“Fe3O4@MIL-101-A selective and regenerable adsorbent for the removal of as species from water”. Folens K, Leus K, Nicomel NR, Meledina M, Turner S, Van Tendeloo G, Du Laing G, Van Der Voort P, European journal of inorganic chemistry 2016, 4395 (2016). http://doi.org/10.1002/EJIC.201600160
Abstract: The chromium-based metal organic framework MIL-101(Cr) served as a host for the in situ synthesis of Fe3O4 nano particles. This hybrid nanomaterial was tested as an adsorbent for arsenite and arsenate species in groundwater and surface water and showed excellent affinity towards As-III and As-V species. The adsorption capacities of 121.5 and 80.0 mg g(-1) for arsenite and arsenate species, respectively, are unprecedented. The presence of Ca2+, Mg2+, and phosphate ions and natural organic matter does not affect the removal efficiency or the selectivity. The structural integrity of the hybrid nanomaterial was maintained during the adsorption process and even after desorption through phosphate elution. Additionally, no significant leaching of Cr or Fe species was observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 27
DOI: 10.1002/EJIC.201600160
|
|
|
“High resolution electron microscopy of recent high Tc superconductors”. Van Tendeloo G, European Crystallographic Meeting 15, 20 (1994)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Chabazite : stable cation-exchanger in hyper alkaline concrete pore water”. Van Tendeloo L, Wangermez W, Kurttepeli M, de Blochouse B, Bals S, Van Tendeloo G, Martens JA, Maes A, Kirschhock CEA, Breynaert E, Environmental science and technology 49, 2358 (2015). http://doi.org/10.1021/es505346j
Abstract: To avoid impact on the environment, facilities for permanent disposal of hazardous waste adopt multibarrier design schemes. As the primary barrier very often consists of cement-based materials, two distinct aspects are essential for the selection of suitable complementary barriers: (1) selective sorption of the contaminants in the repository and (2) long-term chemical stability in hyperalkaline concrete-derived media. A multidisciplinary approach combining experimental strategies from environmental chemistry and materials science is therefore essential to provide a reliable assessment of potential candidate materials. Chabazite is typically synthesized in 1 M KOH solutions but also crystallizes in simulated young cement pore water, a pH 13 aqueous solution mainly containing K+ and Na+ cations. Its formation and stability in this medium was evaluated as a function of temperature (60 and 85 °C) over a timeframe of more than 2 years and was also asessed from a mechanistic point of view. Chabazite demonstrates excellent cation-exchange properties in simulated young cement pore water. Comparison of its Cs+ cation exchange properties at pH 8 and pH 13 unexpectedly demonstrated an increase of the KD with increasing pH. The combined results identify chabazite as a valid candidate for inclusion in engineered barriers for concrete-based waste disposal.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.198
Times cited: 13
DOI: 10.1021/es505346j
|
|
|
“Diatom silica-titania photocatalysts for air purification by bio-accumulation of different titanium sources”. Van Eynde E, Hu Z-Y, Tytgat T, Verbruggen SW, Watte J, Van Tendeloo G, Van Driessche I, Blust R, Lenaerts S, Environmental science : nano 3, 1052 (2016). http://doi.org/10.1039/C6EN00163G
Abstract: We present a green, biological production route for silica-titania photocatalysts using diatom microalgae. Diatoms are single-celled, eukaryotic microalgae (2-2000 mu m) that self-assemble soluble silicon (Si(OH)(4)) into intricate silica cell walls, called frustules. These diatom frustules are formed under ambient conditions and consist of hydrated silica with specific 3D morphologies and micro-meso or macroporosity. A remarkable characteristic of diatoms is their ability to bioaccumulate soluble titanium from cell culture medium and incorporate them into their nanostructured silica cell wall. Controlled cultivation of the diatom Pinnularia sp. on soluble titanium in a batch process resulted in the biological immobilisation of titanium dioxide in the porous 3D architecture of the frustules. Six different titanium sources are tested. The silica-titania frustules were isolated by treating the harvested Pinnularia cells with nitric acid (65%) or by high temperature treatment. Thermal annealing converted the amorphous titania into crystalline titania. The