Abstract: Superconducting Cu mixed oxyfluoride, Sr,Cu(O, F)(4+delta), was Obtained via fluorination of Sr2CuO3 by XeF2 in the 100-250 degrees C temperature range in a closed Ni container. The prepared samples exhibited a lower T-c in comparison with earlier reported values. Different samples in the Sr-Cu-O-F system were prepared by a solid-state reaction at 220-400 degrees C, but no formation of the oxyfluoride was detected even with an addition of xenon difluoride. These data allow one to draw conclusions on the metastability of the oxyfluoride under the conditions used, Electron microscopy and X-ray powder diffraction studies revealed large amounts of badly crystallized SrF2; this could be a reason for the small superconducting volume fraction as well as for the inhomogeneous distribution of the anions.

Abstract: We report on the preparation of CuBa(2)(Sr(x)Ca(1-x))(n)Cu(n-1)O(y) compounds by fabrication of (Ba,Sr,Ca)CuO(2) superlattices with pulsed laser deposition (PLD). A technique called interval deposition is used to suppress multi-level or island growth resulting in high-quality superlattice structures. Both, the applicability of PLD to atomic engineering as well as the fabrication of artificial superconductors is demonstrated. The (Sr,Ca)CuO(2)-BaCuO(2) superlattices are characterized by X-ray diffraction, high-resolution electron microscopy (HREM) and selected area electron diffraction. The superlattice period has been deduced from electron diffraction patterns and XRD measurements. For Sr containing films, the best growth behavior is observed and films with the highest degree of crystallinity are obtained, whereas superconductivity is only found in less crystalline, Ca containing films. Under some deposition conditions and depending on the amount of Ba containing layers in the superlattice, it was observed that the BaCuO(2) material is converted to Ba(2)CuO(4-delta). Image simulations to interpret the HREM contrast are performed. (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: Analytical and high resolution electron microscopy have been used to study the effect of Zn- and Fe-doping on the micro structure of [001] YBa2Cu3O7-x thin films on [001] MgO substrates grown by magnetron sputtering. Special attention was paid to the presence of second phase inclusions and surface outgrowths such as CuO, Y2Ba1Cu1O5-x, Y2O3 in order to establish a relationship with the critical current density.

Abstract: The microstructure of (Bi,Pb)2Sr2Ca2Cu3Ox (Bi-2223) tapes has been investigated by means of transmission electron microscopy (TEM) and high-resolution TEM. The emphasis has been placed on: (1) an examination of the grain morphology and size, (2) grain and colony boundary angles, which are formed during the tape processing, (3) a study of the grain boundaries on an atomic scale, including intergrowth investigations. Tapes with different process parameters have been compared with respect to the microstructure. A fully processed tape has on the average 50% thicker Bi-2223 grains than a tape after the first annealing. The angles of c-axis tilt grain boundaries are on average 14° and 26° for the fully processed tape and the tape after the first annealing, respectively. The intergrowth content (15%) and distribution are similar in these two tapes.

Abstract: The variation of structures and superconducting properties by changing extra oxygen or fluorine atoms concentration in Hg-based Cu mixed oxides and YBa2Cu3O6+delta was studied. The data obtained by NPD study of Hg-1201 can be considered as an evidence of the conventional oxygen doping mechanism with 2 delta holes per (CuO2) layer. The extra oxygen atom was found to be located in the middle of the Hg mesh only. Different formal charges of oxygen and fluorine inserted into reduced 123 structure results in its distinct variations. The fluorine incorporation into strongly reduced YBa2Cu3O6+delta causes a significant structural rearrangement and the formation of a new compound with a composition close to YBa2Cu3O6F2 (tetragonal alpha = 3.87 Angstrom and c approximate to 13 Angstrom), which structure was deduced from the combined results of X-ray diffraction, electron diffraction and high resolution electron microscopy. Fluorination treatment by XeF2 of nonsuperconducting 123 samples causes an appearance of bulk superconductivity with T-c up to 94K.

Abstract: Experimental results show that the room-temperature carrier mobility in bulk layers of undoped or Si-doped GaN grown by LP-MOVPE on sapphire substrate shows a sudden increase as soon as the carrier density exceeds a critical value of about 10(18) cm(-3). We show that such a behavior can be theoretically reproduced by assuming that the columnar structure i.e. the dislocation microstructure is responsible for internal electronic barriers. (C) 1999 Elsevier Science B.V. All rights reserved.

Abstract: We report a microstructural and compositional study of a 90% Pb(Mg1/3Nb2/3)O-3 – 10% PbTiO3 ceramic sample. High resolution transmission electron microscopy (HRTEM) revealed the presence of compositional ordered nano-domains (1 – 4 mn), observable in two specific orientations, [0 (1) over bar 1] and [1 1 (2) over bar]. However, the visibility and the ordering degree of the nano-domains on the HRTEM images are not at all obvious. Fourier filtering of the images clearly revealed the ordered domains. Antiphase boundaries lying in the (111) planes separate them, while (100) and (111) facets separate the ordered domains from the disordered matrix. Their shape is plate-like, not uniformly spread in the disordered matrix. Their average size varies in different regions of the sample, most probably due to a non-uniform distribution of Ti, as observed by energy dispersive X-ray spectroscopy. (c) 2007 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim.