“Immersion calorimetry as a tool to evaluate the catalytic performance of titanosilicate materials in the epoxidation of cyclohexene”. Vernimmen J, Guidotti M, Silvestre-Albero J, Jardim EO, Mertens M, Lebedev OI, Van Tendeloo G, Psaro R, Rodríguez-Reinoso F, Meynen V, Cool P, Langmuir: the ACS journal of surfaces and colloids 27, 3618 (2011). http://doi.org/10.1021/la104808v
Abstract: Different types of titanosilicates are synthesized, structurally characterized, and subsequently catalytically tested in the liquid-phase epoxidation of cyclohexene. The performance of three types of combined zeolitic/mesoporous materials is compared with that of widely studied Ti-grafted-MCM-41 molecular sieve and the TS-1 microporous titanosilicate. The catalytic test results are correlated with the structural characteristics of the different catalysts. Moreover, for the first time, immersion calorimetry with the same substrate molecule as in the catalytic test reaction is applied as an extra means to interpret the catalytic results. A good correlation between catalytic performance and immersion calorimetry results is found. This work points out that the combination of catalytic testing and immersion calorimetry can lead to important insights into the influence of the materials structural characteristics on catalysis. Moreover, the potential of using immersion calorimetry as a screening tool for catalysts in epoxidation reactions is shown.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.833
Times cited: 19
DOI: 10.1021/la104808v
|
|
|
“Implementation of micro-ball nanodiamond anvils for high-pressure studies above 6 Mbar”. Dubrovinsky L, Dubrovinskaia N, Prakapenka VB, Abakumov AM, Nature communications 3, 1163 (2012). http://doi.org/10.1038/ncomms2160
Abstract: Since invention of the diamond anvil cell technique in the late 1950s for studying materials at extreme conditions, the maximum static pressure generated so far at room temperature was reported to be about 400 GPa. Here we show that use of micro-semi-balls made of nanodiamond as second-stage anvils in conventional diamond anvil cells drastically extends the achievable pressure range in static compression experiments to above 600 GPa. Micro-anvils (10-50 mu m in diameter) of superhard nano-diamond (with a grain size below similar to 50 nm) were synthesized in a large volume press using a newly developed technique. In our pilot experiments on rhenium and gold we have studied the equation of state of rhenium at pressures up to 640 GPa and demonstrated the feasibility and crucial necessity of the in situ ultra high-pressure measurements for accurate determination of material properties at extreme conditions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 150
DOI: 10.1038/ncomms2160
|
|
|
“Importance of twinning in static and dynamic compression of a Ti-6Al-4V titanium alloy with an equiaxed microstructure”. Coghe F, Tirry W, Rabet L, Schryvers D, Van Houtte P, Materials science and engineering: part A: structural materials: properties, microstructure and processing 537, 1 (2012). http://doi.org/10.1016/j.msea.2011.12.047
Abstract: Whereas deformation twinning is known to be an important deformation mechanism for hexagonal materials like magnesium and pure titanium, so far almost no literature exists on the twinning behaviour of the Ti-6Al-4V alloy. In this work it was shown that the activation of twinning as a deformation mechanism could have a pronounced effect on the mechanical behaviour of the Ti-6Al-4V alloy. This effect is even more pronounced under dynamic loading conditions. Transmission electron microscopy showed that only the {1 0 1 2}{1 0 1 1} tensile twin system was activated under certain loading conditions. Light-optical microscopy and electron backscatter diffraction data were afterwards used to experimentally determine the twin fractions. The importance of twinning for the texture evolution was also studied. It was shown that even small twin fractions can lead to distinct texture features, especially due to the discrete reorientation of the c-axes. The experimental results were compared to simulated results that were obtained with a viscoplastic self-consistent crystal plasticity code, after experimental validation that twinning can be reliably modelled as a unidirectional slip system. Although good agreement was obtained for the experimental and simulated stress-strain curves, the simulated results concerning twinning correlated well only on a qualitative basis as the simulated twin fractions were systematically higher than the experimental fractions. This seems to strengthen the hypothesis made by other research groups that complete grains might reorient by twinning. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 35
