“_Sr{2}GaScO5, Sr10Ga6Sc4O25, and SrGa0.75Sc0.25O2.5 : a play in the octahedra to tetrahedra ratio in oxygen-deficient perovskites”. Chernov SV, Dobrovolsky YA, Istomin SY, Antipov EV, Grins J, Svensson G, Tarakina NV, Abakumov AM, Van Tendeloo G, Eriksson SG, Rahman SMH;, Inorganic chemistry 51, 1094 (2012). http://doi.org/10.1021/ic202236h
Abstract: Three different perovskite-related phases were isolated in the SrGa(1-x)Sc(x)O(2.5) system: Sr(2)GaScO(5), Sr(10)Ga(6)Sc(4)O(25), and SrGa(0.75)Sc(0.25)O(2.5), Sr(2)GaScO(5) (x = 0.5) crystallizes in a brownrnillerite-type structure [space group (S.G.) Icmm, a = 5.91048(5) angstrom, b = 15.1594(1) angstrom, and c = 5.70926(4) angstrom] with complete ordering of Sc(3+) and Ga(3+) over octahedral and tetrahedral positions, respectively. The crystal structure of Sr(10)Ga(6)Sc(4)O(25) (x = 0.4) was determined by the Monte Carlo method and refined using a combination of X-ray, neutron, and electron diffraction data [S.G. I4(1)/a, a = 17.517(1) angstrom, c = 32.830(3) angstrom]. It represents a novel type of ordering of the B cations and oxygen vacancies in perovskites. The crystal structure of Sr(10)Ga(6)Sc(4)O(25) can be described as a stacking of eight perovskite layers along the c axis ...[-(Sc/Ga)O(1.6)-SrO(0.8)-(Sc/Ga)O(1.8)-SrO(0.8)-](2 center dot center dot center dot) Similar to Sr(2)GaScO(5), this structure features a complete ordering of the Sc(3+) and Ga(3+) cations over octahedral and tetrahedral positions, respectively, within each layer. A specific feature of the crystal structure of Sr(10)Ga(6)Sc(4)O(25) is that one-third of the tetrahedra have one vertex not connected with other Sc/Ga cations. Further partial replacement of Sc(3+) by Ga(3+) leads to the formation of the cubic perovskite phase SrGa(0.75)Sc(0.25)O(2.5) (x = 0.25) with a = 3.9817(4) angstrom. This compound incorporates water molecules in the structure forming SrGa(0.75)Sc(0.25)O(2.5)center dot xH(2)O hydrate, which exhibits a proton conductivity of similar to 2.0 x 10(-6) S/cm at 673 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 14
DOI: 10.1021/ic202236h
|
“Two New Arsenides, Eu7Cu44As23 and Sr7Cu44As23, With a New Filled Variety of the BaHg11 Structure”. Charkin DO, Demchyna R, Prots Y, Borrmann H, Burkhardt U, Schwarz U, Schnelle W, Plokhikh IV, Kazakov SM, Abakumov AM, Batuk D, Verchenko VY, Tsirlin AA, Curfs C, Grin Y, Shevelkov AV;, Inorganic chemistry 53, 11173 (2014). http://doi.org/10.1021/ic5017615
Abstract: Two new ternary arsenides, namely, Eu7Cu44As23 and Sr7Cu44As23, were synthesized from elements at 800 degrees C. Their crystal structure represents a new filled version of the BaHg11 motif with cubic voids alternately occupied by Eu(Sr) and As atoms, resulting in a 2 x 2 x 2 superstructure of the aristotype: space group Fm (3) over barm, a = 16.6707(2) angstrom and 16.7467(2) angstrom, respectively. The Eu derivative exhibits ferromagnetic ordering below 17.5 K. In agreement with band structure calculations both compounds are metals, exhibiting relatively low thermopower, but high electrical and low thermal conductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 9
DOI: 10.1021/ic5017615
|
“Bi(3n+1)Ti7Fe(3n-3)O(9n+11) Homologous Series: Slicing Perovskite Structure with Planar Interfaces Containing Anatase-like Chains”. Batuk D, Tsirlin AA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev A, Hadermann J, Abakumov AM, Inorganic chemistry 55, 1245 (2016). http://doi.org/10.1021/acs.inorgchem.5b02465
Abstract: The n = 3-6 members of a new perovskite-based homologous series Bi(3n+1)Ti7Fe(3n-3)O(9n+11) are reported. The crystal structure of the n = 3 Bi10Ti7Fe6O38 member is refined using a combination of X-ray and neutron powder diffraction data (a = 11.8511(2) A, b = 3.85076(4) A, c = 33.0722(6) A, S.G. Immm), unveiling the partially ordered distribution of Ti(4+) and Fe(3+) cations and indicating the presence of static random displacements of the Bi and O atoms. All Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures are composed of perovskite blocks separated by translational interfaces parallel to the (001)p perovskite planes. The thickness of the perovskite blocks increases with n, while the atomic arrangement at the interfaces remains the same. The interfaces comprise chains of double edge-sharing (Fe,Ti)O6 octahedra connected to the octahedra of the perovskite blocks by sharing edges and corners. This configuration shifts the adjacent perovskite blocks relative to each other over a vector (1/2)[110]p and creates S-shaped tunnels along the [010] direction. The tunnels accommodate double columns of the Bi(3+) cations, which stabilize the interfaces owing to the stereochemical activity of their lone electron pairs. The Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures can be formally considered either as intergrowths of perovskite modules and polysynthetically twinned modules of the Bi2Ti4O11 structure or as intergrowths of the 2D perovskite and 1D anatase fragments. Transmission electron microscopy (TEM) on Bi10Ti7Fe6O38 reveals that static atomic displacements of Bi and O inside the perovskite blocks are not completely random; they are cooperative, yet only short-range ordered. According to TEM, the interfaces can be laterally shifted with respect to each other over +/-1/3a, introducing an additional degree of disorder. Bi10Ti7Fe6O38 is paramagnetic in the 1.5-1000 K temperature range due to dilution of the magnetic Fe(3+) cations with nonmagnetic Ti(4+). The n = 3, 4 compounds demonstrate a high dielectric constant of 70-165 at room temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 3
DOI: 10.1021/acs.inorgchem.5b02465
|
“Pb2MnTeO6 double perovskite : an antipolar anti-ferromagnet”. Retuerto M, Skiadopoulou S, Li MR, Abakumov AM, Croft M, Ignatov A, Sarkar T, Abbett BM, Pokorný, J, Savinov M, Nuzhnyy D, Prokleška J, Abeykoon M, Stephens PW, Hodges JP, Vaněk P, Fennie CJ, Rabe KM, Kamba S, Greenblatt M;, Inorganic chemistry 55, 4320 (2016). http://doi.org/10.1021/acs.inorgchem.6b00054