produced silica-titania material is evaluated towards photocatalytic activity for acetaldehyde (C2H4O) abatement. Frustules cultivated with TiBaldH showed the highest photocatalytic performance. Comparison of the photocatalytic activity with P25 reveals that P25 has a 4 fold higher photocatalytic activity, but when photocatalytic activity is normalized for titania content, the frustules show double activity. Further material characterization (morphology, crystallinity, surface area and elemental distribution) of the TiBaldH silica-titania frustules provides additional insight into their structure-activity relationship. These natural biosilicatitania materials have excellent properties for photocatalytic purposes, including high surface area (108 m(2) g(-1)) and good porosity, and show reliable immobilization of TiO2 in the ordered structure of the diatom frustule.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 6.047
Times cited: 7
DOI: 10.1039/C6EN00163G
|
|
|
“Platinum particle size and support effects in NOx mediated carbon oxidation over platinum catalysts”. Villani K, Vermandel W, Smets K, Liang D, Van Tendeloo G, Martens JA, Environmental science &, technology 40, 2727 (2006). http://doi.org/10.1021/es051871h
Abstract: Platinum metal was dispersed on microporous, mesoporous, and nonporous support materials including the zeolites Na-Y, Ba-Y, Ferrierite, ZSM-22, ETS-10, and AlPO-11, alumina, and titania. The oxidation of carbon black loosely mixed with catalyst powder was monitored gravimetrically in a gas stream containing nitric oxide, oxygen, and water. The carbon oxidation activity of the catalysts was found to be uniquely related to the Pt dispersion and little influenced by support type. The optimum dispersion is around 3-4% corresponding to relatively large Pt particle sizes of 2040 nm. The carbon oxidation activity reflects the NO oxidation activity of the platinum catalyst, which reaches an optimum in the 20-40 nm Pt particle size range. The lowest carbon oxidation temperatures were achieved with platinum loaded ZSM-22 and AlPO-11 zeolite crystallites bearing platinum of optimum dispersion on their external surfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.198
Times cited: 29
DOI: 10.1021/es051871h
|
|
|
“Experimental validation of edge strength model for glass with polished and cut edge finishing”. Vandebroek M, Belis J, Louter C, Van Tendeloo G, Engineering fracture mechanics 96, 480 (2012). http://doi.org/10.1016/j.engfracmech.2012.08.019
Abstract: In literature, the experimental validation of a glass edge strength model is lacking. Therefore, in this study, an edge strength model was established and validated. The short-term parameters of the edge strength model, i.e. the flaw geometry and depth, were determined by means of testing at a high stress rate. This was done for polished and cut edges. Next, the strength model, including subcritical crack growth, was established. Finally, the edge strength model was validated by the test results at a low stress rate. The assessed model was found to be slightly conservative, compared to the test results.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.151
Times cited: 15
DOI: 10.1016/j.engfracmech.2012.08.019
|
|
|
“Solidelectrolyte interphase evolution of carbon-coated silicon nanoparticles for lithium-ion batteries monitored by transmission electron microscopy and impedance spectroscopy”. Van Havenbergh K, Turner S, Driesen K, Bridel J-S, Van Tendeloo G, Energy technology 3, 699 (2015). http://doi.org/10.1002/ente.201500034
Abstract: The main drawbacks of silicon as the most promising anode material for lithium-ion batteries (theoretical capacity=3572 mAh g−1) are lithiation-induced volume changes and the continuous formation of a solidelectrolyte interphase (SEI) upon cycling. A recent strategy is to focus on the influence of coatings and composite materials. To this end, the evolution of the SEI, as well as an applied carbon coating, on nanosilicon electrodes during the first electrochemical cycles is monitored. Two specific techniques are combined: Transmission Electron Microscopy (TEM) is used to study the surface evolution of the nanoparticles on a very local scale, whereas electrochemical impedance spectroscopy (EIS) provides information on the electrode level. A TEMEELS fingerprint signal of carbonate structures from the SEI is discovered, which can be used to differentiate between the SEI and a graphitic carbon matrix. Furthermore, the shielding effect of the carbon coating and the thickness evolution of the SEI are described.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.789
