Abstract: A novel anion-deficient perovskite-based compound, Pb2.4Ba2.6Fe2Sc2TiO13, was synthesized via the citrate-based route. This compound is an n = 5 member of the A(n)B(n)O(3n-2) homologous series with unit-cell parameters related to the perovskite subcell a(p) approximate to 4.0 angstrom as a(p)root 2 x a(p) x 5a(p)root 2. The crystal structure of Pb2.4Ba2.6Fe2Sc2TiO13 consists of quasi-2D perovskite blocks with a thickness of three octahedral layers separated by the 1/2[110]((1) over bar 01)(p) crystallographic shear (CS) planes, which are parallel to the {110} plane of the perovskite subcell. The CS planes transform the corner-sharing octahedra into chains of edge-sharing distorted tetragonal pyramids. Using a combination of neutron powder diffraction, Fe-57 Mossbauer spectroscopy and atomic resolution electron energy-loss spectroscopy we demonstrate that the B-cations in Pb2.4Ba2.6Fe2Sc2TiO13 are ordered along the {110} perovskite layers with Fe3+ in distorted tetragonal pyramids along the CS planes, Ti4+ preferentially in the central octahedra of the perovskite blocks and Sc3+ in the outer octahedra of the perovskite blocks. Magnetic susceptibility and Mossbauer spectroscopy indicate a broadened magnetic transition around T-N similar to 45 K and the onset of local magnetic fields at low temperatures. The magnetic order is probably reminiscent of that in other A(n)B(n)O(3n-2) homologues, where G-type AFM order within the perovskite blocks has been observed.

Abstract: The properties of a clean superconductor with nanoscale dimensions are governed by quantum confinement of the electrons. This results in a spatially inhomogeneous superconducting condensate and in the formation of new Andreev-type quasiparticle states. These states are mainly located beyond regions where the superconducting condensate is enhanced. A numerical self-consistent solution of the Bogoliubov-de Gennes equations for a cylindrical metallic nanowire shows that these new Andreev-type states decrease the ratio of the energy gap to the critical temperature.

Abstract: The split diffuse maxima around the {110} and {100} positions in the diffraction pattern of short-range-ordered Cu1-xPdx alloys (x=0.10...0.60) are attributed to small atomic clusters, being part of the underlying fee lattice. By analyzing the reciprocal space geometry, our cluster method identifies two prominent cluster types: the tetrahedron of nearest neighbors and a linear three-points cluster along the [110] directions. Since both cluster types contain different information on the same nearest-neighbor correlations, local anisotropy has to be assumed. It is shown that the three interatomic pair interactions within these basic clusters are sufficient to generate the spot splitting in the diffraction pattern. A ground-state analysis with these interactions reproduces the results of the anisotropic next-nearest-neighbor Ising model.

Abstract: The electron wave functions in the inversion layer are analyzed in the case where the dielectric barriers are not infinite. This forces the electron concentration closer to the interface silicon/oxide and reduces the subband energy. This treatment of the inversion layer is extended to the calculation of the electron mobility degradation due to remote Coulomb scattering on a high-k dielectric stacked transistor. The subband energy reduction leads to a decrease of the scattering charge needed to explain the experimental results. This model can also fit better the experimental data when compared with the case where no barrier permeation is considered.

Abstract: The effects of high dose ion irradiation in β CuZnAl were investigated between room temperature and 150 °C. Single crystal samples with surface normal close to [001]β were irradiated with 300 keV Cu+ ions. Microstructural changes were characterized using transmission electron microscopy. Irradiation induced cavities located on the surface exposed to the irradiation were observed. The morphology, size and density distribution of these cavities were analyzed as a function of different irradiation conditions. The shape and location of the cavities with respect to the irradiation surface were not affected by irradiation temperature or irradiation dose. Instead, the cavity size distribution showed a bi-modal shape for a dose of 15 dpa, regardless of irradiation temperature. For a dose of 30 dpa the bi-modal distribution was only observed after room temperature irradiation. The diffusion effects of vacancies produced by irradiation are analyzed in shape memory CuZnAl alloys, which main characteristic is the diffusionless martensitic transformation. Particularly, the cavity size distributions were analyzed in terms of nucleation, growth and coalescence.

