“Phase assembly and microstructure of CeO2-doped ZrO2 ceramics prepared by spark plasma sintering”. Xu T, Wang P, Fang P, Kan Y, Chen L, Vleugels J, Van der Biest O, van Landuyt J, Journal of the European Ceramic Society 25, 3437 (2005). http://doi.org/10.1016/j.jeurceramsoc.2004.09.004
Abstract: CeO2-doped ZrO2, (8 mol%) starting powder was sintered by means of spark plasma sintering (SPS) at 1300 degrees C without holding time. The stability of the tetragonal ZrO2 phase in the Ce-ZrO2 ceramic sintered under strongly reducing conditions was investigated. The SPS sample consisted of monoclinic and tetragonal ZrO2 phase, with a volume ratio of two to one, as well as a trace amount of a Zr-Ce-O cubic solid solution phase. In contrast, the same powder sintered by hot-pressing in nitrogen at 1300 and 1500 degrees C for 1h showed no tetragonal ZrO2. Microstructural observation of the SPS ceramic by SEM and TEM revealed grains with and without twins. The reason for the appearance of the tetragonal phase in the SPS sample sintered under strongly reducing conditions is discussed. (c) 2004 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 13
DOI: 10.1016/j.jeurceramsoc.2004.09.004
|
|
|
“Characterization of oxide precipitates in heavily B-doped silicon by infrared spectroscopy”. de Gryse O, Clauws P, Vanhellemont J, Lebedev OI, van Landuyt J, Simoen E, Claeys C, Journal of the electrochemical society 151, G598 (2004). http://doi.org/10.1149/1.1776592
Abstract: Infrared absorption spectra of oxygen precipitates in boron-doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function representation of composite materials. The aspect ratio of the platelet precipitates is determined by transmission electron microscopy measurements. The analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOγ precipitates are formed with the same composition as in the lightly doped case. In the heavily boron-doped (>10(18) cm(-3)) samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3, with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case. (C) 2004 The Electrochemical Society.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 13
DOI: 10.1149/1.1776592
|
|
|
“Fe and Co nanowires and nanotubes synthesized by template electrodeposition: a HRTEM and EELS study”. Verbeeck J, Lebedev OI, Van Tendeloo G, Cagnon L, Bougerol C, Tourillon T, Journal of the electrochemical society 150, E468 (2003). http://doi.org/10.1149/1.1601230
Abstract: Co and Fe nanowires and/or nanotubes are electrochemically synthesized through nanoporous membranes. By combining high-resolution transmission electron microscopy (HRTEM), electron energy loss spectroscopy (EELS), and energy filtered TEM techniques, their structural and crystallographic characteristics are precisely determined. The synthesis was shown to produce cigar-shaped single monocrystalline Co and Fe nanowires with a diameter of about 60 nm. All wires were surrounded by an epitaxial oxide layer (Co3O4 or Fe3O4) of roughly 10 nm. The Fe nanotubes were built up of Fe3O4 nanocrystals. Electron diffraction showed that all nanocrystals had a common crystallographic axis, creating a pseudomonocrystalline wall in the nanotubes. (C) 2003 The Electrochemical Society.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 41
DOI: 10.1149/1.1601230
|
|
|
“Investigation by convergent beam electron diffraction of the stress around shallow trench isolation structures”. Stuer C, van Landuyt J, Bender H, de Wolf I, Rooyackers R, Badenes G, Journal of the electrochemical society 148, G597 (2001). http://doi.org/10.1149/1.1404970
Abstract: Convergent beam electron diffraction (CBED) is used in this study to investigate the stress distribution around shallow trench isolation (STI) structures. Attention is given to the influence of the different processing parameters and the width and spacing of the structures. The use of a wet or a dry pregate oxidation is found to have a strong influence on the stress behavior. Isolated lines show more stress, leading to the formation of defects in the silicon substrate if a wet pregate oxidation is used. The CBED analyses are compared with micro-Raman and bright-field transmission electron microscopy measurements. (C) 2001 The Electrochemical Society.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 13
DOI: 10.1149/1.1404970
|
|
|
“Microstructural aspects of the degradation behavior of SnO2-based anodes for aluminum electrolysis”. Vassiliev SY, Laurinavichute VK, Abakumov AM, Govorov VA, Bendovskii EB, Turner S, Filatov AY, Tarasovskii VP, Borzenko AG, Alekseeva AM, Antipov EV, Journal of the electrochemical society 157, C178 (2010). http://doi.org/10.1149/1.3327903
Abstract: The performance of SnO2 ceramic anodes doped with copper and antimony oxides was examined in cryolite alumina melts under anodic polarization at different cryolite ratios, temperatures, times, and current densities. The corroded part consists of a narrow strong corrosion zone at the anode surface with damage of the intergrain contacts and a large increase in porosity, a wider moderate corrosion zone with a smaller porosity increase, and a Cu depletion zone, where the ceramic retains its initial microstructure and a slight porosity increase occurs due to the removal of the Cu-rich inclusions. Mechanical destruction of the anode was never observed in the 10100 h tests. A microstructural model of the ceramic was suggested, consisting of grains with an Sb-doped SnO2 grain core surrounded by an ~200 to 500 nm grain shell where SnO2 was simultaneously doped with Sb and Mn+ (M=Cu2+,Fe3+,Al3+). The grains were separated by a few nanometers thick Cu-enriched grain boundaries. Different secondary charge carrier (holes) concentrations and electric conductivities in the grain core and grain shell result in a higher current density at the intergrain regions that leads to their profound degradation, especially in the low temperature acidic melt.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 3