DOI: 10.1002/ente.201500034
|
|
|
“The mechanical behavior during (de)lithiation of coated silicon nanoparticles as anode material for lithium-ion batteries studied by InSitu transmission electron microscopy”. Van Havenbergh K, Turner S, Marx N, Van Tendeloo G, Energy technology 4, 1005 (2016). http://doi.org/10.1002/ENTE.201600057
Abstract: One approach to cope with the continuous irreversible capacity loss in Si-based electrodes, attributed to lithiation-induced volume changes and the formation of a solid-electrolyte interface (SEI), is by coating silicon nanoparticles. A coating can improve the conductivity of the electrode, form a chemical shield against the electrolyte, or provide mechanical confinement to reduce the volume increase. The influence of such a coating on the mechanical behavior of silicon nanoparticles during Li insertion and Li extraction was investigated by insitu transmission electron microscopy. The type of coating was shown to influence the size of the unreacted core that remains after reaction of silicon with lithium. Furthermore, two mechanisms to relieve the stress generated during volume expansion are reported: the initiation of cracks and the formation of nanovoids. Both result in a full reaction of the silicon nanoparticles, whereas with the formation of cracks, additional surface area is created, on which an SEI can be formed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.789
Times cited: 6
DOI: 10.1002/ENTE.201600057
|
|
|
“Interface cation migration kinetics induced oxygen release heterogeneity in layered lithium cathodes”. Li C-F, Zhao K, Liao X, Hu Z-Y, Zhang L, Zhao Y, Mu S, Li Y, Li Y, Van Tendeloo G, Sun C, Energy Storage Materials 36, 115 (2021). http://doi.org/10.1016/J.ENSM.2020.12.018
Abstract: The irreversible release of the lattice oxygen in layered cathodes is one of the major degradation mechanisms of lithium ion batteries, which accounts for a number of battery failures including the voltage/capacity fade, loss of cation ions and detachment of the primary particles, etc. Oxygen release is generally attributed to the stepwise thermodynamic controlled phase transitions from the layered to spinel and rock salt phases. Here, we report a strong kinetic effect from the mobility of cation ions, whose migration barrier can be significantly modulated by the phase epitaxy at the degrading interface. It ends up with a clear oxygen release heterogeneity and completely different reaction pathways between the thin and thick areas, as well as the interparticle valence boundaries, both of which widely exist in the mainstream cathode design with the secondary agglomerates. This work unveils the origin of the heterogenous oxygen release in the layered cathodes. It also sheds light on the rational design of cathode materials with enhanced oxygen stability by suppressing the cation migration.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.ENSM.2020.12.018
|
|
|
“Enhanced electrical properties of Bi2-xSbxTe3 nanoflake thin films through interface engineering”. Wu X, Ding J, Cui W, Lin W, Xue Z, Yang Z, Liu J, Nie X, Zhu W, Van Tendeloo G, Sang X, Energy &, environment materials , e12755 (2024). http://doi.org/10.1002/EEM2.12755
Abstract: The structure-property relationship at interfaces is difficult to probe for thermoelectric materials with a complex interfacial microstructure. Designing thermoelectric materials with a simple, structurally-uniform interface provides a facile way to understand how these interfaces influence the transport properties. Here, we synthesized Bi2-xSbxTe3 (x = 0, 0.1, 0.2, 0.4) nanoflakes using a hydrothermal method, and prepared Bi2-xSbxTe3 thin films with predominantly (0001) interfaces by stacking the nanoflakes through spin coating. The influence of the annealing temperature and Sb content on the (0001) interface structure was systematically investigated at atomic scale using aberration-corrected scanning transmission electron microscopy. Annealing and Sb doping facilitate atom diffusion and migration between adjacent nanoflakes along the (0001) interface. As such it enhances interfacial connectivity and improves the electrical transport properties. Interfac reactions create new interfaces that increase the scattering and the Seebeck coefficient. Due to the simultaneous optimization of electrical conductivity and Seebeck coefficient, the maximum power factor of the Bi1.8Sb0.2Te3 nanoflake films reaches 1.72 mW m(-1) K-2, which is 43% higher than that of a pure Bi2Te3 thin film.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1002/EEM2.12755
