“New anion-conducting solid solutions Bi1-xTex(O,F)2+\delta (x >, 0.5) and glassceramic material on their base”. Prituzhalov VA, Ardashnikova EI, Vinogradov AA, Dolgikh VA, Videau J-J, Fargin E, Abakumov AM, Tarakina NV, Van Tendeloo G, Journal of fluorine chemistry 132, 1110 (2011). http://doi.org/10.1016/j.jfluchem.2011.06.042
Abstract: The anion-excess fluorite-like solid solutions with general composition Bi1−xTex(O,F)2+δ (x > 0.5) have been synthesized by a solid state reaction of TeO2, BiF3 and Bi2O3 at 873 K with following quenching. The homogeneity areas and polymorphism of the I ↔ IV Bi1−xTex(O,F)2+δ phases were investigated. The crystal structure of the low temperature IV-Bi1−xTex(O,F)2+δ phase has been solved using electron diffraction and X-ray powder diffraction (a = 11.53051(9) Å, S.G. Ia-3, RI = 0.046, RP = 0.041). Glass formation area in the Bi2O3BiF3TeO2 (10% TiO2) system was investigated. IVBi1−xTex(O,F)2+δ phase starts to crystallize at short-time (0.53 h) annealing of oxyfluoride glasses at temperatures above Tg (600615 K). The ionic conductivity of the crystalline Bi1−xTex(O,F)2+δ phase and corresponding glass-ceramics was investigated. Activation energy of conductivity Ea = 0.41(2) eV for the IV-Bi1−xTex(O,F)2+δ crystalline samples and Ea = 0.73 eV for the glass-ceramic samples were obtained. Investigation of the oxyfluoride samples with a constant cation ratio demonstrates essential influence of excess fluorine anions on the ionic conductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.101
Times cited: 2
DOI: 10.1016/j.jfluchem.2011.06.042
|
|