DOI: 10.1149/1.3327903
|
|
|
“Reversible Li-intercalation through oxygen reactivity in Li-rich Li-Fe-Te oxide materials”. McCalla E, Prakash AS, Berg E, Saubanere M, Abakumov AM, Foix D, Klobes B, Sougrati MT, Rousse G, Lepoivre F, Mariyappan S, Doublet ML, Gonbeau D, Novak P, Van Tendeloo G, Hermann RP, Tarascon JM;, Journal of the electrochemical society 162, A1341 (2015). http://doi.org/10.1149/2.0991507jes
Abstract: Lithium-rich oxides are a promising class of positive electrode materials for next generation lithium-ion batteries, and oxygen plays a prominent role during electrochemical cycling either by forming peroxo-like species and/or by irreversibly forming oxygen gas during first charge. Here, we present Li-Fe-Te-O materials which show a tremendous amount of oxygen gas release. This oxygen release accounts for nearly all the capacity during the first charge and results in vacancies as seen by transmission electron microscopy. There is no oxidation of either metal during charge but significant changes in their environments. These changes are particularly extreme for tellurium. XRD and neutron powder diffraction both show limited Changes during cycling and no appreciable change in lattice parameters. A density functional theory study of this material is performed and demonstrates that the holes created on some of the oxygen atoms upon oxidation are partially stabilized through the formation of shorter O-O bonds, i.e. (O-2)(n-) species which on further delithiation show a spontaneous O-2 de-coordination from the cationic network and migration to the now empty lithium layer. The rate limiting step during charge is undoubtedly the diffusion of oxygen either out along the lithium layer or via columns of oxygen atoms. (C) 2015 The Electrochemical Society. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 23
DOI: 10.1149/2.0991507jes
|
|
|
“Purification of catalytically produced multi-wall nanotubes”. Colomer J-F, Piedigrosso P, Willems I, Journet C, Bernier P, Van Tendeloo G, Fonseca A, Nagy JB, Journal of the Chemical Society : Faraday transactions: physical chemistry and chemical physics 94, 3753 (1998). http://doi.org/10.1039/a806804f
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 92
DOI: 10.1039/a806804f
|
|
|
“{110}-Layered B-cation ordering in the anion-deficient perovskite Pb2.4Ba2.6Fe2Sc2TiO13 with the crystallographic shear structure”. Tyablikov OA, Batuk D, Tsirlin AA, Batuk M, Verchenko VY, Filimonov DS, Pokholok KV, Sheptyakov DV, Rozova MG, Hadermann J, Antipov EV, Abakumov AM;, Journal of the Chemical Society : Dalton transactions 44, 10753 (2015). http://doi.org/10.1039/c4dt03867c
Abstract: A novel anion-deficient perovskite-based compound, Pb2.4Ba2.6Fe2Sc2TiO13, was synthesized via the citrate-based route. This compound is an n = 5 member of the A(n)B(n)O(3n-2) homologous series with unit-cell parameters related to the perovskite subcell a(p) approximate to 4.0 angstrom as a(p)root 2 x a(p) x 5a(p)root 2. The crystal structure of Pb2.4Ba2.6Fe2Sc2TiO13 consists of quasi-2D perovskite blocks with a thickness of three octahedral layers separated by the 1/2[110]((1) over bar 01)(p) crystallographic shear (CS) planes, which are parallel to the {110} plane of the perovskite subcell. The CS planes transform the corner-sharing octahedra into chains of edge-sharing distorted tetragonal pyramids. Using a combination of neutron powder diffraction, Fe-57 Mossbauer spectroscopy and atomic resolution electron energy-loss spectroscopy we demonstrate that the B-cations in Pb2.4Ba2.6Fe2Sc2TiO13 are ordered along the {110} perovskite layers with Fe3+ in distorted tetragonal pyramids along the CS planes, Ti4+ preferentially in the central octahedra of the perovskite blocks and Sc3+ in the outer octahedra of the perovskite blocks. Magnetic susceptibility and Mossbauer spectroscopy indicate a broadened magnetic transition around T-N similar to 45 K and the onset of local magnetic fields at low temperatures. The magnetic order is probably reminiscent of that in other A(n)B(n)O(3n-2) homologues, where G-type AFM order within the perovskite blocks has been observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 1
DOI: 10.1039/c4dt03867c
|
|
|
“Direct-synthesis method towards copper-containing periodic mesoporous organosilicas : detailed investigation of the copper distribution in the material”. Lin F, Meng, Kukueva E, Altantzis T, Mertens M, Bals S, Cool P, Van Doorslaer S, Journal of the Chemical Society : Dalton transactions 44, 9970 (2015). http://doi.org/10.1039/c4dt03719g
