“N-doped ordered mesoporous carbons prepared by a two-step nanocasting strategy as highly active and selective electrocatalysts for the reduction of O2 to H2O2”. Sheng X, Daems N, Geboes B, Kurttepeli M, Bals S, Breugelmans T, Hubin A, Vankelecom IFJ, Pescarmona PP, Applied catalysis : B : environmental 176-177, 212 (2015). http://doi.org/10.1016/j.apcatb.2015.03.049
Abstract: A new, two-step nanocasting method was developed to prepare N-doped ordered mesoporous carbon (NOMC) electrocatalysts for the reduction of O2 to H2O2. Our strategy involves the sequential pyrolysis of two inexpensive and readily available N and C precursors, i.e. aniline and dihydroxynaphthalene (DHN), inside the pores of a SBA-15 hard silica template to obtain N-doped graphitic carbon materials with well-ordered pores and high surface areas (764 and 877 m2g−1). By tuning the ratio of carbon sources to silica template, it was possible to achieve an optimal filling of the pores of the SBA-15 silica and to minimise carbon species outside the pores. These NOMC materials displayed outstanding electrocatalytic activity in the oxygen reduction reaction, achieving a remarkably enhanced kinetic current density compared to state-of-the-art N-doped carbon materials (−16.7 mA cm−2 at −0.35 V vs. Ag/AgCl in a 0.1 M KOH solution as electrolyte). The NOMC electrocatalysts showed high selectivity toward the two-electron reduction of oxygen to hydrogen peroxide and excellent long-term stability.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 9.446
Times cited: 111
DOI: 10.1016/j.apcatb.2015.03.049
|
|
|
“Nickel-containing N-doped carbon as effective electrocatalysts for the reduction of CO2 to CO in a continuous-flow electrolyzer”. Daems N, De Mot B, Choukroun D, Van Daele K, Li C, Hubin A, Bals S, Hereijgers J, Breugelmans T, Sustainable energy &, fuels 4, 1296 (2019). http://doi.org/10.1039/C9SE00814D
Abstract: Nickel-containing N-doped carbons were synthesized for the electrochemical reduction of CO2 to CO, which is a promising approach to reduce the atmospheric CO2 levels and its negative impact on the environment. Unfortunately, poor performance (activity, selectivity and/or stability) is still a major hurdle for the economical implementation of this type of materials. The electrocatalysts were prepared through an easily up-scalable and easily tunable method based on the pyrolysis of Ni-containing N-doped carbons. Ni–N–AC–B1 synthesized with a high relative amount of nitrogen and nickel with respect to carbon, was identified as the most promising candidate for this reaction based on its partial CO current density (4.2 mA cm−2), its overpotential (0.57 V) and its faradaic efficiency to CO (>99%). This results in unprecedented values for the current density per g active sites (690 A g−1 active sites). Combined with its decent stability and its high performance in an actual electrolyzer setup, this makes it a promising candidate for the electrochemical reduction of CO2 to CO on a larger scale. Finally, the evaluation of this kind of material in a flow-cell setup has been limited and to the best of our knowledge never included an evaluation of several crucial parameters (e.g. electrolyte type, anode composition and membrane type) and is an essential investigation in the move towards up-scaling and ultimately industrial application of this technique. This study resulted in an optimal cell configuration, consisting of Pt as an anode, Fumatech® as the membrane and 1 M KHCO3 and 2 M KOH as catholyte and anolyte, respectively. In conclusion, this research offers a unique combination of electrocatalyst development and reactor optimization.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Times cited: 14
DOI: 10.1039/C9SE00814D
|
|
|
“Enhanced CO2 electroreduction with metal-nitrogen-doped carbons in a continuous flow reactor”. Duarte M, Daems N, Hereijgers J, Arenas Esteban D, Bals S, Breugelmans T, Journal Of Co2 Utilization 50, 101583 (2021). http://doi.org/10.1016/J.JCOU.2021.101583
