to reduce the size of the nanocapsule; moreover, zeta-potential was shown to be polymer-type dependent. Comparative studies on the cytotoxicity and cellular uptake of the different formulations by He La cells, in the presence and absence of excess folic acid, were carried out using MTT assay and Confocal Laser Scanning Microscopy, respectively. Both results confirmed the selective uptake and cytotoxicity of the folic acid targeted nanocapsules to the folate enriched cancer cells in a folate-dependent manner. Finally, the passive tumor accumulation and the active targeting of the nanocapsules to folate-expressing cells were confirmed upon intravenous administration in He La or IGROV-1 tumor-bearing mice. The developed nanocapsules provide a system for targeted delivery of a range of hydrophobic anticancer drugs in vivo.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 144
DOI: 10.1021/nn405155b
|
“Design of zeolite by inverse sigma transformation”. Verheyen E, Joos L, Van Havenbergh K, Breynaert E, Kasian N, Gobechiya E, Houthoofd K, Martineau C, Hinterstein M, Taulelle F, Van Speybroeck V, Waroquier M, Bals S, Van Tendeloo G, Kirschhock CEA, Martens JA;, Nature materials 11, 1059 (2012). http://doi.org/10.1038/NMAT3455
Abstract: Although the search for new zeolites has traditionally been based on trial and error, more rational methods are now available. The theoretical concept of inverse transformation of a zeolite framework to generate a new structure by removal of a layer of framework atoms and contraction has for the first time been achieved experimentally. The reactivity of framework germanium atoms in strong mineral acid was exploited to selectively remove germanium-containing four-ring units from an UTL type germanosilicate zeolite. Annealing of the leached framework through calcination led to the new all-silica COK-14 zeolite with intersecting 12- and 10-membered ring channel systems. An intermediate stage of this inverse transformation with dislodged germanate four-rings still residing in the pores could be demonstrated. Inverse transformation involving elimination of germanium-containing structural units opens perspectives for the synthesis of many more zeolites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
Times cited: 140
DOI: 10.1038/NMAT3455
|
“Selective bifunctional catalytic conversion of cellulose over reshaped ni particles at the tip of carbon nanofibers”. Van de Vyver S, Geboers J, Dusselier M, Schepers H, Vosch T, Zhang L, Van Tendeloo G, Jacobs PA, Sels BF, Chemsuschem 3, 698 (2010). http://doi.org/10.1002/cssc.201000087
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 7.226
Times cited: 136
DOI: 10.1002/cssc.201000087
|
“The influence of the alcohol concentration on the structural ordering of mesoporous silica: cosurfactant versus cosolvent”. Liu S, Cool P, Collart O, van der Voort P, Vansant EF, Lebedev OI, Van Tendeloo G, Jiang M, The journal of physical chemistry : B : condensed matter, materials, surfaces, interfaces and biophysical 107, 10405 (2003). http://doi.org/10.1021/jp034410w
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.177
Times cited: 134
DOI: 10.1021/jp034410w
|
“Ball milling effect on the structure of single-wall carbon nanotubes”. Pierard N, Fonseca A, Colomer J-F, Bossuot C, Benoit J-M, Van Tendeloo G, Pirard J-P, Nagy JB, Carbon 42, 1691 (2004). http://doi.org/10.1016/j.carbon.2004.02.031
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 133
DOI: 10.1016/j.carbon.2004.02.031
|
“Structural evolution of the BiFeO3-LaFeO3 system”. Rusakov D, Abakumov AM, Yamaura K, Belik AA, Van Tendeloo G, Takayama-Muromachi E, Chemistry of materials 23, 285 (2011). http://doi.org/10.1021/cm1030975