Abstract: Three-dimensional cubic Fm (3) over barm mesoporous copper-containing ethane-bridged PMO materials have been prepared through a direct-synthesis method at room temperature in the presence of cetyltrimethylammonium bromide as surfactant. The obtained materials have been unambiguously characterized in detail by several sophisticated techniques, including XRD, UV-Vis-Dr, TEM, elemental mapping, continuous- wave and pulsed EPR spectroscopy. The results show that at lower copper loading, the Cu2+ species are well dispersed in the Cu-PMO materials, and mainly exist as mononuclear Cu2+ species. At higher copper loading amount, Cu2+ clusters are observed in the materials, but the distribution of the Cu2+ species is still much better in the Cu-PMO materials prepared through the direct-synthesis method than in a Cu-containing PMO material prepared through an impregnation method. Moreover, the evolution of the copper incorporation during the PMO synthesis has been followed by EPR. The results show that the immobilization of the Cu2+ ion/complex and the formation of the PMO materials are taking place simultaneously. The copper ions are found to be situated on the inner surface of the mesopores of the materials and are accessible, which will be beneficial for the catalytic applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 4.029
Times cited: 11
DOI: 10.1039/c4dt03719g
|
|
|
“Oxygen-driven competition between low-dimensional structures of Sr3CoMO6 and Sr3CoMO7-\delta with M = Ru,Ir”. Mikhailova D, Reichel P, Tsirlin AA, Abakumov AM, Senyshyn A, Mogare KM, Schmidt M, Kuo CY, Pao CW, Pi TW, Lee JF, Hu Z, Tjeng LH;, Journal of the Chemical Society : Dalton transactions 43, 13883 (2014). http://doi.org/10.1039/c4dt01893a
Abstract: We have realized a reversible structure transformation of one-dimensional 1D K4CdCl6-type Sr3CoMO6 with the Co2+/M4+ cation ordering into the two-dimensional 2D double layered Ruddlesden-Popper structure Sr3CoMO7-delta with a random distribution of Co and M (with M = Ru, Ir) upon increasing the partial oxygen pressure. The combined soft and hard X-ray absorption spectroscopy studies show that under transformation, Co and M cations were oxidized to Co3+ and M5+. During oxidation, high-spin Co2+ in Sr3CoMO6 first transforms into high-spin Co3+ in oxygen-deficient Sr3CoMO7-delta, and then further transforms into low-spin Co3+ in fully oxidized Sr3CoMO7 upon further increasing the partial pressure of oxygen. The 1D Sr3CoMO6 compound is magnetically ordered at low temperatures with the magnetic moments lying along the c-axis. Their alignment is parallel for Sr3CoRuO6 and antiparallel for Sr3CoIrO6. The 2D compounds reveal a spin-glass-like behavior related to the random distribution of magnetic cations in the structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 7
DOI: 10.1039/c4dt01893a
|
|
|
“A pseudo-tetragonal tungsten bronze superstructure: a combined solution of the crystal structure of K6.4(Nb,Ta)36.3O94 with advanced transmission electron microscopy and neutron diffraction”. Paria Sena R, Babaryk AA, Khainakov S, Garcia-Granda S, Slobodyanik NS, Van Tendeloo G, Abakumov AM, Hadermann J, Journal of the Chemical Society : Dalton transactions 45, 973 (2016). http://doi.org/10.1039/c5dt03479e
Abstract: The crystal structure of the K6.4Nb28.2Ta8.1O94 pseudo-tetragonal tungsten bronze-type oxide was determined using a combination of X-ray powder diffraction, neutron diffraction and transmission electron microscopy techniques, including electron diffraction, high angle annular dark field scanning transmission electron microscopy (HAADF-STEM), annular bright field STEM (ABF-STEM) and energy-dispersive X-ray compositional mapping (STEM-EDX). The compound crystallizes in the space group Pbam with unit cell parameters a = 37.468(9) A, b = 12.493(3) A, c = 3.95333(15) A. The structure consists of corner sharing (Nb,Ta)O6 octahedra forming trigonal, tetragonal and pentagonal tunnels. All tetragonal tunnels are occupied by K(+) ions, while 1/3 of the pentagonal tunnels are preferentially occupied by Nb(5+)/Ta(5+) and 2/3 are occupied by K(+) in a regular pattern. A fractional substitution of K(+) in the pentagonal tunnels by Nb(5+)/Ta(5+) is suggested by the analysis of the HAADF-STEM images. In contrast to similar structures, such as K2Nb8O21, also parts of the trigonal tunnels are fractionally occupied by K(+) cations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 6
DOI: 10.1039/c5dt03479e
|
|
|
“Synthesis and cation distribution in the new bismuth oxyhalides with the Sillen-Aurivillius intergrowth structures”. Charkin DO, Akinfiev VS, Alekseeva AM, Batuk M, Abakumov AM, Kazakov SM, Journal of the Chemical Society : Dalton transactions 44, 20568 (2015). http://doi.org/10.1039/c5dt02620b
Abstract: About 20 new compounds with the Sillen-Aurivillius intergrowth structure, (MeMeBi3Nb2O11X)-Me-1-Bi-2 (Me-1 = Pb, Sr, Ba; Me-2 = Ca, Sr, Ba; X = Cl, Br, I), have been prepared. They are composed of stacking of [ANb(2)O(7)] perovskite blocks, fluorite-type [M2O2] blocks and halogen sheets. The cation distribution between the fluorite and perovskite layers has been studied for Ba2Bi3Nb2O11I, Ca1.25Sr0.75Bi3Nb2O11Cl, BaCaBi3Nb2O11Br and Sr2Bi3Nb2O11Cl. The smaller Me cations tend to reside in the perovskite block while the larger ones are situated in the fluorite-type block. The distribution of the elements was confirmed for BaCaBi3Nb2O11Br using energy dispersive X-ray analysis combined with scanning transmission electron microscopy (STEM-EDX). An electron diffraction study of this compound reveals a local symmetry lowering caused by weakly correlated rotation of NbO6 octahedra. Based on our findings, we suggest a new stability criterion for mixed-layer structures, which is that net charges of any two consecutive layers do not compensate for each other and only the whole layer sequence is electroneutral.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 5
DOI: 10.1039/c5dt02620b
|
|
|