Abstract: Pb2MnTeO6, a new double perovskite, was synthesized. Its crystal structure was determined by synchrotron X-ray and powder neutron diffraction. Pb2MnTeO6 is monoclinic (I2/m) at room temperature with a regular arrangement of all the cations in their polyhedra. However, when the temperature is lowered to similar to 120 K it undergoes a phase transition from I2/m to C2/c structure. This transition is accompanied by a displacement of the Pb atoms from the center of their polyhedra due to the 6s2 lone-pair electrons, together with a surprising off-centering of Mn2+ (d5) magnetic cations. This strong first-order phase transition is also evidenced by specific heat, dielectric, Raman, and infrared spectroscopy measurements. The magnetic characterizations indicate an anti-ferromagnetic (AFM) order below TN approximate to 20 K; analysis of powder neutron diffraction data confirms the magnetic structure with propagation vector k = (0 1 0) and collinear AFM spins. The observed jump in dielectric permittivity near similar to 150 K implies possible anti-ferroelectric behavior; however, the absence of switching suggests that Pb2MnTeO6 can only be antipolar. First-principle calculations confirmed that the crystal and magnetic structures determined are locally stable and that anti-ferroelectric switching is unlikely to be observed in Pb2MnTeO6.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 9
DOI: 10.1021/acs.inorgchem.6b00054
|
“Layered-to-Tunnel Structure Transformation and Oxygen Redox Chemistry in LiRhO2upon Li Extraction and Insertion”. Mikhailova D, Karakulina OM, Batuk D, Hadermann J, Abakumov AM, Herklotz M, Tsirlin AA, Oswald S, Giebeler L, Schmidt M, Eckert J, Knapp M, Ehrenberg H, Inorganic chemistry 55, 7079 (2016). http://doi.org/10.1021/acs.inorgchem.6b01008
Abstract: Layered Li(M,Li)O2 (where M is a transition metal) ordered rock-salt-type structures are used in advanced metal-ion batteries as one of the best hosts for the reversible intercalation of Li ions. Besides the conventional redox reaction involving oxidation/reduction of the M cation upon Li extraction/insertion, creating oxygen-located holes because of the partial oxygen oxidation increases capacity while maintaining the oxidized oxygen species in the lattice through high covalency of the M–O bonding. Typical degradation mechanism of the Li(M,Li)O2 electrodes involves partially irreversible M cation migration toward the Li positions, resulting in gradual capacity/voltage fade. Here, using LiRhO2 as a model system (isostructural and isoelectronic to LiCoO2), for the first time, we demonstrate an intimate coupling between the oxygen redox and M cation migration. A formation of the oxidized oxygen species upon electrochemical Li extraction coincides with transformation of the layered Li1–xRhO2 structure into the γ-MnO2-type rutile–ramsdellite intergrowth LiyRh3O6 structure with rutile-like [1 × 1] channels along with bigger ramsdellite-like [2 × 1] tunnels through massive and concerted Rh migration toward the empty positions in the Li layers. The oxidized oxygen dimers with the O–O distances as short as 2.26 Å are stabilized in this structure via the local Rh–O configuration reminiscent to that in the μ-peroxo-μ-hydroxo Rh complexes. The LiyRh3O6 structure is remarkably stable upon electrochemical cycling illustrating that proper structural implementation of the oxidized oxygen species can open a pathway toward deliberate employment of the anion redox chemistry in high-capacity/high-voltage positive electrodes for metal-ion batteries. Upon chemical or electrochemical oxidation, layered LiRhO2 shows a unique structural transformation that involves both cation migration and oxidation of oxygen resulting in a stable tunnel-like rutile−ramsdellite intergrowth LiyRh3O6 structure. This structure demonstrates excellent performance with the steady and reversible capacity of ∼200 mAh/g. The stability of LiyRh3O6 is rooted in the accommodation of partially oxidized oxygen species through the formation of short O−O distances that are compatible with the connectivity of RhO6 octahedra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 12
DOI: 10.1021/acs.inorgchem.6b01008
|
“Crystal Structure, Defects, Magnetic and Dielectric Properties of the Layered Bi3n+1Ti7Fe3n-3,O9n+11 Perovskite-Anatase lntergrowths”. Batuk D, Batuk M, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Tyablikov OA, Hadermann J, Abakumov AM, Inorganic chemistry 56, 931 (2017). http://doi.org/10.1021/ACS.INORGCHEM.6B02559
Abstract: The Bi3n+1Ti7Fe3n-3,O9n+11 materials are built of (001)(p) plane parallel perovskite blocks with a thickness of n (Ti,Fe)O-6 octahedra, separated by periodic translational interfaces. The interfaces are based on anatase-like chains of edge -sharing (Ti,Fe)O-6 octahedra. Together with the octahedra of the perovskite blocks, they create S-shaped tunnels stabilized by lone pair Bi3+ cations. In this work, the structure of the n = 4-6 Bi3n+1Ti7Fe3n-3,O9n+11 homologues is analyzed in detail using advanced transmission electron microscopy, powder X-ray diffraction, and Mossbauer spectroscopy. The connectivity of the anatase-like chains to the perovskite blocks results in,a 3ap periodicity along the interfaces, so that they can be located either on top of each other or with shifts of +/- a(p) along [100](p). The ordered arrangement of the interfaces gives rise to orthorhombic Immm and monoclinic A2/m polymorphs with the unit cell parameters a = 3a(p), b = b(p), c = 2(n + 1)c(p) and a = 3a(p), b = b(p), c = 2(n + 1)c(p) – a(p), respectively. While the n = 3 compound is orthorhombic, the monoclinic modification is more favorable in higher homologues. The Bi3n+1Ti7Fe3n-3,O9n+11 structures demonstrate intricate patterns of atomic displacements in the perovskite blocks, which are supported by the stereochemical activity of the Bi3+ cations. These patterns are coupled to the cationic coordination of the oxygen atoms in the (Ti,Fe)O-2 layers at the border of the perovskite blocks. The coupling is strong in the 1/ = 3, 4 homologues, but gradually reduces with the increasing thickness of the perovskite blocks, so that, in the n = 6 compound, the dominant mode of atomic displacements is aligned along the interface planes. The displacements in the adjacent perovskite blocks tend to order antiparallel, resulting in an overall antipolar structure. The Bi3n+1Ti7Fe3n-3,O9n+11 materials demonstrate an unusual diversity of structure defects. The n = 4-6 homologues are robust antiferromagnets below T-N = 135, 220, and 295 K, respectively. They show a high dielectric constant that weakly increases with temperature and is relatively insensitive to the Ti/Fe ratio.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 3
