Abstract: Twenty-seven glass fragments containing dark coloured grisaille paint layers of different qualities were collected from ten windows of the cathedral St. Michael & St. Gudule in Brussels (Belgium). The windows were made by J.-B. Capronnier (18141891) and cover the period between 1843 and 1878. The samples were cross-sectioned and examined in an electron microscope. Grisaille paint layers are not homogeneous and therefore, it is not meaningful to characterize them in terms of their average composition. Instead, parameters such as granularity, the number of residual gas bubbles per running millimetre of paint, the type of pigments, and the thickness of the paint layer were used to characterize them. The microscopic morphology allows a classification of the grisaille paint layers in four groups, every group associated with a quality level. Moreover, the main causes of the accelerated degradation of some of these paint layers could be explained. The classification made it possible to distinguish two periods in the work of Capronnier: (1) the early period (18431848) is characterized by the presence of either single granular paint layers or of double-layered systems consisting of a granular paint layer on top of a well-melted paint layer. The granular grisaille paint layers tend to pulverize; (2) the later period (18481878) is characterized by the presence of only well-vitrified paint layers. No sign of deterioration was found on the well-vitrified paint layers.

Abstract: Lignin determination in lignocellulose with the conventional two-step acid hydrolysis method is highly laborious and time-consuming. However, its quantification is crucial to monitor fungal pretreatment of wood, as the increase of acid-insoluble lignin (AIL) degradation linearly correlates with the achievable enzymatic saccharification yield. Therefore, in this study, a new attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy method was developed to track fungal delignification in an easy and rapid manner. Partial least square regression (PLSR) with cross-validation (CV) was applied to correlate the ATR-FTIR spectra with the AIL content (19.9%–27.1%). After variable selection and normalization, a PLSR model with a high coefficient of determination (

Abstract: We aimed to achieve improved instrumental sensitivity and detection limits for the analysis of several elements (Cu, Ni, Zn, Pb and Cd) in aqueous samples with energy dispersive X-ray fluorescence spectrometry (EDXRF). The metals were pre-concentrated from aqueous solutions using commercially available organic-based solid-phase extraction (SPE) disks functionalized with iminodiacetate groups. These thin-layer organic materials provide an ideal support for XRF analysis. The elements were collected on the SPE extraction disks using a simple filtration procedure (starting with 1 L of aqueous sample) that allows direct XRF measurements to be performed in the field (in situ). We evaluated the analytical possibilities and drawbacks of using this pre-concentration procedure in combination with the following XRF configurations: a handheld unit, a benchtop EDXRF system and a high-energy polarized-beam EDXRF instrument (HE-P-EDXRF). Using the HE-P-EDXRF system, the detection limits for all metals were more than one order of magnitude lower than those attained using handheld and benchtop EDXRF instrumentation. For the detection of metal concentrations higher than similar to 20 mu g/L, however, handheld or benchtop systems remain a very good option due to their extreme simplicity of operation and low-cost, compact design. We demonstrate the application of these methodologies, using the three equipment systems, to the analysis of trace concentrations of metals in different types of aqueous samples, including tap water and waste water. (C) 2011 Elsevier B.V. All rights reserved.

Abstract: A polynomial approach is applied for a number of data from the Posener-tables to calculate the values of the intensity distribution function of atomic absorption lines – H(a, 0.726a) – at the tabulated damping-parameter values with an error not worse than 0.044 %. For the resultant H(a, 0.726a) data, the ninth and sixth order polynomials can be fitted according to the damping parameter range of 0-2, and 2-10, respectively, which results in a minimal error of approximation. The derived functions are simply applicable to the calculation of any H(a, 0.726a) value belonging to a damping-parameter of any arbitrarily selected spectral line, implying the influence of Doppler- and Lorentz-broadening. The overall error of the described method is lower than 0.4 %.

Abstract: The control of damage to individual environmental particles by a laser beam during Raman spectroscopy carried out in ambient air is generally well understood. The nature and control of damage under vacuum conditions (e.g. in the scanning electron microscopy with energy X-ray detection combined with micro-Raman spectroscopyinterfaced SEM-EDX/MRS) are more complex and less well comprehended. The physical and chemical processes that affect the damage caused to small particles by lasers still remain somewhat unclear, but certainly the atmosphere (vacuum/air) and the beam intensity have very significant influences. Furthermore, it has been determined that some particles (e.g. haematite), although stable under an electron beam, are damaged by the laser beam, hampering their analysis. Additionally, when simultaneous analyses by SEM/EDX and MRS are considered, the correct choice of the collection surface plays a crucial role. As a result, the following collection substrates were tested to determine their influence on the laser beam damage process to the particle: silver and aluminium foils and silicon wafers. A test study was performed using artificial examples of haematite (Fe2O3) particles. Exposure of Fe2O3 particles in vacuum to 514- and 785-nm laser radiation often leads to their melting, transformation and evaporation. The dependence of the damage caused by the laser beam on the particle structure is reported here. Molecular and crystallographic changes have also been revealed. Formation of magnetite (as an effect of re-crystallisation) and Raman inactive structures was detected.

Abstract: As swipe samples from enrichment activities typically contain uranium particles with a detectable amount of fluorine, the question was raised whether the analysis of fluorine in particles could complement the information on the uranium isotope ratios. For this, uranium oxyfluoride particles were prepared from the controlled hydrolysis of uranium hexafluoride (UF6). The relative amount of fluorine was characterized by scanning electron microscopy combined with energy-dispersive X-ray spectrometry (SEM-EDX), as well as ion-microprobe secondary ion mass spectrometry (IM-SIMS). Of particular interest was the assessment of the reduction of the amount of fluorine over time, and after exposure to UV-light and high temperatures. Micro-Raman spectrometry (MRS) was applied to look for differences in molecular structure between these various sample types. Both SEM-EDX and IM-SIMS showed a general reduction of the fluorine-to-uranium ratio after 12 years of storage. The exposure to UV-light and high temperatures was found to have accelerated the loss of fluorine. A distinct peak at 865 cm− 1 Raman shift was detected for the majority of particles analyzed by MRS. For the particles that were heat-treated, the Raman spectra were similar to the spectrum of U3O8. Although often large variations were observed between particles from the same sample, the three particle measurement techniques (IM-SIMS, SEM-EDX and MRS) showed some consistent trends. They therefore appear promising in terms of the ability to place bounds on particle age, as well as shedding light on the complex processes involved in UO2F2 particle ageing.