“Structure and magnetotransport properties of La2/3Ca1/3MnO3 thin films prepared by pulsed laser deposition”. Lebedev OI, Van Tendeloo G, Amelinckx S, Leibold B, Habermeier HU, Phillipp F, Materials Research Society symposium proceedings
T2 –, Symposium on Advances in Laser Ablation of Materials at the 1998 MRS, Spring Meeting, April 13-16, 1998, San Francisco, Calif. , 219 (1998). http://doi.org/10.1557/PROC-526-219
Abstract: La1-xCaxMnO3-delta (LCMO) thin films are grown by pulsed laser deposition on a (100) SrTiO3 substrate at temperatures between 530 degrees C and 890 degrees C. The magnetotransport properties show a high negative magnetoresistance and a shift of the maximum of the R(T) curve as function of temperature. The Curie temperature changes with deposition temperature and film quality in the range of 100-220K. The film quality is characterised by X-ray diffraction and transmission electron microscopy (TEM); film and target compositions were verified by atomic emission spectroscopy. The local structure of the film depends on the growth conditions and substrate temperature. TEM reveals a slight distortion of the film leading to a breakdown of the symmetry from orthorhombic to monoclinic. At the highest growth temperatures, a well defined interface is observed within the LCMO film, parallel to the substrate surface; this interface divides the film into two lamellae with a different microstructure. The lamella close to the substrate is perfectly coherent with the substrate, suggesting that it is strained as a result of the lattice parameter mismatch; the upper lamella shows a typical domain structure with unusual translation interfaces characterised by a displacement vector of the type 1/2[010](m) and 1/2[001](m) when referred ten the monoclinic lattice.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
DOI: 10.1557/PROC-526-219
|
|
|
“Measurement of local crystal lattice strain variations in dealloyed nanoporous gold”. Mahr C, Müller-Caspary K, Graf M, Lackmann A, Grieb T, Schowalter M, Krause FF, Mehrtens T, Wittstock A, Weissmueller J, Rosenauer A, Materials research letters 6, 84 (2018). http://doi.org/10.1080/21663831.2017.1396263
Abstract: Reversible macroscopic length changes in nanoporous structures can be achieved by applying electric potentials or by exposing them to different gases or liquids. Thus, these materials are interesting candidates for applications as sensors or actuators. Macroscopic length changes originate from microscopic changes of crystal lattice parameters. In this report, we show spatially resolved measurements of crystal lattice strain in dealloyed nanoporous gold. The results confirm theory by indicating a compression of the lattice along the axis of cylindrically shaped ligaments and an expansion in radial direction. Furthermore, we show that curved npAu surfaces show inward relaxation of the surface layer. [GRAPHICS] .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.773
Times cited: 4
DOI: 10.1080/21663831.2017.1396263
|
|
|
“Self-assembly of gas-phase synthesized magnesium nanoparticles on room temperature substrates”. Venturi F, Calizzi M, Bals S, Perkisas T, Pasquini L, Materials research express 2, 015007 (2015). http://doi.org/10.1088/2053-1591/2/1/015007
Abstract: Magnesium nanoparticles (NPs) with initial size in the 10-50 nmrange were synthesized by inert gas condensation under helium flow and deposited on room temperature substrates. The morphology and crystal structure of the NPs ensemble were investigated as a function of the deposition time by complementary electron microscopy techniques, including high resolution imaging and chemical mapping. With increasing amount of material, strong coarsening phenomena were observed at room temperature: small NPs disappeared while large faceted NPs developed, leading to a 5-fold increase of the average NPs size within a few minutes. The extent of coarsening and the final morphology depended also on the nature of the substrate. Furthermore, large single-crystal NPs were seen to arise from the self-organization of primary NPs units, providing a mechanism for crystal growth. The dynamics of the self-assembly process involves the basic steps of NPs sticking, diffusion on substrate, coordinated rotation and attachment/coalescence. Key features are the surface energy anisotropy, reflected by the faceted shape of the NPs, and the low melting point of the material. The observed phenomena have strong implications in relation to the synthesis and stability of nanostructures based on Mg or other elements with similar features.