DOI: 10.1021/ACS.INORGCHEM.6B02559
|
“Molybdenum oxide nitrides of the Mo2(O,N,\square)5 type : on the way to Mo2O5”. Weber D, Huber M, Gorelik TE, Abakumov AM, Becker N, Niehaus O, Schwickert C, Culver SP, Boysen H, Senyshyn A, Poettgen R, Dronskowski R, Ressler T, Kolb U, Lerch M, Inorganic chemistry 56, 8782 (2017). http://doi.org/10.1021/ACS.INORGCHEM.7B00551
Abstract: Blue-colored molybdenum oxide nitrides of the Mo-2(O,N,square)(5) type were synthesized by direct nitridation of commercially available molybdenum trioxide with a mixture of gaseous ammonia and oxygen. Chemical composition, crystal structure, and stability of the obtained and hitherto unknown compounds are studied extensively. The average oxidation state of +5 for molybdenum is proven by Mo K near-edge X-ray absorption spectroscopy; the magnetic behavior is in agreement with compounds exhibiting (MoO6)-O-v units. The new materials are stable up to similar to 773 K in an inert gas atmosphere. At higher temperatures, decomposition is observed. X-ray and neutron powder diffraction, electron diffraction, and high-resolution transmission electron microscopy reveal the structure to be related to VNb9O24.9-type phases, however, with severe disorder hampering full structure determination. Still, the results demonstrate the possibility of a future synthesis of the potential binary oxide Mo2O5. On the basis of these findings, a tentative suggestion on the crystal structure of the potential compound Mo2O5, backed by electronic-structure and phonon calculations from first principles, is given.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 3
DOI: 10.1021/ACS.INORGCHEM.7B00551
|
“Chemistry, local molybdenum clustering, and electrochemistry in the Li2+xMo1-xO3 solid solutions”. Savina AA, Saiutina VV, Morozov AV, Boev AO, Aksyonov DA, Dejoie C, Batuk M, Bals S, Hadermann J, Abakumov AM, Inorganic chemistry 61, 5637 (2022). http://doi.org/10.1021/ACS.INORGCHEM.2C00420
Abstract: A broad range of cationic nonstoichiometry has been demonstratedfor the Li-rich layered rock-salt-type oxide Li2MoO3, which has generally been considered as a phase with a well-defined chemical composition. Li2+xMo1-xO3(-0.037 <= x <= 0.124) solid solutions were synthesized via hydrogen reduction ofLi2MoO4in the temperature range of 650-1100 degrees C, withxdecreasing with theincrease of the reduction temperature. The solid solutions adopt a monoclinicallydistorted O3-type layered average structure and demonstrate a robust localordering of the Li cations and Mo3triangular clusters within the mixed Li/Mocationic layers. The local structure was scrutinized in detail by electron diffractionand aberration-corrected scanning transmission electron microcopy (STEM),resulting in an ordering model comprising a uniform distribution of the Mo3clusters compatible with local electroneutrality and chemical composition. The geometry of the triangular clusters with their oxygenenvironment (Mo3O13groups) has been directly visualized using differential phase contrast STEM imaging. The established localstructure was used as input for density functional theory (DFT)-based calculations; they support the proposed atomic arrangementand provide a plausible explanation for the staircase galvanostatic charge profiles upon electrochemical Li+extraction fromLi2+xMo1-xO3in Li cells. According to DFT, all electrochemical capacity in Li2+xMo1-xO3solely originates from the cationic Moredox process, which proceeds via oxidation of the Mo3triangular clusters into bent Mo3chains where the electronic capacity of the clusters depends on the initial chemical composition and Mo oxidation state defining the width of the first charge low-voltageplateau. Further oxidation at the high-voltage plateau proceeds through decomposition of the Mo3chains into Mo2dimers and further into individual Mo6+cations
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
Times cited: 3
DOI: 10.1021/ACS.INORGCHEM.2C00420
|
“Mixed tellurides Ni3-xGaTe2 (0\leq x\leq0.65): crystal and electronic structures, properties, and nickel deficiency effects on vacancy ordering”. Isaeva AA, Makarevich ON, Kutznetsov AN, Doert T, Abakumov AM, Van Tendeloo G, European journal of inorganic chemistry , 1395 (2010). http://doi.org/10.1002/ejic.200901027
Abstract: The Ni3-xGaTe2 series of compounds (0 x 0.65) was synthesized by a high-temperature ceramic technique at 750 °C. Crystal structures of three compounds in the series were determined by X-ray powder diffraction: Ni2.98(1)GaTe2 (RI = 0.042, Rp = 0.023, Rwp = 0.035), Ni2.79(1)GaTe2 (RI = 0.053, Rp = 0.028, Rwp = 0.039), Ni2.58(1)GaTe2 (RI = 0.081, Rp = 0.037, Rwp = 0.056); the structures were verified by electron diffraction and, for the former compound, high-resolution electron microscopy. The compounds crystallize in a hexagonal lattice with P63/mmc, and the structures can be regarded as a hexagonal close-packed array with a -Ga-Te-Te- stacking sequence. The octahedral and trigonal bipyramidal voids in the hcp structure are selectively filled with Ni atoms to form one entirely occupied and two partially occupied sites, thus allowing variations in the nickel content in the series of compounds Ni3-xGaTe2 (0 x 0.65). A superstructure with asup = 2asub (P63/mmc) has been identified for Ni3-xGaTe2 (0.5 x 0.65) by electron diffraction. Real-space, high-resolution images confirm an ordering of Ni atoms and vacancies inthe ab plane. Quantum-chemical calculations performed forNi3-xGaTe2 (x = 0, 0.25, 0.75, 1) suggest anisotropic metallic conductivity and Pauli paramagnetic behavior that are experimentally confirmed for Ni3GaTe2.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 8
DOI: 10.1002/ejic.200901027
|
“Tuning the crystal structure of A2CoPO4F(A=Li,Na) fluoride-phosphates : a new layered polymorph of LiNaCoPO4F”. Fedotov SS, Aksyonov DA, Samarin AS, Karakulina OM, Hadermann J, Stevenson KJ, Khasanova NR, Abakumov AM, Antipov E V, European journal of inorganic chemistry 2019, 4365 (2019). http://doi.org/10.1002/EJIC.201900660