“Synthesis, structure and magnetic ordering of the mullite-type Bi2Fe4-xCrxO9 solid solutions with a frustrated pentagonal Cairo lattice”. Rozova MG, Grigoriev VV, Bobrikov IA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Tsirlin AA, Abakumov AM, Journal of the Chemical Society : Dalton transactions 45, 1192 (2016). http://doi.org/10.1039/c5dt04296h
Abstract: Highly homogeneous mullite-type solid solutions Bi2Fe4-xCrxO9 (x = 0.5, 1, 1.2) were synthesized using a soft chemistry technique followed by a solid-state reaction in Ar. The crystal structure of Bi2Fe3CrO9 was investigated using X-ray and neutron powder diffraction, transmission electron microscopy and Fe-57 Mossbauer spectroscopy (S.G. Pbam, a = 7.95579(9) angstrom , b = 8.39145(9) angstrom, c = 5.98242(7) angstrom, R-F(X-ray) = 0.022, R-F(neutron) = 0.057). The ab planes in the structure are tessellated with distorted pentagonal loops built up by three tetrahedrally coordinated Fe sites and two octahedrally coordinated Fe/Cr sites, linked together in the ab plane by corner-sharing forming a pentagonal Cairo lattice. Magnetic susceptibility measurements and powder neutron diffraction show that the compounds order antiferromagnetically (AFM) with the Neel temperatures decreasing upon increasing the Cr content from T-N similar to 250 K for x = 0 to T-N similar to 155 K for x = 1.2. The magnetic structure of Bi2Fe3CrO9 at T = 30 K is characterized by a propagation vector k = (1/2,1/2,1/2). The tetrahedrally coordinated Fe cations form singlet pairs within dimers of corner-sharing tetrahedra, but spins on the neighboring dimers are nearly orthogonal. The octahedrally coordinated (Fe, Cr) cations form antiferromagnetic up-up-down-down chains along c, while the spin arrangement in the ab plane is nearly orthogonal between nearest neighbors and collinear between second neighbors. The resulting magnetic structure is remarkably different from the one in pure Bi2Fe4O9 and features several types of spin correlations even on crystallographically equivalent exchange that may be caused by the simultaneous presence of Fe and Cr on the octahedral site.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
DOI: 10.1039/c5dt04296h
|
|
|
“Composition-dependent charge transfer and phase separation in the V1-xRexO2 solid solution”. Mikhailova D, Kuratieva NN, Utsumi Y, Tsirlin AA, Abakumov AM, Schmidt M, Oswald S, Fuess H, Ehrenberg H, Journal of the Chemical Society : Dalton transactions 46, 1606 (2017). http://doi.org/10.1039/C6DT04389E
Abstract: The substitution of vanadium in vanadium dioxide VO2 influences the critical temperatures of structural and metal-to-insulator transitions in different ways depending on the valence of the dopant. Rhenium adopts valence states between + 4 and + 7 in an octahedral oxygen surrounding and is particularly interesting in this context. Structural investigation of V1-xRexO2 solid solutions (0.01 <= x <= 0.30) between 80 and 1200 K using synchrotron X-ray powder diffraction revealed only two polymorphs that resemble VO2: the low-temperature monoclinic MoO2-type form (space group P2(1)/c), and the tetragonal rutile-like form (space group P4(2)/mnm). However, for compositions with 0.03 < x <= 0.15 a phase separation in the solid solution was observed below 1000 K upon cooling down from 1200 K, giving rise to two isostructural phases with slightly different lattice parameters. This is reflected in the appearance of two metal-toinsulator transition temperatures detected by magnetization and specific heat measurements. Comprehensive X-ray photoelectron spectroscopy studies showed that an increased amount of Re leads to a change in the Re valence state from solely Re6+ at a low doping level (<= 3 at% Re) via mixed-valence states Re4+/Re6+ for at least 0.03 < x <= 0.10, up to nearly pure Re4+ in V0.70Re0.30O2. Thus, compositions V1-xRexO2 with only one valence state of Re in the material (Re6+ or Re4+) can be obtained as a single phase, while intermediate compositions are subjected to a phase separation, presumably due to different valence states of Re.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 1
DOI: 10.1039/C6DT04389E
|
|
|
“Small-moment paramagnetism and extensive twinning in the topochemically reduced phase Sr2ReLiO5.5”. Hasanli N, Gauquelin N, Verbeeck J, Hadermann J, Hayward MA, Journal of the Chemical Society : Dalton transactions 47, 15783 (2018). http://doi.org/10.1039/C8DT03463J
Abstract: Reaction of the cation-ordered double perovskite Sr2ReLiO6 with dilute hydrogen at 475 degrees C leads to the topochemical deintercalation of oxide ions from the host lattice and the formation of a phase of composition Sr2ReLiO5.5, as confirmed by thermogravimetric and EELS data. A combination of neutron and electron diffraction data reveals the reduction process converts the -Sr2O2-ReLiO4-Sr2O2-ReLiO4- stacking sequence of the parent phase into a -Sr2O2-ReLiO3-Sr2O2-ReLiO4-, partially anion-vacant ordered sequence. Furthermore a combination of electron diffraction and imaging reveals Sr2ReLiO5.5 exhibits extensive twinning – a feature which can be attributed to the large, anisotropic volume expansion of the material on reduction. Magnetisation data reveal a strongly reduced moment of (eff) = 0.505(B) for the d(1) Re6+ centres in the phase, suggesting there remains a large orbital component to the magnetism of the rhenium centres, despite their location in low symmetry coordination environments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
DOI: 10.1039/C8DT03463J
|
|
|