Keywords: A1 Journal article; Engineering Management (ENM); Electron microscopy for materials research (EMAT)
Impact Factor: 1.068
Times cited: 14
DOI: 10.1088/2053-1591/2/1/015007
|
|
|
“Nanoscale photovoltage mapping in CZTSe/CuxSe heterostructure by using kelvin probe force microscopy”. Vishwakarma M, Varandani D, Hendrickx M, Hadermann J, Mehta BR, Materials Research Express 7, 016418 (2020). http://doi.org/10.1088/2053-1591/AB65E6
Abstract: In the present work, kelvin probe force microscopy (KPFM) technique has been used to study the CZTSe/CuxSe bilayer interface prepared by multi-step deposition and selenization process of metal precursors. Transmission electron microscopy (TEM) confirmed the bilayer configuration of the CZTSe/CuxSe sample. Two configuration modes (surface mode and junction mode) in KPFM have been employed in order to measure the junction voltage under illumination conditions. The results show that CZTSe/CuxSe has small junction voltage of similar to 21 mV and the presence of CuxSe secondary phase in the CZTSe grain boundaries changes the workfunction of the local grain boundaries region. The negligible photovoltage difference between grain and grain boundaries in photovoltage image indicates that CuxSe phase deteriorates the higher photovoltage at grain boundaries normally observed in CZTSe based device. These results can be important for understanding the role of secondary phases in CZTSe based junction devices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1088/2053-1591/AB65E6
|
|
|
“Crystal structure and magnetic properties of the Cr-doped spiral antiferromagnet BiMnFe2O6”. Batuk D, de Dobbelaere C, Tsirlin AA, Abakumov AM, Hardy A, van Bael MK, Greenblatt M, Hadermann J, Materials research bulletin 48, 2993 (2013). http://doi.org/10.1016/j.materresbull.2013.04.038
Abstract: We report the Cr3+ for Mn3+ substitution in the BiMnFe2O6 structure. The BiCrxMn1-xFe2O6 solid solution is obtained by the solution-gel synthesis technique for the x values up to 0.3. The crystal structure investigation using a combination of X-ray powder diffraction and transmission electron microscopy demonstrates that the compounds retain the parent BiMnFe2O6 structure (for x = 0.3, a = 5.02010(6)angstrom, b = 7.06594(7)angstrom, c = 12.6174(1)angstrom, S.G. Pbcm, R-1 = 0.036, R-p = 0.011) with only a slight decrease in the cell parameters associated with the Cr3+ for Mn3+ substitution. Magnetic susceptibility measurements suggest strong similarities in the magnetic behavior of BiCrxMn1-xFe2O6 (x = 0.2; 0.3) and parent BiMnFe2O6. Only T-N slightly decreases upon Cr doping that indicates a very subtle influence of Cr3+ cations on the magnetic properties at the available substitution rates. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 3
DOI: 10.1016/j.materresbull.2013.04.038
|
|
|
“Crystal structure and properties of the new complex vanadium oxide K2SrV3O9”. Tsirlin AA, Chernaya VV, Shpanchenko RV, Antipov EV, Hadermann J, Materials research bulletin 40, 800 (2005). http://doi.org/10.1016/j.materresbull.2005.02.004
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 9
DOI: 10.1016/j.materresbull.2005.02.004
|
|
|
“Crystal structures of superconducting sodium intercalates of hafnium nitride chloride”. Oró-Solé, J, Frontera C, Beltrán-Porter D, Lebedev OI, Van Tendeloo G, Fuertes A, Materials research bulletin 41, 934 (2006). http://doi.org/10.1016/j.materresbull.2006.03.018
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 8
DOI: 10.1016/j.materresbull.2006.03.018
|
|
|
“Electron microscopy and diffraction study of the composition dependency of the 3R microtwinned martensite in Ni-Al”. Schryvers D, de Saegher B, van Landuyt J, Materials research bulletin 26, 57 (1991)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 11
|
|
|