Abstract: The (1 − x)BiFeO3−xLaFeO3 system has been investigated and characterized by room-temperature and high-temperature laboratory and synchrotron powder X-ray diffraction, electron diffraction, high-resolution transmission electron microscopy, differential scanning calorimetry, and magnetization measurements. At room temperature, the ferroelectric R3c phase is observed for 0.0 ≤ x ≤ 0.10. The PbZrO3-related √2ap × 2√2ap × 4ap superstructure (where ap is the parameter of the cubic perovskite subcell) is observed for Bi0.82La0.18FeO3, while an incommensurately modulated phase is formed for 0.19 ≤ x ≤ 0.30 with the √2ap × 2ap × √2ap basic unit cell. The GdFeO3-type phase with space group Pnma (√2ap × 2ap × √2ap) is stable at 0.50 ≤ x ≤ 1. Bi0.82La0.18FeO3 has no detectable homogeneity range (space group Pnam, a = 5.6004(1) Å, b = 11.2493(3) Å, c = 15.6179(3) Å). The incommensurately modulated Bi0.75La0.25FeO3 structure was solved from synchrotron X-ray powder diffraction data (Imma(00γ)s00 superspace group, a = 5.5956(1) Å, b = 7.8171(1) Å, c = 5.62055(8) Å, q = 0.4855(4)c*, RP = 0.023, RwP = 0.033). In this structure, cooperative displacements of the Bi and O atoms occur, which order within the (AO) (where A = Bi, La) layers, resulting in an antipolar structure. Local fluctuations of the intralayer antipolar ordering are compensated by an interaction with the neighboring (AO) layers. A coupling of the antipolar displacements with the cooperative tilting distortion of the perovskite octahedral framework is proposed as the origin of the incommensurability. All the phases transform to the GdFeO3-type structure at high temperatures. Bi0.82La0.18FeO3 shows an intermediate PbZrO3-type phase with √2ap × 2√2ap × 2ap (space group Pbam; a = 5.6154(2) Å, b = 11.2710(4) Å, and c = 7.8248(2) Å at 570 K). The compounds in the compositional range of 0.18 ≤ x ≤ 0.95 are canted antiferromagnets.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 133
DOI: 10.1021/cm1030975
|
“Preparation of sulfonated ordered mesoporous carbon and its use for the esterification of fatty acids”. Peng L, Philippaerts A, Ke X, van Noyen J, de Cleppel F, Van Tendeloo G, Jacobs PA, Sels BF, Catalysis today 150, 140 (2010). http://doi.org/10.1016/j.cattod.2009.07.066
Abstract: Mesoporous carbon, which can be replicated from mesoporous silica and whose surface is hydrophobic, can be an ideal catalyst for the esterification of fatty acids. Here we report an easy and low cost way to prepare sulfonic acid group-functionalized mesoporous carbon. A sample of calcined mesoporous silica SBA-15 was added to an aqueous sucrose solution followed by drying and calcination at different temperatures. In contrast to existing procedures, the obtained hybrid Si/C material was then first sulfonated in H2SO4, before the final removal of the silica template in order to stabilize the porous structure towards the liquid phase sulfonation treatment. Thus the silicacarbon composites, instead of the mesoporous carbon, were successfully sulfonated to introduce SO3H groups, while keeping the ordered mesoporous structure intact. The influence of carbonization temperature was investigated, suggesting an optimum temperature of 873 K. The SO3H group-functionalized mesoporous carbon, denoted as CMK-3-873-SO3H, was characterized by means of XRD, N2 physisorption, SEM, FT-IR, elemental analysis and TEM. It followed that a uniform mesoporous carbon was obtained with an average pore size of 3.89 nm, a specific surface of 807 m2/g and a SO3H group loading of 0.39 meq/g of dry material. Compared with other solid acid catalysts, the resulting material shows enhanced activity in the acid-catalyzed esterification of oleic acid with methanol, and can be used repeatedly. The increased catalytic performance is attributed to the hydrophobic surface and larger pore size of the new catalyst. It can effectively accommodate long chain fatty acids and reject formed water, making the active sites easily accessible.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.636
Times cited: 132
DOI: 10.1016/j.cattod.2009.07.066
|
“Au@Ag nanoparticles : halides stabilize {100} facets”. Gómez-Graña S, Goris B, Altantzis T, Fernández-López C, Carbó-Argibay E, Guerrero-Martínez A, Almora-Barrios N, López N, Pastoriza-Santos I, Pérez-Juste J, Bals S, Van Tendeloo G, Liz-Marzán LM;, The journal of physical chemistry letters 4, 2209 (2013). http://doi.org/10.1021/jz401269w