DOI: 10.1016/j.msea.2011.12.047
|
|
|
“Improved multislice calculations for including higher-order Laue zones effects”. Lobato I, van Dyck D, Ultramicroscopy 119, 63 (2012). http://doi.org/10.1016/j.ultramic.2012.01.003
Abstract: A new method for including higher-order Laue zones (HOLZs) effects in an efficient way in electron scattering simulations has been developed and tested by detail calculations. The calculated results by the conventional multislice (CMS) method and the improved conventional multislice (ICMS) method using a large dynamical aperture to avoid numerical errors are compared with accurate results. We have found that the zero-order Laue zones (ZOLZs) reflection cannot be properly described only using the projected potential in the whole unit cell; in general, we need to subslice the electrostatic potential inside the unit cell. It is shown that the ICMS method has higher accuracy than the CMS method for the calculation of the ZOLZ, HOLZ and Pseudo-HOLZ reflections. Hence, ICMS method allows to use a larger slice thickness than the CMS method and reduces the calculation time. (C) 2012 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 6
DOI: 10.1016/j.ultramic.2012.01.003
|
|
|
“Improvement of the oxidation stability and the mechanical properties of flexible graphite foil by boron oxide impregnation”. Savchenko DV, Serdan AA, Morozov VA, Van Tendeloo G, Ionov SG, New carbon materials 27, 12 (2012). http://doi.org/10.1016/S1872-5805(12)60001-8
Abstract: Flexible graphite foil produced by rolling expanded graphite impregnated with boron oxide was analyzed by laser mass spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy and thermogravimetry. It was shown that the modification of the graphite foil by boron oxide increases the onset temperature of oxidation by ∼ 150 °C. Impregnation of less than 2 mass% boron oxide also increased the tensile strength of the materials. The observed improvement was attributed to the blocking of active sites by boron oxide, which is probably chemically bonded to the edges of graphene sheets in expanded graphite particles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
DOI: 10.1016/S1872-5805(12)60001-8
|
|
|
“In situ high resolution electron microscopy observation of electron-irradiation-induced martensitic transformation in a Ni63Al37 alloy”. Muto S, Schryvers D, Journal of alloys and compounds 199, 1 (1993). http://doi.org/10.1016/0925-8388(93)90422-J
Abstract: An electron-irradiation-induced transformation from cubic beta2 austenite to monoclinic 7M martensite was observed in situ under high resolution electron microscopy conditions in a thin foil of Ni63Al37 beta2 phase (B2, CsCl structure), with the start temperature of the martensitic transformation below but very close to room temperature. The structure of the martensite is consistent with thermoelastic or stress-induced martensite at this composition, including the existence of multiple stacking faults. The transformation is described by a gradual increase in the shear and shuffle amplitudes already existing in the precursor domains. Possible origins of the transformation are discussed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.999
Times cited: 8
DOI: 10.1016/0925-8388(93)90422-J
|
|
|
“In situ HREM irradiation study of point-defect clustering in MBE-grown strained Si1-xGex/(001)Si structures”. Fedina L, Lebedev OI, Van Tendeloo G, van Landuyt J, Mironov OA, Parker EHC, Physical review : B : condensed matter and materials physics 61, 10336 (2000). http://doi.org/10.1103/PhysRevB.61.10336
