“Multi-step loading of titania on mesoporous silica: influence of the morphology and the porosity on the catalytic degradation of aqueous pollutants and VOC's”. de Witte K, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Sepúlveda-Escribano A, Rodríguez-Reinoso F, Vansant EF, Cool P, Applied catalysis : B : environmental 84, 125 (2008). http://doi.org/10.1016/j.apcatb.2008.03.015
Abstract: Titania nanoparticles have been deposited on inert porous silica supports with high specific surface area. These materials have potential applications in paint and textile industry as the titania particles selectively deposited on the inner surface of the silica supports act as a photocatalyst. The inert external surface is necessary to avoid photodegradation of the textile material or the paint components. The photocatalytic activity of the catalysts has been evaluated with two catalytic setups. One setup in aqueous phase, for the degradation of dyes such as rhodamine-6G, is commonly used. The second setup is a continuous flow gaseous phase setup which was used for the mineralization of ethanol as a representative volatile organic compound (VOC). The influence of the porosity and the morphology of the silica supports on the photocatalytic activity are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 9.446
Times cited: 24
DOI: 10.1016/j.apcatb.2008.03.015
|
|
|
“Nanodiamond photoemitters based on strong narrow-band luminescence from silicon-vacancy defects”. Vlasov II, Barnard AS, Ralchenko VG, Lebedev OI, Kanzyuba MV, Saveliev AV, Konov VI, Goovaerts E, Advanced materials 21, 808 (2009). http://doi.org/10.1002/adma.200802160
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 98
DOI: 10.1002/adma.200802160
|
|
|
“Negative magnetoresistance in a V3+/V4+ mixed valent vanadate”. Maignan A, Lebedev OI, Van Tendeloo G, Martin C, Hébert S, Applied physics letters 96, 232502 (2010). http://doi.org/10.1063/1.3446892
Abstract: The magnetotransport and magnetic properties of the PbV6O11 vanadate, crystallizing in the P63mc space group, reveal the existence of a negative magnetoresistance related to its ferromagnetic state (TC ∼ 90 K). The maximum effect is observed at 20 K reaching −30% in 9 T. The structural study of this ceramic reveals a V/Pb ratio smaller than expected from the formula. This is explained by the presence of numerous stacking faults observed by high resolution transmission electron microscopy. The existence of these planar defects acting as resistive barriers along the c axis could be responsible for tunneling magnetoresistance.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
DOI: 10.1063/1.3446892
|
|
|
“New insights in the formation of combined zeolitic/mesoporous materials by using a one-pot templating synthesis”. Vernimmen J, Meynen V, Herregods SJF, Mertens M, Lebedev OI, Van Tendeloo G, Cool P, European journal of inorganic chemistry , 4234 (2011). http://doi.org/10.1002/ejic.201100268
Abstract: Zeolitic growth is often absent or occurs in separate phases when synthetic strategies based on the combination of zeolite templates and mesopore templating agents are applied. In this work, zeolitic growth and mesopore formation have been investigated at different temperatures by applying a one-pot templating approach, based on a TS-1 zeolite synthesis whereby part of the microtemplate (tetrapropylammonium hydroxide, TPAOH) is replaced by a mesotemplate (hexadecyltrimethylammonium bromide, CTMABr). Moreover, the synthesis duration and the molar ratio of the microtemplate/mesotemplate have also been studied. The different syntheses clearly show the inherent competitive mechanism between zeolitic growth and mesopore formation. These insights have led to the conclusion that by following a one-pot templating strategy with standard, nonexotic commercial templates, i.e. CTMABr and TPAOH, it is not possible to develop a true hierarchical mesoporous zeolite, meaning a mesoporous siliceous material with highly crystalline zeolitic walls. The resultant materials are instead combined zeolitic/mesoporous composite structures with, however, highly tuneable and controllable porosity characteristics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.444