Abstract: As part of a mitigation and adaptation approach to increasing carbon dioxide atmospheric concentrations, we report superior performance of various metal-nitrogen-doped carbon catalysts, synthesized using an easily up-scalable method, for the electrochemical reduction to carbon monoxide and/or formate at industrially relevant current densities up to 200 mAcm−2. Altering the embedded transition metal (i.e. Sn, Co, Fe, Mn and Ni) allowed to tune the selectivity towards the desired product. Mn-N-C and Fe-N-C performance was compromised by its high CO* binding energy, while Co-N-C catalyzed preferentially the HER. Ni-N-C and Sn-N-C revealed to be promising electrocatalysts, the latter being evaluated for the first time in a flow reactor. A productivity of 589 L CO m-2 h-1 at -1.39 VRHE with Ni-N-C and 751 g HCOO- m-2 h-1 at -1.47 VRHE with Sn-N-C was achieved with no signs of degradation detected after 24 h of operation at industrially relevant current densities (100 mAcm−2). Stable operation at 200 mAcm−2 led to turnover frequencies for the production of carbon products of up to 5176 h-1. These enhanced productivities, in combination with high stability, constitute an essential step towards the scalability and ultimately towards the economical valorization of CO2 electrolyzers using metal-containing nitrogen-doped catalysts.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 4.292
Times cited: 14
DOI: 10.1016/J.JCOU.2021.101583
|
|
|
“Enhanced Pomegranate‐Structured SnO2Electrocatalysts for the Electrochemical CO2Reduction to Formate”. Daele KV, Arenas‐Esteban D, Choukroun D, Hoekx S, Rossen A, Daems N, Pant D, Bals S, Breugelmans T, ChemElectroChem (2023). http://doi.org/10.1002/celc.202201024
Abstract: Although most state-of-the-art Sn-based electrocatalysts yield promising results in terms of selectivity and catalyst activity, their stability remains insufficient to date. Here, we demonstrate the successful application of the recently developed pomegranate-structured SnO2 (Pom. SnO2) and SnO2@C (Pom. SnO2@C) nanocomposite electrocatalysts for the efficient electrochemical conversion of CO2 to formate. With an initial selectivity of 83 and 86% towards formate and an operating potential of -0.72 V and -0.64 V vs. RHE, respectively, these pomegranate SnO2 electrocatalysts are able to compete with most of the current state-of-the-art Sn-based electrocatalysts in terms of activity and selectivity. Given the importance of electrocatalyst stability, long-term experiments (24 h) were performed and a temporary loss in selectivity for the Pom. SnO2@C electrocatalyst was largely restored to its initial selectivity upon drying and exposure to air. Of all the used (24 h) electrocatalysts, the pomegranate SnO2@C had the highest selectivity over a time period of one hour, reaching an average recovered FE of 85%, while the commercial SnO2 and bare pomegranate SnO2 electrocatalysts reached an average of 79 and 80% FE towards formate, respectively. Furthermore, the pomegranate structure of Pom. SnO2@C was largely preserved due to the presence of the heterogeneous carbon shell, which acts as a protective layer, physically inhibiting particle segregation/pulverisation and agglomeration.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 4
DOI: 10.1002/celc.202201024
|
|
|
“Synergy or Antagonism? Exploring the Interplay of SnO2and an N-OMC Carbon Capture Medium for the Electrochemical CO2Reduction toward Formate”. Van Daele K, Balalta D, Hoekx S, Jacops R, Daems N, Altantzis T, Pant D, Breugelmans T, ACS Applied Energy Materials 7, 5517 (2024). http://doi.org/10.1021/acsaem.4c00994
Abstract: Closing the anthropogenic carbon cycle by means of the sustainable electrochemical CO2 reduction (eCO2R) toward formate (FA) is a promising strategy for CO2 abatement, clearing the path toward a carbon neutral future. Currently, three possible reaction pathways have been identified for the eCO2R toward FA, all of which are initiated by the adsorption of CO2 on the electrocatalyst’s surface. Therefore, a possible strategy to enhance the availability of CO2 near the active sites is to combine an active electrocatalyst material (here, SnO2) with a known carbon capture medium (here, nitrogen-doped ordered mesoporous carbon (N-OMC)). SnO2 was introduced in situ during the N-OMC synthesis, yielding SnO2-N-OMCs. We approached the state of the art for Sn-based N-doped carbon electrocatalysts in terms of performance under industrially relevant currents with an average FEFA of 59% for SnO2-N-OMC (6) and 61% for SnO2-N-OMC (2). Moreover, the SnO2-N-OMC electrocatalysts require a low overpotential, courtesy of the N-OMC support, compared to the state of the art, for the selective conversion of CO2 toward FA at the industrially relevant current density of 100 mA cm–2. Additionally, the 24 h stability of the best performing SnO2-N-OMC electrocatalysts is explored, and pulverization/agglomeration and in situ SnO2 reduction are identified as major degradation pathways, allowing future research to be steered more accurately toward more stable Sn-based electrocatalysts for the eCO2R toward FA. An optimal combination of both the SnO2 species and the N-OMC carbon capture medium could result in a synergistic effect, especially when utilization of the N-OMC support material is optimized to morphologically stabilize the SnO2 active species.