Abstract: We present a detailed analysis of the point-defect clustering in strained Si/Si(1-x)Ge(x)/(001)Si structures, including the interaction of the point defects with the strained interfaces and the sample surface during 400 kV electron irradiation at room temperature. Point-defect cluster formation is very sensitive to the type and magnitude of the strain in the Si and Si(1-x)Ge(x) layers. A small compressive strain (-0.3%) in the SiGe alloy causes an aggregation of vacancies in the form of metastable [110]-oriented chains. They are located on {113} planes and further recombine with interstitials. Tensile strain in the Si layer causes an aggregation of interstitial atoms in the forms of additional [110] rows which are inserted on {113} planes with [001]-split configurations. The chainlike configurations are characterized by a large outward lattice relaxation for interstitial rows (0.13 +/-0.01 nm) and a very small inward relaxation for vacancy chains (0.02+/-0.01 nm). A compressive strain higher than -0.5% strongly decreases point-defect generation inside the strained SiGe alloy due to the large positive value of the formation volume of a Frenkel pair. This leads to the suppression of point-defect clustering in a strained SiGe alloy so that SiGe relaxes via a diffusion of vacancies from the Si layer, giving rise to an intermixing at the Si/SiGe interface. In material with a 0.9% misfit a strongly increased flow of vacancies from the Si layer to the SiGe layer and an increased biaxial strain in SiGe bath promote the preferential aggregation of vacancies in the (001) plane, which relaxes to form intrinsic 60 degrees dislocation loops.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 27
DOI: 10.1103/PhysRevB.61.10336
|
|
|
“In-situ HREM irradiation study of point defect clustering in strained GexSi1-x/(001)Si heterostructure”. Fedina L, Lebedev OI, Van Tendeloo G, van Landuyt J, Conference series of the Institute of Physics 157, 55 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
|
|
|
“In-situ HREM observation of electron-irradation-induced martensitic transformation in a Ni63Al37 alloy”. Muto S, Schryvers D, Journal of alloys and compounds 199, 1 (1993)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.999
Times cited: 8
|
|
|
“In situ HREM study of electron irradiation effects in AgCl microcrystals”. Goessens C, Schryvers D, de Keyzer R, van Landuyt J Eurem 92, Granada, page 646 (1992).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“In situ HREM study of electron irradiation effects in AgCl microcrystals”. Goessens C, Schryvers D, van Landuyt J, de Keyzer R, Ultramicroscopy 40, 151 (1992). http://doi.org/10.1016/0304-3991(92)90056-P
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.436
Times cited: 10
DOI: 10.1016/0304-3991(92)90056-P
|
|
|
“In-situ HVEM study of dislocation generation in patterned stress fields at silicon surfaces”. Vanhellemont J, Claeys C, van Landuyt J, Physica status solidi: A: applied research 150, 497 (1995). http://doi.org/10.1002/pssa.2211500144
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1002/pssa.2211500144
|
|
|
“A La2−xGdxZr2O7layer deposited by chemical solution: a promising seed layer for the fabrication of high Jcand low cost coated conductors”. Muguerra H, Pescheux A-C, Meledin A, Van Tendeloo G, Soubeyroux J-L, Journal of materials chemistry C : materials for optical and electronic devices 3, 11766 (2015). http://doi.org/10.1039/C5TC03365A
Abstract: We deposited La2-xGdxZr2O7 seed layers by a chemical solution method on a Ni-5%W substrate to study the influence of these layers on the growth process of a 60 nm-thick La2Zr2O7 layer. We measured the performances of these new buffer layers integrated in a coated conductor with a 300 nm-thick Y0.5Gd0.5Ba2Cu3O7-x layer. For the seed layers{,} we considered two different gadolinium contents (x = 0.2 and x = 0.8) and three different thicknesses for these compositions (20 nm{,} 40 nm{,} and 60 nm). The most promising buffer layer stacks are those with 20 nm of the La1.8Gd0.2Zr2O7 layer or La1.2Gd0.8Zr2O7. Indeed the La2-xGdxZr2O7/La2Zr2O7 films are highly textured{,} similar to a 100 nm-thick La2Zr2O7 layer{,} but their roughness is four times lower. Moreover they contain less and smaller pores in the seed layer than a pure La2Zr2O7 layer. The surface of La2Zr2O7 is also homogenous