Abstract: As-prepared and heat-treated oxyfluoride glasses, co-doped with Ag nanoclusters/nanoparticles, are prepared at 0.15 at. % Ag concentration. The as-prepared glass shows an absorption band in the UV/violet attributed to the presence of amorphous Ag nanoclusters with an average size of 1.1 nm. The luminescence spectra of the untreated glass can also be ascribed to these Ag nanoclusters. Upon heat-treatment, the clusters coalesce into Ag nanoparticles with an average size of 2.3 nm, and the glasses show an extra surface plasmon absorption band in the visible. These particles, however, cease to emit due to ascribing plasmonic properties of bulk silver.

Abstract: Addition of yttrium in HfO(2) thin films prepared on silicon by metal organic chemical vapor deposition is investigated in a wide compositional range (2.0-99.5 at. %). The cubic structure of HfO(2) is stabilized for 6.5 at. %. The permittivity is maximum for yttrium content of 6.5-10 at. %; in this range, the effective permittivity, which results from the contribution of both the cubic phase and silicate phase, is of 22. These films exhibit low leakage current density (5x10(-7) A/cm(2) at -1 V for a 6.4 nm film). The cubic phase is stable upon postdeposition high temperature annealing at 900 degrees C under NH(3). (c) 2006 American Institute of Physics.

Abstract: A transmission electron microscopy study of epitaxial C-60 and C-70 films grown on a GeS (001) surface is presented. The relationship between the orientation of the substrate and the films and structural defects in the films, such as grain boundaries, unknown in bulk C-60 and C-70 crystals, are studied. Small misalignments of the overlayers with respect to the orientation of the substrate, so-called epitaxial rotations, exist mainly in C-70 films, but also sporadically in the C-60 overlayers. A simple symmetry model, previously used to predict the rotation of hexagonal overlayers on hexagonal substrates, is numerically tested and applied to the present situation. Some qualitative conclusions concerning the substrate-film interaction are deduced. (C) 1996 American Institute of Physics.

Abstract: Sr1-xLaxCuO2-delta (x=0.10-0.20) thin films exhibiting an oxygen-deficient 2 root 2a(p)x2 root a(p) x c structure (a(p) and c represent the cell parameters of the perovskite subcell) were epitaxially grown by means of pulsed laser deposition in low-pressure oxygen ambient. (001) KTaO3 and (001) SrTiO3 single crystals were used as substrates, with BaTiO3 as buffer layer. The Sr1-xLaxCuO2-delta films were oxidized during cooling down in order to yield the infinite-layer-type structure. By applying this method, high quality single-phase Sr1-xLaxCuO2 thin films could be obtained for 0.10 <= x <= 0.175 doping range. The films grown on BaTiO3/KTaO3 show superconductivity for 0.15 <= x <= 0.175 with optimum doping at x=0.15, in contrast with previously reported data. (c) 2006 American Institute of Physics.

Abstract: We demonstrate the epitaxial growth of Fe₃O₄ films on ZnO by a simple reactive deposition procedure using molecular oxygen as an oxidizing agent. X-ray photoelectron spectroscopy results evidence that the iron-oxide surface is nearly stoichiometric magnetite. X-ray diffraction results indicate monocrystalline epitaxy and almost complete structural relaxation. Scanning transmission electron micrographs reveal that the microstructure consists of domains which are separated by antiphase boundaries or twin boundaries. The magnetite films show rather slow magnetization behavior in comparison with bulk crystals probably due to reduced magnetization at antiphase boundaries in small applied fields.

Abstract: Single-crystalline MnOOH and Mn3O4 nanowires have been prepared by hydrothermal treatment of commercial bulky manganese oxide particles. beta-MnO2 and alpha-Mn2O3 nanowires were prepared by calcination of MnOOH nanowires. Transmission electron microscopy analysis demonstrates that MnOOH nanowires grow directly from MnO2 raw particles. The diameter of the nanowires is 20-70 nm, while the length can reach several micrometers. MnOOH nanowires grow preferentially along the [010] direction and Mn3O4 nanowires prefer to grow along the [001] direction; the long dimension of both beta-MnO2 and alpha-Mn2O3 nanowires is along [001]. Electron energy-loss spectroscopy analysis shows that the position of the prepeak of the oxygen K edge shifts to higher energy and the energy separation between the two main peaks of the oxygen K edge decreases with decreasing manganese oxidation state. The manganese-white-line ratios (L-3/L-2) were calculated. (C) 2005 American Institute of Physics.

Abstract: Three series of poly(butylene succinate) (PBSu) nanocomposites containing 0.5, 1 and 2.5 wt% strontium hydroxyapatite [Sr-5(PO4)(3)OH] nanorods (SrHAp nrds) were prepared by in situ polymerisation. The structural effects of Sr-5(PO4)(3)OH nanorods, for the different concentrations, inside the polymeric matrix (PBSu), were studied through high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). HAADF-STEM measurements revealed that the SrHAp nanorods at low concentrations are dispersed inside the polymeric PBSu matrix while in 1 wt% some aggregates are formed. These aggregations affect the mechanical properties giving an enhancement for the concentration of 0.5 wt% SrHAp nrds in tensile strength, while a reduction is recorded for higher loadings of the nanofiller. Studies on enzymatic hydrolysis revealed that all nanocomposites present higher hydrolysis rates than neat PBSu, indicating that nanorods accelerate the hydrolysis degradation process. In vitro bioactivity tests prove that SrHAp nrds promote the formation of hydroxyapatite on the PBSu surface. All nanocomposites were tested also in relevant cell culture using osteoblast-like cells (MG-63) to demonstrate their biocompatibility showing SrHAp nanorods support cell attachment.

Abstract: We studied the morphology of ramps in REBa2CU3O7 (REBCO) epitaxial films on SrTiO3 substrates, fabricated by RF magnetron sputter deposition and pulsed laser deposition (PLD), by scanning probe microscopy (SPM) and high resolution electron microscopy (HREM). The ramps were fabricated by Ar ion beam etching using masks of standard photoresist and TIN. AFM-studies on ramps in sputter deposited films show a strong dependence, i.e. formation of facets and ridges, on the angle of incidence of the ion beam with respect to the substrate surface as well as the rotation angle with respect to the crystal axes of the substrate. Ramps in pulsed laser deposited films did not show this dependence, Furthermore, we studied the effect of an anneal step prior to the deposition of barrier layers (i.e. PrBa2CU3O7, SrTiO3, CeO2) on the ramp. First results show a recrystallization of the ramp surface, resulting in terraces and a non-homogeneous growth of the barrier material on top of it. The thickness variations, for thin layers of barrier material, con even become much larger than expected from the amount of deposited material and are dependent on the deposition and anneal conditions. HREM studies show a well defined interface between barrier layer and electrodes. The angle of the ramp depends on the etch rate of the mask and REBCO, and on the angle of incidence of the ion beam. TiN has a much lower etch rate compared to photoresist, resulting in an angle of the ramp comparable to the angle of incidence, resulting in a low etching rate on the ramp. These results will lead to improved electrical characteristics of ramp-type junctions.

Abstract: The thermal stability of amorphous Al2O3 films (similar to8 and 80 nut thick) deposited by atomic layer deposition on HF-last and thin SiO2 covered (001) Si substrates is studied by transmission electron microscopy. The layers are in- and ex-situ annealed in the same temperature range.