Abstract: We are reporting an unexpected metal insulator transition at the ferromagnetic phase-transition temperature for thin films of La0.9Sr0.1MnO3 (< 50 nm), grown on a (100) face of SrTiO3 substrate. For the thicker films (> 50 nm), similar to the single crystal, no such transition is observed below T-C. Additionally, we observe the suppression of the features associated with charge or orbital ordering in intentionally La-deficient thin films of La0.88Sr0.1MnO3 (< 75 nm). In thin films, transmission electron microscopy reveals a compressive strain due to the epitaxial growth, that is, lattice parameters adopt those of the cubic lattice of SrTiO3. As the film thickness increases, coherent microtwinning is observed in the films and the films relax to a orthorhombic structure. (C) 2000 American Institute of Physics. [S0003-6951(00)00402-2].

Abstract: Two CoSi2/Si1-xGex/Si(100) heterostructures, with different Ge content, made by molecular beam epitaxy are characterized by high resolution electron microscopy. In general, the interface between the CoSi2 thin film and the Si1-xGex layer is of a high structural quality and the strained Si1-xGex layer exhibits few defects. For both samples, different interface structures are present, although the dominant interfacial configuration is similar to the unreconstructed interface present at the CoSi2/Si(100) interface. Only occasionally (2x1) reconstructed interface regions are found which are just a few nanometers in length. Phenomena such as Ge segregation and the introduction of defects are also observed in the Si1-xGex layer. We attribute the minimal presence of the reconstructed interface to both the (2x8):Si1-xGex(100) surface reconstruction and the Ge segregation that takes place. (C) 1999 American Institute of Physics. [S0021-8979(99)02104-0].

Abstract: Variations in local bond length and coordination in boron-doped nanocrystalline diamond (NCD) films have been studied through changes in the fine structure of boron and carbon K-edges in electron energy-loss spectra, acquired in a scanning transmission electron microscope. The presence of high concentrations of B in pristine diamond regions and enrichment of B at defects in single NCD grains is demonstrated. Local bond length variations are evidenced through an energy shift of the carbon 1s → σ* edge at B-rich defective regions within single diamond grains, indicating an expansion of the diamond bond length at sites with local high B content.

Abstract: An Er3Fe5O12 ceramic has been sintered in oxygen atmosphere at 1400 °C for dielectric measurements. Its structural quality at room temperature has been checked by combining transmission electron microscopy and X-ray diffraction. It crystallizes in the cubic space group Ia3d with a = 12.3488(1). The dielectric permittivity ([variantgreekepsilon]′) and losses (tan δ) measurements as a function of temperature reveal the existence of two anomalies, a broad one between 110 K and 80 K, attributed to the Er3+ spin reorientation, and a second sharper feature at about 45 K associated to the appearance of irreversibility on the magnetic susceptibility curves. In contrast to the lack of magnetic field impact on [variantgreekepsilon]′ for the former anomaly, a complex magnetic field effect has been evidenced below 45 K. The isothermal [variantgreekepsilon]′(H) curves show the existence of positive magnetodielectric effect, reaching a maximum of 0.14% at 3 T and 10 K. Its magnitude decreases as H is further increased. Interestingly, for the lowest H values, a linear regime in the [variantgreekepsilon]′(H) curve is observed. From this experimental study, it is concluded that the [variantgreekepsilon]′ anomaly, starting above the compensation temperature Tc (75 K) and driven by the internal magnetic field, is not sensitive to an applied external magnetic field. Thus, below 45 K, it is the magnetic structure which is responsible for the coupling between spin and charge in this iron garnet.

Abstract: Sr2FeMoO6/SrTiO3/CoFe2 trilayers grown by pulsed laser deposition on SrTiO3 (001) are investigated by transmission electron microscopy and electron energy loss spectroscopy. The stack is epitaxial, independent of whether the CoFe2 electrode is grown at 500 or at 50 degrees C. Thus it is possible to obtain epitaxy near room temperature. The SrTiO3/CoFe2 interface is quite sharp, while the Sr2FeMoO6/SrTiO3 interface presents regions of Fe depletion. The chemical composition of the films is close to the nominal stoichiometries. These results could be useful for the growth of heteroepitaxial devices and magnetic tunnel junctions. (C) 2007 American Institute of Physics.

