“Diagnostic mirrors with transparent protection layer for ITER”. Razdobarin AG, Mukhin EE, Semenov VV, Tolstyakov SY, Kochergin MM, Kurskiev GS, Podushnikova KA, Kirilenko DA, Sitnikova AA, Konovalov VG, Solodovchenko SI, Nekhaieva OM, Skorik OA, Bondarenko VN, Voitsenya VS;, Fusion engineering and design 86, 1341 (2011). http://doi.org/10.1016/j.fusengdes.2011.02.052
Abstract: Fast degradation of in-vessel optics is one of the most serious problems for all optical diagnostics in ITER. To provide the resistance to mechanical and thermal stresses along with a high stability of optical characteristics under deposition-dominated conditions we suggest using high-reflective metallic (Ag or Al) film mirrors coated on silicon substrate and protected with thin oxide film in the divertor Thomson Scattering (TS) diagnostics. The mirrors coated with Al2O3 and ZrO2 films were tested under irradiation by deuterium ions. The experimental results on the oxide films sputtering are discussed in the context of their applicability for the first mirror protection in ITER.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.319
Times cited: 6
DOI: 10.1016/j.fusengdes.2011.02.052
|
|
|
“High reflective mirrors for in-vessel applications in ITER”. Razdobarin AG, Mukhin EE, Semenov VV, YuTolstyakov S, Kochergin MM, Kurskiev GS, Podushnikova KA, Kirilenko DA, Sitnikova AA, Gorodetsky АЕ, Bukhovets VL, Zalavutdinov RK, Zakharov АP, Arkhipov II, Voitsenya VS, Bondarenko VN, Konovalov VG, Ryzhkov IV;, Nuclear instruments and methods in physics research : A: accelerators, spectrometers, detectors and associated equipment 623, 809 (2010). http://doi.org/10.1016/j.nima.2010.04.047
Abstract: The structure and surface morphology of aluminum and silver mirrors covered with protective dielectric oxide layer were studied by means of TEM and SEM. The presence of needle-like pores throughout the thickness of the ZrO(2) film and bubble-like pores in Al(2)O(3) was observed. The test for resistivity to deuterium ion bombardment shows that the exposition to a fluence of similar to 2 x 10(20) ions/cm(2) with the ion energy of 40-50 eV results in appearance of blisters on the surface of mirrors covered wit h Al(2)O(3). For the mirrors protected with ZrO(2) no noticeable changes in surface morphology and reflectivity were found even after order of magnitude higher ion fluence. The effect of different porous structures on blistering phenomena is discussed. (C) 2010 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.362
Times cited: 4
DOI: 10.1016/j.nima.2010.04.047
|
|
|
“Monodisperse spherical mesoporous silica particles : fast synthesis procedure and fabrication of photonic-crystal films”. Trofimova EY, Kurdyukov DA, Yakovlev SA, Kirilenko DA, Kukushkina YA, Nashchekin AV, Sitnikova AA, Yagovkina MA, Golubev VG, Nanotechnology 24, 155601 (2013). http://doi.org/10.1088/0957-4484/24/15/155601
Abstract: A procedure for the synthesis of monodisperse spherical mesoporous silica particles (MSMSPs) via the controlled coagulation of silica/surfactant clusters into spherical aggregates with mean diameters of 250-1500 nm has been developed. The synthesis is fast (taking less than 1 h) because identical clusters are simultaneously formed in the reaction mixture. The results of microscopic, x-ray diffraction, adsorption and optical measurements allowed us to conclude that the clusters are similar to 15 nm in size and have hexagonally packed cylindrical pore channels. The channel diameters in MSMSPs obtained with cethyltrimethylammonium bromide and decyltrimethylammonium bromide as structure-directing agents were 3.1 +/- 0.15 and 2.3 +/- 0.12 nm, respectively. The specific surface area and the pore volume of MSMSP were, depending on synthesis conditions, 480-1095 m(2) g(-1) and 0.50-0.65 cm(3) g(-1). The MSMSP were used to grow opal-like photonic-crystal films possessing a hierarchical macro-mesoporous structure, with pores within and between the particles. A selective filling of mesopore channels with glycerol, based on the difference between the capillary pressures in macro- and mesopores, was demonstrated. It is shown that this approach makes it possible to control the photonic bandgap position in mesoporous opal films by varying the degree of mesopore filling with glycerol. Online supplementary data available from stacks.iop.org/Nano/24/155601/mmedia
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 49
DOI: 10.1088/0957-4484/24/15/155601
|
|
|
“One-step synthesis of a suspended ultrathin graphene oxide film: Application in transmission electron microscopy”. Kirilenko DA, Dideykin AT, Aleksenskiy AE, Sitnikova AA, Konnikov SG, Vul' AY, Micron 68, 23 (2015). http://doi.org/10.1016/j.micron.2014.08.006
Abstract: Ultrathin graphene films find their use as advantageous support for nano- and biomaterials investigations. Thin film causes a very slight deterioration to measured signals, thus providing more details of the object's structure at nanoscale. The ultimate thinness of graphene works in the best way for this purpose. However, obtaining suspended thin film of a large-area, which is convenient for applications, is often a relatively complicated and time-consuming task. Here we present a one-step 1-min technique for synthesis of an extremely thin (about 1-2 nm) continuous film suspended over cells of a conventional copper grid (50-400 mu m mesh). This technique enables us to acquire a large-area film which is water-resistant, stable in organic solvents and can act as a support when studying nanoparticles or biomaterials. Moreover, the very mechanism of the film formation can be interesting from the point of view of other applications of ultrathin graphene oxide papers. (C) 2014 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.98
Times cited: 13
DOI: 10.1016/j.micron.2014.08.006
|
|