Abstract: Seed-mediated growth is the most efficient methodology to control the size and shape of colloidal metal nanoparticles. In this process, the final nanocrystal shape is defined by the crystalline structure of the initial seed as well as by the presence of ligands and other additives that help to stabilize certain crystallographic facets. We analyze here the growth mechanism in aqueous solution of silver shells on presynthesized gold nanoparticles displaying various well-defined crystalline structures and morphologies. A thorough three-dimensional electron microscopy characterization of the morphology and internal structure of the resulting core-shell nanocrystals indicates that {100} facets are preferred for the outer silver shell, regardless of the morphology and crystallinity of the gold cores. These results are in agreement with theoretical analysis based on the relative surface energies of the exposed facets in the presence of halide ions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.353
Times cited: 131
DOI: 10.1021/jz401269w
|
“Magnetic monopole field exposed by electrons”. Béché, A, Van Boxem R, Van Tendeloo G, Verbeeck J, Nature physics 10, 26 (2014). http://doi.org/10.1038/NPHYS2816
Abstract: The experimental search for magnetic monopole particles(1-3) has, so far, been in vain. Nevertheless, these elusive particles of magnetic charge have fuelled a rich field of theoretical study(4-10). Here, we created an approximation of a magnetic monopole in free space at the end of a long, nanoscopically thin magnetic needle(11). We experimentally demonstrate that the interaction of this approximate magnetic monopole field with a beam of electrons produces an electron vortex state, as theoretically predicted for a true magnetic monopole(3,11-18). This fundamental quantum mechanical scattering experiment is independent of the speed of the electrons and has consequences for all situations where electrons meet such monopole magnetic fields, as, for example, in solids. The set-up not only shows an attractive way to produce electron vortex states but also provides a unique insight into monopole fields and shows that electron vortices might well occur in unexplored solid-state physics situations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 22.806
Times cited: 131
DOI: 10.1038/NPHYS2816
|
“Structure and microstructure of La1-xCaxMnO3- thin films prepared by pulsed layer deposition”. Lebedev OI, Van Tendeloo G, Amelinckx S, Leibold B, Habermeier H-U, Physical review : B : condensed matter and materials physics 58, 8065 (1998). http://doi.org/10.1103/PhysRevB.58.8065
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 131
DOI: 10.1103/PhysRevB.58.8065
|
“Well shaped Mn3O4 nano-octahedra with anomalous magnetic behavior and enhanced photodecomposition properties”. Li Y, Tan H, Yang X-Y, Goris B, Verbeeck J, Bals S, Colson P, Cloots R, Van Tendeloo G, Su B-L, Small 7, 475 (2011). http://doi.org/10.1002/smll.201001403
Abstract: Very uniform and well shaped Mn3O4 nano-octahedra are synthesized using a simple hydrothermal method under the help of polyethylene glycol (PEG200) as a reductant and shape-directing agent. The nano-octahedra formation mechanism is monitored. The shape and crystal orientation of the nanoparticles is reconstructed by scanning electron microscopy and electron tomography, which reveals that the nano-octahedra only selectively expose {101} facets at the external surfaces. The magnetic testing demonstrates that the Mn3O4 nano-octahedra exhibit anomalous magnetic properties: the Mn3O4 nano-octahedra around 150 nm show a similar Curie temperature and blocking temperature to Mn3O4 nanoparticles with 10 nm size because of the vertical axis of [001] plane and the exposed {101} facets. With these Mn3O4 nano-octahedra as a catalyst, the photodecomposition of rhodamine B is evaluated and it is found that the photodecomposition activity of Mn3O4 nano-octahedra is much superior to that of commercial Mn3O4 powders. The anomalous magnetic properties and high superior photodecomposition activity of well shaped Mn3O4 nano-octahedra should be related to the special shape of the nanoparticles and the abundantly exposed {101} facets at the external surfaces. Therefore, the shape preference can largely broaden the application of the Mn3O4 nano-octahedra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 131