|
|
|
“Study of ramp-type Josephson junctions by HREM”. Verbist K, Lebedev OI, Van Tendeloo G, Verhoeven MAJ, Rijnders AJHM, Blank DHA, Electronic Applications, Vol 2: Large Scale And Power Applications , 49 (1997)
Abstract: Structural aspects of ramp-type Josephson junctions based on REBa2Cu3O7-delta high-T-c superconductors, are investigated by cross-section transmission electron microscopy and results related to fabrication process or physical properties. The barrier layer material is PrBa2Cu3-xGaxO7-delta. The ramp-geometry depends on the etching conditions. High levels of Ga doping (x>0.7) influence the microstructure of the barrier layer thereby changing the junctions properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Structure of Y123 and Y247 fluorinated phases by HREM”. Lebedev OI, Van Tendeloo G, Abakumov AM, Shpanchenko RV, Rozova MG, Antipov EV, Electron microscopy: vol. 3 , 297 (1998)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Characterization of MO derived nanostructured titania powders”. Ahonen PP, Kauppinen EI, Tapper U, Nenonen P, Joubert JC, Deschanvres JL, Van Tendeloo G, Electron microscopy: vol. 2 , 373 (1998)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“HREM investigation of La1-xCaxMnO3- thin films”. Lebedev OI, Van Tendeloo G, Amelinckx S, Leibold B, Habermeier H-U, Electron microscopy: vol. 2 , 517 (1998)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Layered structures accomodating stoichiometry in M2X2O7 systems, as seen by diffraction and HREM”. Nihoul G, Leroux C, Cesari C, Van Tendeloo G, Electron microscopy: vol. 2 , 295 (1998)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Microstructural investigation of a La1.9Sr0.1CuO4 thin film grown by MBE under a large compressive strain”. Seo JW, Perret J, Fompeyrine J, Loquet J-P, Van Tendeloo G, Electron microscopy: vol. 2 , 287 (1998)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Microstructure of artificial [100] 45°, twist grain boundaries in YBa2Cu3O7-”. Verbist K, Tafuri F, Miletto Granozio F, di Chiara S, Van Tendeloo G, Electron microscopy: vol. 2 , 593 (1998)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Fine structure of CMR perovskites by HREM and CBEM”. Van Tendeloo G, Richard O, Schuddinck W, Hervieu M, Electron microscopy: vol. 1 , 383 (1998)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Crystalline and amorphous frameworks with giant pores: what information ca we expect from advanced TEM?”.Lebedev OI, Van Tendeloo G, Electron microscopy and multiscale modeling: proceedings of the AIP conference proceedings 999, 245 (2008)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Microstructure of artificial [100] 45 degrees twist grain boundaries in YBa2Cu3O7-delta”. Verbist K, Tafuri F, Granozio FM, Di Chiara S, Van Tendeloo G, Electron Microscopy 1998, Vol 2: Materials Science 1 , 593 (1998)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Ordering and defects in BanTaxTiyO3n ternary oxides”. Nistor L, Van Tendeloo G, Amelinckx S, Shpanchenko RV, van Landuyt J, Electron Microscopy 1994, Vols 2a And 2b: Applications In Materials Sciences , 869 (1994)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Multi-functional copper oxide nanosystems for H2 sustainable production and sensing”. Gasparotto A, Barreca D, Fornasiero P, Gombac V, Lebedev O, Maccato C, Montini T, Tondello E, Van Tendeloo G, Comini E, Sberveglieri G, ECS transactions 25, 1169 (2009)
Abstract: This work focuses on the use of tailored copper oxide nanoarchitectures as multi-functional materials for the sustainable production of hydrogen and its on-line detection. An innovative copper(II) precursor, Cu(hfa)2TMEDA, was adopted in the CVD of CuxO (x=1,2) nanosystems under both O2 and O2+H2O atmospheres on Si(100) and Al2O3 substrates. A multi-technique characterization indicates that both the phase composition (from Cu2O to CuO) and morphology (from continuous films to entangled quasi-1D nanosystems) can be tailored by varying the growth temperature and reaction atmosphere. The obtained CuxO nanodeposits are active in the photocatalytic H2 production from aqueous solutions under UV-Vis irradiation and display interesting gas sensing performances towards hydrogen detection even at moderate temperatures.