and crystalline with an orientation deviation from the ideal ?011? (100) direction below 10[degree]. With the 20 nm La2-xGdxZr2O7 seed layers we obtain in the coated conductors an efficiently textured transfer with no gradual degradation from the substrate throughout the superconducting layer. The highest Tc and Jc values are achieved with the La1.8Gd0.2Zr2O7 layer and are{,} respectively{,} 91 K and 1.4 MA cm-2. This trend seems to be due to an improvement of the surface quality of the Ni5%W substrate by the addition of a thin seed layer. Our results offer the potential of the La2-xGdxZr2O7 seed layers as promising alternatives for the classic Ni-5%W/LZO/CeO2/YBCO architectures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.256
Times cited: 4
DOI: 10.1039/C5TC03365A
|
|
|
“In situ investigation of the fast microstructure evolution during electropulse treatment of cold drawn NiTi wires”. Malard B, Pilch J, Sittner P, Delville R, Curfs C, Acta materialia 59, 1542 (2011). http://doi.org/10.1016/j.actamat.2010.11.018
Abstract: Microstructural changes taking place during the heat treatment of cold-worked NiTi alloy are of key interest in shape memory alloy technology, since they are responsible for setting the austenite shape and functional properties of the heat-treated alloy. In this work, microstructural evolution during non-conventional electropulse heat treatment of thin NiTi filaments was investigated in a unique high-speed in situ synchrotron X-ray diffraction experiment with simultaneous evaluation of the tensile force and electrical resistivity of the treated wire. The in situ results provide direct experimental evidence on the evolution of the internal stress and density of defects during fast heating from 20 °C to ∼700 °C. This evidence is used to characterize a sequence of dynamic recovery and recrystallization processes responsible for the microstructure and superelastic functional property changes during the electropulse treatments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 48
DOI: 10.1016/j.actamat.2010.11.018
|
|
|
“In situ study of the phase transition in Bi2Ti4O11”. Nistor L, Van Tendeloo G, Amelinckx S, Kahlenberg V, Böhm H, Journal of solid state chemistry 119, 281 (1995). http://doi.org/10.1016/0022-4596(95)80042-N
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 10
DOI: 10.1016/0022-4596(95)80042-N
|
|
|
“In-situ TEM study of the Ni5Al3 to B2 + L12 decomposition in Ni65Al35”. Schryvers D, Ma Y, Materials letters 23, 105 (1995). http://doi.org/10.1016/0167-577X(95)00030-5
Abstract: Homogenised and quenched Ni65Al35 samples were heated and studied in situ in a CM20 electron microscope up to 900 degrees C. The Ni5Al3 phase first forming around 550 degrees C in the quenched L1(0) microtwinned martensite starts to decompose around 800 degrees C yielding B2 precipitates in a twinned L1(2) matrix. The latter twinning is a remainder of the microtwinning in the original room temperature martensite. Also the crystallographic relations between precipitates and matrix can be traced back to the original formation of twinned martensite plates within the austenite. Some aspects of the dynamics of the process are discussed on the basis of snap shots and video recordings.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.489
Times cited: 5
DOI: 10.1016/0167-577X(95)00030-5
|
|
|
“In situ transmission electron microscopy of stress-induced martensite with focus on martensite twinning”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 420 (2008). http://doi.org/10.1016/j.msea.2006.12.214
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 22
DOI: 10.1016/j.msea.2006.12.214
|
|
|
“In situ transmission electron microscopy study of Ni silicide phases formed on (001) Si active lines”. Teodorescu V, Nistor L, Bender H, Steegen A, Lauwers A, Maex K, van Landuyt J, Journal of applied physics 90, 167 (2001). http://doi.org/10.1063/1.1378812
