“Crystal structure of a lightweight borohydride from submicrometer crystallites by precession electron diffraction”. Hadermann J, Abakumov A, Van Rompaey S, Perkisas T, Filinchuk Y, Van Tendeloo G, Chemistry of materials 24, 3401 (2012). http://doi.org/10.1021/cm301548k
Abstract: We demonstrate that precession electron diffraction at low-dose conditions can be successfully applied for structure analysis of extremely electron-beam-sensitive materials. Using LiBH4 as a test material, complete structural information, including the location of the H atoms, was obtained from submicrometer-sized crystallites. This demonstrates for the first time that, where conventional transmission electron microscopy techniques fail, quantitative precession electron diffraction can provide structural information from submicrometer particles of such extremely electron-beam-sensitive materials as complex lightweight hydrides. We expect the precession electron diffraction technique to be a useful tool for nanoscale investigations of thermally unstable lightweight hydrogen-storage materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 17
DOI: 10.1021/cm301548k
|
|
|
“The crystal structure of \alpha-K3AIF6: elpasolites and double perovskites with broken corner-sharing connectivity of the octahedral framework”. Abakumov AM, King G, Laurinavichute VK, Rozova MG, Woodward PM, Antipov EV, Inorganic chemistry 48, 9336 (2009). http://doi.org/10.1021/ic9013043
Abstract: The crystal structure of α-K3AlF6 was solved and refined from a combination of powder X-ray and neutron diffraction data (a = 18.8385(3)Å, c = 33.9644(6)Å, S.G. I41/a, Z = 80, RP(X-ray) = 0.037, RP(neutron) = 0.053). The crystal structure is of the A2BB′X6 elpasolite type with the a = b ≈ ae√5, c = 4ae superstructure (ae, parameter of the elpasolite subcell) and rock-salt-type ordering of the K and Al cations over the B and B′ positions, respectively. The remarkable feature of α-K3AlF6 is a rotation of 2/5 of the AlF6 octahedra by π/4 around one of the crystal axes of the elpasolite subcell, coinciding with the 4-fold symmetry axes of the AlF6 octahedra. The rotation of the AlF6 octahedra replaces the corner-sharing between the K and Al polyhedra by edge-sharing, resulting in an increase of coordination numbers of the K cations at the B positions up to 7 and 8. Due to significant deformations of the K polyhedra, the corner-sharing connectivity of the octahedral elpasolite framework is broken and the rotations of the AlF6 octahedra do not have a cooperative character. Elpasolites and double perovskites with similar structural organization are discussed. The difference in ionic radii of the B and B′ cations as well as the tolerance factor are proposed to be the parameters governing the formation of elpasolites and double perovskites with broken corner-sharing connectivity of the octahedral framework.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 20
DOI: 10.1021/ic9013043
|
|
|
“The crystal structure of Ba8Ta6NiO24: cation ordering in hexagonal perovskites”. Abakumov AM, Van Tendeloo G, Scheglov AA, Shpanchenko RV, Antipov EV, Journal of solid state chemistry 125, 102 (1996). http://doi.org/10.1006/jssc.1996.0270
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 38
DOI: 10.1006/jssc.1996.0270
|
|
|
“Crystal structure of Bi6Sr8-xCa3+xO22(-0.5\leq x\leq1.7): a mixed valence bismuth oxide related to perovskite”. Luhrs CC, Molins E, Van Tendeloo G, Beltran-Porter D, Fuertes A, Chemistry of materials 10, 1875 (1998). http://doi.org/10.1021/cm9800377