Abstract: Co-containing fluoride-phosphates are of interest in sense of delivering high electrode potentials and attractive specific energy values as positive electrode materials for rechargeable batteries. In this paper we report on a new Co-based fluoride-phosphate, LiNaCoPO4F, with a layered structure (2D), which was Rietveld-refined based on X-ray powder diffraction data [P2(1)/c, a = 6.83881(4) angstrom, b = 11.23323(5) angstrom, c = 5.07654(2) angstrom, beta = 90.3517(5) degrees, V = 389.982(3) angstrom(3)] and validated by electron diffraction and high-resolution scanning transmission electron microscopy. The differential scanning calorimetry measurements revealed that 2D-LiNaCoPO4F forms in a narrow temperature range of 520-530 degrees C and irreversibly converts to the known 3D-LiNaCoPO4F modification (Pnma) above 530 degrees C. The non-carbon-coated 2D-LiNaCoPO4F shows reversible electrochemical activity in Li-ion cell in the potential range of 3.0-4.9 V vs. Li/Li+ with an average potential of approximate to 4.5 V and in Na-ion cell in the range of 3.0-4.5 V vs. Na/Na+ exhibiting a plateau profile centered around 4.2 V, in agreement with the calculated potentials by density functional theory. The energy barriers for both Li+ and Na+ migration in 2D-LiNaCoPO4F amount to 0.15 eV along the [001] direction rendering 2D-LiNaCoPO4F as a viable electrode material for high-power Li- and Na-ion rechargeable batteries. The discovery and stabilization of the 2D-LiNaCoPO4F polymorph indicates that temperature influence on the synthesis of A(2)MPO(4)F fluoride-phosphates needs more careful examination with perspective to unveil new structures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
DOI: 10.1002/EJIC.201900660
|
“Structure of Y123 and Y247 fluorinated phases by HREM”. Lebedev OI, Van Tendeloo G, Abakumov AM, Shpanchenko RV, Rozova MG, Antipov EV, Electron microscopy: vol. 3 , 297 (1998)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Li-ion diffusion in LixNb9PO25”. Drozhzhin OA, Vorotyntsev MA, Maduar SR, Khasanova NR, Abakumov AM, Antipov EV, Electrochimica acta 89, 262 (2013). http://doi.org/10.1016/j.electacta.2012.11.017
Abstract: Wadsley-Roth phase LixNb6PO25 has been studied as a potential candidate for anode material of Li-ion batteries. Its crystal structure, which consists of ReO3-type blocks of NbO6 octahedra connected with PO4 tetrahedra, provides a good stability and performance during Li+ insertion/removal. Li-ion chemical diffusion coefficient (D-chem) in LixNb6PO25 was determined by means of potentiostatic intermittent titration technique and electrochemical impedance spectroscopy. Different data treatments (classical Warburg equation or the model of an electrode system with ohmic potential drop and/or slow kinetics of the interfacial Li+ ion transfer across the electrode/electrolyte interface) were used for calculation of D-chem of the Li ion inside this material; their applicability is discussed in the article. D-chem changes with the Li-ion doping degree, x, in LixNb3PO25 and has a sharp minimum near the two-phase region at appr. 1.7V vs. Li+/Li. These values of D-chem in LixNb9PO25 (similar to 10(-9)-10(-11) cm(2) s(-1)) were found to be in average noticeably higher than in the widely studied anode material, Li4Ti5O12. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.798
Times cited: 11
DOI: 10.1016/j.electacta.2012.11.017
|
“Switching between solid solution and two-phase regimes in the Li1-xFe1-yMnyPO4 cathode materials during lithium (de)insertion: combined PITT, in situ XRPD and electron diffraction tomography study”. Drozhzhin OA, Sumanov VD, Karakulina OM, Abakumov AM, Hadermann J, Baranov AN, Stevenson KJ, Antipov EV, Electrochimica acta 191, 149 (2016). http://doi.org/10.1016/j.electacta.2016.01.018
Abstract: The electrochemical properties and phase transformations during (de)insertion of Li+ in LiFePO4, LiFe0.9Mn0.1PO4 and LiFe0.5Mn0.5PO4 are studied by means of galvanostatic cycling, potential intermittent titration technique (PITT) and in situ X-ray powder diffraction. Different modes of switching between the solid solution and two-phase regimes are revealed which are influenced by the Mn content in Li1-xFe1-yMnyPO4. Additionally, an increase in electrochemical capacity with the Mn content is observed at high rates of galvanostatic cycling (10C, 20C), which is in good agreement with the numerically estimated contribution of the solid solution mechanism determined from PITT data. The observed asymmetric behavior of the phase transformations in Li1-xFe0.5Mn0.5PO4 during charge and discharge is discussed. For the first time, the crystal structures of electrochemically deintercalated Li1-xFe0.5Mn0.5PO4 with different Li content – LiFe0.5Mn0.5PO4, Li0.5Fe0.5Mn0.5PO4 and Li0.1Fe0.5Mn0.5PO4 – are refined, including the occupancy factors of the Li position. This refinement is done using electron diffraction tomography data. The crystallographic analyses of Li1-xFe0.5Mn0.5PO4 reveal that at x = 0.5 and 0.9 the structure retains the Pnma symmetry and the main motif of the pristine x = 0 structure without noticeable short range order effects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.798
Times cited: 27
DOI: 10.1016/j.electacta.2016.01.018
|
“Rationalizing the influence of the Mn(IV)/Mn(III) red-Ox transition on the electrocatalytic activity of manganese oxides in the oxygen reduction reaction”. Ryabova AS, Napolskiy FS, Poux T, Istomin SY, Bonnefont A, Antipin DM, Baranchikov AY, Levin EE, Abakumov AM, Kéranguéven G, Antipov EV, Tsirlina GA, Savinova ER;, Electrochimica acta 187, 161 (2016). http://doi.org/10.1016/j.electacta.2015.11.012