“Fluorine intercalation in the n=1 and n=2 layered manganites Sr2MnO3.5+x and Sr3Mn2O6”. Sullivan E, Gillie LJ, Hadermann J, Greaves C, Materials research bulletin 48, 1598 (2013). http://doi.org/10.1016/j.materresbull.2012.12.073
Abstract: Fluorine insertion into the oxygen defect superstructure manganite Sr2MnO3.5+x has been shown by transmission electron microscopy (TEM) to result in two levels of fluorination. In the higher fluorine content sections, the fluorine anions displace oxygen anions from their apical positions into the equatorial vacancies, thus destroying the superstructure and reverting to a K2NiF4-type structure (a = 3.8210(1) angstrom and c = 12.686(1) angstrom). Conversely, lower fluorine content sections retain the Sr2MnO3.5+x defect superstructure, crystallising in the P2(1)/c space group. Fluorine intercalation into the reduced double-layer manganite Sr3Mn2O6 occurs in a step-wise fashion according to the general formula Sr3Mn2O6Fy with y = 1, 2, and 3. It is proposed that the y = 1 phase (a = 3.815(1)angstrom, c = 20.29(2) angstrom) is produced by the filling of all the equatorial oxygen vacancies by fluorine atoms whilst the y = 2 phase (a = 3.8222(2) angstrom, c = 21.2435(3)angstrom) has a random distribution of fluorine anions throughout both interstitial rocksalt and equatorial sites. Neutron powder diffraction data suggest that the fully fluorinated y = 3 phase (a = 3.8157(6) angstrom, c = 23.666(4) angstrom) corresponds to the complete occupation of all the equatorial oxygen vacancies and the interstitial sites by intercalated fluorine. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2012.12.073
|
|
|
“Fluorite-like phases in the BaF2-BiF3-Bi2O3 system-synthesis, conductivity and defect clustering”. Serov TV, Dombrovski EN, Ardashnikova EI, Dolgikh VA, el Omari M, el Omari M, Abaouz A, Senegas J, Chaban NG, Abakumov AM, Van Tendeloo G, Materials research bulletin 40, 821 (2005). http://doi.org/10.1016/j.materresbull.2005.02.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2005.02.007
|
|
|
“Influence of laser and isothermal treatments on microstructural properties of SnO2 films”. Rembeza ES, Richard O, van Landuyt J, Materials research bulletin 34, 1527 (1999). http://doi.org/10.1016/S0025-5408(99)00188-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 17
DOI: 10.1016/S0025-5408(99)00188-9
|
|
|
“New lead vanadium phosphate with langbeinite-type structure: Pb1.5V2(PO4)3”. Shpanchenko RV, Lapshina OA, Antipov EV, Hadermann J, Kaul EE, Geibel C, Materials research bulletin 40, 1569 (2005). http://doi.org/10.1016/j.materresbull.2005.04.037
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 14
DOI: 10.1016/j.materresbull.2005.04.037
|
|
|
“Properties and thermal stability of solution processed ultrathin, high-k bismuth titanate (Bi2Ti2O7) films”. Hardy A, Van Elshocht S, De Dobbelaere C, Hadermann J, Pourtois G, De Gendt S, Afanas'ev VV, Van Bael MK, Materials research bulletin 47, 511 (2012). http://doi.org/10.1016/j.materresbull.2012.01.001
Abstract: Ultrathin bismuth titanate films (Bi2Ti2O7, 5-25 nm) are deposited onto SiO2/Si substrates by aqueous chemical solution deposition and their evolution during annealing is studied. The films crystallize into a preferentially oriented, pure pyrochlore phase between 500 and 700 degrees C, depending on the film thickness and the total thermal budget. Crystallization causes a strong increase of surface roughness compared to amorphous films. An increase of the interfacial layer thickness is observed after anneal at 600 degrees C, together with intermixing of bismuth with the substrate as shown by TEM-EDX. The band gap was determined to be similar to 3 eV from photoconductivity measurements and high dielectric constants between 30 and 130 were determined from capacitance voltage measurements, depending on the processing conditions. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.446
