Abstract: CoFe2/CoFe2O4 bilayers were made by pulsed laser ablation of a CoFe2 target on Si(I 0 0) substrates. The metallic layer was deposited first, in vacuum. The oxide was then deposited in an oxidizing O-2:N-2 (20:80) atmosphere. Two different procedures were used for the introduction of the oxidizing atmosphere in the deposition chamber: the laser ablation of the target was either stopped (discontinuous deposition process) or maintained (continuous deposition process) during the 20 min necessary for the establishment of the desired O-2:N-2 pressure. In both cases, the different electronegativities of Fe and Co cause an important modification of the Fe/Co ratio at the metal/oxide interface, with a depletion of Fe in the metal region and of Co in the oxide region. In the continuous procedure, the combination of the kinetic energy given by the ablation process to the Fe and Co adatoms with the one they get from their different affinity towards oxidation allows the formation of a low roughness metal/oxide interface with a high (111) preferred orientation of the CoFe2O4 layer, an induced re-crystallisation of the metal layer underneath and an unusual antiferromagnetic metal/oxide magnetic coupling. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Abstract: We report crystal structure, electronic structure, and magnetism of manganese tetraboride, MnB4, synthesized under high-pressure, high-temperature conditions. In contrast to superconducting FeB4 and metallic CrB4, which are both orthorhombic, MnB4 features a monoclinic crystal structure. Its lower symmetry originates from a Peierls distortion of the Mn chains. This distortion nearly opens the gap at the Fermi level, but despite the strong dimerization and the proximity of MnB4 to the insulating state, we find indications for a sizable paramagnetic effective moment of about 1.7 mu(B)/f.u., ferromagnetic spin correlations, and, even more surprisingly, a prominent electronic contribution to the specific heat. However, no magnetic order has been observed in standard thermodynamic measurements down to 2 K. Altogether, this renders MnB4 a structurally simple but microscopically enigmatic material; we argue that its properties may be influenced by electronic correlations.

Abstract: Korund-artiges ε-Mn2O3 und Perowskit-artiges ζ-Mn2O3, zwei neue Phasen von Mn2O3, wurden unter hohen Drücken bei hohen Temperaturen synthetisiert. Die Manganatome können vollständig die A- und B-Positionen der Perowskitstruktur besetzen. ζ-Mn2O3 (siehe Bild, A-Positionsordnung) enthält Mn in den drei Oxidationsstufen +II, +III und +IV.

Abstract: Epitaxial double perovskite La2CoMnO6 (LCMO) films were grown by metalorganic aerosol deposition on SrTiO3(111) substrates. A high Curie temperature, T-C = 226 K, and large magnetization close to saturation, M-S(5 K) = 5.8 mu(B)/f.u., indicate a 97% degree of B-site (Co,Mn) ordering within the film. The Co/Mn ordering was directly imaged at the atomic scale by scanning transmission electron microscopy with energy-dispersive X-ray spectroscopy (STEM-EDX). Local electron-energy-loss spectroscopy (EELS) measurements reveal that the B-sites are predominantly occupied by Co2+ and Mn4+ ions in quantitative agreement with magnetic data. Relatively small values of the (1/2 1/2 1/2) superstructure peak intensity, obtained by X-ray diffraction (XRD), point out the existence of ordered domains with an arbitrary phase relationship across the domain boundary. The size of these domains is estimated to be in the range 35-170 nm according to TEM observations and modelling the magnetization data. These observations provide important information towards the complexity of the cation ordering phenomenon and its implications on magnetism in double perovskites, and similar materials.

Abstract: In this work, photoelectric yield and electrical properties of several types of epitaxial erbium silicide on silicon Schottky diodes are studied, Different preparation conditions are used simultaneously on n- and p-Si(111) substrates for the 200 Angstrom thick silicide films. A last type of sample consists in 1.3 monolayer of epitaxial silicide with root 3 X root 3 superstructure on the Si substrate and covered by silver on the top. Photocurrent measurements are done as a function of photon energy at several temperatures. All these samples show barrier heights near 1 eV on p-type Si, even for the interface comprising only 1.3 monolayer of silicide whereas barrier heights on n-rype Si span the range from 0.28 to 0.67 eV for this last kind of sample, the sum of the barriers always exceeding the silicon band gap, These photoelectric results are confirmed by electrical characterisations, All these results show that the Fermi level is pinned 0.1 eV below the conduction band edge on p-type Si but shifts to various positions lower within the band gap on n-type Si. This fact leads to the hypothesis of a density of -7 interface states close to the charge change in the Si depletion zone from p- to n-type, namely 10(12) eV(-1) cm(-2). Although some inhomogeneities and defects at the interface are detected by electron microscopy for samples annealed at 750 degrees C, Fermi level position seems rather insensitive to the structural details of the interface while the silicide thickness plays a role on n-type Si.

Abstract: Graphene exhibits exciting potentials for high-speed wideband photodetection and high quantum efficiency solar energy harvest because of its broad spectral absorption, fast photoelectric response, and potential carrier multiplication. Although photocurrent can be generated near a metalgraphene interface in lateral devices, the photoactive area is usually limited to a tiny one-dimensional line-like interface region. Here, we report photoelectric devices based on vertical graphene two-dimensional homojunction, which is fabricated via vertically stacking four graphene monolayers with asymmetric metal contacts. The devices show excellent photovoltaic output with excitation wavelength ranging from visible light to mid-infrared. The wavelength dependence of the internal quantum efficiency gives direct evidence of the carrier multiplication effect in graphene. The simple fabrication process, easy scale-up, large photoresponsive active area, and broadband response of the vertical graphene device are very promising for practical applications in optoelectronics and photovoltaics.

Abstract: Surface plasmon modes in metallic nanostructures largely determine their optoelectronic properties. Such plasmon modes can be manipulated by changing the morphology of the nanoparticles or by bringing plasmonic nanoparticle building blocks close to each other within organized assemblies. We report the EELS mapping of such plasmon modes in pure Ag nanocubes, Au@Ag coreshell nanocubes, and arrays of Au@Ag nanocubes. We show that these arrays enable the creation of interesting plasmonic structures starting from elementary building blocks. Special attention will be dedicated to the plasmon modes in a triangular array formed by three nanocubes. Because of hybridization, a combination of such nanotriangles is shown to provide an antenna effect, resulting in strong electrical field enhancement at the narrow gap between the nanotriangles.

Abstract: Pristine and oxygen plasma functionalised carbon nanotubes (CNTs) were studied after the evaporation of Pt and Pd atoms. High resolution transmission electron microscopy shows the formation of metal nanoparticles at the CNT surface. Oxygen functional groups grafted by the plasma functionalization act as nucleation sites for metal nanoparticles. Analysis of the C1s core level spectra reveals that there is no covalent bonding between the Pt or Pd atoms and the CNT surface. Unlike other transition metals such as titanium and copper, neither Pd nor Pt show strong oxygen interaction or surface oxygen scavenging behaviour.

Abstract: The interaction between evaporated Pt and pristine or oxygen-plasma-treated multiwall carbon nanotubes (CNTs) is investigated. Pt is found to nucleate at defect sites, whether initially present or introduced by oxygen plasma treatment. The plasma treatment induces a uniform dispersion of Pt nanoparticles at the CNT surface. The absence of additional features in the C 1s core level spectrum indicates that no mixed PtC phase is formed. The formation of COPt bonds at the cluster-CNT interface is suggested to reduce the electronic interaction between Pt nanoparticles and the CNT surface.