Abstract: The crystal structure of BiSr8-xCa3+xO22 has been determined by single-crystal X-ray diffraction. This phase is the same as Bi9Sr11Ca5Oy that was previously studied by several authors as a secondary phase in the Bi-Sr-Ca-Cu-O system and coexists in thermodynamic equilibrium with the superconductors Bi2Sr2CuO6 and Bi2Sr2CaCu2O8 It crystallizes in the monoclinic space group P2(1)/c, with cell parameters a 11.037(3) Angstrom, b = 5.971(2) Angstrom, c = 19.703(7) Angstrom, beta = 101.46(3)degrees Z = 2. The structure was solved by direct methods and full-matrix least-squares refinement. It is built up by perovskite-related blocks of composition [Sr8-xBi2Ca3+xO16] that intergrow with double rows [Bi4O6] running along b. The perovskite blocks are formed by groups of five octahedra that are shifted from each other 3/2 root 2a(p) along [110](p) (a(p) being the parameter of the cubic perovskite subcell) in a zigzag configuration and are aligned with this direction parallel to the one forming an angle of 25" with the c axis. In turn, the perovskite blocks [Sr8-xBi2Ca3+xO16] are shifted from each other 1/2 of both a(p) and root 2a(p) along [100](p) and [110](p), respectively. In the double rows, two trivalent bismuth atoms are placed, forming dimeric anion complexes [Bi2O6].(6-).6- The oxygen atoms around bismuth in these dimers are placed in the vertexes of a distorted trigonal bipyramid, with one vacant position that would be occupied by the lone pairs characteristic for the electronic configuration of Bi(III). The B sites in the perovskite blocks are occupied by pentavalent bismuth atoms and calcium atoms; the remaining Sr and Ca ions occupy the A sites of the perovskite blocks with coordination numbers with oxygen ranging from 10 to 12. The mean valence for Bi is +3.67 [33.3% of Bi(V) and 66.7% of Bi(III)]. The oxygen vacancies are located in the boundaries between domains having the two possible configurations of the perovskite subcell as in the anionic superconductor Bi3BaO5.5. The oxidation of Bi6Sr8-xCa3+xO22 at 650 degrees C allows the complete filling of the oxygen vacancies to form the double perovskite (Sr2-xCax)Bi1.4Ca0.6O6 that shows 92.5% of bismuth in +5 oxidation state. The experimental high-resolution electon microscopy image and the electron diffraction pattern of powder samples along the [010]* zone axis are in good agreement with those calculated from the structural model obtained by single-crystal X-ray diffraction. The material is almost free of defects and the occurrence of planar defects is very exceptional.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/cm9800377
|
|
|
“The crystal structure of Ca3ReO6”. Abakumov AM, Shpanchenko RV, Antipov EV, Lebedev OI, Van Tendeloo G, Journal of solid state chemistry 131, 305 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 10
|
|
|
“The crystal structure of YSr2Cu3O6+x determined by HREM”. Lebedev O, Van Tendeloo G, Marezio M, Licci F, Gilioli E, Gauzzi A, Prodi A s.l., page 877 (2002).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Crystal structure of the double Hg-layer copper oxide superconductor (Hg, Pr)2Ba2(Y, Ca)Cu2O8-\delta as a function of doping”. Radaelli PG, Marezio M, Tholence JL, de Brion S, Santoro A, Huang Q, Capponi JJ, Chaillout C, Krekels T, Van Tendeloo G, The journal of physics and chemistry of solids 56, 1471 (1995)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.853
Times cited: 16
|
|
|
“Crystal-structure of the double-hg-layer copper-oxide superconductor (Hg,Pr)2Ba2(Y,Ca)Cu2O8-\deltaas a function of doping”. Radaelli PG, Marezio M, Tholence JL, Debrion S, Santoro A, Huang Q, Capponi JJ, Chaillout C, Krekels T, Van Tendeloo G, The journal of physics and chemistry of solids 56, 1471 (1995). http://doi.org/10.1016/0022-3697(95)00084-4