DOI: 10.1002/smll.201001403
|
“Control of the outer diameter of thin carbon nanotubes synthesized by catalytic decomposition of hydrocarbons”. Willems I, Konya Z, Colomer JF, Van Tendeloo G, Nagaraju N, Fonseca A, Nagy JB, Chemical physics letters 317, 71 (2000). http://doi.org/10.1016/S0009-2614(99)01300-7
Abstract: Multi-wall carbon nanotubes have been produced by the catalytic decomposition of acetylene. Go-Mo, Co-V and Co-Fe mixtures supported either on zeolite or corundum alumina were used as catalysts. When Fe or V is added to Co, the carbon deposit increases. The nanotubes were characterized by both low and high resolution TEM. From histograms representing the outer diameter distributions, it is clear that the outer diameter of the nanotubes can be controlled by choosing the appropriate catalyst. (C) 2000 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 130
DOI: 10.1016/S0009-2614(99)01300-7
|
“Discovery of a superhard iron tetraboride superconductor”. Gou H, Dubrovinskaia N, Bykova E, Tsirlin AA, Kasinathan D, Schnelle W, Richter A, Merlini M, Hanfland M, Abakumov AM, Batuk D, Van Tendeloo G, Nakajima Y, Kolmogorov AN, Dubrovinsky L;, Physical review letters 111, 157002 (2013). http://doi.org/10.1103/PhysRevLett.111.157002
Abstract: Single crystals of novel orthorhombic (space group Pnnm) iron tetraboride FeB4 were synthesized at pressures above 8 GPa and high temperatures. Magnetic susceptibility and heat capacity measurements demonstrate bulk superconductivity below 2.9 K. The putative isotope effect on the superconducting critical temperature and the analysis of specific heat data indicate that the superconductivity in FeB4 is likely phonon mediated, which is rare for Fe-based superconductors. The discovered iron tetraboride is highly incompressible and has the nanoindentation hardness of 62(5) GPa; thus, it opens a new class of highly desirable materials combining advanced mechanical properties and superconductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 127
DOI: 10.1103/PhysRevLett.111.157002
|
“High resolution mapping of surface reduction in ceria nanoparticles”. Turner S, Lazar S, Freitag B, Egoavil R, Verbeeck J, Put S, Strauven Y, Van Tendeloo G, Nanoscale 3, 3385 (2011). http://doi.org/10.1039/c1nr10510h
Abstract: Surface reduction of ceria nano octahedra with predominant {111} and {100} type surfaces is studied using a combination of aberration-corrected Transmission Electron Microscopy (TEM) and spatially resolved electron energy-loss spectroscopy (EELS) at high energy resolution and atomic spatial resolution. The valency of cerium ions at the surface of the nanoparticles is mapped using the fine structure of the Ce M4,5 edge as a fingerprint. The valency of the surface cerium ions is found to change from 4+ to 3+ owing to oxygen deficiency (vacancies) close to the surface. The thickness of this Ce3+ shell is measured using atomic-resolution Scanning Transmission Electron Microscopy (STEM)-EELS mapping over a {111} surface (the predominant facet for this ceria morphology), {111} type surface island steps and {100} terminating planes. For the {111} facets and for {111} surface islands, the reduction shell is found to extend over a single fully reduced surface plane and 12 underlying mixed valency planes. For the {100} facets the reduction shell extends over a larger area of 56 oxygen vacancy-rich planes. This finding provides a plausible explanation for the higher catalytic activity of the {100} surface facets in ceria.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 127
DOI: 10.1039/c1nr10510h
|
“From VO2(B) to VO2(R): theoretical structures of VO2 polymorphs and in situ electron microscopy”. Leroux C, Nihoul G, Van Tendeloo G, Physical review : B : condensed matter and materials physics 57, 5111 (1998). http://doi.org/10.1103/PhysRevB.57.5111