Abstract: We compare the magnetic properties of pure and oxidized Co nanoparticles embedded in an amorphous Al2O3 matrix. Nanoparticles with diameters of 2 or 3 nm were prepared by alternate pulsed laser deposition in high vacuum conditions, and some of them were exposed to O-2 after production and before being embedded. The nanoparticles are organized in layers, the effective edge-to-edge in-depth separation being 5 or 10 nm. The lower saturation magnetizations per Co atom for the samples containing oxidized nanoparticles provide evidence for the formation of antiferromagnetic CoO shells in the nanoparticles. None of the samples with Co/CoO nanoparticles show exchange bias, while vertical hysteresis loop shifts and enhanced coercivities (as compared to samples with pure Co nanoparticles) are observed. This constitutes evidence for the nanoparticles size being in all cases smaller than the critical size for exchange bias. The difference in coercivity versus temperature dependences for the samples with pure and oxidized Co nanoparticles shows that the exchange anisotropy in Co/CoO nanoparticles appears at temperatures lower than 50 K. (c) 2007 American Institute of Physics.

Abstract: Faraday rotation has been used to investigate a series of polymer films doped with magnetic iron oxide nanoparticles. The films have been prepared by spin-coating and melt-processing. In each case, upon varying the angle of optical incidence on the films, an in-plane magnetic anisotropy is observed. The effect of such an anisotropy on the Faraday rotation as a function of the angle of optical incidence is verified by comparison with magnetically poled films. These results demonstrate that care should be taken upon analyzing the magnetic behavior of such films on account of the sample preparation techniques themselves being able to affect the magnetization.

Abstract: As-prepared and heat-treated oxyfluoride glasses, co-doped with Ag nanoclusters/nanoparticles, are prepared at 0.15 at. % Ag concentration. The as-prepared glass shows an absorption band in the UV/violet attributed to the presence of amorphous Ag nanoclusters with an average size of 1.1 nm. The luminescence spectra of the untreated glass can also be ascribed to these Ag nanoclusters. Upon heat-treatment, the clusters coalesce into Ag nanoparticles with an average size of 2.3 nm, and the glasses show an extra surface plasmon absorption band in the visible. These particles, however, cease to emit due to ascribing plasmonic properties of bulk silver.

Abstract: Addition of yttrium in HfO(2) thin films prepared on silicon by metal organic chemical vapor deposition is investigated in a wide compositional range (2.0-99.5 at. %). The cubic structure of HfO(2) is stabilized for 6.5 at. %. The permittivity is maximum for yttrium content of 6.5-10 at. %; in this range, the effective permittivity, which results from the contribution of both the cubic phase and silicate phase, is of 22. These films exhibit low leakage current density (5x10(-7) A/cm(2) at -1 V for a 6.4 nm film). The cubic phase is stable upon postdeposition high temperature annealing at 900 degrees C under NH(3). (c) 2006 American Institute of Physics.

Abstract: A transmission electron microscopy study of epitaxial C-60 and C-70 films grown on a GeS (001) surface is presented. The relationship between the orientation of the substrate and the films and structural defects in the films, such as grain boundaries, unknown in bulk C-60 and C-70 crystals, are studied. Small misalignments of the overlayers with respect to the orientation of the substrate, so-called epitaxial rotations, exist mainly in C-70 films, but also sporadically in the C-60 overlayers. A simple symmetry model, previously used to predict the rotation of hexagonal overlayers on hexagonal substrates, is numerically tested and applied to the present situation. Some qualitative conclusions concerning the substrate-film interaction are deduced. (C) 1996 American Institute of Physics.

Abstract: Sr1-xLaxCuO2-delta (x=0.10-0.20) thin films exhibiting an oxygen-deficient 2 root 2a(p)x2 root a(p) x c structure (a(p) and c represent the cell parameters of the perovskite subcell) were epitaxially grown by means of pulsed laser deposition in low-pressure oxygen ambient. (001) KTaO3 and (001) SrTiO3 single crystals were used as substrates, with BaTiO3 as buffer layer. The Sr1-xLaxCuO2-delta films were oxidized during cooling down in order to yield the infinite-layer-type structure. By applying this method, high quality single-phase Sr1-xLaxCuO2 thin films could be obtained for 0.10 <= x <= 0.175 doping range. The films grown on BaTiO3/KTaO3 show superconductivity for 0.15 <= x <= 0.175 with optimum doping at x=0.15, in contrast with previously reported data. (c) 2006 American Institute of Physics.