DOI: 10.1016/j.materresbull.2012.01.001
|
|
|
“Structural phase transition at low temperature, corresponding to charge ordering in the CMR perovskites LN0.5A0.5MNO3”. Laffez P, Van Tendeloo G, Millange F, Caignaert V, Hervieu M, Raveau B, Materials research bulletin 31, 905 (1996). http://doi.org/10.1016/S0025-5408(96)00090-6
Abstract: The magneto resistive perovskites Nd0.5Sr0.5MnO3 and Pr0.5Sr0.41Ca0.09MnO3 undergo a transition from anti ferromagnetic insulator to ferromagnetic metal as function of temperature. The room temperature phase is orthorhombic with the space group Imma and the cell parameters a approximate to root 2a(p), b approximate to 2a(p), and c approximate to root 2a(p). A structural phase transition related to charge ordering accompanying the transition from ferromagnetic state to antiferromagnetic state has been evidenced by low temperature electron diffraction. This transition is reversible and a new superstructure, with a P-type orthorhombic cell. and lattice parameters parameters a approximate to 2 root 2a(p), b approximate to 2a(p), and c approximate to root 2a(p), is formed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 25
DOI: 10.1016/S0025-5408(96)00090-6
|
|
|
“Structure and magnetic properties of a new anion-deficient perovskite Pb2Ba2BiFe4ScO13 with crystallographic shear structure”. Batuk M, Tyablikov OA, Tsirlin AA, Kazakov SM, Rozova MG, Pokholok KV, Filimonov DS, Antipov EV, Abakumov AM, Hadermann J, Materials research bulletin 48, 3459 (2013). http://doi.org/10.1016/j.materresbull.2013.05.028
Abstract: Pb2Ba2BiFe4ScO13, a new n = 5 member of the oxygen-deficient perovskite-based A(n)B(n)O(3n-2) homologous series, was synthesized using a solid-state method. The crystal structure of Pb2Ba2BiFe4ScO13 was investigated by a combination of synchrotron X-ray powder diffraction, electron diffraction, high-angle annular dark-field scanning transmission electron microscopy and Mossbauer spectroscopy. At 900 K, it crystallizes in the Ammm space group with the unit cell parameters a = 5.8459(1) angstrom, b = 4.0426(1) angstrom, and c=27.3435(1) angstrom. In the Pb2Ba2BiFe4ScO13 structure, quasi-two-dimensional perovskite blocks are periodically interleaved with 1/2[1 1 0] ((1) over bar 0 1)(p) crystallographic shear (CS) planes. At the CS planes, the corner-sharing FeO6 octahedra are transformed into chains of edge-sharing FeO5 distorted tetragonal pyramids. B-positions of the perovskite blocks between the CS planes are jointly occupied by Fe3+ and Sc3+. The chains of the FeO5 pyramids and (Fe,Sc)O-6 octahedra delimit six-sided tunnels that are occupied by double columns of cations with a lone electron pair (Pb2+). The remaining A-cations (Bi3+, Ba2+) occupy positions in the perovskite block. According to the magnetic susceptibility measurements, Pb2Ba2BiFe4ScO13 is antiferromagnetically ordered below T-N approximate to 350 K. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 2
DOI: 10.1016/j.materresbull.2013.05.028
|
|
|
“Structure of the hexagonal 16l perovskites Ba4Ca0.9Mn3.1O11.3 and Ba4Ca0.5Mn3Cu0.5O12-\delta by high-resolution electron microscopy”. Schuddinck W, Van Tendeloo G, Hervieu M, Floros N, Raveau B, Materials research bulletin 36, 2689 (2001). http://doi.org/10.1016/S0025-5408(01)00744-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/S0025-5408(01)00744-9
|
|
|
“TEM study of laser induced phase transition in iron thin films”. Teodorescu VS, Nistor LC, van Landuyt J, Dinescu M, Materials research bulletin 29, 63 (1994). http://doi.org/10.1016/0025-5408(94)90106-6