Abstract: The crystal structure of the newly discovered double-Hg-layer copper oxide superconductor (Hg, Pr)(2)Ba-2(Y, Ca)Cu2O8-delta was studied as a function of chemical doping using neutron and electron diffraction and high-resolution transmission electron microscopy (HREM). Rietveld refinements of the structural parameters from neutron powder diffraction data indicate that the oxygen site O3 on the mercury plane is highly defective, being both partially occupied and displaced from the high-symmetry position. The variable concentration of oxygen vacancies partially compensates for the cation doping and, together with the O3 displacement field, makes some of the Hg atoms acquire an unusual pyramidal coordination. HREM images confirm that the structure is of the '2212' type, with very few defects. In some grains, faint superstructure reflections were evidenced by electron diffraction, suggesting that both the oxygen vacancies and the O3 displacement field may order at least on a local scale.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.853
Times cited: 16
DOI: 10.1016/0022-3697(95)00084-4
|
|
|
“Crystal structure of the group of optical materials Ln2MeGe4O12 (Me = Ca, Mn)”. Tarakina NV, Zubkov VG, Leonidov II, Tyutunnik AP, Surat LL, Hadermann J, Van Tendeloo G, Zeitschrift für Kristallographie , 401 (2009). http://doi.org/10.1524/zksu.2009.0059
Abstract: The crystal structure of the group of optical materials Ln2MeGe4O12, Ln = Eu, Gd, Dy-Lu, Y; Me = Ca, Mn and of the solid solution (Y1-xErx)2CaGe4O12 (x = 0 – 1), promising materials for photonics, has been studied in detail. The crystal structure of all compounds exhibit two alternating layers: one formed by Ln and Me atoms and another by cyclic [Ge4O12]8- anions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1524/zksu.2009.0059
|
|
|
“Crystal structure, phase transition, and magnetic ordering in perovskitelike Pb2-xBaxFe2O5 solid solutions”. Nikolaev IV, d' Hondt H, Abakumov AM, Hadermann J, Balagurov AM, Bobrikov IA, Sheptyakov DV, Pomjakushin VY, Pokholok KV, Filimonov DS, Van Tendeloo G, Antipov EV, Physical review : B : condensed matter and materials physics 78, 024426 (2008). http://doi.org/10.1103/PhysRevB.78.024426
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 29
DOI: 10.1103/PhysRevB.78.024426
|
|
|
“Crystal structure, polymorphism, and properties of the new vanadyl phosphate Na4VO(PO4)2”. Panin RV, Shpanchenko RV, Mironov AV, Velikodny YA, Antipov EV, Hadermann J, Tarnopolsky VA, Yaroslavtsev AB, Kaul EE, Geibel C, Chemistry of materials 16, 1048 (2004). http://doi.org/10.1021/cm0351543
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 11
DOI: 10.1021/cm0351543
|
|
|
“Crystal structures of superconducting sodium intercalates of hafnium nitride chloride”. Oró-Solé, J, Frontera C, Beltrán-Porter D, Lebedev OI, Van Tendeloo G, Fuertes A, Materials research bulletin 41, 934 (2006). http://doi.org/10.1016/j.materresbull.2006.03.018
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 8
DOI: 10.1016/j.materresbull.2006.03.018
|
|
|
“Crystalline and amorphous frameworks with giant pores: what information ca we expect from advanced TEM?”.Lebedev OI, Van Tendeloo G, Electron microscopy and multiscale modeling: proceedings of the AIP conference proceedings 999, 245 (2008)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Crystalline structure of very hard tungsten carbide thin films obtained by reactive pulsed laser deposition”. Mihailescu IN, Gyorgy E, Marin G, Popescu M, Teodorescu VS, van Landuyt J, Grivas C, Hatziapostolou A, Journal of vacuum science and technology: A: vacuum surfaces and films 17, 249 (1999). http://doi.org/10.1116/1.581579
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.374
Times cited: 8
DOI: 10.1116/1.581579
|
|
|
“Crystallization of fullerene nanopraticles in an aerosol flow reactor”. Joutsensaari J, Ahonen PP, Tapper U, Kauppinen EI, Pauwels B, Amelinckx S, Van Tendeloo G, (1999)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Crystallization of PZT in porous alumina membrane channels”. Zhigalina OM, Mishina ED, Sherstyuk NE, Vorotilov KA, Vasiljev VA, Sigov AS, Lebedev OI, Grigoriev YV, de Santo MP, Barberi R, Rasing T, Ferroelectrics 336, 247 (2006). http://doi.org/10.1080/00150190600697756
