“Atomic scale characterization of supported and assembled nanoparticles”. Pauwels B, Yandouzi M, Schryvers D, Van Tendeloo G, Verschoren G, Lievens P, Hou M, van Swygenhoven H, , B8.3 (2001)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
“Atomic scale modeling of supported and assembled nanoparticles”. Zhurkin E, Hou M, van Swygenhoven H, Pauwels B, Yandouzi M, Schryvers D, Van Tendeloo G, Lievens P, Verschoren G, Kuriplach J, van Peteghem S, Segers D, Dauwe C, , B8.2 (2001)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
“Structural characterisation of nanostructured Ni3Al processed by inert gas condensation”. Yandouzi M, Pauwels B, Schryvers D, van Swygenhoven H, Van Tendeloo G, Defects and diffusion in metals 213/215, 19 (2003)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
“Structural characterization of nanostructured Ni3Al processed by inert gas condensation”. Yandouzi M, Pauwels B, Schryvers D, Van Swygenhoven H, Van Tendeloo G, Diffusion and defect data : solid state data : part A : defect and diffusion forum 213, 19 (2003)
Abstract: High-resolution transmission electron microscopy was performed on compacted Ni(3)Al nanostructured material prepared by the inert gas condensation technique. From electron diffraction data an incomplete L1(2) ordering of the crystallites is observed in the free particles as well as in the room temperature compacted samples. However, a completely ordered L1(2) structure with much bigger and well-defined crystallites exhibiting several defects is observed in material compacted and annealed at 773 K. Sharp crystallite boundaries as well as amorphous material and voids are observed in between crystallites in all samples, the former being dominant in the annealed material, the latter in the as-prepared one.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Deciphering the interactions between single arm dislocation sources and coherent twin boundary in nickel bi-crystal”. Samaee V, Dupraz M, Pardoen T, VAn Swygenhoven H, Schryvers D, Idrissi H, Nature Communications 12, 962 (2021). http://doi.org/10.1038/S41467-021-21296-Z
Abstract: The introduction of a well-controlled population of coherent twin boundaries (CTBs) is an attractive route to improve the strength ductility product in face centered cubic (FCC) metals. However, the elementary mechanisms controlling the interaction between single arm dislocation sources (SASs), often present in nanotwinned FCC metals, and CTB are still not well understood. Here, quantitative in-situ transmission electron microscopy (TEM) observations of these mechanisms under tensile loading are performed on submicron Ni bi-crystal. We report that the absorption of curved screw dislocations at the CTB leads to the formation of constriction nodes connecting pairs of twinning dislocations at the CTB plane in agreement with large scale 3D atomistic simulations. The coordinated motion of the twinning dislocation pairs due to the presence of the nodes leads to a unique CTB sliding mechanism, which plays an important role in initiating the fracture process at a CTB ledge. TEM observations of the interactions between non-screw dislocations and the CTB highlight the importance of the synergy between the repulsive force of the CTB and the back stress from SASs when the interactions occur in small volumes. Interactions of dislocations with coherent twin boundaries contribute to strength and ductility in metals, but investigating the interaction mechanisms is challenging. Here the authors unravel these mechanisms through quantitative in-situ transmission electron microscopy observations in nickel bi-crystal samples under tensile loading.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
DOI: 10.1038/S41467-021-21296-Z
|