Times cited: 7
DOI: 10.1002/ejic.201100268
|
|
|
“A new iron oxophosphate SrFe3(PO4)3O with chain-like structure”. Morozov VA, Pokholok KV, Lazoryak BI, Malakho AP, Lachgar A, Lebedev OI, Van Tendeloo G, Journal of solid state chemistry 170, 411 (2003). http://doi.org/10.1016/S0022-4596(02)00133-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 12
DOI: 10.1016/S0022-4596(02)00133-0
|
|
|
“New molybdenum oxides Ag4M2Zr(MoO4)6 (M=Mg, Mn, Co, Zn) with a channel-like structure”. Khobrakova ET, Morozov VA, Khasanov SS, Tsyrenova GD, Khaikina EG, Lebedev OI, Van Tendeloo G, Lazoryak BI, Solid state sciences 7, 1397 (2005). http://doi.org/10.1016/j.solidstatesciences.2005.08.010
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 9
DOI: 10.1016/j.solidstatesciences.2005.08.010
|
|
|
“New nano-architectures of mesoporous silica spheres analyzed by advanced electron microscopy”. Lebedev OI, Turner S, Liu S, Cool P, Van Tendeloo G, Nanoscale 4, 1722 (2012). http://doi.org/10.1039/c2nr11715k
Abstract: Using template-containing silica microspheres as a precursor, novel ordered mesoporous silica nanoparticles with a narrow pore size distribution and high crystallinity have been synthesized by various hydrothermal merging processes. Several architectures like chains, dumbbells, triangles, squares and flowers have been discovered. The linking mechanisms of these interacting silica spheres leading to the formation of ordered nano-structures are studied by HRTEM, HAADF-STEM and electron tomography and a plausible model is presented for several merging processes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 7.367
Times cited: 5
DOI: 10.1039/c2nr11715k
|
|
|
“A new structure type of the ternary sulfide Eu1.3Nb1.9S5”. Khasanova NR, Van Tendeloo G, Lebedev OI, Amelinckx S, Grippa AY, Abakumov AM, Istomin SY, D'yachenko OG, Antipov EV, Journal of solid state chemistry 164, 345 (2002). http://doi.org/10.1006/jssc.2001.9501
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1006/jssc.2001.9501
|
|
|
“Nickel/carbon composite materials based on expanded graphite”. Afanasov IM, Lebedev OI, Kolozhvary BA, Smirnov AV, Van Tendeloo G, New carbon materials 26, 335 (2011). http://doi.org/10.1016/S1872-5805(11)60085-1
Abstract: Monolithic nickel/carbon (Ni/C) composites were prepared from coal tar pitch-impregnated compressed expanded graphite pre-decorated with NiO particles (EGNiO) by pyrolysis at 550 °C and subsequent steam activation at 800 °C. The microstructural arrangement of the Ni-comprising nanoparticles in the composites was investigated using transmission electron microscopy. The specific surface area and porosity of the composites were analyzed by nitrogen adsorption. The catalytic activity of the composites was compared with the material obtained by the conventional H2 treatment of EGNiO using hydrocracking of 2,2,3-trimethylpentane as a model reaction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1016/S1872-5805(11)60085-1
|
|
|
“Nitrogen and luminescent nitrogen-vacancy defects in detonation nanodiamond”. Vlasov II, Shenderova O, Turner S, Lebedev OI, Basov AA, Sildos I, Rähn M, Shiryaev AA, Van Tendeloo G, Small 6, 687 (2010). http://doi.org/10.1002/smll.200901587
Abstract: An efficient method to investigate the microstructure and spatial distribution of nitrogen and nitrogen-vacancy (N-V) defects in detonation nanodiamond (DND) with primary particle sizes ranging from approximately 3 to 50 nm is presented. Detailed analysis reveals atomic nitrogen concentrations as high as 3 at% in 50% of diamond primary particles with sizes smaller than 6 nm. A non-uniform distribution of nitrogen within larger primary DND particles is also presented, indicating a preference for location within the defective central part or at twin boundaries. A photoluminescence (PL) spectrum with well-pronounced zero-phonon lines related to the N-V centers is demonstrated for the first time for electron-irradiated and annealed DND particles at continuous laser excitation. Combined Raman and PL analysis of DND crystallites dispersed on a Si substrate leads to the conclusion that the observed N-V luminescence originates from primary particles with sizes exceeding 30 nm. These findings demonstrate that by manipulation of the size/nitrogen content in DND there are prospects for mass production of nanodiamond photoemitters based on bright and stable luminescence from nitrogen-related defects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 84