“Highly porous palladium nanodendrites : wet-chemical synthesis, electron tomography and catalytic activity”. Mourdikoudis S, Montes-Garcia V, Rodal-Cedeira S, Winckelmans N, Perez-Juste I, Wu H, Bals S, Perez-Juste J, Pastoriza-Santos I, Journal of the Chemical Society : Dalton transactions 48, 3758 (2019). http://doi.org/10.1039/C9DT00107G
Abstract: A simple procedure to obtain highly porous hydrophilic palladium nanodendrites in one-step is described. The synthetic strategy is based on the thermal reduction of a Pd precursor in the presence of a positively charged polyelectrolyte such as polyethylenimine (PEI). Advanced electron microscopy techniques combined with X-ray diffraction (XRD), thermogravimetry and BET analysis demonstrate the polycrystalline nature of the nanodendrites as well as their high porosity and active surface area, facilitating a better understanding of their unique morphology. Besides, catalytic studies performed using Raman scattering and UV-Vis spectroscopies revealed that the nanodendrites exhibit a superior performance as recyclable catalysts towards hydrogenation reaction compared to other noble metal nanoparticles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 23
DOI: 10.1039/C9DT00107G
|
|
|
“An in-depth study of Sn substitution in Li-rich/Mn-rich NMC as a cathode material for Li-ion batteries”. Paulus A, Hendrickx M, Bercx M, Karakulina OM, Kirsanova MA, Lamoen D, Hadermann J, Abakumov AM, Van Bael MK, Hardy A, Journal of the Chemical Society : Dalton transactions 49, 10486 (2020). http://doi.org/10.1039/D0DT01047B
Abstract: Layered Li-rich/Mn-rich NMC (LMR-NMC) is characterized by high initial specific capacities of more than 250 mA h g(-1), lower cost due to a lower Co content and higher thermal stability than LiCoO2. However, its commercialisation is currently still hampered by significant voltage fade, which is caused by irreversible transition metal ion migration to emptied Li positionsviatetrahedral interstices upon electrochemical cycling. This structural change is strongly correlated with anionic redox chemistry of the oxygen sublattice and has a detrimental effect on electrochemical performance. In a fully charged state, up to 4.8 Vvs.Li/Li+, Mn4+ is prone to migrate to the Li layer. The replacement of Mn4+ for an isovalent cation such as Sn4+ which does not tend to adopt tetrahedral coordination and shows a higher metal-oxygen bond strength is considered to be a viable strategy to stabilize the layered structure upon extended electrochemical cycling, hereby decreasing voltage fade. The influence of Sn4+ on the voltage fade in partially charged LMR-NMC is not yet reported in the literature, and therefore, we have investigated the structure and the corresponding electrochemical properties of LMR-NMC with different Sn concentrations. We determined the substitution limit of Sn4+ in Li1.2Ni0.13Co0.13Mn0.54-xSnxO2 by powder X-ray diffraction and transmission electron microscopy to be x approximate to 0.045. The limited solubility of Sn is subsequently confirmed by density functional theory calculations. Voltage fade for x= 0 andx= 0.027 has been comparatively assessed within the 3.00 V-4.55 V (vs.Li/Li+) potential window, from which it is concluded that replacing Mn4+ by Sn4+ cannot be considered as a viable strategy to inhibit voltage fade within this window, at least with the given restricted doping level.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4
DOI: 10.1039/D0DT01047B
|
|
|
“The influence of the 6s², configuration of Bi³+ on the structures of A ' BiNb₂O₇, (A ' = Rb, Na, Li) layered perovskite oxides”. Mallick S, Khalsa G, Kaaret JZ, Zhang W, Batuk M, Gibbs AS, Hadermann J, Halasyamani PS, Benedek NA, Hayward MA, Journal of the Chemical Society : Dalton transactions 50, 15359 (2021). http://doi.org/10.1039/D1DT02974F
Abstract: Solid state compounds which exhibit non-centrosymmetric crystal structures are of great interest due to the physical properties they can exhibit. The 'hybrid improper' mechanism – in which two non-polar distortion modes couple to, and stabilize, a further polar distortion mode, yielding an acentric crystal structure – offers opportunities to prepare a range of novel non-centrosymmetric solids, but examples of compounds exhibiting acentric crystal structures stabilized by this mechanism are still relatively rare. Here we describe a series of bismuth-containing layered perovskite oxide phases, RbBiNb2O7, LiBiNb2O7 and NaBiNb2O7, which have structural frameworks compatible with hybrid-improper ferroelectricity, but also contain Bi3+ cations which are often observed to stabilize acentric crystal structures due to their 6s(2) electronic configurations. Neutron powder diffraction analysis reveals that RbBiNb2O7 and LiBiNb2O7 adopt polar crystal structures (space groups I2cm and B2cm respectively), compatible with stabilization by a trilinear coupling of non-polar and polar modes. The Bi3+ cations present are observed to enhance the magnitude of the polar distortions of these phases, but are not the primary driver for the acentric structure, as evidenced by the observation that replacing the Bi3+ cations with Nd3+ cations does not change the structural symmetry of the compounds. In contrast the non-centrosymmetric, but non-polar structure of NaBiNb2O7 (space group P2(1)2(1)2(1)) differs significantly from the centrosymmetric structure of NaNdNb2O7, which is attributed to a second-order Jahn-Teller distortion associated with the presence of the Bi3+ cations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1039/D1DT02974F