Keywords: A1 Journal Article; nitrogen-doped ordered mesoporous carbon, SnO2, degradation pathways, electrochemical CO2 reduction, formate; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 6.4
DOI: 10.1021/acsaem.4c00994
|
|
|
“Bifunctional nickel-nitrogen-doped-carbon-supported copper electrocatalyst for CO2 reduction”. Choukroun D, Daems N, Kenis T, Van Everbroeck T, Hereijgers J, Altantzis T, Bals S, Cool P, Breugelmans T, Journal Of Physical Chemistry C 124, 1369 (2020). http://doi.org/10.1021/ACS.JPCC.9B08931
Abstract: Bifunctionality is a key feature of many industrial catalysts, supported metal clusters and particles in particular, and the development of such catalysts for the CO2 reduction reaction (CO2RR) to hydrocarbons and alcohols is gaining traction in light of recent advancements in the field. Carbon-supported Cu nanoparticles are suitable candidates for integration in the state-of-the-art reaction interfaces, and here, we propose, synthesize, and evaluate a bifunctional Ni–N-doped-C-supported Cu electrocatalyst, in which the support possesses active sites for selective CO2 conversion to CO and Cu nanoparticles catalyze either the direct CO2 or CO reduction to hydrocarbons. In this work, we introduce the scientific rationale behind the concept, its applicability, and the challenges with regard to the catalyst. From the practical aspect, the deposition of Cu nanoparticles onto carbon black and Ni–N–C supports via an ammonia-driven deposition precipitation method is reported and explored in more detail using X-ray diffraction, thermogravimetric analysis, and hydrogen temperature-programmed reduction. High-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy-dispersive X-ray spectroscopy (EDXS) give further evidence of the presence of Cu-containing nanoparticles on the Ni–N–C supports while revealing an additional relationship between the nanoparticle’s composition and the electrode’s electrocatalytic performance. Compared to the benchmark carbon black-supported Cu catalysts, Ni–N–C-supported Cu delivers up to a 2-fold increase in the partial C2H4 current density at −1.05 VRHE (C1/C2 = 0.67) and a concomitant 10-fold increase of the CO partial current density. The enhanced ethylene production metrics, obtained by virtue of the higher intrinsic activity of the Ni–N–C support, point out toward a synergistic action between the two catalytic functionalities.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 3.7
Times cited: 24
DOI: 10.1021/ACS.JPCC.9B08931
|
|
|
“Size-controlled electrodeposition of Cu nanoparticles on gas diffusion electrodes in methanesulfonic acid solution”. Pacquets L, Irtem E, Neukermans S, Daems N, Bals S, Breugelmans T, Journal Of Applied Electrochemistry 51 (2020). http://doi.org/10.1007/S10800-020-01474-5
Abstract: In this paper electrodeposition is used to obtain Cu nanoparticles, as it allows good control over particle size and distribution. These Cu particles were deposited onto a gas diffusion electrode which increased the resulting surface area. Prior to deposition, the surface was pre-treated with NaOH, HNO3, MQ and TX100 to investigate the influence on the electrodeposition of Cu on the gas diffusion electrode (GDE). When using HNO3, the smallest particles with the most homogeneous distribution and high particle roughness were obtained. Once the optimal substrate was determined, we further demonstrated that by altering the electrodeposition parameters, the particle size and density could be tuned. On the one hand, increasing the nucleation potential led to a higher particle density resulting in smaller particles because of an increased competition between particles. Finally, the Cu particle size increased when applying a greater growth charge and growth potential. This fundamental study thus opens up a path towards the synthesis of supported Cu materials with increased surface areas, which is interesting from a catalytic point of view. Larger surface areas are generally correlated with a better catalyst performance and thus higher product yields. This research can contributed in obtaining new insides into the deposition of metallic nanoparticles on rough surfaces. [GRAPHICS] .