DOI: 10.1002/smll.200901587
|
|
|
“Novel MoVSbOx-type catalysts for selective isobutane oxidation”. Paul JS, Groothaert MH, Kirschhock CEA, Lebedev OI, Jacobs PA, Maier WF, Catalysis today
T2 –, 7th European Workshop Meeting on Selective Oxidation, AUG 31-SEP 04, 2003, Innsbruck, AUSTRIA 91-2, 265 (2004). http://doi.org/10.1016/j.cattod.2004.03.041
Abstract: A new sol-gel synthesis procedure is proposed for the preparation of MoVSbOx catalysts for the selective oxidation of isobutane. Physico-chemical characterization of the materials calcined at 400 degreesC, showed essentially amorphous catalysts, with long-range order. Increase of calcination temperature, however, resulted in the formation of small crystalline regions, confirmed through TEM. EPR measurements on the calcined samples pointed to the presence of isolated and magnetically interacting V(IV) species. The reported catalysts proved to be much more selective for partial oxidation compared to a literature reference catalyst. Furthermore, it is shown that this versatile synthesis recipe forms an excellent start for high-throughput and combinatorial studies. (C) 2004 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.636
Times cited: 12
DOI: 10.1016/j.cattod.2004.03.041
|
|
|
“Observation of Sb203 nanocrystals in SiO2 after Sb ion implantation”. Ignatova VA, Lebedev OI, Wätjen U, van Vaeck L, van Landuyt J, Gijbels R, Adams F, Microchimica acta 139, 77 (2002). http://doi.org/10.1007/s006040200043
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.58
Times cited: 3
DOI: 10.1007/s006040200043
|
|
|
“Off-stoichiometry effects on the crystalline and defect structure of hexagonal manganite REMnO3 films (RE = Y, Er, Dy)”. Gélard J, Jehanathan N, Roussel H, Gariglio S, Lebedev OI, Van Tendeloo G, Dubourdieu C, Chemistry of materials 23, 1232 (2011). http://doi.org/10.1021/cm1029358
Abstract: The crystalline and defect structure of epitaxial hexagonal RExMnyO3 (RE = Er, Dy) films with varying cationic composition was investigated by X-ray diffraction and transmission electron microscopy. The films are composed of a strained layer at the interface with the substrate and of a relaxed layer on top of it. The critical thickness is of 10 to 25 nm. For Mn-rich films (or RE deficient), an off-stoichiometric composition maintaining the hexagonal LuMnO3-type structure is stabilized over a large range of the RE/Mn ratio (0.72−1.00), with no Mn-rich secondary phases observed. A linear dependence of the out-of-plane lattice parameter with RE/Mn is observed in this range. Out-of-phase boundary (OPB) extended defects are observed in all films and exhibit a local change in stoichiometry. Such a large solubility limit in the RE deficient region points toward the formation of vacancies on the RE site (RExMnO3−δ, with 0.72 ≤ x < 1), a phenomenon that is encountered in perovskite manganites such as LaxMnO3−δ (x < 1) and that may strongly impact the physical properties of hexagonal manganites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 17
DOI: 10.1021/cm1029358
|
|
|
“One-step synthesis of shelled PbS nanoparticles in a layered double hydroxide matrix”. Lukashin AV, Eliseev AA, Zhuravleva NG, Vertegel AA, Tretyakov YD, Lebedev OI, Van Tendeloo G, Mendeleev communications , 174 (2004). http://doi.org/10.1070/MC2004v014n04ABEH001973
Abstract: The one-step preparation of capped PbS nanoparticles in an inorganic matrix via UV-induced decomposition of lead thiosulfate complexes intercalated into a hydrotalcite-type layered double hydroxide is reported.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.741
Times cited: 9
DOI: 10.1070/MC2004v014n04ABEH001973
|
|
|
“Ordering of tetrahedral chains in the Sr2MnGaO5 brownmillerite”. Abakumov AM, Alekseeva AM, Rozova MG, Antipov EV, Lebedev OI, Van Tendeloo G, Journal of solid state chemistry 174, 319 (2003). http://doi.org/10.1016/S0022-4596(03)00226-3