|
|
|
“The crystal and defect structures of polar KBiNb2O7”. Mallick S, Zhang W, Batuk M, Gibbs AS, Hadermann J, Halasyamani PS, Hayward MA, Journal of the Chemical Society : Dalton transactions 51, 1866 (2022). http://doi.org/10.1039/D1DT04064B
Abstract: KBiNb2O7 was prepared from RbBiNb2O7 by a sequence of cation exchange reactions which first convert RbBiNb2O7 to LiBiNb2O7, before KBiNb2O7 is formed by a further K-for-Li cation exchange. A combination of neutron, synchrotron X-ray and electron diffraction data reveal that KBiNb2O7 adopts a polar, layered, perovskite structure (space group A11m) in which the BiNb2O7 layers are stacked in a (0, ½, z) arrangement, with the K+ cations located in half of the available 10-coordinate interlayer cation sites. The inversion symmetry of the phase is broken by a large displacement of the Bi3+ cations parallel to the y-axis. HAADF-STEM images reveal that KBiNb2O7 exhibits frequent stacking faults which convert the (0. ½, z) layer stacking to (½, 0, z) stacking and vice versa, essentially switching the x- and y-axes of the material. By fitting the complex diffraction peak shape of the SXRD data collected from KBiNb2O7 it is estimated that each layer has approximately an ~11% chance of being defective – a high level which is attributed to the lack of cooperative NbO6 tilting in the material, which limits the lattice strain associated with each fault.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4
DOI: 10.1039/D1DT04064B
|
|
|
“An oxysulfate Fe2O(SO4)2 electrode for sustainable Li-based batteries”. Sun M, Rousse G, Abakumov AM, Van Tendeloo G, Sougrati M-T, Courty M, Doublet M-L, Tarascon J-M, Journal of the American Chemical Society 136, 12658 (2014). http://doi.org/10.1021/ja505268y
Abstract: High-performing Fe-based electrodes for Li-based batteries are eagerly pursued because of the abundance and environmental benignity of iron, with especially great interest in polyanionic compounds because of their flexibility in tuning the Fe3+/Fe2+ redox potential. We report herein the synthesis and structure of a new Fe-based oxysulfate phase, Fe2O(SO4)(2), made at low temperature from abundant elements, which electrochemically reacts with nearly 1.6 Li atoms at an average voltage of 3.0 V versus Li+/Li, leading to a sustained reversible capacity of similar to 125 mAh/g. The Li insertiondeinsertion process, the first ever reported in any oxysulfate, entails complex phase transformations associated with the position of iron within the FeO6 octahedra. This finding opens a new path worth exploring in the quest for new positive electrode materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 11
DOI: 10.1021/ja505268y
|
|
|
“Artificial construction of the layered Ruddlesden-Popper manganite La2Sr2Mn3O10 by reflection high energy electron diffraction monitored pulsed laser deposition”. Palgrave RG, Borisov P, Dyer MS, McMitchell SRC, Darling GR, Claridge JB, Batuk M, Tan H, Tian H, Verbeeck J, Hadermann J, Rosseinsky MJ;, Journal of the American Chemical Society 134, 7700 (2012). http://doi.org/10.1021/ja211138x
Abstract: Pulsed laser deposition has been used to artificially construct the n = 3 Ruddlesden Popper structure La2Sr2Mn3O10 in epitaxial thin film form by sequentially layering La1-xSrxMnO3 and SrO unit cells aided by in situ reflection high energy electron diffraction monitoring. The interval deposition technique was used to promote two-dimensional SrO growth. X-ray diffraction and cross-sectional transmission electron microscopy indicated that the trilayer structure had been formed. A site ordering was found to differ from that expected thermodynamically, with the smaller Sr2+ predominantly on the R site due to kinetic trapping of the deposited cation sequence. A dependence of the out-of-plane lattice parameter on growth pressure was interpreted as changing the oxygen content of the films. Magnetic and transport measurements on fully oxygenated films indicated a frustrated magnetic ground state characterized as a spin glass-like magnetic phase with the glass temperature T-g approximate to 34 K. The magnetic frustration has a clear in-plane (ab) magnetic anisotropy, which is maintained up to temperatures of 150 K. Density functional theory calculations suggest competing antiferromagnetic and ferromagnetic long-range orders, which are proposed as the origin of the low-temperature glassy state.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 27
DOI: 10.1021/ja211138x
|
|
|
“Control of surface plasmon localization via self-assembly of silver nanoparticles along silver nanowires”. Tran ML, Centeno SP, Hutchison JA, Engelkamp H, Liang D, Van Tendeloo G, Sels BF, Hofkens J, Uji-i H, Journal of the American Chemical Society 130, 17240 (2008). http://doi.org/10.1021/ja807218e
Abstract: A simple and low-cost method to create metal−metal hybrid nanostructures possessing fairly regularly spaced hot-spots of surface plasmon resonances is proposed. The nanohybrid structure was prepared via self-assembly during a simple drop-casting procedure, using chemically synthesized silver nanowires and silver nanoparticles prepared in a single batch of a polyol process. Wide field illumination of these nanohybrids produced hot-spots with spacings of around 500 nm to 1 ìm. The intensity of the emission/scattering from the hot-spots fluctuates over time. The proposed structure can be useful for the development of molecular-sensors or as a substrate for surface enhanced Raman/fluorescence spectroscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 51
