“Round-robin investigation of silicon-oxide on silicon reference materials for ellipsometry”. Vanhellemont J, Maes HE, Schaekers M, Armigliato A, Cerva H, Cullis A, de Sande J, Dinges H, Hallais J, Nayar V, Pickering C, Stehlé, JL, Van Landuyt J, Walker C, Werner H, Salieri P;, Applied surface science
T2 –, SYMP ON DIAGNOSTIC TECHNIQUES FOR SEMICONDUCTOR MATERIALS ANALYSIS AND, FABRICATION PROCESS CONTROL, AT THE 1992 SPRING CONF OF THE EUROPEAN, MATERIALS RESEARCH SOC, JUN 02-05, 1992, STRASBOURG, FRANCE 63, 45 (1993). http://doi.org/10.1016/0169-4332(93)90062-G
Abstract: The main results and conclusions are presented of a round robin study of silicon oxide on silicon reference samples for ellipsometry. The oxide films with nominal thicknesses of 10, 50 and 120 nm are grown by thermal oxidation. The oxide film thicknesses have been determined by single wavelength ellipsometry (SWE), by spectroscopic ellipsometry (SE) and by cross-sectional conventional and high-resolution transmission electron microscopy (TEM and HREM) in different laboratories. The main conclusions are that special precautions have to be taken in order to use TEM as a reliable thickness measurement technique; that single wavelength ellipsometry can be used with great accuracy and reproducibility for the 50 and 120 nm film thicknesses but that it shows some inherent problems for the 10 nm films; and that spectroscopic ellipsometry showed for all film thicknesses an accuracy and reproducibility which is clearly superior to that of SWE.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.711
Times cited: 13
DOI: 10.1016/0169-4332(93)90062-G
|
“Photoelectric and electrical responses of several erbium silicide/silicon interfaces”. Muret P, Nguyen TTA, Frangis N, Van Tendeloo G, van Landuyt J, Applied surface science
T2 –, International Symposium on Si Heterostructures –, From Physics to Devices, SEP 11-14, 1995, IRAKLION, GREECE 102, 173 (1996). http://doi.org/10.1016/0169-4332(96)00042-6
Abstract: In this work, photoelectric yield and electrical properties of several types of epitaxial erbium silicide on silicon Schottky diodes are studied, Different preparation conditions are used simultaneously on n- and p-Si(111) substrates for the 200 Angstrom thick silicide films. A last type of sample consists in 1.3 monolayer of epitaxial silicide with root 3 X root 3 superstructure on the Si substrate and covered by silver on the top. Photocurrent measurements are done as a function of photon energy at several temperatures. All these samples show barrier heights near 1 eV on p-type Si, even for the interface comprising only 1.3 monolayer of silicide whereas barrier heights on n-rype Si span the range from 0.28 to 0.67 eV for this last kind of sample, the sum of the barriers always exceeding the silicon band gap, These photoelectric results are confirmed by electrical characterisations, All these results show that the Fermi level is pinned 0.1 eV below the conduction band edge on p-type Si but shifts to various positions lower within the band gap on n-type Si. This fact leads to the hypothesis of a density of -7 interface states close to the charge change in the Si depletion zone from p- to n-type, namely 10(12) eV(-1) cm(-2). Although some inhomogeneities and defects at the interface are detected by electron microscopy for samples annealed at 750 degrees C, Fermi level position seems rather insensitive to the structural details of the interface while the silicide thickness plays a role on n-type Si.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.711
Times cited: 3
DOI: 10.1016/0169-4332(96)00042-6
|