Abstract: Knowledge on the mechanisms of oxygen reduction reaction (ORR) and descriptors linking the catalytic activity to the structural and electronic properties of transition metal oxides enable rational design of more efficient catalysts. In this work ORR electrocatalysis was studied on a set of single and complex Mn (III) oxides with a rotating disc electrode method and cyclic voltammetry. We discovered an exponential increase of the specific electrocatalytic activity with the potential of the surface Mn(IV)/Mn(III) red-ox couple, suggesting the latter as a new descriptor for the ORR electrocatalysis. The observed dependence is rationalized using a simple mean-field kinetic model considering availability of the Mn( III) centers and adsorbate-adsorbate interactions. We demonstrate an unprecedented activity of Mn2O3, ca. 40 times exceeding that of MnOOH and correlate the catalytic activity of Mn oxides to their crystal structure. (C) 2015 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.798
Times cited: 51
DOI: 10.1016/j.electacta.2015.11.012
|
“Oxidation potential in the Earth's lower mantle as recorded by ferropericlase inclusions in diamond”. Kaminsky FV, Ryabchikov ID, McCammon CA, Longo M, Abakumov AM, Turner S, Heidari H, Earth and planetary science letters 417, 49 (2015). http://doi.org/10.1016/j.epsl.2015.02.029
Abstract: Ferropericlase (fPer) inclusions from kimberlitic lower-mantle diamonds recovered in the Juina area, Mato Grosso State, Brazil were analyzed with transmission electron microscopy, electron energy-loss spectroscopy and the flank method. The presence of exsolved non-stoichiometric Fe3+-enriched clusters, varying in size from 1-2 nm to 10-15 nm and comprising similar to 3.64 vol.% of fPer was established. The oxidation conditions necessary for fPer formation within the uppermost lower mantle (P = 25 GPa, T = 1960 K) vary over a wide range: Delta log f(o2) (IW) from 1.58 to 7.76 (Delta = 6.2), reaching the fayalite-magnetite-quartz (FMQ) oxygen buffer position. This agrees with the identification of carbonates and free silica among inclusions within lower-mantle Juina diamonds. On the other hand, at the base of the lower mantle Delta log f(o2) values may lie at and below the iron-wustite (IW) oxygen buffer. Hence, the variations of Delta log f(o2) values within the entire sequence of the lower mantle may reach ten logarithmic units, varying from the IW buffer to the FMQ buffer values. The similarity between lower- and upper-mantle redox conditions supports whole mantle convection, as already suggested on the basis of nitrogen and carbon isotopic compositions in lower- and upper-mantle diamonds. The mechanisms responsible for redox differentiation in the lower mantle may include subduction of oxidized crustal material, mechanical separation of metallic phase(s) and silicate-oxide mineral assemblages enriched in ferric iron, as well as transfer of fused silicate-oxide material presumably also enriched in ferric iron through the mantle. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.409
Times cited: 23
DOI: 10.1016/j.epsl.2015.02.029
|
“Semiclathrates of the GePTe system : synthesis and crystal structures”. Kirsanova MA, Reshetova LN, Olenev AV, Abakumov AM, Shevelkov AV, Chemistry: a European journal 17, 5719 (2011). http://doi.org/10.1002/chem.201003553
Abstract: Novel compounds [Ge46−xPx]Tey (13.9≤x≤15.6, 5.92≤y≤7.75) with clathrate-like structures have been prepared and structurally characterized. They crystallize in the space group Fmequation image with the unit cell parameter changing from 20.544(2) to 20.698(2) Å (Z=8) on going from x=13.9 to x=15.6. Their crystal structure is composed of a covalently bonded Ge[BOND]P framework that hosts tellurium atoms in the guest positions and can be viewed as a peculiar variant of the type I clathrate superstructure. In contrast to the conventional type I clathrates, [Ge46−xPx]Tey contain tricoordinated (3b) atoms and no vacancies in the framework positions. As a consequence of the transformation of the framework, the majority of the guest tellurium atoms form a single covalent bond with the host framework and thus the title compounds are the first representative of semiclathrates with covalent bonding. A comparison is made with silicon clathrates and the evolution of the crystal structure upon changing the tellurium content is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 17
DOI: 10.1002/chem.201003553
|
“Spatial separation of covalent, ionic, and metallic interactions in Mg11Rh18B8 and Mg3Rh5B3”. Alekseeva AM, Abakumov AM, Leither-Jasper A, Schnelle W, Prots Y, Van Tendeloo G, Antipov EV, Grin Y, Chemistry: a European journal 19, 17860 (2013). http://doi.org/10.1002/chem.201301512
Abstract: The crystal structures of Mg11Rh18B8 and Mg3Rh5B3 have been investigated by using single-crystal X-ray diffraction. Mg11Rh18B8: space group P4/mbm; a=17.9949(7), c=2.9271(1)angstrom; Z=2. Mg3Rh5B3: space group Pmma; a=8.450(2), b=2.8644(6), c=11.602(2)angstrom; Z=2. Both crystal structures are characterized by trigonal prismatic coordination of the boron atoms by rhodium atoms. The [BRh6] trigonal prisms form arrangements with different connectivity patterns. Analysis of the chemical bonding by means of the electron-localizability/electron-density approach reveals covalent BRh interactions in these arrangements and the formation of BRh polyanions. The magnesium atoms that are located inside the polyanions interact ionically with their environment, whereas, in the structure parts, which are mainly formed by Mg and Rh atoms, multicenter (metallic) interactions are observed. Diamagnetic behavior and metallic electron transport of the Mg11Rh18B8 and Mg3Rh5B3 phases are in agreement with the bonding picture and the band structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 5
DOI: 10.1002/chem.201301512
|
“Anion rearrangements in fluorinated Nd2CuO3.5”. Corbel G, Attfield JP, Hadermann J, Abakumov AM, Alekseeva AM, Rozova MG, Antipov EV, Chemistry of materials 15, 189 (2003). http://doi.org/10.1021/cm021102m
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 9
DOI: 10.1021/cm021102m
|
“Antiferroelectric (Pb,Bi)1-xFe1+xO3-y perovskites modulated by crystallographic shear planes”. Abakumov AM, Batuk D, Hadermann J, Rozova MG, Sheptyakov DV, Tsirlin AA, Niermann D, Waschowski F, Hemberger J, Van Tendeloo G, Antipov EV, Chemistry of materials 23, 255 (2011). http://doi.org/10.1021/cm102907h