Abstract: Tetrahedral chain ordering in the Sr2MnGaO5 structure is studied using electron diffraction (ED) and high-resolution electron microscopy. The ED patterns show the presence of satellite reflections, which indicate a commensurately modulated structure with a = 5.4056(8) Angstrom b 16.171(3) Angstrom, c = 5.5592(7) Angstrom, q – 1/2c*, superspace group Immma(00gamma,)s00. The Superstructure arises due to ordering of the two types of symmetry related tetrahedral chains (L and R) according to a ... LRLR ... sequence, where L and R chains alternate along the c-axis within the same (GaO) layer. Numerous defects at different structural levels were observed, comprising interleaving L and R chains, violation of the ... LRLR ... chain sequence within one layer, different stacking modes of the ... LRLR ... ordered layers with subsequent alternation of blocks of different width along the h-axis of the brownmillerite subcell and island fragmentation of the modulated superstructure. By in situ heating ED experiments it is found that the long-range ordering of the tetrahedral chains is stable tip to 665degreesC and is completely suppressed at 905degreesC. (C) 2003 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 34
DOI: 10.1016/S0022-4596(03)00226-3
|
|
|
“Origin of different deactivation of Pd/SnO2 and Pd/GeO2 catalysts in methanol dehydrogenation and reforming: a comparative study”. Lorenz H, Zhao Q, Turner S, Lebedev OI, Van Tendeloo G, Kloetzer B, Rameshan C, Pfaller K, Applied catalysis : A : general 381, 242 (2010). http://doi.org/10.1016/j.apcata.2010.04.015
Abstract: Pd particles supported on SnO2 and GeO2 have been structurally investigated by X-ray diffraction, (High-Resolution) transmission and scanning electron microscopy after different reductive treatments to monitor the eventual formation of bimetallic phases and catalytically tested in methanol dehydrogenation/ reforming. For both oxides this included a thin film sample with well-defined Pd particles and a powder catalyst prepared by incipient wetness impregnation. The hexagonal and the tetragonal polymorph were studied for powder GeO2. Pd2Ge formation was observed on all GeO2-supported catalysts, strongly depending on the specific sample used. Reduction of the thin film at 573K resulted in full transformation into the bimetallic state. The partial solubility of hexagonal GeO2 in water and its thermal structural instability yielded Pd2Ge formation at 473 K, at the cost of a structurally inhomogeneous support and Ge metal formation at higher reduction temperatures. Pd on tetragonal GeO2 entered a state of strong metalsupport interaction after reduction at 573673 K, resulting in coalescing Pd2Ge particles on a sintered and re-crystallized support, apparently partially covering the bimetallic particles and decreasing the catalytic activity. Pd2Ge on amorphous thin film and hexagonal GeO2 converted methanol primarily via dehydrogenation to CO and H2. At 573 K, formation of Pd2Sn and also PdSn occurred on the Pd/SnO2 thin film. Pd3Sn2 (and to some extent Pd2Sn) were predominantly obtained on the respective powder catalyst. Strong deactivation with increasing reduction temperature was observed, likely not based on the classical strong metalsupport interaction effect, but rather on a combination of missing active structural ensembles on Sn-enriched bimetallic phases and the formation of metallic -Sn. Correlations to Pd and its bimetallics supported on ZnO, Ga2O3 and In2O3 were also discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 14
DOI: 10.1016/j.apcata.2010.04.015
|
|
|
“Oxygen and fluorine doping in Sr2MnGaO5 brownmillerite”. Antipov EV, Abakumov AM, Alekseeva AM, Rozova MG, Hadermann J, Lebedev OI, Van Tendeloo G, Physica status solidi: A: applied research 201, 1403 (2004). http://doi.org/10.1002/pssa.200304428
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 9
DOI: 10.1002/pssa.200304428
|
|
|