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 122
DOI: 10.1103/PhysRevB.57.5111
|
“Molecular shape-selectivity of MFI zeolite nanosheets in n-decane isomerization and hydrocracking”. Verheyen E, Jo C, Kurttepeli M, Vanbutsele G, Gobechiya E, Korányi TI, Bals S, Van Tendeloo G, Ryoo R, Kirschhock CEA, Martens JA;, Journal of catalysis 300, 70 (2013). http://doi.org/10.1016/j.jcat.2012.12.017
Abstract: MFI zeolite nanosheets with thickness of 2 and 8 nm were synthesized, transformed into bifunctional catalysts by loading with platinum and tested in n-decane isomerization and hydrocracking. Detailed analysis of skeletal isomers and hydrocracked products revealed that the MFI nanosheets display transition-state shape-selectivity similar to bulk MFI zeolite crystals. The suppressed formation of bulky skeletal isomers and C5 cracking products are observed both in the nanosheets and the bulk crystals grown in three dimensions. This is typical for restricted transition-state shape-selectivity, characteristic for the MFI type pores. It is a first clear example of transition-state shape-selectivity inside a zeolitic nanosheet. Owing to the short diffusion path across the sheets, expression of diffusion-based discrimination of reaction products in the MFI nanosheets was limited. The 2-methylnonane formation among monobranched C10 isomers and 2,7-dimethyloctane among dibranched C10 isomers, which in MFI zeolite are favored by product diffusion, was much less favored on the nanosheets compared to the reference bulk ZSM-5 material.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 121
DOI: 10.1016/j.jcat.2012.12.017
|
“Three-dimensional atomic imaging of colloidal core-shell nanocrystals”. Bals S, Casavola M, van Huis MA, Van Aert S, Batenburg KJ, Van Tendeloo G, Vanmaekelbergh D, Nano letters 11, 3420 (2011). http://doi.org/10.1021/nl201826e
Abstract: Colloidal coreshell semiconductor nanocrystals form an important class of optoelectronic materials, in which the exciton wave functions can be tailored by the atomic configuration of the core, the interfacial layers, and the shell. Here, we provide a trustful 3D characterization at the atomic scale of a free-standing PbSe(core)CdSe(shell) nanocrystal by combining electron microscopy and discrete tomography. Our results yield unique insights for understanding the process of cation exchange, which is widely employed in the synthesis of coreshell nanocrystals. The study that we present is generally applicable to the broad range of colloidal heteronanocrystals that currently emerge as a new class of materials with technological importance.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 12.712
Times cited: 121
DOI: 10.1021/nl201826e
|
“Monitoring galvanic replacement through three-dimensional morphological and chemical mapping”. Goris B, Polavarapu L, Bals S, Van Tendeloo G, Liz-Marzán LM, Nano letters 14, 3220 (2014). http://doi.org/10.1021/nl500593j
Abstract: Galvanic replacement reactions on metal nanoparticles are often used for the preparation of hollow nanostructures with tunable porosity and chemical composition, leading to tailored optical and catalytic properties. However, the precise interplay between the three-dimensional (3D) morphology and chemical composition of nanostructures during galvanic replacement is not always well understood as the 3D chemical imaging of nanoscale materials is still challenging. It is especially far from straightforward to obtain detailed information from the inside of hollow nanostructures using electron microscopy techniques such as SEM or TEM. We demonstrate here that a combination of state-of-the-art EDX mapping with electron tomography results in the unambiguous determination of both morphology transformation and elemental composition of nanostructures in 3D, during galvanic replacement of Ag nanocubes. This work provides direct and unambiguous experimental evidence toward understanding the galvanic replacement reaction. In addition, the powerful approach presented here can be applied to a wide range of nanoscale transformation processes, which will undoubtedly guide the development of novel nanostructures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 120