Abstract: The formation of Ni silicides is studied by transmission electron microscopy during in situ heating experiments of 12 nm Ni layers on blanket silicon, or in patterned structures covered with a thin chemical oxide. It is shown that the first phase formed is the NiSi2 which grows epitaxially in pyramidal crystals. The formation of NiSi occurs quite abruptly around 400 degreesC when a monosilicide layer covers the disilicide grains and the silicon in between. The NiSi phase remains stable up to 800 degreesC, at which temperature the layer finally fully transforms to NiSi2. The monosilicide grains show different epitaxial relationships with the Si substrate. Ni2Si is never observed. (C) 2001 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 97
DOI: 10.1063/1.1378812
|
|
|
“In situ transmission electron microscopy study of the silicidation process in Co thin films on patterned (001) Si substrates”. Ghica C, Nistor L, Bender H, Steegen A, Lauwers A, Maex K, van Landuyt J, Journal of materials research 16, 701 (2001). http://doi.org/10.1557/JMR.2001.0121
Abstract: The results of an in situ transmission electron microscopy study of the formation of Co-silicides on patterned (001) Si substrates are discussed. It is shown that the results of the in situ heating experiments agreed very well with the data based on standard rapid thermal annealing experiments. Fast heating rates resulted in better definition of the silicide lines. Also, better lines were obtained for samples that received already a low-temperature ex situ anneal. A Ti cap layer gave rise to a higher degree of epitaxy in the CoSi2 silicide.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.673
Times cited: 4
DOI: 10.1557/JMR.2001.0121
|
|
|
“InAs p-n diodes grown on GaAs and GaAs-coated Si by molecular beam epitaxy”. Dobbelaere W, de Boeck J, Heremans P, Mertens R, Borghs G, Luyten W, van Landuyt J, Applied physics letters 60, 868 (1992). http://doi.org/10.1063/1.106490
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.302
Times cited: 20
DOI: 10.1063/1.106490
|
|
|
“InAs0.85Sb0.15 infrared photodiodes grown on GaAs and GaAs-coated Si by molecular beam epitaxy”. Dobbelaere W, de Boeck J, Heremans P, Mertens R, Borghs G, Luyten W, van Landuyt J, Applied physics letters 600, 3256 (1992). http://doi.org/10.1063/1.106711
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.302
Times cited: 32
DOI: 10.1063/1.106711
|
|
|
“Inclusions in magnetron sputtered YBa2Cu3-x MxO7-d thin films: a study by means of electron microscopy”. Verbist K, Van Tendeloo G, Ye M, Schroeder J, Mehbod M, Deltour R, Microscopy, microanalysis, microstructures 7, 17 (1996). http://doi.org/10.1051/mmm:1996104
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1051/mmm:1996104
|
|
|
“Incommensurate crystallographic shear structures and magnetic properties of the cation deficient perovskite (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29”. Malo S, Lepoittevin C, Pérez O, Hébert S, Van Tendeloo G, Hervieu M, Chemistry of materials 22, 1788 (2010). http://doi.org/10.1021/cm903288s
Abstract: The origin of the incommensurability in the crystallographic shear (CS) structure of the ferri-Manganite (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29, related to the cation deficient perovskite, has been determined by careful analysis of the boundaries between the two variants constituting the phasoid. High Resolution Electron Microscopy/HAADF-STEM images allow the structural mechanisms to be understood through the presence of structural units common to both phases, responsible of the incommensurate character observed in the electron diffraction patterns. The structural analysis allows for identifying different types of CS phases in the Pb−Sr−Fe(Mn)−O diagram and shows that the stabilization of the six-sided tunnels requires a higher A/B cationic ratio. A description of these phases is proposed through simple structural building units (SBU), based on chains of octahedra bordered by two pyramids. The (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29 CS compound exhibits a strong antiferromagnetic and insulating behavior, similar to the Fe-2201 and terrace ferrites but differs by the presence of a hysteresis, with a small coercive field.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/cm903288s
|
|
|
“Incommensurate modulation and luminescence in the CaGd2(1-x)Eu2x(MoO4)4(1-y)(WO)4y (0\leq x\leq1, 0\leq y\leq1) red phosphors”. Morozov VA, Bertha A, Meert KW, Van Rompaey S, Batuk D, Martinez GT, Van Aert S, Smet PF, Raskina MV, Poelman D, Abakumov AM, Hadermann J;, Chemistry of materials 25, 4387 (2013). http://doi.org/10.1021/cm402729r