Abstract: Laser induced phase transition from b.c.c.(alpha) to f.c.c.(gamma) iron thin films is studied by high resolution TEM. The iron film has been covered on both sides with carbon layers to protect it against oxidation. Single pulse, tau FWHM = 20ns KrF (lambda = 248nm) excimer laser irradiation was performed in air with the film on the substrate. The laser pulse acts like a heat pulse followed by a rapid quenching revealing sequential aspects of the phase transition process. The presence of a fine mixture of the alpha + gamma phases between the alpha and gamma regions of the film has been interpreted as an incomplet transformation. The results are explained by assuming that the transformation took place via a phonon drag mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 2
DOI: 10.1016/0025-5408(94)90106-6
|
|
|
“:Ba2.1Bi0.9(O, F)6.8-\delta: a new ordered anion-excess fluorite”. Prituzhalov VA, Abakumov AM, Ardashnikova EI, Dolgikh VA, Van Tendeloo G, Materials research bulletin 42, 861 (2007). http://doi.org/10.1016/j.materresbull.2006.08.023
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2006.08.023
|
|
|
“Doping of Bi4Fe5O13F with pentagonal Cairo lattice with Cr and Mn: Synthesis, structure and magnetic properties”. Rozova MG, Grigoriev VV, Tyablikov OA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Abakumov AM, Materials research bulletin 87, 54 (2017). http://doi.org/10.1016/J.MATERRESBULL.2016.11.018
Abstract: The substitution of Cr3+ and Mn3+ for Fe3+ in the Bi4Fe6O13F oxyfluoride featuring the magnetically frustrated pentagonal Cairo lattice is reported. Bi4Fe4.1Cr0.9O13F and BiFe4.2Mn0.8O13F have been prepared using a solid state reaction in inert atmosphere. Their crystal structures were studied with transmission electron microscopy, powder X-ray diffraction and Fe-57 Mossbauer spectroscopy (S.G. P4(2)/mbc, a = 8.27836(2)angstrom, c = 18.00330(9) angstrom, R-F = 0.031 (Bi4Fe4.1Cr0.9O13F)), a= 8.29535(3)angstrom, c= 18.0060(1)angstrom, R-F = 0.027 (Bi4Fe4.1Cr0.9O13F)). The structures are formed by infinite rutile-like chains of the edge sharing BO6 octahedra (B transition metal cations) linked by the Fe2O7 groups of two corner-sharing tetrahedra. The"voids in thus formed framework are occupied by the Bi4F tetrahedra. The Fe-57 Mossbauer spectroscopy reveals that Cr3+ and Mn3+ replace Fe3+. exclusively at the octahedral positions. The Mn- and Cr-doped compounds demonstrate antiferromagnetic ordering below T-N =165 K and 120 K, respectively. (C) 2016 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 1
DOI: 10.1016/J.MATERRESBULL.2016.11.018
|
|
|
“In-situ TEM study of the Ni5Al3 to B2 + L12 decomposition in Ni65Al35”. Schryvers D, Ma Y, Materials letters 23, 105 (1995). http://doi.org/10.1016/0167-577X(95)00030-5
Abstract: Homogenised and quenched Ni65Al35 samples were heated and studied in situ in a CM20 electron microscope up to 900 degrees C. The Ni5Al3 phase first forming around 550 degrees C in the quenched L1(0) microtwinned martensite starts to decompose around 800 degrees C yielding B2 precipitates in a twinned L1(2) matrix. The latter twinning is a remainder of the microtwinning in the original room temperature martensite. Also the crystallographic relations between precipitates and matrix can be traced back to the original formation of twinned martensite plates within the austenite. Some aspects of the dynamics of the process are discussed on the basis of snap shots and video recordings.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.489
Times cited: 5
DOI: 10.1016/0167-577X(95)00030-5
|
|
|
“On the use of TEM in the characterization of nanocomposites”. Monticelli O, Musina Z, Russo S, Bals S, Materials letters 61, 3446 (2007). http://doi.org/10.1016/j.matlet.2006.11.086
