“Microstructure of adiabatic shear bands in Ti6Al4V”. Peirs J, Tirry W, Amin-Ahmadi B, Coghe F, Verleysen P, Rabet L, Schryvers D, Degrieck J, Materials characterization 75, 79 (2013). http://doi.org/10.1016/j.matchar.2012.10.009
Abstract: Microstructural deformation mechanisms in adiabatic shear bands in Ti6Al4V are studied using traditional TEM and selected area diffraction, and more advanced microstructural characterisation techniques such as energy dispersive X-ray spectroscopy, high angle annular dark field STEM and conical dark field TEM. The shear bands under investigation are induced in Ti6Al4V samples by high strain rate compression of cylindrical and hat-shaped specimens in a split Hopkinson pressure bar setup. Samples from experiments interrupted at different levels of deformation are used to study the evolution of the microstructure in and nearby the shear bands. From the early stages of adiabatic shear band formation, TEM revealed strongly elongated equiaxed grains in the shear band. These band-like grains become narrower towards the centre of the band and start to fraction even further along their elongated direction to finally result in a nano-crystalline region in the core. In fully developed shear bands, twins and a needle-like martensite morphology are observed near the shear band.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 56
DOI: 10.1016/j.matchar.2012.10.009
|
|
|
“Dynamic shear localization in Ti6Al4V”. Peirs J, Verleysen P, Tirry W, Rabet L, Schryvers D, Degrieck J, Procedia Engineering
T2 –, 11th International Conference on the Mechanical Behavior of Materials, (ICM), 2011, Como, ITALY (ICM11) , 1 (2011). http://doi.org/10.1016/j.proeng.2011.04.386
Abstract: The alloy Ti6Al4V is known to be prone to the formation of adiabatic shear bands when dynamically loaded in shear. This causes a catastrophic decrease of the load carrying capacity and is usually followed by fracture. Although, the main mechanism is recognized to be the competition between strain hardening and thermal softening, a detailed understanding of the role of microstructural plasticity mechanisms and macroscopic loading conditions does not exist yet. To study strain localization and shear fracture, different high strain rate shear tests have been carried out: compression of hat-shaped specimens, torsion of thin walled tubular specimens and in-plane shear tests. The value of the three techniques in studying shear localization is evaluated. Post-mortem analysis of the fracture surface and the materials' microstructure is performed with optical and electron microscopy. In all cases a ductile fracture is observed. SEM and TEM techniques are used to study the local microstructure and composition in the shear band and as such the driving mechanism for the ASB formation. (C) 2011 Published by Elsevier Ltd. Selection and/or peer-review under responsibility of ICM11
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 4
DOI: 10.1016/j.proeng.2011.04.386
|
|