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 2.9
Times cited: 3
DOI: 10.1007/S10800-020-01474-5
|
|
|
“Use of nanoscale carbon layers on Ag-based gas diffusion electrodes to promote CO production”. Pacquets L, Van den Hoek J, Arenas Esteban D, Ciocarlan R-G, Cool P, Baert K, Hauffman T, Daems N, Bals S, Breugelmans T, ACS applied nano materials 5, 7723 (2022). http://doi.org/10.1021/ACSANM.2C00473
Abstract: A promising strategy for the inhibition of the hydrogen evolution reaction along with the stabilization of the electrocatalyst in electrochemical CO2 reduction cells involves the application of a nanoscale amorphous carbon layer on top of the active catalyst layer in a gas diffusion electrode. Without modifying the chemical nature of the electrocatalyst itself, these amorphous carbon layers lead to the stabilization of the electrocatalyst, and a significant improvement with respect to the inhibition of the hydrogen evolution reaction was also obtained. The faradaic efficiencies of hydrogen could be reduced from 31.4 to 2.1% after 1 h of electrolysis with a 5 nm thick carbon layer. Furthermore, the impact of the carbon layer thickness (5–30 nm) on this inhibiting effect was investigated. We determined an optimal thickness of 15 nm where the hydrogen evolution reaction was inhibited and a decent stability was obtained. Next, a thickness of 15 nm was selected for durability measurements. Interestingly, these durability measurements revealed the beneficial impact of the carbon layer already after 6 h by suppressing the hydrogen evolution such that an increase of only 37.9% exists compared to 56.9% without the use of an additional carbon layer, which is an improvement of 150%. Since carbon is only applied afterward, it reveals its great potential in terms of electrocatalysis in general.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 5.9
Times cited: 3
DOI: 10.1021/ACSANM.2C00473
|
|
|
“Quantification of boron in cells for evaluation of drug agents used in boron neutron capture therapy”. Verlinden B, Van Hoecke K, Aerts A, Daems N, Dobney A, Janssens K, Cardinaels T, Journal Of Analytical Atomic Spectrometry 36, 598 (2021). http://doi.org/10.1039/D0JA00456A
Abstract: Boron neutron capture therapy (BNCT) is an extensively studied radiotherapeutic strategy for cancer treatment. BNCT is based on irradiation of malignant tumour cells with neutrons after uptake of a B-10 containing molecule. Alpha particles, locally produced by neutron irradiation kill the cancer cells. Important for ongoing research regarding cellular uptake and cytotoxicity of a large variety of B-10 containing molecules is the accurate determination of boron concentrations in cell cultures. In this work, the sample preparation for quantitative inductively coupled plasma mass spectrometry (ICP-MS) analysis on cell cultures was optimized. By making use of acid digestion combined with UV digestion, low detection limits (0.4 mu g L-1) and full recoveries of boron could be achieved while measurements were free of spectral and non-spectral interferences. Finally, cell-associated boron in the form of 4-borono-l-phenylalanine (l-BPA) in vascular endothelial cell cultures could be determined with ICP-MS as (1.26 +/- 0.10) x 10(9) boron atoms per cell. The developed method can prove its importance for further BNCT research and elemental analysis of cell cultures.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
DOI: 10.1039/D0JA00456A
|
|
|
“3D characterization of the structural transformation undergone by Cu@Ag core-shell nanoparticles following CO₂, reduction reaction”. Arenas Esteban D, Pacquets L, Choukroun D, Hoekx S, Kadu AA, Schalck J, Daems N, Breugelmans T, Bals S, Chemistry of materials 35, 6682 (2023). http://doi.org/10.1021/ACS.CHEMMATER.3C00649
Abstract: The increasing use of metallic nanoparticles (NPs) is significantly advancing the field of electrocatalysis. In particular, Cu/Ag bimetallic interfaces are widely used to enhance the electrochemical CO2 reduction reaction (eCO(2)RR) toward CO and, more recently, C-2 products. However, drastic changes in the product distribution and performance when Cu@Ag core-shell configurations are used can often be observed under electrochemical reaction conditions, especially during the first few minutes of the reaction. Possible structural changes that generate these observations remain underexplored; therefore, the structure-property relationship is hardly understood. In this study, we use electron tomography to investigate the structural transformation mechanism of Cu@Ag core-shells NPs during the critical first minutes of the eCO(2)RR. In this manner, we found that the crystallinity of the Cu seed determines whether the formation of a complete and homogeneous Ag shell is possible. Moreover, by tracking the particles' transformations, we conclude that modifications of the Cu-Ag interface and Cu2O enrichment at the surface of the NPs are key factors contributing to the product generation changes. These insights provide a better understanding of how bimetallic core-shell NPs transform under electrochemical conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 8.6
