Abstract: High-resolution transmission electron microscopy was performed on compacted Ni(3)Al nanostructured material prepared by the inert gas condensation technique. From electron diffraction data an incomplete L1(2) ordering of the crystallites is observed in the free particles as well as in the room temperature compacted samples. However, a completely ordered L1(2) structure with much bigger and well-defined crystallites exhibiting several defects is observed in material compacted and annealed at 773 K. Sharp crystallite boundaries as well as amorphous material and voids are observed in between crystallites in all samples, the former being dominant in the annealed material, the latter in the as-prepared one.

Abstract: We apply the exact diagonalization technique to calculate the ground and excited states of a bipolar artificial molecule composed of two vertically coupled quantum dots containing different types of carriers electrons and holes in equilibrium. In this system, the magnetic field tunes the relative role of intra-dot Coulomb interaction while the inter-dot separation sets the strength of inter-dot correlations. We find an intricate pattern of the switching of the ground-state angular momentum with increasing magnetic field and a rearrangement of approximate single-particle levels as a function of the inter-dot coupling strength.

Abstract: Semiconductor heterostructures are used for the fabrication of optoelectronic devices. Performance of such devices is governed by their chemical morphology. The composition distribution of quantum wells and dots is influenced by kinetic growth processes which are not understood completely at present. To obtain more information about these effects, methods for composition determination with a spatial resolution at a near atomic scale are necessary. In this paper we focus on the present state of the composition evaluation by the lattice fringe analysis (CELFA) technique and explain the basic ideas, optimum imaging conditions, precision and accuracy.

Abstract: We measured the electrical resistivity R(T) and specific heat C-p(T) between room temperature (RT) and 4.2 K as well as the microstructure by transmission electron microscopy (TEM) of a Ni-52 Ti-48 SMA quenched from 1000degreesC (B2-Phase range) to RT and then annealed for 1h at T=380degreesC, 550degreesC and 650degreesC. In the “as quenched” and the “650degreesC annealed” state no martensitic transformations (MT's) occur. The diffraction patterns show faint reflections originating from coherent Ni4Ti3 precipitates in an early state of formation. Additional reflections of the type 1/2 <110>, 1/2 <111> and 1/3 <110> result from various lattice displacement waves, which are precursors of the MT's to the B19' and R-phase, respectively. Indeed, high resolution TEM micrographs of the [001] zone of the “as quenched” sample reveal transverse 1/2 <110> <110> lattice displacement waves, precursors of the B19' martensite. The coherent Ni4Ti3 precipitates, homogeneously distributed on a small length scale, binder the MT's in the “as quenched” and the “650degreesC annealed” state, and thus only the precursors appear. When annealed at T=380degreesC, however, coherent Ni4Ti3 precipitates with a length of 10nm are clearly visible in TEM. These precipitates trigger the NIT from the B2 to the R-phase on cooling, as evidenced also by anomalies in R(T) and C-p(T). Annealing at T-550degreesC leads to the well known two step MT's from the B2 to the R-phase and then into the B19'-phase. These martensitic transitions are clearly seen as additional peaks in the specific heat and anomalies in the resistance, while the “as quenched” and 650degreesC annealed samples show weak features in R(T) and C-p(T).

Abstract: Calibration curves with two quasi-linear sections ("double sloping'') were observed for the medium volatile elements, Cr and Cu, with the use of a SIMAA 6000 graphite furnace atomic absorption spectrometer under interrupted internal gas flow conditions. If a standard transversally heated graphite atomizer (THGA) tube was shortened by 0.5 mm at both of its ends, (i.e. the gaps were enlarged between graphite furnace housing and tube ends), a stronger declination of the calibration curves resulted. Elements with fairly high diffusion coefficients (>5.8 cm(2) s(-1)) and with short appearance time of their transients (<0.6 s), such as Cr and Cu, have shown the most characteristic sensitivity drop towards higher concentrations. This anomalous feature could be eliminated in three different ways; (1) by applying end-capped THGA tubes, (2) using mini-flow (50 cm(3) min(-1)) conditions during the atomization stage, and (3) by adding Pd-Mg chemical modifier. For the low volatile Mo and V, the calibration curves had no irregular shape. For Ag, Co, Cr, Cu, Mn and Ni, the mini-flow settings improved the linearity of the calibration curves and extended the upper limit of the linear calibration range by a factor of 1.5-2.0. The irregular characteristic of the analytical curves was interpreted as an increased vapour loss at higher analyte concentrations through the opened ends of the standard THGA tubes. This vapour loss was associated with the significantly diverse expulsion velocities of atoms, caused by the difference in temperature and concentration gradients, when evaporating amounts of analytes with more than one order of magnitude difference.