“Smart heating profiles for the synthesis of benzene bridged periodic mesoporous organosilicas”. Smeulders G, van Oers C, Van Havenbergh K, Houthoofd K, Mertens M, Martens JA, Bals S, Maes BUW, Meynen V, Cool P, Chemical engineering journal 175, 585 (2011). http://doi.org/10.1016/j.cej.2011.09.116
Abstract: In this study the effects of the heating rate and heating time on the formation of crystal-like benzene bridged periodic mesoporous organosilicas (PMOs) are investigated. The time needed to heat up an autoclave during the hydrothermal treatment has shown to be crucial in the synthesis of PMOs, while the total duration of heating gave rise to only minor differences. By choosing a smart heating profile, superior PMO materials can be obtained in a short time. Different heating profiles in a range from one minute to one hour are adopted by microwave equipment and compared with conventional heating methods. The heating rate has a large influence on the porosity characteristics and the uniformity of the obtained particles. Moreover, two new alternative synthetic strategies to adopt the smart heating profile are presented, in order to give some possible solutions for the expensive microwave equipment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Impact Factor: 6.216
Times cited: 7
DOI: 10.1016/j.cej.2011.09.116
|
“Systematic evaluation of thermal and mechanical stability of different commercial and synthetic photocatalysts in relation to their photocatalytic activity”. Ribbens S, Beyers E, Schellens K, Mertens M, Ke X, Bals S, Van Tendeloo G, Meynen V, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 156, 62 (2012). http://doi.org/10.1016/j.micromeso.2012.01.036
Abstract: The effect of thermal treatment and mechanical stress on the structural and photocatalytic properties of eight different (synthetic and commercial) photocatalysts has been thoroughly investigated. Different mesoporous Ti-based materials were prepared via surfactant based synthesis routes (e.g. Pluronic 123, CTMABr = Cetyltrimethylammonium bromide) or via template-free synthesis routes (e.g. trititanate nanotubes). Also, the stabilizing effect of the NaOH/NH4OH post-treatment on the templated mesoporous materials and their photocatalytic activity was investigated. Furthermore, the thermal and mechanical properties of commercially available titanium dioxides such as P25 Evonik® and Millenium PC500® were studied. The various photocatalysts were analyzed with N2-sorption, X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA) to obtain information concerning the specific surface area, pore volume, crystal structure, morphology, phase transitions, etc. In general, results show that the NaOH post-treatment leads to an increased control of the crystallization process during calcination resulting in a higher thermal stability, but at the same time diminishes the photocatalytic activity. Mesoporous materials in which pre-synthesized nanoparticles are used as titania source have the best mechanical stability whereas the mechanical stability of the nanotubes is the most limited. At increased temperatures and pressures, the tested commercial titanium dioxides lose their superior photocatalytic activity caused by a decreased accessibility of the active sites. The observed changes in adsorption capacities and photocatalytic activities cannot be assigned to one single phenomenon. In this respect, it shows the need to define a general/standard method to compare different photocatalysts. Furthermore, it is shown that the photocatalytic properties do not necessarily deteriorate under thermal stress, but can be improved due to crystallization, even though the initial material is (partially) destroyed. It is shown that the usefulness of a specific type of photocatalyst strongly depends on the application and the temperature/pressure to which it needs to resist.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 8
DOI: 10.1016/j.micromeso.2012.01.036
|
“Zeolite \beta nanoparticles based bimodal structures : mechanism and tuning of the porosity and zeolitic properties”. van Oers CJ, Kurttepeli M, Mertens M, Bals S, Meynen V, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 185, 204 (2014). http://doi.org/10.1016/j.micromeso.2013.11.021
