“Quantitative electron microscopy of (Bi,Pb)2Sr2Ca2Cu3O10+\delta/Ag multifilament tapes during initial stages of annealing”. Bals S, Verbeeck J, Van Tendeloo G, Liu Y-L, Grivel J-C, Journal of the American Ceramic Society 88, 431 (2005). http://doi.org/10.1111/j.1551-2916.2005.00094.x
Abstract: The microstructural and compositional evolution during initial annealing of a superconducting (Bi,Pb)(2)Sr2Ca2Cu3O10+delta/Ag tape is studied using quantitative transmission electron microscopy. Special attention is devoted to the occurrence of Pb-rich liquids, which are crucial for the Bi2Sr2CaCu2O8+delta to (Bi,Pb)(2)Sr2Ca2Cu3O10+delta transformation. Ca and/or Pb-rich (Bi,Pb)(2)Sr2CaCu2O8+delta grains dissolve into a liquid, which reacts with Ca-rich phases to increase the liquid's Ca-content. This leads to (Bi,Pb)(2)Sr2Ca2Cu3O10+delta formation. Apparently, a Ca/Sr ratio of around I is sufficient to keep (Bi,Pb)(2)Sr2Ca2Cu3O10+delta nucleation going. It is confirmed that Ag particles are transported from the Ag-sheath into the oxide core by the liquid and not by mechanical treatment of the tape.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.841
Times cited: 1
DOI: 10.1111/j.1551-2916.2005.00094.x
|
“Fundamental mechanisms responsible for the temperature coefficient of resonant frequency in microwave dielectric ceramics”. Zhang S, Sahin H, Torun E, Peeters F, Martien D, DaPron T, Dilley N, Newman N, Journal of the American Ceramic Society 100, 1508 (2017). http://doi.org/10.1111/JACE.14648
Abstract: The temperature coefficient of resonant frequency ((f)) of a microwave resonator is determined by three materials parameters according to the following equation: (f)=-(1/2 (epsilon) + 1/2 + (L)), where (L), (epsilon), and are defined as the linear temperature coefficients of the lattice constant, dielectric constant, and magnetic permeability, respectively. We have experimentally determined each of these parameters for Ba(Zn1/3Ta2/3)O-3, 0.8 at.% Ni-doped Ba(Zn1/3Ta2/3)O-3, and Ba(Ni1/3Ta2/3)O-3 ceramics. These results, in combination with density functional theory calculations, have allowed us to develop a much improved understanding of the fundamental physical mechanisms responsible for the temperature coefficient of resonant frequency, (f).
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.841
Times cited: 6
DOI: 10.1111/JACE.14648
|
“Effect of powder coating on stabilizer distribution in CeO2-stabilized ZrO2 ceramics”. Fang Pa, Gu H, Wang Pl, Van Landuyt J, Vleugels J, Van der Biest O;, Journal of the American Ceramic Society 88, 1929 (2005). http://doi.org/10.1111/j.1551-2916.2005.00342.x
Abstract: The phase and microstructure relationship of 12 mol% CeO2-stabilized ZrO2 ceramics prepared from coated powder was investigated using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy-dispersed Xray spectroscopy (EDS). As compared with the sample prepared with co-precipitated method, which exhibited a similar grain size distribution, the EDS analysis revealed that the powder coating induced a wide distribution of CeO2 solubility, which decreases monotonically with the increase of grain size. This variation of stabilizer content from grain to grain rendered many large grains in the monoclinic phase. Stronger cerium segregation to grain boundaries was observed between large grains, which often form thin amorphous films there. The inhomogeneous; CeO2 distribution keeps more tetragonal ZrO2 grains close to the phase boundary to facilitate the transforming toughness. Addition of an Al2O3 precursor in coated powders effectively raises the overall CeO2 stabilizer content in the grains and preserves more transformable tetragonal phase in the microstructure, which further enhanced the fracture toughness. The dependence of CeO2 solubility on grain size may be explained in a simple coating-controlled diffusion and growth process that deserves further investigation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.841
Times cited: 11
DOI: 10.1111/j.1551-2916.2005.00342.x
|
“Chemistry and structure of anion-deficient perovskites with translational interfaces”. Abakumov AM, Hadermann J, Van Tendeloo G, Antipov EV, Journal of the American Ceramic Society 91, 1807 (2008). http://doi.org/10.1111/j.1551-2916.2008.02351.x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.841
Times cited: 39
DOI: 10.1111/j.1551-2916.2008.02351.x
|