Abstract: Scheelite related compounds (A',A '') [(B',B '')O-4], with B', B '' = W and/or Mo are promising new light-emitting materials for photonic applications, including phosphor converted LEDs (light-emitting diodes). In this paper, the creation and ordering of A-cation vacancies and the effect of cation substitutions in the scheelite-type framework are investigated as a factor for controlling the scheelite-type structure and luminescent properties. CaGd2(1-x)Eu2x(MoO4)(4(1-y))(WO4)(4y) (0 <= x <= 1, 0 <= y <= 1) solid solutions with scheelite-type structure were synthesized by a solid state method, and their structures were investigated using a combination of transmission electron microscopy techniques and powder X-ray diffraction. Within this series all complex molybdenum oxides have (3 + 2)D incommensurately modulated structures with superspace group I4(1)/a(alpha,beta,0)00(-beta,alpha,0)00, while the structures of all tungstates are (3 + 1)D incommensurately modulated with superspace group I2/b(alpha beta 0)00. In both cases the modulation arises because of cation-vacancy ordering at the A site. The prominent structural motif is formed by columns of A-site vacancies running along the c-axis. These vacant columns occur in rows of two or three aligned along the [110] direction of the scheelite subcell. The replacement of the smaller Gd3+ by the larger Eu3+ at the A-sublattice does not affect the nature of the incommensurate modulation, but an increasing replacement of Mo6+ by W6+ switches the modulation from (3 + 2)D to (3 + 1)D regime. Thus, these solid solutions can be considered as a model system where the incommensurate modulation can be monitored as a function of cation nature while the number of cation vacancies at the A sites remain constant upon the isovalent cation replacement. All compounds' luminescent properties were measured, and the optical properties were related to the structural properties of the materials. CaGd2(1-x)(MoO4)(4(1-y))(WO4)(4y) phosphors emit intense red light dominated by the D-5(0)-F-7(2) transition at 612 nm, along with other transitions from the D-5(1) and D-5(0) excited states. The intensity of the 5D0-7F2 transition reaches a maximum at x = 0.5 for y = 0 and 1.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 63
DOI: 10.1021/cm402729r
|
|
|
“The incommensurate structure of (Sr, Ca)14Cu24O41: a study by electron diffraction and high-resolution microscopy”. Milat O, Van Tendeloo G, Amelinckx S, Mehbod M, Deltour R, Acta crystallographica A48, 618 (1992). http://doi.org/10.1107/S0108767392002204
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.307
Times cited: 22
DOI: 10.1107/S0108767392002204
|
|
|
“Incorporation and localization of substitutional Mn2+ ions in cubic ZnS quantum dots”. Nistor SV, Stefan M, Nistor LC, Goovaerts E, Van Tendeloo G, Physical review : B : condensed matter and materials physics 81, 035336 (2010). http://doi.org/10.1103/PhysRevB.81.035336
Abstract: Multifrequency electron paramagnetic resonance (EPR) and high resolution transmission electron microscopy (HRTEM) investigations were performed on small (2 nm) cubic ZnS nanocrystals (quantum dotsQDs) doped with 0.2% mol Mn2+, self-assembled into a mesoporous structure. The EPR data analysis shows that the substitutional Mn2+ ions are localized at Zn2+ sites subjected to a local axial lattice distortion, resulting in the observed zero-field-splitting parameter |D|=41×10−4 cm−1. The local distortion is attributed to the presence in the second shell of ligands of a stacking fault or twin, which alters the normal stacking sequence of the cubic structure. The HRTEM results confirm the presence of such extended planar defects in a large percentage of the investigated QDs, which makes possible the proposed substitutional Mn2+ impurity ions localization model. Based on these results it is suggested that the high doping levels of Mn2+ ions observed in cubic ZnS and possible in other II-VI semiconductor QDs prepared at low temperatures can be explained by the assistance of the extended lattice defects in the impurities incorporation.