Abstract: We study the coherent dynamics of pairing in a nanoscale superconductor, that is intrinsically multiband, after an external perturbation in the non-adiabatic regime. The description of the dynamics of the pairing order is within the density-matrix approach based on the BCS model and the Bogoliubov-de Gennes equations. We find that for certain resonant wire widths the superconducting order parameter exhibits two oscillatory frequencies which are determined by the long-time asymptotic values of the subgaps. This in turn leads to a pronounced beating phenomenon. (C) 2014 Elsevier B.V. All rights reserved.

Abstract: A methodology for the quantitative compositional characterization of nickel silicides by high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) imaging is presented. HAADF-STEM images of a set of nickel silicide reference samples Ni3Si, Ni31Si12, Ni2Si, NiSi and NiSi2 are taken at identical experimental conditions. The correlation between sample thickness and HAADF-STEM intensity is discussed. In order to quantify the relationship between the experimental Z-contrast intensities and the composition of the analysed layers, the ratio of the HAADF-STEM intensity to the sample thickness or to the intensity of the silicon substrate is determined for each nickel silicide reference sample. Diffraction contrast is still detected on the HAADF-STEM images, even though the detector is set at the largest possible detection angle. The influence on the quantification results of intensity fluctuations caused by diffraction contrast and channelling is examined. The methodology is applied to FUSI gate devices and to horizontal TFET devices with different nickel silicides formed on source, gate and drain. It is shown that, if the elements which are present are known, this methodology allows a fast quantitative 2-dimensional compositional analysis.

Abstract: A classical two-dimensional (2D) model for an artificial atom is used to make a numerical exact study of elastic and nonelastic scattering. Interesting differences in the scattering angle distribution between this model and the well-known Rutherford scattering are found in the small energy and/or small impact parameter scattering regime. For scattering off a classical 2D hydrogen atom different phenomena such as ionization, exchange of particles, and inelastic scattering can occur. A scattering regime diagram is constructed as function of the impact parameter (b) and the initial velocity (v) of the incoming particle. In a small regime of the (b,v) space the system exhibits chaos, which is studied in more detail. Analytic expressions for the scattering angle are given in the high impact parameter asymptotic limit.

Abstract: We investigate the influence of an external perpendicular magnetic field on the lowest-energy states of an electron bound to a donor which is located near a semiconductor-metal interface. The problem is treated within the effective mass approach and the lowest-energy states are obtained through (1) the “numerically exact” finite element method, and (2) a variational approach using a trial wave function where all image charges that emerge due to the presence of the metallic gate are taken into account. The trial wave functions are constructed such that they reduce to an exponential behavior for sufficiently small magnetic fields and become Gaussian for intermediate and large magnetic fields. The average electron-donor distance can be controlled by the external magnetic field. We find that the size of the 2p(z) state depends strongly on the magnetic field when the donor is close to the interface, showing a nonmonotonic behavior, in contrast with the ground and the other excited states. DOI: 10.1103/PhysRevB.87.075313

Abstract: The effect of mold hardness on the microstructure of ductile iron and the contraction porosity was investigated. Molds with different hardnesses (0.41, 0.48, 0.55, 0.62 MPa) and a sand mold prepared by Co2 method were used. The influence of silicon content on the induced expansion pressure owing to the formation of graphite was also investigated. The contraction during solidification can be compensated by an induced expansion owing to the graphite relief when the hardness of mold increases; therefore, the possibility of achieving a sound product without using any riser increases.

Abstract: The growth features of FeCr2S4 spinel single crystals prepared by chemical vapour transport were studied by means of scanning electron microscopy, transmission electron microscopy, high resolution electron microscopy, electron diffraction and X-ray analysis. Our results indicate that the epitaxial growth of the new phases FeCr7S12 and FeCr8S12, both based on the NiAs structure, can essentially inhibit the growth of large FeCr2S4 spinel single crystals in the octahedral habit. The new phases are fully characterised and the effects of defect ordering in these new phases are also reported.

Abstract: Nb-rich precipitates in the matrix of as-cast and annealed Ni45.5Ti45.5Nb9 alloys are investigated by scanning and scanning transmission electron microscopy, including slice-and-view and geometric phase analysis (GPA). The Nb-rich bcc nano-precipitates in the as-cast alloy have a 10% lattice parameter difference with the B2 matrix and reveal compensating interface dislocations. The 3D reconstruction of the configuration of small Nb-rich precipitates in the annealed alloy reveals a wall-like distribution of precipitates, which may increase the thermal hysteresis of the material.