DOI: 10.1021/ja807218e
|
|
|
“Copper benzene tricarboxylate metal-organic framework with wide permanent mesopores stabilized by keggin polyoxometallate ions”. Wee LH, Wiktor C, Turner S, Vanderlinden W, Janssens N, Bajpe SR, Houthoofd K, Van Tendeloo G, De Feyter S, Kirschhock CEA, Martens JA;, Journal of the American Chemical Society 134, 10911 (2012). http://doi.org/10.1021/ja302089w
Abstract: Porous solids with organized multiple porosity are of scientific and technological importance for broadening the application range from traditional areas of catalysis and adsorption/separation to drug release and biomedical imaging. Synthesis of crystalline porous materials offering a network of uniform micro- and mesopores remains a major scientific challenge. One strategy is based on variation of synthesis parameters of microporous networks, such as, for example, zeolites or metal organic frameworks (MOFs). Here, we show the rational development of an hierarchical variant of the microporous cubic Cu-3(BTC)(2) (BTC = 1,3,5-benzenetricarboxylate) HKUST-1 MOF having strictly repetitive S inn wide mesopores separated by uniform microporous walls in a single crystal structure. This new material coined COK-15 (COK = Centrum voor Oppervlaktechemie en Katalyse) was synthesized via a dual-templating approach. Stability was enhanced by Keggin type phosphotungstate (HPW) systematically occluded in the cavities constituting the walls between the mesopores.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 83
DOI: 10.1021/ja302089w
|
|
|
“F-doped Co3O4 photocatalysts for sustainable H2 generation from water/ethanol”. Gasparotto A, Barreca D, Bekermann D, Devi A, Fischer RA, Fornasiero P, Gombac V, Lebedev OI, Maccato C, Montini T, Van Tendeloo G, Tondello E, Journal of the American Chemical Society 133, 19362 (2011). http://doi.org/10.1021/ja210078d
Abstract: p-Type Co3O4 nanostructured films are synthesized by a plasma-assisted process and tested in the photocatalytic production of H2 from water/ethanol solutions under both near-UV and solar irradiation. It is demonstrated that the introduction of fluorine into p-type Co3O4 results in a remarkable performance improvement with respect to the corresponding undoped oxide, highlighting F-doped Co3O4 films as highly promising systems for hydrogen generation. Notably, the obtained yields were among the best ever reported for similar semiconductor-based photocatalytic processes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 114
DOI: 10.1021/ja210078d
|
|
|
“Facile synthesis of Ba1-xKxFe2As2 superconductors via hydride route”. Zaikina JV, Batuk M, Abakumov AM, Navrotsky A, Kauziarich SM, Journal of the American Chemical Society 136, 16932 (2014). http://doi.org/10.1021/ja509907r
Abstract: We have developed a fast, easy, and scalable synthesis method for Ba1xKxFe2As2 (0 ≤ x ≤ 1) superconductors using hydrides BaH2 and KH as a source of barium and potassium metals. Synthesis from hydrides provides better mixing and easier handling of the starting materials, consequently leading to faster reactions and/or lower synthesis temperatures. The reducing atmosphere provided by the evolved hydrogen facilitates preparation of oxygen-free powders. By a combination of methods we have shown that Ba1xKxFe2As2 obtained via hydride route has the same characteristics as when it is prepared by traditional solid-state synthesis. Refinement from synchrotron powder X-ray diffraction data confirms a linear dependence of unit cell parameters upon K content as well as the tetragonal to orthorhombic transition at low temperatures for compositions with x < 0.2. Magnetic measurements revealed dome-like dependence of superconducting transition temperature Tc upon K content with a maximum of 38 K for x close to 0.4. Electron diffraction and high-resolution high-angle annular dark-field scanning transmission electron microscopy indicates an absence of Ba/K ordering, while local inhomogeneity in the Ba/K distribution takes place at a scale of several angstroms along [110] crystallographic direction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 13
DOI: 10.1021/ja509907r
|
|
|
“Fluorinated heterometallic \beta-diketonates as volatile single-source precursors for the synthesis of low-valent mixed-metal fluorides”. Navulla A, Tsirlin AA, Abakumov AM, Shpanchenko RV, Zhang H, Dikarev EV, Journal of the American Chemical Society 133, 692 (2011). http://doi.org/10.1021/ja109128r
Abstract: Hexafluoroacetylacetonates that contain lead and divalent first-row transition metals, PbM(hfac)4 (M = Ni (1), Co (2), Mn (3), Fe (4), and Zn (5)), have been synthesized. Their heterometallic structures are held together by strong Lewis acid−base interactions between metal atoms and diketonate ligands acting in chelating−bridging fashion. Compounds 1−5 are highly volatile and decompose below 350 °C. Fluorinated heterometallic β-diketonates have been used for the first time as volatile single-source precursors for the preparation of mixed-metal fluorides. Complex fluorides of composition Pb2MF6 have been obtained by decomposition of 1−5 in a two-zone furnace under low-pressure nitrogen flow. Lead−transition metal fluorides conform to orthorhombically distorted Aurivillius-type structure with layers of corner-sharing [MF6] octahedra separated by α-PbO-type (Pb2F2) blocks. Pb2NiF6 and Pb2CoF6 were found to exhibit magnetic ordering below 80 and 43 K, respectively. The ordering is antiferromagnetic, with a weak, uncompensated moment due to the canting of spins. The Pb2MF6 fluorides represent a new class of prospective magnetoelectric materials combining transition metals and lone-pair main-group cations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 28