Abstract: We demonstrate for the first time a possibility to vary the anion content in perovskites over a wide range through a long-range-ordered arrangement of crystallographic shear (CS) planes. Anion-deficient perovskites (Pb,Bi)1−xFe1+xO3−y with incommensurately modulated structures were prepared as single phases in the compositional range from Pb0.857Bi0.094Fe1.049O2.572 to Pb0.409Bi0.567Fe1.025O2.796. Using a combination of electron diffraction and high-resolution scanning transmission electron microscopy, we constructed a superspace model describing a periodic arrangement of the CS planes. The model was verified by refinement of the Pb0.64Bi0.32Fe1.04O2.675 crystal structure from neutron powder diffraction data ((3 + 1)D S.G. X2/m(α0γ), X = [1/2,1/2,1/2,1/2], a = 3.9082(1) Å, b = 3.90333(8) Å, c = 4.0900(1) Å, β = 91.936(2)°, q = 0.05013(4)a* + 0.09170(3)c* at T = 700 K, RP = 0.036, RwP = 0.048). The (Pb,Bi)1−xFe1+xO3−y structures consist of perovskite blocks separated by CS planes confined to nearly the (509)p perovskite plane. Along the CS planes, the perovskite blocks are shifted with respect to each other over the 1/2[110]p vector that transforms the corner-sharing connectivity of the FeO6 octahedra in the perovskite framework to an edge-sharing connectivity of the FeO5 pyramids at the CS plane, thus reducing the oxygen content. Variation of the chemical composition in the (Pb,Bi)1−xFe1+xO3−y series occurs mainly because of a changing thickness of the perovskite block between the interfaces, that can be expressed through the components of the q vector as Pb6γ+2αBi1−7γ−αFe1+γ−αO3−3γ−α. The Pb, Bi, and Fe atoms are subjected to strong displacements occurring in antiparallel directions on both sides of the perovskite blocks, resulting in an antiferroelectric-type structure. This is corroborated by the temperature-, frequency-, and field-dependent complex permittivity measurements. Pb0.64Bi0.32Fe1.04O2.675 demonstrates a remarkably high resistivity >0.1 T Ω cm at room temperature and orders antiferromagnetically below TN = 608(10) K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 29
DOI: 10.1021/cm102907h
|
“Article Structure and magnetic properties of BiFe0.75Mn0.25O3 perovskite prepared at ambient and high pressure”. Belik AA, Abakumov AM, Tsirlin AA, Hadermann J, Kim J, Van Tendeloo G, Takayama-Muromachi E, Chemistry of materials 23, 4505 (2011). http://doi.org/10.1021/cm201774y
Abstract: Solid solutions of BiFe1xMnxO3 (0.0 ≤ x ≤ 0.4) were prepared at ambient pressure and at 6 GPa. The ambient-pressure (AP) phases crystallize in space group R3c similarly to BiFeO3. The high-pressure (HP) phases crystallize in space group R3c for x = 0.05 and in space group Pnma for 0.15 ≤ x ≤ 0.4. The structure of HP-BiFe0.75Mn0.25O3 was investigated using synchrotron X-ray powder diffraction, electron diffraction, and transmission electron microscopy. HP-BiFe0.75Mn0.25O3 has a PbZrO3-related √2ap × 4ap × 2√2ap (ap is the parameter of the cubic perovskite subcell) superstructure with a = 5.60125(9) Å, b = 15.6610(2) Å, and c = 11.2515(2) Å similar to that of Bi0.82La0.18FeO3. A remarkable feature of this structure is the unconventional octahedral tilt system, with the primary ab0a tilt superimposed on pairwise clockwise and counterclockwise rotations around the b-axis according to the oioi sequence (o stands for out-of-phase tilt, and i stands for in-phase tilt). The (FeMn)O6 octahedra are distorted, with one longer metaloxygen bond (2.222.23 Å) that can be attributed to a compensation for covalent BiO bonding. Such bonding results in the localization of the lone electron pair on Bi3+ cations, as confirmed by electron localization function analysis. The relationship between HP-BiFe0.75Mn0.25O3 and antiferroelectric structures of PbZrO3 and NaNbO3 is discussed. On heating in air, HP-BiFe0.75Mn0.25O3 irreversibly transforms to AP-BiFe0.75Mn0.25O3 starting from about 600 K. Both AP and HP phases undergo an antiferromagnetic ordering at TN ≈ 485 and 520 K, respectively, and develop a weak net magnetic moment at low temperatures. Additionally, ceramic samples of AP-BiFe0.75Mn0.25O3 show a peculiar phenomenon of magnetization reversal.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 57
DOI: 10.1021/cm201774y
|
“Comment on ALaMn2O6-y (A = K, Rb): novel ferromagnetic manganites exhibiting negative giant magnetoresistance”. Hadermann J, Abakumov AM, Van Rompaey S, Mankevich AS, Korsakov IE, Chemistry of materials 21, 2000 (2009). http://doi.org/10.1021/cm900298a
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 4
DOI: 10.1021/cm900298a
|
“Coupled cation and charge ordering in the CaMn306 tunnel structure”. Hadermann J, Abakumov AM, Gillie LJ, Martin C, Hervieu M, Chemistry of materials 18, 5530 (2006). http://doi.org/10.1021/cm0618998
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 33
DOI: 10.1021/cm0618998
|
“Crystal Structure and Luminescent Properties of R2-xEux(MoO4)(3) (R = Gd, Sm) Red Phosphors”. Morozov VA, Raskina MV, Lazoryak BI, Meert KW, Korthout K, Smet PF, Poelman D, Gauquelin N, Verbeeck J, Abakumov AM, Hadermann J;, Chemistry of materials 26, 7124 (2014). http://doi.org/10.1021/cm503720s
Abstract: The R-2(MoO4)(3) (R = rare earth elements) molybdates doped with Eu3+ cations are interesting red-emitting materials for display and solid-state lighting applications. The structure and luminescent properties of the R2-xEux(MoO4)(3) (R = Gd, Sm) solid solutions have been investigated as a function of chemical composition and preparation conditions. Monoclinic (alpha) and orthorhombic (beta') R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) modifications were prepared by solid-state reaction, and their structures were investigated using synchrotron powder X-ray diffraction and transmission electron microscopy. The pure orthorhombic beta'-phases could be synthesized only by quenching from high temperature to room temperature for Gd2-xEux(MoO4)(3) in the Eu3+-rich part (x > 1) and for all Sm2-xEux(MoO4)(3) solid solutions. The transformation from the alpha-phase to the beta'-phase results in a notable increase (similar to 24%) of the unit cell volume for all R2-xEux(MoO4)(3) (R = Sm, Gd) solid solutions. The luminescent properties of all R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) solid solutions were measured, and their optical properties were related to their structural properties. All R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) phosphors emit intense red light dominated by the D-5(0)-> F-7(2) transition at similar to 616 nm. However, a change in the multiplet splitting is observed when switching from the monoclinic to the orthorhombic structure, as a consequence of the change in coordination polyhedron of the luminescent ion from RO8 to RO7 for the alpha- and beta'-modification, respectively. The Gd2-xEux(MoO4)(3) solid solutions are the most efficient emitters in the range of 0 < x < 1.5, but their emission intensity is comparable to or even significantly lower than that of Sm2-xEux(MoO4)(3) for higher Eu3+ concentrations (1.5 <= x <= 1.75). Electron energy loss spectroscopy (EELS) measurements revealed the influence of the structure and element content on the number and positions of bands in the ultraviolet-visible-infrared regions of the EELS spectrum.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 24