Abstract: Both an organically modified commercial clay of montmorillonite type (MMT) and its nanocomposites, based either on polyamide 6 (PA6) or an epoxy resin, as matrix polymer, have been characterized by transmission electron microscopy (TEM). Sample micrographs, taken at increasing exposure times (t(e)), have shown the gradual disappearance of clay layers, because of an amorphisation of the MMT crystalline structures caused by prolonged sample exposure to electron beam. Indeed, the above phenomenon, which is mostly evident in the case of intercalated nanocomposites, makes the detection of the layered silicate dispersion in the polymer matrix rather difficult and compels to perform TEM measurements using very short exposure times. Moreover, the microscopy accelerating voltage has turned out to affect sample stability; namely, when decreasing the above parameter, the disappearance of clay structure occurs at lower exposure times. (C) 2006 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.572
Times cited: 28
DOI: 10.1016/j.matlet.2006.11.086
|
|
|
“Shape selective growth of single crystalline MnOOH multipods and 1D nanowires by a reductive hydrothermal method”. Mi Y, Zhang X, Yang Z, Li Y, Zhou S, Zhang H, Zhu W, He D, Wang J, Van Tendeloo G, Materials letters 61, 1781 (2007). http://doi.org/10.1016/j.matlet.2006.07.130
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.572
Times cited: 13
DOI: 10.1016/j.matlet.2006.07.130
|
|
|
“A hidden single-stage martensitic transformation from B2 parent phase to B19 ' martensite phase in an aged Ni51Ti49 alloy”. Zeng CY, Cao S, Li YY, Zhao ZX, Yao XY, Ma X, Zhang XP, Materials letters 253, 99 (2019). http://doi.org/10.1016/J.MATLET.2019.06.055
Abstract: The aged Ni-rich NiTi shape memory alloys (SMAs) exhibit the multi-stage martensitic transformation (MMT), which has important influences on functional properties and practical applications of the NiTi SMAs. A hidden single-stage martensitic transformation from B2 parent phase to B19' martensite phase is found in an aged Ni51Ti49 alloy, which happens concurrently with a commonly observed two-stage martensitic transformation B2-R-B19' (R: martensite phase) and actually composes one stage of a multi-stage martensitic transformation (MMT) together with the two-stage one. B2-B19' martensitic transformation occurs in the NiTi matrix containing Ni4Ti3 precipitates with relatively large inter-particle space, while B2-R-B19' transformation takes place in the NiTi matrix with Ni4Ti3 precipitates having relatively small inter-particle space. (C) 2019 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.572
DOI: 10.1016/J.MATLET.2019.06.055
|
|
|
“Identification of nano-width variants in a fully monoclinic martensitic Ni50Ti50 alloy by scanning electron microscope-based transmission Kikuchi diffraction and improved groupoid structure approach”. Zhao ZX, Ma X, Cao S, Li YY, Zeng CY, Wang DX, Yao X, Deng ZJ, Zhang XP, Materials Letters 281, 128624 (2020). http://doi.org/10.1016/J.MATLET.2020.128624
Abstract: Nano-width martensite plates in a fully martensitic Ni50Ti50 alloy are indexed successfully by using the off-axis transmission Kikuchi diffraction in scanning electron microscope (i.e., SEM-based TKD). The data obtained by SEM-TKD are effectively interpreted using an improved approach based on the framework of the theoretical groupoid structure method, where the equivalent variants transformed from the monoclinic variants are introduced to calculate all theoretical axis/angle pairs of rotation, and to formulate a complete list of source martensite to target martensite pairs. Consequently, B19' monoclinic martensite variants in NiTi alloys are identified unambiguously, by using numerical comparison between the experimental and theoretical rotation components, without the reference of retained parent phase. (C) 2020 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3
DOI: 10.1016/J.MATLET.2020.128624
|
|
|