DOI: 10.1021/ja109128r
|
|
|
“Fragmentation of an infinite ZnO2 square plane into discrete [ZnO2]2- linear units in the oxyselenide Ba2ZnO2Ag2Se2”. Herkelrath SJC, Saratovsky I, Hadermann J, Clarke SJ, Journal of the American Chemical Society 130, 14426 (2008). http://doi.org/10.1021/ja8063414
Abstract: Analysis of single crystal X-ray diffraction, neutron powder diffraction, electron diffraction and Zn−K-edge EXAFS data show that Ba2ZnO2Ag2Se2 contains unusual isolated [ZnO2]2− moieties resulting from fragmentation of a ZnO2 infinite plane placed under tension.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 13
DOI: 10.1021/ja8063414
|
|
|
“GaN@ZIF-8 : selective formation of gallium nitride quantum dots inside a zinc methylimidazolate framework”. Esken D, Turner S, Wiktor C, Kalidindi SB, Van Tendeloo G, Fischer RA, Journal of the American Chemical Society 133, 16370 (2011). http://doi.org/10.1021/ja207077u
Abstract: The microporous zeolitic imidazolate framework [Zn(MeIM)2; ZIF-8; MeIM = imidazolate-2-methyl] was quantitatively loaded with trimethylamine gallane [(CH3)3NGaH3]. The obtained inclusion compound [(CH3)3NGaH3]@ZIF-8 reveals three precursor molecules per host cavity. Treatment with ammonia selectively yields the caged cyclotrigallazane intermediate (H2GaNH2)3@ZIF-8, and further annealing gives GaN@ZIF-8. This new composite material was characterized with FT-IR spectroscopy, solid-state NMR spectroscopy, powder X-ray diffraction, elemental analysis, (scanning) transmission electron microscopy combined with electron energy-loss spectroscopy, photoluminescence (PL) spectroscopy, and N2 sorption measurements. The data give evidence for the presence of GaN nanoparticles (13 nm) embedded in the cavities of ZIF-8, including a blue-shift of the PL emission band caused by the quantum size effect.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 82
DOI: 10.1021/ja207077u
|
|
|
“A generalized electrochemical aggregative growth mechanism”. Ustarroz J, Hammons JA, Altantzis T, Hubin A, Bals S, Terryn H, Journal of the American Chemical Society 135, 11550 (2013). http://doi.org/10.1021/ja402598k
Abstract: The early stages of nanocrystal nucleation and growth are still an active field of research and remain unrevealed. In this work, by the combination of aberration-corrected transmission electron microscopy (TEM) and electrochemical characterization of the electrodeposition of different metals, we provide a complete reformulation of the VolmerWeber 3D island growth mechanism, which has always been accepted to explain the early stages of metal electrodeposition and thin-film growth on low-energy substrates. We have developed a Generalized Electrochemical Aggregative Growth Mechanism which mimics the atomistic processes during the early stages of thin-film growth, by incorporating nanoclusters as building blocks. We discuss the influence of new processes such as nanocluster self-limiting growth, surface diffusion, aggregation, and coalescence on the growth mechanism and morphology of the resulting nanostructures. Self-limiting growth mechanisms hinder nanocluster growth and favor coalescence driven growth. The size of the primary nanoclusters is independent of the applied potential and deposition time. The balance between nucleation, nanocluster surface diffusion, and coalescence depends on the material and the overpotential, and influences strongly the morphology of the deposits. A small extent of coalescence leads to ultraporous dendritic structures, large surface coverage, and small particle size. Contrarily, full recrystallization leads to larger hemispherical monocrystalline islands and smaller particle density. The mechanism we propose represents a scientific breakthrough from the fundamental point of view and indicates that achieving the right balance between nucleation, self-limiting growth, cluster surface diffusion, and coalescence is essential and opens new, exciting possibilities to build up enhanced supported nanostructures using nanoclusters as building blocks.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 124
DOI: 10.1021/ja402598k
|
|
|
“Mn(I) in an extended oxide : the synthesis and characterization of La1-xCaxMnO2+\delta (0.6\leq x\leq1)”. Dixon E, Hadermann J, Ramos S, Goodwin AL, Hayward MA, Journal of the American Chemical Society 133, 18397 (2011). http://doi.org/10.1021/ja207616c
Abstract: Reduction of La1xCaxMnO3 (0.6 ≤ x ≤ 1) perovskite phases with sodium hydride yields materials of composition La1xCaxMnO2+δ. The calcium-rich phases (x = 0.9, 1) adopt (La0.9Ca0.1)0.5Mn0.5O disordered rocksalt structures. However local structure analysis using reverse Monte Carlo refinement of models against pair distribution functions obtained from neutron total scattering data reveals lanthanum-rich La1xCaxMnO2+δ (x = 0.6, 0.67, 0.7) phases adopt disordered structures consisting of an intergrowth of sheets of MnO6 octahedra and sheets of MnO4 tetrahedra. X-ray absorption data confirm the presence of Mn(I) centers in La1xCaxMnO2+δ phases with x < 1. Low-temperature neutron diffraction data reveal La1xCaxMnO2+δ (x = 0.6, 0.67, 0.7) phases become antiferromagnetically ordered at low temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 33
DOI: 10.1021/ja207616c
|
|