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.551
Times cited: 10
DOI: 10.1080/00150190600697756
|
|
|
“Crystallographic and magnetic characterisation of the brownmillerite Sr2Co2O5”. Sullivan E, Hadermann J, Greaves C, Journal of solid state chemistry 184, 649 (2011). http://doi.org/10.1016/j.jssc.2011.01.026
Abstract: Sr2Co2O5 with the perovskite-related brownmillerite structure has been synthesised via quenching, with the orthorhombic unit cell parameters a=5.4639(3) Å, b=15.6486(8) Å and c=5.5667(3) Å based on refinement of neutron powder diffraction data collected at 4 K. Electron microscopy revealed LRLR-intralayer ordering of chain orientations, which require a doubling of the unit cell along the c-parameter, consistent with the assignment of the space group Pcmb. However, on the length scale pertinent to NPD, no long-range order is observed and the disordered space group Imma appears more appropriate. The magnetic structure corresponds to G-type order with a moment of 3.00(4) μB directed along [1 0 0].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 19
DOI: 10.1016/j.jssc.2011.01.026
|
|
|
“Crystallographic and magnetic structures of Y0.8Sr2.2Mn2GaO8-\delta: a new vacancy-ordered perovskite structure”. Gillie LJ, Palmer HM, Wright AJ, Hadermann J, Van Tendeloo G, Greaves C, The journal of physics and chemistry of solids 65, 87 (2004). http://doi.org/10.1016/j.jpcs.2003.08.012
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.059
Times cited: 15
DOI: 10.1016/j.jpcs.2003.08.012
|
|
|
“Crystallographic aspects related to advanced tribological multilayers of Cr/CrN and Ti/TiN types produced by pulsed laser deposition (PLD)”. Major L, Morgiel J, Major B, Lackner JM, Waldhauser W, Ebner R, Nistor L, Van Tendeloo G, Surface and coatings technology 200, 6190 (2006). http://doi.org/10.1016/j.surfcoat.2005.11.021
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.589
Times cited: 32
DOI: 10.1016/j.surfcoat.2005.11.021
|
|
|
“Crystallographic aspects related to the high pressure-high temperature phase transformation of boron nitride”. Nistor LC, Van Tendeloo G, Dincã, G, Philosophical magazine 85, 1145 (2005). http://doi.org/10.1080/14786430412331325058
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.505
Times cited: 13
DOI: 10.1080/14786430412331325058
|
|
|
“Crystallographic shear structures as a route to anion-deficient perovskites”. Abakumov AM, Hadermann J, Bals S, Nikolaev IV, Antipov EV, Van Tendeloo G, Angewandte Chemie: international edition in English 45, 6697 (2006). http://doi.org/10.1002/anie.200602480
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 62
DOI: 10.1002/anie.200602480
|
|
|
“Crystallography of fullerites and related graphene textures”. van Landuyt J, Van Tendeloo G, Amelinckx S, Zhang XF, Zhang XB, Luyten W, Materials science forum 150/151, 53 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Cuprate/manganite superlattices: a model system for a bulk ferromagnetic superconductor”. Habermeier H-U, Cristiani G, Kremer RK, Lebedev O, Van Tendeloo G, Physica: C : superconductivity 364/365, 298 (2001). http://doi.org/10.1016/S0921-4534(01)00775-4
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 91
DOI: 10.1016/S0921-4534(01)00775-4
|
|
|
“CVD of copper oxides from a \beta-diketonate diamine precursor: tailoring the nano-organization”. Barreca D, Gasparotto A, Maccato C, Tondello E, Lebedev OI, Van Tendeloo G, Crystal growth &, design 9, 2470 (2009). http://doi.org/10.1021/cg801378x