“Pd@MOF-5: limitations of gas-phase infiltration and solution impregnation of [Zn4O(bdc)3] (MOF-5) with metalorganic palladium precursors for loading with Pd nanoparticles”. Esken D, Zhang X, Lebedev OI, Schröder F, Fischer RA, Journal of materials chemistry 19, 1314 (2009). http://doi.org/10.1039/b815977g
Abstract: The limitations of the loading of the porous metalorganic framework [Zn4O(bdc)3] (bdc = benzene-1,4-dicarboxylate; MOF-5 or IRMOF-1) with Pd nanoparticles was investigated. First, the volatile organometallic precursor [Pd(5-C5H5)(3-C3H5)] was employed to get the inclusion compound [Pd(5-C5H5)(3-C3H5)]x@MOF-5 via gas-phase infiltration at 10-3 mbar. A loading of four molecules of [Pd(5-C5H5)(3-C3H5)] per formula unit of MOF-5 (x = 4) can be reached (35 wt.% Pd). Second, the metalorganic precursor [Pd(acac)2] (acac = 2,4-pentanedionate) was used and the inclusion materials [Pd(acac)2]x@MOF-5 of different Pd loadings were obtained by incipient wetness infiltration. However, the maximum loading was lower as compared with the former case with about two precursor molecules per formula unit of MOF-5. Both loading routes are suitable for the synthesis of Pd nanoparticles inside the porous host matrix. Homogeneously distributed nanoparticles with diameter of 2.4(±0.2) nm can be achieved by photolysis of the inclusion compounds [Pd(5-C5H5)(3-C3H5)]x@MOF-5 (x 4), while the hydrogenolysis of [Pd(acac)2]x@MOF-5 (x 2) leads to a mixture of small particles inside the network (< 3 nm) and large Pd agglomerates (40 nm) on the outer surface of the MOF-5 specimens. The pure Pdx@MOF-5 materials proved to be stable under hydrogen pressure (2 bar) at 150 °C over many hours. Neither hydrogenation of the bdc linkers nor particle growth was observed. The new composite materials were characterized by 1H/13C-MAS-NMR, powder XRD, ICP-AES, FT-IR, N2 sorption measurements and high resolution TEM. Raising the Pd loading of a representative sample Pd4@MOF-5 (35 wt.% Pd) by using [Pd(5-C5H5)(3-C3H5)] as precursor in a second cycle of gas-phase infiltration and photolysis was accompanied by the collapse of the long-range crystalline order of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 100
DOI: 10.1039/b815977g
|
|
|
“Periodic microtwinning as a possible mechanism for the accommodation of the epitaxial film-substrate mismatch in the La1-xSrxMnO3/SrTiO3 system”. Lebedev OI, Van Tendeloo G, Amelinckx S, Razavi F, Habermeier H-U, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 81, 797 (2001)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Phase competition between Y2BaCuO5 and Y2O3 precipitates in Y-rich YBCO thin films”. Scotti di Uccio U, Miletto Granozio F, di Chiara A, Tafuri F, Lebedev OI, Verbist K, Van Tendeloo G, Physica: C : superconductivity 321, 162 (1999)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 17
|
|
|
“Phase selection enabled formation of abrupt axial heterojunctions in branched oxide nanowires”. Gao J, Lebedev OI, Turner S, Li YF, Lu YH, Feng YP, Boullay P, Prellier W, Van Tendeloo G, Wu T, Nano letters 12, 275 (2012). http://doi.org/10.1021/nl2035089
Abstract: Rational synthesis of nanowires via the vaporliquidsolid (VLS) mechanism with compositional and structural controls is vitally important for fabricating functional nanodevices from bottom up. Here, we show that branched indium tin oxide nanowires can be in situ seeded in vapor transport growth using tailored AuCu alloys as catalyst. Furthermore, we demonstrate that VLS synthesis gives unprecedented freedom to navigate the ternary InSnO phase diagram, and a rare and bulk-unstable cubic phase can be selectively stabilized in nanowires. The stabilized cubic fluorite phase possesses an unusual almost equimolar concentration of In and Sn, forming a defect-free epitaxial interface with the conventional bixbyite phase of tin-doped indium oxide that is the most employed transparent conducting oxide. This rational methodology of selecting phases and making abrupt axial heterojunctions in nanowires presents advantages over the conventional synthesis routes, promising novel composition-modulated nanomaterials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 25
DOI: 10.1021/nl2035089
|
|
|