DOI: 10.1021/cm503720s
|
“Frustrated octahedral tilting distortion in the incommensurately modulated Li3xNd2/3-xTiO3 perovskites”. Abakumov AM, Erni R, Tsirlin AA, Rossell MD, Batuk D, Nénert G, Van Tendeloo G, Chemistry of materials 25, 2670 (2013). http://doi.org/10.1021/cm4012052
Abstract: Perovskite-structured titanates with layered A-site ordering form remarkably complex superstructures. Using transmission electron microscopy, synchrotron X-ray and neutron powder diffraction, and ab initio structure relaxation, we present the structural solution of the incommensurately modulated Li3xNd2/3xTiO3 perovskites (x = 0.05, superspace group Pmmm(α1,1/2,0)000(1/2,β2 0)000, a = 3.831048(5) Å, b = 3.827977(4) Å, c = 7.724356(8) Å, q1 = 0.45131(8)a* + 1/2b*, q2 = 1/2a* + 0.41923(4)b*). In contrast to earlier conjectures on the nanoscale compositional phase separation in these materials, all peculiarities of the superstructure can be understood in terms of displacive modulations related to an intricate octahedral tilting pattern. It involves fragmenting the pattern of the out-of-phase tilted TiO6 octahedra around the a- and b-axes into antiphase domains, superimposed on the pattern of domains with either pronounced or suppressed in-phase tilt component around the c-axis. The octahedral tilting competes with the second order JahnTeller distortion of the TiO6 octahedra. This competition is considered as the primary driving force for the modulated structure. The A cations are suspected to play a role in this modulation affecting it mainly through the tolerance factor and the size variance. The reported crystal structure calls for a revision of the structure models proposed for the family of layered A-site ordered perovskites exhibiting a similar type of modulated structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 23
DOI: 10.1021/cm4012052
|
“Incommensurate modulation and luminescence in the CaGd2(1-x)Eu2x(MoO4)4(1-y)(WO)4y (0\leq x\leq1, 0\leq y\leq1) red phosphors”. Morozov VA, Bertha A, Meert KW, Van Rompaey S, Batuk D, Martinez GT, Van Aert S, Smet PF, Raskina MV, Poelman D, Abakumov AM, Hadermann J;, Chemistry of materials 25, 4387 (2013). http://doi.org/10.1021/cm402729r
Abstract: Scheelite related compounds (A',A '') [(B',B '')O-4], with B', B '' = W and/or Mo are promising new light-emitting materials for photonic applications, including phosphor converted LEDs (light-emitting diodes). In this paper, the creation and ordering of A-cation vacancies and the effect of cation substitutions in the scheelite-type framework are investigated as a factor for controlling the scheelite-type structure and luminescent properties. CaGd2(1-x)Eu2x(MoO4)(4(1-y))(WO4)(4y) (0 <= x <= 1, 0 <= y <= 1) solid solutions with scheelite-type structure were synthesized by a solid state method, and their structures were investigated using a combination of transmission electron microscopy techniques and powder X-ray diffraction. Within this series all complex molybdenum oxides have (3 + 2)D incommensurately modulated structures with superspace group I4(1)/a(alpha,beta,0)00(-beta,alpha,0)00, while the structures of all tungstates are (3 + 1)D incommensurately modulated with superspace group I2/b(alpha beta 0)00. In both cases the modulation arises because of cation-vacancy ordering at the A site. The prominent structural motif is formed by columns of A-site vacancies running along the c-axis. These vacant columns occur in rows of two or three aligned along the [110] direction of the scheelite subcell. The replacement of the smaller Gd3+ by the larger Eu3+ at the A-sublattice does not affect the nature of the incommensurate modulation, but an increasing replacement of Mo6+ by W6+ switches the modulation from (3 + 2)D to (3 + 1)D regime. Thus, these solid solutions can be considered as a model system where the incommensurate modulation can be monitored as a function of cation nature while the number of cation vacancies at the A sites remain constant upon the isovalent cation replacement. All compounds' luminescent properties were measured, and the optical properties were related to the structural properties of the materials. CaGd2(1-x)(MoO4)(4(1-y))(WO4)(4y) phosphors emit intense red light dominated by the D-5(0)-F-7(2) transition at 612 nm, along with other transitions from the D-5(1) and D-5(0) excited states. The intensity of the 5D0-7F2 transition reaches a maximum at x = 0.5 for y = 0 and 1.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 63
DOI: 10.1021/cm402729r
|
“Layered oxychlorides [PbBiO2]An+1BnO3n-1Cl2(A = Pb/Bi, B = Fe/Ti) : intergrowth of the hematophanite and sillen phases”. Batuk M, Batuk D, Tsirlin AA, Filimonov DS, Sheptyakov DV, Frontzek M, Hadermann J, Abakumov AM, Chemistry of materials 27, 2946 (2015). http://doi.org/10.1021/acs.chemmater.5b00233
