Abstract: The morphology and structure of hexagonal graphitic BN (h-BN) powders with graphitization indices GI <5, used as precursors for the synthesis of cubic BN (c-BN) crystals, has been investigated by transmission electron microscopy in diffraction contrast and high resolution. We show that besides the GI, which is a general parameter for controlling the structural quality of h-EN ponders, some other microstructural features strongly influence the synthesis of c-BN. In our opinion, the high reactivity of some h-BN powders results from the presence of some nucleation centers for c-BN, observed at the edges of the h-BN particles. They are formed by a rearrangement of the graphitic (0002) planes by bending back, joining in pairs and forming locally nanoarches (half nanotubes). In these particular places, the nature of bonding locally turns towards sp(3), as in the case of c-BN, (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: Synchrotron radiation, high-resolution transmission electron microscopy (HRTEM), X-ray powder diffraction, and Raman spectroscopy were used to study the structure and thermal behavior of malayaite, CaSnSiO5. No indications of deviation from A2/a symmetry and no structural transitions were observed between 100 and 870 K. HRTEM revealed that the material is free of domains and antiphase boundaries. However, the lattice constants, cell volume, and Raman-active phonons show a thermal discontinuity near 500 K, which is possibly related to variation of the coordination sphere around the highly anisotropic Ca position.

Abstract: The ternary oxides Ba8Ta4Ti3O24 and Ba10Ta7.04Ti1.2O30 were synthesized and their crystal structures and defects were studied by means of X-ray powder diffraction, electron diffraction, and high resolution electron microscopy. The crystal structure of Ba8Ta4Ti3O24 is based on the 8H (cchc)(2) close-packed stacking (a 10.0314 Angstrom, c = 18.869 Angstrom, SG P6(3)/mcm, Z = 3) and that of Ba10Ta7.04Ti1.2O30 and on the 10H (cchcc)(2) close-packed stacking (a = 5.7981 Angstrom, c = 23.755 Angstrom, SG P6(3)/mmc, Z = 1) of BaO3 layers. The structural refinements gave the following values for the R factors for Ba8Ta4Ti3O24 (Ba10Ta7.04Ti1.2O30) R(I) = 0.041 (0.039), R(P) = 0.108 (0.118), and R(wP) = 0.094 (0.099). The main feature of both structures is the presence of two types of face-sharing octahedra (FSO) with different occupancies by Ta atoms, Ti atoms, and vacancies, which results in the formation of a superstructure. It was shown that in the Ba8Ta4Ti3O24 structure these pairs of FSO occur in an ordered fashion and in the Ba10Ta7.04Ti1.2O30 structure in a disordered fashion. The existence of the wide range of solid solutions was shown to be also a consequence of the presence of one of the two types of face-sharing octahedra. (C) 1995 Academic Press, Inc,

Abstract: The formation of Ni silicides is studied by transmission electron microscopy during in situ heating experiments of 12 nm Ni layers on blanket silicon, or in patterned structures covered with a thin chemical oxide. It is shown that the first phase formed is the NiSi2 which grows epitaxially in pyramidal crystals. The formation of NiSi occurs quite abruptly around 400 degreesC when a monosilicide layer covers the disilicide grains and the silicon in between. The NiSi phase remains stable up to 800 degreesC, at which temperature the layer finally fully transforms to NiSi2. The monosilicide grains show different epitaxial relationships with the Si substrate. Ni2Si is never observed. (C) 2001 American Institute of Physics.