DOI: 10.1021/nl500593j
|
“2D atomic mapping of oxidation states in transition metal oxides by scanning transmission electron microscopy and electron energy-loss spectroscopy”. Tan H, Turner S, Yücelen E, Verbeeck J, Van Tendeloo G, Physical review letters 107, 107602 (2011). http://doi.org/10.1103/PhysRevLett.107.107602
Abstract: Using a combination of high-angle annular dark-field scanning transmission electron microscopy and atomically resolved electron energy-loss spectroscopy in an aberration-corrected transmission electron microscope we demonstrate the possibility of 2D atom by atom valence mapping in the mixed valence compound Mn3O4. The Mn L2,3 energy-loss near-edge structures from Mn2+ and Mn3+ cation sites are similar to those of MnO and Mn2O3 references. Comparison with simulations shows that even though a local interpretation is valid here, intermixing of the inelastic signal plays a significant role. This type of experiment should be applicable to challenging topics in materials science, such as the investigation of charge ordering or single atom column oxidation states in, e.g., dislocations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 115
DOI: 10.1103/PhysRevLett.107.107602
|
“F-doped Co3O4 photocatalysts for sustainable H2 generation from water/ethanol”. Gasparotto A, Barreca D, Bekermann D, Devi A, Fischer RA, Fornasiero P, Gombac V, Lebedev OI, Maccato C, Montini T, Van Tendeloo G, Tondello E, Journal of the American Chemical Society 133, 19362 (2011). http://doi.org/10.1021/ja210078d
Abstract: p-Type Co3O4 nanostructured films are synthesized by a plasma-assisted process and tested in the photocatalytic production of H2 from water/ethanol solutions under both near-UV and solar irradiation. It is demonstrated that the introduction of fluorine into p-type Co3O4 results in a remarkable performance improvement with respect to the corresponding undoped oxide, highlighting F-doped Co3O4 films as highly promising systems for hydrogen generation. Notably, the obtained yields were among the best ever reported for similar semiconductor-based photocatalytic processes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 114
DOI: 10.1021/ja210078d
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
“End-to-end assembly of shape-controlled nanocrystals via a nanowelding approach mediated by gold domains”. Figuerola A, Franchini IR, Fiore A, Mastria R, Falqui A, Bertoni G, Bals S, Van Tendeloo G, Kudera S, Cingolani R, Manna L, Advanced materials 21, 550 (2009). http://doi.org/10.1002/adma.200801928
Abstract: Welding nanocrystals for assembly: The welding of Au domains grown on the tips of shape-controlled cadmium chalcogenide colloidal nanocrystals is used as a strategy for their assembly. Iodine-induced coagulation of selectively grown Au domains leads to assemblies such as flowerlike structures based on bullet-shaped nanocrystals, linear and cross-linked chains of nanorods, and globular networks with tetrapods as building blocks.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 110
DOI: 10.1002/adma.200801928
|
“Synthesis of single wall carbon nanotubes by catalytic decomposition of hydrocarbons”. Colomer J-F, Bister G, Willems I, Konya Z, Fonseca A, Van Tendeloo G, Nagy JB, Chemical communications , 1343 (1999). http://doi.org/10.1039/a903142a
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 110
DOI: 10.1039/a903142a
|
“Investigation of the morphology of the mesoporous SBA-16 and SBA-15 materials”. Stevens WJJ, Lebeau K, Mertens M, Van Tendeloo G, Cool P, Vansant EF, The journal of physical chemistry : B : condensed matter, materials, surfaces, interfaces and biophysical 110, 9183 (2006). http://doi.org/10.1021/jp0548725
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 3.177
Times cited: 109
DOI: 10.1021/jp0548725
|