Keywords: A2 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Fullerenen: een nieuwe vorm van koolstof”. Van Tendeloo G, Echo 3: essays voor chemie-onderwijs , 79 (1995)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Optimization of the amount of catalyst and reaction time in single wall nanotube production”. Horvath ZE, Biro LP, Van Tendeloo G, Tondeur C, Bister G, Pierard N, Fonseca A, Nagy JB, Diffusion and defect data : solid state data : part B : solid state phenomena 94, 271 (2003)
Abstract: The influence of the amount of catalyst and the reaction time on the quantity and quality of catalytically grown single wall carbon nanotubes (SWNT) was investigated. The aim was to optimize some of the SWNT growth parameters using TEM and HRTEM. The thickness of catalyst layer influences the synthesis of the nanotube because the gas composition can differ between top and bottom. Microscopic investigation of the grown SWNT samples showed that the thicker the catalyst layer the lower relative nanotube content, so the deeper parts of the catalyst layer are less effective: The optimum time for the reaction was found to be 10 minutes. This may be understood assuming that nanotube growth needs an initial incubation time while the activity of the catalyst decreases steadily until the nariotube growth stops.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Structural characterization of nanostructured Ni3Al processed by inert gas condensation”. Yandouzi M, Pauwels B, Schryvers D, Van Swygenhoven H, Van Tendeloo G, Diffusion and defect data : solid state data : part A : defect and diffusion forum 213, 19 (2003)
Abstract: High-resolution transmission electron microscopy was performed on compacted Ni(3)Al nanostructured material prepared by the inert gas condensation technique. From electron diffraction data an incomplete L1(2) ordering of the crystallites is observed in the free particles as well as in the room temperature compacted samples. However, a completely ordered L1(2) structure with much bigger and well-defined crystallites exhibiting several defects is observed in material compacted and annealed at 773 K. Sharp crystallite boundaries as well as amorphous material and voids are observed in between crystallites in all samples, the former being dominant in the annealed material, the latter in the as-prepared one.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Analytical TEM study of CVD diamond growth on TiO2 sol-gel layers”. Lu Y-G, Verbeeck J, Turner S, Hardy A, Janssens SD, De Dobbelaere C, Wagner P, Van Bael MK, Van Tendeloo G, Diamond and related materials 23, 93 (2012). http://doi.org/10.1016/j.diamond.2012.01.022
Abstract: The early growth stages of chemical vapor deposition (CVD) diamond on a solgel TiO2 film with buried ultra dispersed diamond seeds (UDD) have been studied. In order to investigate the diamond growth mechanism and understand the role of the TiO2 layer in the growth process, high resolution transmission electron microscopy (HRTEM), energy-filtered TEM and electron energy loss spectroscopy (EELS) techniques were applied to cross sectional diamond film samples. We find evidence for the formation of TiC crystallites inside the TiO2 layer at different diamond growth stages. However, there is no evidence that diamond nucleation starts from these crystallites. Carbon diffusion into the TiO2 layer and the chemical bonding state of carbon (sp2/sp3) were both extensively investigated. We provide evidence that carbon diffuses through the TiO2 layer and that the diamond seeds partially convert to amorphous carbon during growth. This carbon diffusion and diamond to amorphous carbon conversion make the seed areas below the TiO2 layer grow and bend the TiO2 layer upwards to form the nucleation center of the diamond film. In some of the protuberances a core of diamond seed remains, covered by amorphous carbon. It is however unlikely that the remaining seeds are still active during the growth process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 16