Times cited: 1
DOI: 10.1021/ACS.CHEMMATER.3C00649
|
|
|
“Synthesis and characterization of a highly electroactive composite based on Au nanoparticles supported on nanoporous activated carbon for electrocatalysis”. Moggia G, Hoekx S, Daems N, Bals S, Breugelmans T, ChemElectroChem , 1 (2023). http://doi.org/10.1002/CELC.202300293
Abstract: A facile, “one-pot”, chemical approach to synthesize gold-based nanoparticles finely dispersed on porous activated carbon (Norit) was demonstrated in this work. The pH of the synthesis bath played a critical role in determining the optimal gold-carbon interaction, which enabled a successful deposition of the gold nanoparticles onto the carbon matrix with a maximized metal utilization of 93 %. The obtained AuNP/C nanocomposite was characterized using SEM, HAADF-STEM electron tomography and electrochemical techniques. It was found that the Au nanoparticles, with diameters between 5 and 20 nm, were evenly distributed over the carbon matrix, both inside and outside the pores. Electrochemical characterization indicated that the composite had a very large electroactive surface area (EASA), as high as 282.4 m2 gAu-1. By exploiting its very high EASA, the catalyst was intended to boost the productivity of glucaric acid in the electrooxidation of its precursor, gluconic acid. However, cyclic voltammetry experiments revealed a very limited reactivity towards gluconic acid oxidation, due to the spacial hindrance of gluconic acid molecule which prevented diffusion inside the catalyst nanopores. On the other hand, the as-synthesized nanocomposite promises to be effective towards the ORR, and might thus find potential application as anode catalyst for fuel cells as well as for the scalability of all those electrochemical reactions involving small molecules with high diffusivity and catalysed by noble metals (i. e. CO2, CH4, N2, etc..). Electrocatalysis: Gold nanoparticles with diameter between 5 and 20 nm evenly distributed onto porous activated carbon (Norit) were obtained using a facile “one-pot” chemical synthesis technique with very high metal utilization. The AuNP/C nanocomposite was characterized using SEM, HAADF-STEM electron tomography and electrochemical techniques, revealing a very large electroactive surface area (EASA). The figure shows the HAADF-STEM image (a) and the respective EDX elemental distribution (b) for the AuNP/C composite with 9.3 % Au-loading developed in this work (Au is marked in red and C in green).image
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 4
Times cited: 1
DOI: 10.1002/CELC.202300293
|
|
|
“How flue gas impurities affect the electrochemical reduction of CO₂, to CO and formate”. Van Daele S, Hintjens L, Hoekx S, Bohlen B, Neukermans S, Daems N, Hereijgers J, Breugelmans T, Applied catalysis : B : environmental 341, 123345 (2024). http://doi.org/10.1016/J.APCATB.2023.123345
Abstract: The electrochemical CO2 reduction offers a promising solution to convert waste CO2 into valuable products like CO and formate. However, CO2 capture and purification remains an energy intensive process and therefore the direct usage of industrially available waste CO2 streams containing SO2, NO and O2 impurities becomes more interesting. This work demonstrates an efficient (Faradaic efficiency > 90 %) and stable performance over 20 h with 200 ppm SO2 or NO in the feed gas stream. However, the addition of 1 % O2 to the CO2 feed causes a significant drop in Faradaic efficiency to C-products due to the competitive oxygen reduction reaction. A potential mitigation strategy is to operate at higher total current density to firstly reduce most O2 and achieve sufficient product output from CO2 reduction. These results aid in understanding the impact of flue gas impurities during CO2 electrolysis which is crucial for potentially bypassing the CO2 purification step.
