“Synthesis and catalytic activity of Ti-MCM-41 nanoparticles with highly active titanium sites”. Lin K, Pescarmona PP, Vandepitte H, Liang D, Van Tendeloo G, Jacobs PA, Journal of catalysis 254, 64 (2008). http://doi.org/10.1016/j.jcat.2007.11.017
Abstract: Ti-MCM-41 nanoparticles 80-160 nm in diameter (Ti-MCM-41 NP) were successfully prepared by a dilute solution route in sodium hydroxide medium at ambient temperature. Ti-MCM-41 NP were characterized by X-ray diffraction, nitrogen adsorption/desorption isotherms, SEM, TEM. FT-IR, and UV-vis spectroscopy. The characterization results showed the existence of highly ordered hexagonal mesoporous structure and tetrahedral Ti species in Ti-MCM-41 NP. In the epoxidation of cyclohexene with aqueous H2O2, Ti-MCM-41 NP displayed higher conversion and initial reaction rate than a Ti-MCM-41 sample with normal particle size (Ti-MCM-41 LP). Diffusion of the reactants was accelerated and the accessibility to the catalytic Ti species was enhanced in the shorter channels in Ti-MCM-41 NP samples. Ti-MCM-41 NP showed much higher selectivity for cyclohexene oxide compared with Ti-MCM-41 LP, suggesting reduced hydrolysis of cyclohexene oxide with water in the former case. The increased selectivity for cyclohexene oxide can be attributed to the lower concentration of residual surface silanols in Ti-MCM-41 NP and the shorter residence time of epoxide in the shorter mesoporous channels. Ti-MCM-41 NP also appears to be a suitable catalyst in the epoxidation of a bulky substrate, like cholesterol, with tert-butyl hydroperoxide. (c) 2007 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 52
DOI: 10.1016/j.jcat.2007.11.017
|
|
|
“Graphitic nanocrystals inside the pores of mesoporous silica : synthesis, characterization and an adsorption study”. de Clippel F, Harkiolakis A, Vosch T, Ke X, Giebeler L, Oswald S, Houthoofd K, Jammaer J, Van Tendeloo G, Martens JA, Jacobs PA, Baron GV, Sels BF, Denayer JFM, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 144, 120 (2011). http://doi.org/10.1016/j.micromeso.2011.04.003
Abstract: This work presents a new carbonsilica hybrid material, denoted as CSM, with remarkable sorption properties. It consists of intraporous graphitic nanocrystals grown in the pores of mesoporous silica. CSM is obtained by a subtle incipient wetness impregnation of Al-containing mesoporous silica with furfuryl alcohol (FA)/hemelitol solutions. Both the volume match of the impregnation solution with that of the silica template pore volume, and the presence of Al3+ in the silica, are crucial to polymerize FA selectively inside the mesopores. Carbonization of the intraporous polymer was then performed by pyrolysis under He up to 1273 K. The resulting CSMs were examined by SEM, HRTEM, 27Al MAS NMR, N2 adsorption, XRD, TGA, TPD, XPS, pycnometry and Raman spectroscopy. Mildly oxidized graphitic-like carbon nanoblocks, consisting of a few graphene-like sheets, were thus identified inside the template mesopores. Random stacking of these carbon crystallites generates microporosity resulting in biporous materials at low carbon content and microporous materials at high carbon loadings. Very narrow pore distributions were obtained when pyrolysis was carried out under slow heating rate, viz. 1 K min−1. Adsorption and shape selective properties of the carbon filled mesoporous silica were studied by performing pulse chromatography and breakthrough experiments, and by measuring adsorption isotherms of linear and branched alkanes. Whereas the parent mesoporous silica shows unselective adsorption, their CSM analogues preferentially adsorb linear alkanes. The sorption capacity and selectivity can be adjusted by changing the pore size of the template or by varying the synthesis conditions. A relation between the carbon crystallites size and the shape selective behaviour of the corresponding CSM for instance is demonstrated. Most interestingly, CSM shows separation factors for linear and branched alkanes up to values comparable to those of zeolitic molecular sieves.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 15
DOI: 10.1016/j.micromeso.2011.04.003
|
|
|
“Silica-supported chromium oxide: colloids as building blocks”. Hermans I, Breynaert E, Poelman H, de Gryse R, Liang D, Van Tendeloo G, Maes A, Peeters J, Jacobs P, Physical chemistry, chemical physics 9, 5382 (2007). http://doi.org/10.1039/b706601e
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.123
Times cited: 8
DOI: 10.1039/b706601e
|
|
|
“Zeotile-2: a microporous analogue of MCM-48”. Kremer SPB, Kirschhock CEA, Aerts A, Aerts CA, Houthoofd KJ, Grobet PJ, Jacobs PA, Lebedev OI, Van Tendeloo G, Martens JA, Solid state sciences 7, 861 (2005). http://doi.org/10.1016/j.solidstatesciences.2005.01.021
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 10
DOI: 10.1016/j.solidstatesciences.2005.01.021
|
|
|
“Synthesis and characterization of nanocrystal zeolite/mesoporous matrix composite material”. Gagea BC, Liang D, Van Tendeloo G, Martens JA, Jacobs PA, Studies in surface science and catalysis 162, 259 (2006). http://doi.org/10.1016/S0167-2991(06)80915-8
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 8
DOI: 10.1016/S0167-2991(06)80915-8
|
|