Abstract: New layered structures corresponding to the general formula [PbBiO2]A(n+1)B(n)O(3n-1)Cl(2) Were prepared. Pb5BiFe3O10Cl2 (n = 3) and Pb5Bi2Fe4O13Cl2 (n = 4) are built as a stacking of truncated A(n+1)B(n)O(3n-1) perovskite blocks and alpha-PbO-type [A(2)O(2)](2+) (A = Pb, Bi) blocks combined with chlorine sheets. The alternation of these structural blocks can be represented as an intergrowth between the hematophanite and Sullen-type structural blocks. The crystal and-Magnetic structures of Pb5BiFe3O10Cl2 and Pb5Bi2Fe4O13Cl2 were investigated in the temperature range of 1.5-700 K using X-ray and neutron powder diffraction, transmission electron microscopy and Fe-57 Mossbauer spectroscopy. Both compounds crystallize in the I4/mmm space group with the unit cell parameters a approximate to a(p) approximate to 3.92 angstrom (a unit-cell parameter of the perovskite-structure), c approximate to 43.0 angstrom for the n = 3 member and c approximate to 53.5 angstrom for the n = 4 member. Despite the large separation between the slabs containing the Fe3+ ions (nearly 14 angstrom), long-range antiferromagnetic order sets in below similar to 600 K with the G-type arrangement of the Fe magnetic moments aligned along the c-axis. The possibility of mixing d(0) and d(n) cations at the B sublattice of these structures was also demonstrated by preparing the Ti-substituted n = 4 member Pb6BiFe3TiO13Cl2.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 11
DOI: 10.1021/acs.chemmater.5b00233
|
“Local oxygen-vacancy ordering and twinned octahedral tilting pattern in the Bi0.81Pb0.19FeO2.905 cubic perovskite”. Dachraoui W, Hadermann J, Abakumov AM, Tsirlin AA, Batuk D, Glazyrin K, McCammon C, Dubrovinsky L, Van Tendeloo G, Chemistry of materials 24, 1378 (2012). http://doi.org/10.1021/cm300178x
Abstract: The structure of Bi0.81Pb0.19FeO2.905 was investigated on different length scales using a combination of electron diffraction, high-resolution scanning transmission electron microscopy, synchrotron X-ray powder diffraction, and Mössbauer spectroscopy. In the 80300 K temperature range, the average crystal structure of Bi0.81Pb0.19FeO2.905 is a cubic Pm3̅m perovskite with a = 3.95368(3) Å at T = 300 K. The (Pb2+, Bi3+) cations and O2 anions are randomly displaced along the 110 cubic directions, indicating the steric activity of the lone pair on the Pb2+ and Bi3+ cations and a tilting distortion of the perovskite framework. The charge imbalance induced by the heterovalent Bi3+ → Pb2+ substitution is compensated by the formation of oxygen vacancies preserving the trivalent state of the Fe cations. On a short scale, oxygen vacancies are located in anion-deficient (FeO1.25) layers that are approximately 6 perovskite unit cells apart and transform every sixth layer of the FeO6 octahedra into a layer with a 1:1 mixture of corner-sharing FeO4 tetrahedra and FeO5 tetragonal pyramids. The anion-deficient layers act as twin planes for the octahedral tilting pattern of adjacent perovskite blocks. They effectively randomize the octahedral tilting and prevent the cooperative distortion of the perovskite framework. The disorder in the anion sublattice impedes cooperative interactions of the local dipoles induced by the off-center displacements of the Pb and Bi cations. Magnetic susceptibility measurements evidence the antiferromagnetic ordering in Bi0.81Pb0.19FeO2.905 at low temperatures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 27
DOI: 10.1021/cm300178x
|
“Multiple twinning as a structure directing mechanism in layered rock-salt-type oxides : NaMnO2 polymorphism, redox potentials, and magnetism”. Abakumov AM, Tsirlin AA, Bakaimi I, Van Tendeloo G, Lappas A, Chemistry of materials 26, 3306 (2014). http://doi.org/10.1021/cm5011696
Abstract: New polymorphs of NaMnO2 have been observed using transmission electron microscopy and synchrotron X-ray powder diffraction. Coherent twin planes confined to the (NaMnO2) layers, parallel to the (10 (1) over bar) crystallographic planes of the monoclinic layered rock-salt-type alpha-NaMnO2 (O3) structure, form quasi-periodic modulated sequences, with the known alpha-and beta-NaMnO2 polymorphs as the two limiting cases. The energy difference between the polymorphic forms, estimated using a DFT-based structure relaxation, is on the scale of the typical thermal energies that results in a high degree of stacking disorder in these compounds. The results unveil the remarkable effect of the twin planes on both the magnetic and electrochemical properties. The polymorphism drives the magnetic ground state from a quasi-1D spin system for the geometrically frustrated alpha-polymorph through a two-leg spin ladder for the intermediate stacking sequence toward a quasi-2D magnet for the beta-polymorph. A substantial increase of the equilibrium potential for Na deintercalation upon increasing the concentration of the twin planes is calculated, providing a possibility to tune the electrochemical potential of the layered rock-salt ABO(2) cathodes by engineering the materials with a controlled concentration of twins.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 35
DOI: 10.1021/cm5011696
|
“A new mixed-valence ferrite with a cubic structure, YBaFe4O7: spin-glass-like behavior”. Caignaert V, Abakumov AM, Pelloquin D, Pralong V, Maignan A, Van Tendeloo G, Raveau B, Chemistry of materials 21, 1116 (2009). http://doi.org/10.1021/cm803312f
Abstract: A new mixed-valence ferrite, YBaFe4O7, has been synthesized. Its unique cubic structure, with a = 8.9595(2) Å, is closely related to that of the hexagonal 114 oxides YBaCo4O7 and CaBaFe4O7. It consists of corner-sharing FeO4 tetrahedra, forming triangular and kagome layers parallel to (111)C. In fact, the YBaFe4O7 and CaBaFe4O7 structures can be described as two different ccc and chch close packings of [BaO3]∞ and [O4]∞ layers, respectively, whose tetrahedral cavities are occupied by Fe2+/Fe3+ cations. The local structure of YBaFe4O7 is characterized by a large amount of stacking faults originating from the presence of hexagonal layers in the ccc cubic close-packed YBaFe4O7 structure. In this way, they belong to the large family of spinels and hexagonal ferrites studied for their magnetic properties. Differently from all the ferrites and especially from CaBaFe4O7, which are ferrimagnetic, YBaFe4O7 is an insulating spin glass with Tg = 50 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 39
DOI: 10.1021/cm803312f
|
“Reply to Comment on “Frustrated octahedral tilting distortion in the incommensurately modulated Li3xNd2/3-xTiO3 perovskites””. Abakumov AM, Erni R, Tsirlin AA, Chemistry of materials 26, 1288 (2014). http://doi.org/10.1021/cm500005d
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 1
DOI: 10.1021/cm500005d
|