“The phase transition and crystal structures of Ba3RM2O7.5 complex oxides (R=rare-earth elements, M = Al,Ga)”. Abakumov AM, Shpanchenko RV, Lebedev OI, Van Tendeloo G, Amelinckx S, Antipov EV, Acta crystallographica: section A: foundations of crystallography 55, 828 (1999). http://doi.org/10.1107/S0108767399002068
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.725
Times cited: 7
DOI: 10.1107/S0108767399002068
|
|
|
“Phase transition and magnetic anisotropy of (La,Sr)MnO3 thin films”. Wang Z-H, Kronmüller H, Lebedev OI, Gross GM, Razavi FS, Habermeier HU, Shen BG, Physical review : B : condensed matter and materials physics 65, 054411 (2002). http://doi.org/10.1103/PhysRevB.65.054411
Abstract: The magnetic proper-ties and their correlation with the microstructure and electrical transport are investigated in La0.88Sr0.1MnO3 films grown on (100)SrTiO3 Single crystal substrates with thickness ranging from 100 to 2500 Angstrom. The ultrathin film (t = 100 Angstrom) has a single ferromagnetic transition (FMT) at T-c of 250 K, whereas the thicker films exhibit two FMTs, with the main one at a lowered T-c of 200 K while the minor one around 300 K. Furthermore, a thickness dependent magnetic anisotropy has been found, strongly indicating the existence of strain effect, which is also revealed by the transmission electron microscopy study. The suppressed Jahn-Teller distortion (JTD) by the epitaxial strain, and the recovered JTD due to the strain relexation are suggested to explain the metallic behavior in thin films and the insulating behavior in the thick film (t = 2500 Angstrom), repectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 23
DOI: 10.1103/PhysRevB.65.054411
|
|
|
“Phase transitions: an alternative for stress accommodation in CMR manganate films”. Lebedev OI, Van Tendeloo G, Zeitschrift für Metallkunde 95, 244 (2004). http://doi.org/10.3139/146.017943
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.3139/146.017943
|
|
|
“Plasma-assisted synthesis of Ag/ZnO nanocomposites : first example of photo-induced H2 production and sensing”. Simon Q, Barreca D, Bekermann D, Gasparotto A, Maccato C, Comini E, Gombac V, Fornasiero P, Lebedev OI, Turner S, Devi A, Fischer RA, Van Tendeloo G, International journal of hydrogen energy 36, 15527 (2011). http://doi.org/10.1016/j.ijhydene.2011.09.045
Abstract: Ag/ZnO nanocomposites were developed by a plasma-assisted approach. The adopted strategy exploits the advantages of Plasma Enhanced-Chemical Vapor Deposition (PE-CVD) for the growth of columnar ZnO arrays on Si(100) and Al2O3 substrates, in synergy with the infiltration power of the Radio Frequency (RF)-sputtering technique for the subsequent dispersion of different amounts of Ag nanoparticles (NPs). The resulting composites, both as-prepared and after annealing in air, were thoroughly characterized with particular attention on their morphological organization, structure and composition. For the first time, the above systems have been used as catalysts in the production of hydrogen by photo-reforming of alcoholic solutions, yielding a stable H2 evolution even by the sole use of simulated solar radiation. In addition, Ag/ZnO nanocomposites presented an excellent response in the gas-phase detection of H2, opening attractive perspectives for advanced technological applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.582
Times cited: 62
DOI: 10.1016/j.ijhydene.2011.09.045
|
|
|
“Positional and orientational disorder in a solid solution of Sr9-xNi1.5-x(PO4)7 (x=0.3)”. Belik A, Izumi F, Ikeda T, Morozov VA, Dilanian R, Torii S, Kopnin E, Lebedev OI, Van Tendeloo G, Lazoryak BI, Chemistry and materials 14, 4464 (2002). http://doi.org/10.1021/cm0206901
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 28
DOI: 10.1021/cm0206901
|
|
|
“Post-synthesis deposition of V-Zeolitic nanoparticles in SBA-15”. Meynen V, Beyers E, Cool P, Vansant EF, Mertens M, Weyten H, Lebedev OI, Van Tendeloo G, Chemical communications , 898 (2004). http://doi.org/10.1039/b400636d
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 6.319
Times cited: 22
DOI: 10.1039/b400636d
|
|
|