Abstract: Despite great efforts in the research area of zeolite nanoparticles and their use in the synthesis of bimodal materials, still little is known about the impact of the synthesis conditions of the zeolite nanoparticles on its own characteristics, and on the properties and the formation mechanism of the final bimodal materials. A zeolite β nanoparticles solution is applied in a mesotemplate-free synthesis method, and the influence of the hydrothermal ageing temperature of the nanoparticles solution on both the zeolitic and porosity characteristics of the final bimodal material has been studied. Transmission electron microscopy in combination with 3-dimensional reconstructions obtained by electron tomography revealed that the zeolite β nanoparticles are connected by neck-like structures, thus creating a wormhole-like mesoporous material. Considering the zeolitic properties, a clear threshold is observed in the synthesis temperature series at 413 K. Below and at this threshold, the biporous materials show no apparent zeolitic characteristics, although these materials exhibit a more condensed and uniform SiOSi network in comparison to Al-MCF. Synthesis temperatures above the threshold lead to bimodal structures with defined zeolitic properties. Moreover, the dimensions of the nanoparticles are studied by TEM, revealing an increasing particle size with increasing temperature under the threshold of 413 K, which is in agreement with a sol-mechanism. This mechanism is disturbed after the threshold due to the start of the crystallisation process.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 10
DOI: 10.1016/j.micromeso.2013.11.021
|
“Zn-Al layered double hydroxides: synthesis, characterization and photocatalytic application”. Seftel EM, Popovici E, Mertens M, de Witte K, Van Tendeloo G, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 113, 296 (2008). http://doi.org/10.1016/j.micromeso.2007.11.029
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 154
DOI: 10.1016/j.micromeso.2007.11.029
|
“Texturing of hydrothermally synthesized BaTiO3 in a strong magnetic field by slip casting”. Özen M, Mertens M, Snijkers F, Van Tendeloo G, Cool P, Ceramics international 42, 5382 (2016). http://doi.org/10.1016/j.ceramint.2015.12.073
Abstract: Barium titanate powder was processed by slip casting in a rotating strong magnetic field of 9.4 T. The orientation factor of the sintered compact was analyzed by the X-ray diffraction technique and the microstructure (grain-size) was analyzed by scanning electron microscope. The hydrothermally prepared barium titanate was used as matrix material and the molten-salt synthesized barium titanate, with a larger particle-size, was used as template for the templated grain-growth process. Addition of large template particles was observed to increase the orientation factor of the sintered cast (5 vol% loading). Template particles acted as starting grains for the abnormal grain-growth process and the average grain-size was increased after sintering. Increasing the solid loading (15 vol%) resulted in a similar orientation factor with a decrease of the average grain size by more than half. However, addition of templates to the 15 vol% cast had a negative effect on the orientation factor. The impingement of growing particles was stated as the primary cause of particle misorientation resulting in a low orientation factor after sintering. Different heating conditions were tested and it was determined that a slow heating rate gave the highest orientation factor, the smallest average grain-size and the highest relative density. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.986
Times cited: 11
DOI: 10.1016/j.ceramint.2015.12.073
|
“SnIV-containing layered double hydroxides as precursors for nano-sized ZnO/SnO2 photocatalysts”. Seftel EM, Popovici E, Mertens M, Stefaniak EA, Van Grieken R, Cool P, Vansant EF, Applied catalysis : B : environmental 84, 699 (2008). http://doi.org/10.1016/J.APCATB.2008.06.006
Abstract: Sn4+-containing LDH was prepared using the co-precipitation method at constant pH, and characterized using X-ray diffraction, UVvis diffuse reflectance spectroscopy and TG/DTG methods. The obtained product was further exposed to different thermal treatments in order to obtain nano-sized coupled ZnO/SnO2 systems with enhanced photocatalytic performances than the ones obtained by mixing the two semiconductor oxides. The formation of a well-defined ZnO/SnO2 system and the crystallite size, fully investigated using XRD, micro-Raman scattering and UVvis DR techniques, were found to be influenced by the nature of the precursors and the calcination temperature. The photocatalytic activity of the ZnO/SnO2 systems, evaluated for the photodegradation of methyl orange (MO) dye, was studied as a function of the initial pH, catalyst loading and the calcination temperature. The metal dispersion supplied by layered structures proved to be an advantage when preparing coupled ZnO/SnO2 systems, the photocatalytic activity being 2.3 times higher comparing with the physical mixtures performances. The maximum photocatalytic activity of the coupled ZnO/SnO2 system having a layered precursor was observed when using neutral pH, at a catalyst loading of 1 g/L calcined at 600 °C for 4 h.
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.APCATB.2008.06.006
|