Abstract: A copper(II) hexafluoroacetylacetonate (1,1,1,5,5,5-hexafluoro-2,4-pentanedionate, hfa) adduct with N,N,N¡ä,N¡ä-tetramethylethylenediamine (TMEDA) [Cu(hfa)2¡¤TMEDA] is used for the first time as precursor for the chemical vapor deposition (CVD) of copper oxide nanosystems. The syntheses are carried out under both O2 and O2+H2O reaction atmospheres on Si(100) substrates, at temperatures ranging between 250 and 550 ¡ãC. Subsequently, the interrelations between the preparative conditions and the system composition, nanostructure, and morphology are elucidated by means of complementary analytical techniques [Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron and X-ray excited auger electron spectroscopies (XPS and XE-AES), glancing incidence X-ray diffraction (GIXRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM)]. The obtained data revealed a gradual transformation from Cu2O, to Cu2O + CuO, to CuO nanosystems upon increasing the deposition temperature from 250 to 550 ¡ãC under both growth atmospheres. Such a phenomenon was accompanied by a progressive morphological evolution from continuous films to 1D hyperbranched nanostructures. Water vapor introduction in the deposition environment enabled to lower the deposition temperature and resulted in a higher aggregate interconnection, attributed to a higher density of nucleation centers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 60
DOI: 10.1021/cg801378x
|
|
|
“A cyclic catalyst pretreatment in CO2 for high yield production of Carbon nanofibers with narrow diameter distribution”. Corthals S, van Noyen J, Liang D, Ke X, Van Tendeloo G, Jacobs P, Sels B, Catalysis letters 141, 1621 (2011). http://doi.org/10.1007/s10562-011-0690-3
Abstract: This paper presents a cyclic catalyst pretreatment process to improve the CNF yield with narrow size distribution by sequentially feeding the CVD reactor with CH4/CO2 mixtures (carbon deposition) and CO2 (carbon removal) prior to the actual growth process. A mechanism based on a break-up of large Ni particles tentatively explains the beneficial effect of the cyclic carbon deposition/removal CVD procedure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.799
Times cited: 1
DOI: 10.1007/s10562-011-0690-3
|
|
|
“DART explained: how to carry out a discrete tomography reconstruction”. Batenburg KJ, Bals S, Sijbers J, Van Tendeloo G, , 295 (2008)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT); Vision lab
|
|
|
“Decomposition of a metastable bcc phase in rapidly solidified Ni-9 at.% Zr and Ni-8 at.%X alloys”. Chandrasekaran M, Ghosh G, Schryvers D, de Graef M, Delaey L, Van Tendeloo G, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 75, 677 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
|
|
|
“Decomposition phenomena in Ni-Mn-Ti austenite”. Schryvers D, Seo JW, Richard O, Vermeulen W, Potapov P s.l., page 887 (1999).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Deconvolution of core electron energy loss spectra”. Verbeeck J, Bertoni G, Ultramicroscopy 109, 1343 (2009). http://doi.org/10.1016/j.ultramic.2009.06.010
Abstract: Different deconvolution methods for removing multiple scattering and instrumental broadening from core loss electron energy loss spectra are compared with special attention to the artefacts they introduce. The Gaussian modifier method, Wiener filter, maximum entropy, and model based methods are described. Their performance is compared on virtual spectra where the true single scattering distribution is known. A test on experimental spectra confirms the good performance of model based deconvolution in comparison to maximum entropy methods and shows the advantage of knowing the estimated error bars from a single spectrum acquisition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 13
DOI: 10.1016/j.ultramic.2009.06.010
|
|
|
“Decorating carbon nanotubes with nickel nanoparticles”. Bittencourt C, Felten A, Ghijsen J, Pireaux J-J, Drube W, Erni R, Van Tendeloo G, Chemical physics letters 436, 368 (2007). http://doi.org/10.1016/j.cplett.2007.01.065
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 78
DOI: 10.1016/j.cplett.2007.01.065
|
|