DOI: 10.1016/j.diamond.2012.01.022
|
|
|
“Characteristic mosaic texture related to orderingin AuCu-9at.%Ag pseudobinary alloy”. Yasuda K, Hisatsune K, Udoh K, Tanaka Y, Van Tendeloo G, van Landuyt J, Dentistry in Japan 29, 91 (1992)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Structural characterisation of nanostructured Ni3Al processed by inert gas condensation”. Yandouzi M, Pauwels B, Schryvers D, van Swygenhoven H, Van Tendeloo G, Defects and diffusion in metals 213/215, 19 (2003)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“High resolution electron tomography”. Bals S, Van Aert S, Van Tendeloo G, Current opinion in solid state and materials science 17, 107 (2013). http://doi.org/10.1016/j.cossms.2013.03.001
Abstract: Reaching atomic resolution in 3D has been the ultimate goal in the field of electron tomography for many years. Significant progress, both on the theoretical as well as the experimental side has recently resulted in several exciting examples demonstrating the ability to visualise atoms in 3D. In this paper, we will review the different steps that have pushed the resolution in 3D to the atomic level. A broad range of methodologies and practical examples together with their impact on materials science will be discussed. Finally, we will provide an outlook and will describe future challenges in the field of high resolution electron tomography.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.938
Times cited: 24
DOI: 10.1016/j.cossms.2013.03.001
|
|
|
“The superconducting bismuth-based mixed oxides”. Antipov EV, Khasanova NR, Pshirkov JS, Putilin SN, Bougerol C, Lebedev OI, Van Tendeloo G, Baranov AN, Park YW, Current applied physics
T2 –, QTSM and QFS 02 Symposium, MAY 08-10, 2002, SEOUL, SOUTH KOREA 2, 425 (2002). http://doi.org/10.1016/S1567-1739(02)00105-0
Abstract: The present paper describes the synthesis, characterization of mixed-valence bismuthates with three- or two-dimensional perovskite-like structures and structural criteria that influence superconductivity in these compounds. Single-phase samples of Sr1-xKxBiO3 were prepared for the broad range of K-content: 0.25 less than or equal to x less than or equal to 0.65. For these bismuthates the symmetry of the structure changes from monoclinic to orthorhombic and finally to tetragonal upon increasing the K-content thus resulting in the decrease of the Bi-O distances and reduction of the network distortions. Superconductivity with maximum T-c = 12 K exists in the narrow range (x approximate to 0.5-0.6) within the stability field of the tetragonal phase (0.33 less than or equal to x less than or equal to 0.65), when the three-dimensional octahedral framework has close to the ideal perovskite structure arrangement. The layered type (Ba,K)(3)Bi2O7 and (Ba,K)(2)BiO4 bismuthates belonging to the A(n+1)B(n)O(3n+1) homologous series were investigated. Buckling of the (BiO2) layers in the structure of the n = 2 member occurs due to the ordering of alkaline- and alkaline-earth cations between two independent positions. The formation of the one-layer bismuthate was revealed by Electron Microscopy and XRPD studies. Both types of compounds are considered to be possible candidates for new superconducting materials among bismuthates. (C) 2002 Published by Elsevier Science B.V.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.971
Times cited: 2
DOI: 10.1016/S1567-1739(02)00105-0
|
|