“A potential method to correlate electrical properties and microstructure of a unique high-Tc superconducting Josephson junction”. Verbist K, Lebedev OI, Van Tendeloo G, Tafuri F, Granozio FM, Di Chiara A, Bender H, Applied physics letters 74, 1024 (1999). http://doi.org/10.1063/1.123443
Abstract: A method to correlate microstructure from cross-section transmission electron microscopy (TEM) investigations and transport properties of a single well characterized high-T-c artificial grain boundary junction is reported. A YBa2Cu3O7-delta 45 degrees twist junction exhibiting the typical phenomenology of high T-c Josephson weak links was employed. The TEM sample preparation is based on focused ion beam etching and allows to easily localize the electron transparent area on a microbridge. The reported technique opens clear perspectives in the determination of the microstructural origin of variations in Josephson junction properties, such as the spread in I-c and IcRN values and the presence of different transport regimes in nominally identical junctions. (C) 1999 American Institute of Physics. [S0003-6951(99)03404-X].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 5
DOI: 10.1063/1.123443
|
|
|
“Preparation and structural characterization of SnO2 and GeO2 methanol steam reforming thin film model catalysts by (HR)TEM”. Lorenz H, Zhao Q, Turner S, Lebedev OI, Van Tendeloo G, Klötzer B, Rameshan C, Penner S, Materials chemistry and physics 122, 623 (2010). http://doi.org/10.1016/j.matchemphys.2010.03.057
Abstract: Structure, morphology and composition of different tin oxide and germanium oxide thin film catalysts for the methanol steam reforming (MSR) reaction have been studied by a combination of (high-resolution) transmission electron microscopy, selected area electron diffraction, dark-field imaging and electron energy-loss spectroscopy. Deposition of the thin films on NaCl(0 0 1) cleavage faces has been carried out by thermal evaporation of the respective SnO2 and GeO2 powders in varying oxygen partial pressures and at different substrate temperatures. Preparation of tin oxide films in high oxygen pressures (10−1 Pa) exclusively resulted in SnO phases, at and above 473 K substrate temperature epitaxial growth of SnO on NaCl(0 0 1) leads to well-ordered films. For lower oxygen partial pressures (10−3 to 10−2 Pa), mixtures of SnO and β-Sn are obtained. Well-ordered SnO2 films, as verified by electron diffraction patterns and energy-loss spectra, are only obtained after post-oxidation of SnO films at temperatures T ≥ 673 K in 105 Pa O2. Preparation of GeOx films inevitably results in amorphous films with a composition close to GeO2, which cannot be crystallized by annealing treatments in oxygen or hydrogen at temperatures comparable to SnO/SnO2. Similarities and differences to neighbouring oxides relevant for selective MSR in the third group of the periodic system (In2O3 and Ga2O3) are also discussed with the aim of cross-correlation in formation of nanomaterials, and ultimately, also catalytic properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.084
Times cited: 15
DOI: 10.1016/j.matchemphys.2010.03.057
|
|
|
“Preparing polymer films doped with magnetic nanoparticles by spin-coating and melt-processing can induce an in-plane magnetic anisotropy”. Wouters J, Lebedev OI, Van Tendeloo G, Yamada H, Sato N, Vanacken J, Moshchalkov VV, Verbiest T, Valev VK, Journal of applied physics 109, 076105 (2011). http://doi.org/10.1063/1.3572048
Abstract: Faraday rotation has been used to investigate a series of polymer films doped with magnetic iron oxide nanoparticles. The films have been prepared by spin-coating and melt-processing. In each case, upon varying the angle of optical incidence on the films, an in-plane magnetic anisotropy is observed. The effect of such an anisotropy on the Faraday rotation as a function of the angle of optical incidence is verified by comparison with magnetically poled films. These results demonstrate that care should be taken upon analyzing the magnetic behavior of such films on account of the sample preparation techniques themselves being able to affect the magnetization.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 10
DOI: 10.1063/1.3572048
|
|