Keywords: A1 Journal article; Nanostructured and organic optical and electronic materials (NANOrOPT); Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 55
DOI: 10.1103/PhysRevB.81.035336
|
|
|
“Incorporation of pure fullerene into organoclays : towards C60-pillared clay structures”. Tsoufis T, Georgakilas V, Ke X, Van Tendeloo G, Rudolf P, Gournis D, Chemistry: a European journal 19, 7937 (2013). http://doi.org/10.1002/chem.201300164
Abstract: In this work, we demonstrate the successful incorporation of pure fullerene from solution into two-dimensional layered aluminosilicate minerals. Pure fullerenes are insoluble in water and neutral in terms of charge, hence they cannot be introduced into the clay galleries by ion exchange or intercalation from water solution. To overcome this bottleneck, we organically modified the clay with quaternary amines by using well-established reactions in clay science in order to expand the interlayer space and render the galleries organophilic. During the reaction with the fullerene solution, the organic solvent could enter into the clay galleries, thus transferring along the fullerene molecules. Furthermore, we demonstrate that the surfactant molecules, can be selectively removed by either simple ion-exchange reaction (e.g., interaction with Al(NO3)3 solution to replace the surfactant molecules with Al3+ ions) or thermal treatment (heating at 350 °C) to obtain novel fullerene-pillared clay structures exhibiting enhanced surface area. The synthesized hybrid materials were characterized in detail by a combination of experimental techniques including powder X-ray diffraction, transmission electron microscopy, X-ray photoemission, and UV/Vis spectroscopy as well as thermal analysis and nitrogen adsorptiondesorption measurements. The reported fullerene-pillared clay structures constitute a new hybrid system with very promising potential for the use in areas such as gas storage and/or gas separation due to their high surface area.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 3
DOI: 10.1002/chem.201300164
|
|
|
“Increasing the solubility limit for tetrahedral aluminium in ZnO:Al nanorods by variation in synthesis parameters”. Kelchtermans A, Adriaensens P, Slocombe D, Kuznetsov VL, Hadermann J, Riskin A, Elen K, Edwards PP, Hardy A, Van Bael MK, Journal of nanomaterials 2015, 1 (2015). http://doi.org/10.1155/2015/546041
Abstract: Nanocrystalline ZnO:Al nanoparticles are suitable building blocks for transparent conductive layers. As the concentration of substitutional tetrahedral Al is an important factor for improving conductivity, here we aim to increase the fraction of substitutional Al. To this end, synthesis parameters of a solvothermal reaction yielding ZnO:Al nanorods were varied. A unique set of complementary techniques was combined to reveal the exact position of the aluminium ions in the ZnO lattice and demonstrated its importance in order to evaluate the potential of ZnO:Al nanocrystals as optimal building blocks for solution deposited transparent conductive oxide layers. Both an extension of the solvothermal reaction time and stirring during solvothermal treatment result in a higher total tetrahedral aluminium content in the ZnO lattice. However, only the longer solvothermal treatment effectively results in an increase of the substitutional positions aimed for.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.871
Times cited: 2
DOI: 10.1155/2015/546041
|
|
|
“Indifference of superconductivity and magnetism to size-mismatched cations in the layered iron arsenides Ba1-xNaxFe2As2”. Cortes-Gil R, Parker DR, Pitcher MJ, Hadermann J, Clarke SJ, Chemistry of materials 22, 4304 (2010). http://doi.org/10.1021/cm100956k
Abstract: The evolution of the structure, magnetic ordering, and superconductivity in the series Ba(1-x)Na(x)Fe(2)As(2) is reported up to the limiting Na-rich composition with x = 0.6; the more Na-rich compositions are unstable at high temperatures with respect to competing phases. The magnetic and superconducting behaviors of the Bai,Na,Fe,As, members are similar to those of the betterinvestigated Ba(1-x)Na(x)Fe(2)As(2) analogues. This is evidently a consequence of the quantitatively similar evolution of the structure of the FeAs layers in the two series. In Ba(1-x)Na(x)Fe(2)As(2) antiferromagnetic order and an associated structural distortion are evident for x <= 0.35 and superconductivity is evident when x exceeds 0.2. For 0.4 <= x <= 0.6 bulk superconductivity is evident, and the long-range antiferromagnetically ordered state is completely suppressed. The maximum T(c) in the Ba(1-x)Na(x)Fe(2)As(2) series, as judged by the onset of diamagnetism, is 34K in Ba(0.6)Na(0.4)Fe(2)As(2). Despite the large mis-match in sizes between the two electropositive cations which separate the FeAs layers, there is no evidence for ordering of these cations on the length scale probed by electron diffraction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 31
DOI: 10.1021/cm100956k
|
|
|
“Inducing superconductivity and structural transformations by fluorination of reduced YBCO”. Shpanchenko RV, Rozova MG, Abakumov AM, Ardashnikova EI, Kovba ML, Putilin SN, Antipov EV, Lebedev OI, Van Tendeloo G, Physica: C : superconductivity 280, 272 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 35
|
|