Keywords: A1 Journal article; Engineering sciences. Technology; Applied Electrochemistry & Catalysis (ELCAT); Electron microscopy for materials research (EMAT)
Impact Factor: 22.1
DOI: 10.1016/J.APCATB.2023.123345
|
|
|
“Improving stability of CO₂, electroreduction by incorporating Ag NPs in N-doped ordered mesoporous carbon structures”. Van den Hoek J, Daems N, Arnouts S, Hoekx S, Bals S, Breugelmans T, ACS applied materials and interfaces 16, 6931 (2024). http://doi.org/10.1021/ACSAMI.3C12261
Abstract: The electroreduction of carbon dioxide (eCO2RR) to CO using Ag nanoparticles as an electrocatalyst is promising as an industrial carbon capture and utilization (CCU) technique to mitigate CO2 emissions. Nevertheless, the long-term stability of these Ag nanoparticles has been insufficient despite initial high Faradaic efficiencies and/or partial current densities. To improve the stability, we evaluated an up-scalable and easily tunable synthesis route to deposit low-weight percentages of Ag nanoparticles (NPs) on and into the framework of a nitrogen-doped ordered mesoporous carbon (NOMC) structure. By exploiting this so-called nanoparticle confinement strategy, the nanoparticle mobility under operation is strongly reduced. As a result, particle detachment and agglomeration, two of the most pronounced electrocatalytic degradation mechanisms, are (partially) blocked and catalyst durability is improved. Several synthesis parameters, such as the anchoring agent, the weight percentage of Ag NPs, and the type of carbonaceous support material, were modified in a controlled manner to evaluate their respective impact on the overall electrochemical performance, with a strong emphasis on operational stability. The resulting powders were evaluated through electrochemical and physicochemical characterization methods, including X-ray diffraction (XRD), N2-physisorption, Inductively coupled plasma mass spectrometry (ICP-MS), scanning electron microscopy (SEM), SEM-energy-dispersive X-ray spectroscopy (SEM-EDS), high-angle annular dark field scanning transmission electron microscopy (HAADF-STEM), STEM-EDS, electron tomography, and X-ray photoelectron spectroscopy (XPS). The optimized Ag/soft-NOMC catalysts showed both a promising selectivity (∼80%) and stability compared with commercial Ag NPs while decreasing the loading of the transition metal by more than 50%. The stability of both the 5 and 10 wt % Ag/soft-NOMC catalysts showed considerable improvements by anchoring the Ag NPs on and into a NOMC framework, resulting in a 267% improvement in CO selectivity after 72 h (despite initial losses) compared to commercial Ag NPs. These results demonstrate the promising strategy of anchoring Ag NPs to improve the CO selectivity during prolonged experiments due to the reduced mobility of the Ag NPs and thus enhanced stability.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 9.5
DOI: 10.1021/ACSAMI.3C12261
|
|
|
“Toward the rational design of Cu electrocatalysts for improved performance of the NO3RR”. Hoekx S, Daems N, Arenas Esteban D, Bals S, Breugelmans T, ACS applied energy materials 7, 3761 (2024). http://doi.org/10.1021/ACSAEM.3C03207
Abstract: Cu is one of the most promising materials as an electrocatalyst for the nitrate reduction reaction (NO3RR) to ammonia, a reaction that can simultaneously remove nitrates from wastewater and produce ammonia, a high-value commodity chemical. However, a rational approach to catalyst design is lacking, limiting efficient catalyst optimization. In this work, we propose a way to synthesize monodisperse, polycrystalline Cu NPs with small variances in size by changing the carbon chain length of the phosphonic acid-based ligand. Cu NPs with 8.3, 10.0, and 11.9 nm diameters are successfully synthesized, and high-resolution electron microscopy and tomography are used to characterize these NPs in depth. By isolating Cu NP size as a parameter, we can unequivocally establish its effect on electrochemical performance for the NO3RR to ammonia under optimal operating conditions for the catalyst (0.1 M KOH electrolyte at -1.25 V vs RHE, as established in the first phase). The smallest Cu NPs (8.3 nm with a TDPA ligand) perform best, achieving Faradaic efficiencies (FEs) of 85.4% and absolute current densities of similar to 250 mA cm(-2), with increasing current densities and constant FEs as the particle size decreases. To allow for a rational approach to Cu-based catalyst design from a stability perspective, this work completed a first study of the main degradation pathway that the Cu NPs undergo during NO3RR. High-resolution electron microscopy and tomography are used to characterize the particles at various stages of the reaction. The NPs undergo agglomeration, pulverization, and particle detachment due to the reaction, starting at a particle size of 8.3 nm and progressively getting smaller, but leveling off, until a NP size of 2.6 nm is reached after 2 h of electrolysis. This decrease in NP size goes paired with a decrease in FE from 83% after the first 15 min to 74% after 2 h at -0.75 V vs RHE, despite the increase in active surface area. These insights into the most prominent degradation mechanisms allow for rational adjustments to future catalysts to combat these changes; for example, by embedding NPs in a tailored support, morphological degradation could be impeded. Therefore, these insights allow for a rational approach to the improvement of the stability of Cu-based catalysts for the NO3RR, a very important but often an overlooked aspect of catalyst design.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 6.4
DOI: 10.1021/ACSAEM.3C03207
|
|