“Formation of carbon nitride nanospheres by ion implantation”. Thomé, T, Colaux JL, Colomer J-F, Bertoni G, Terwagne G, Materials chemistry and physics 103, 290 (2007). http://doi.org/10.1016/j.matchemphys.2007.02.028
Abstract: Carbon nitride nanospheres have been synthesized into copper by simultaneous high fluence (10(18) at. cm(-2)) implantations of C-12 and N-15 ions. The composition of the implanted region has been measured using C-12(d,p(0))C-13 and N-15(d,alpha(0))C-13 nuclear reactions induced by a 1.05 MeV deuteron beam. The C-12 and N-15 depth profiles are very close and the retained doses into copper are relatively high, which indicates that carbon and nitrogen diffusion processes are likely limited during implantation. High resolution transmission electron microscopy (HRTEM) observations and electron diffraction (ED) analyses have been carried out to determine the structure of the nanospheres formed during implantation. Some consist in small hollow amorphous nanocapsules with sizes ranging from 30 to 100 nm. Large gas bubbles with diameters up to 300 mn have also been observed in the copper matrix. Electron energy-loss spectroscopy (EELS) measurements performed on the small nanocapsules indicate that their shells are composed of carbon and nitrogen. (c) 2007 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.084
Times cited: 1
DOI: 10.1016/j.matchemphys.2007.02.028
|
|
|
“Gold clusters on WO3 nanoneedles grown via AACVD : XPS and TEM studies”. Navío C, Vallejos S, Stoycheva T, Llobet E, Correig X, Snyders R, Blackman C, Umek P, Ke X, Van Tendeloo G, Bittencourt C;, Materials chemistry and physics 134, 809 (2012). http://doi.org/10.1016/j.matchemphys.2012.03.073
Abstract: We have prepared tungsten oxide films decorated with gold particles on Si substrates by aerosol assisted chemical vapor deposition (AACVD) and characterized them using scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). SEM shows that the films are composed of needle-like structures and TEM shows that both the needles and the gold particles are crystalline. XPS indicates the presence of oxygen vacancies, i.e. the films are WO3−x, and hence the deposited material is composed of semiconducting nanostructures and that the interaction between the gold particles and the WO3 needles surface is weak. The synthesis of semiconducting tungsten oxide nanostructures decorated with metal particles represents an important step towards the development of sensing devices with optimal properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.084
Times cited: 52
DOI: 10.1016/j.matchemphys.2012.03.073
|
|
|
“Preparation and structural characterization of SnO2 and GeO2 methanol steam reforming thin film model catalysts by (HR)TEM”. Lorenz H, Zhao Q, Turner S, Lebedev OI, Van Tendeloo G, Klötzer B, Rameshan C, Penner S, Materials chemistry and physics 122, 623 (2010). http://doi.org/10.1016/j.matchemphys.2010.03.057
Abstract: Structure, morphology and composition of different tin oxide and germanium oxide thin film catalysts for the methanol steam reforming (MSR) reaction have been studied by a combination of (high-resolution) transmission electron microscopy, selected area electron diffraction, dark-field imaging and electron energy-loss spectroscopy. Deposition of the thin films on NaCl(0 0 1) cleavage faces has been carried out by thermal evaporation of the respective SnO2 and GeO2 powders in varying oxygen partial pressures and at different substrate temperatures. Preparation of tin oxide films in high oxygen pressures (10−1 Pa) exclusively resulted in SnO phases, at and above 473 K substrate temperature epitaxial growth of SnO on NaCl(0 0 1) leads to well-ordered films. For lower oxygen partial pressures (10−3 to 10−2 Pa), mixtures of SnO and β-Sn are obtained. Well-ordered SnO2 films, as verified by electron diffraction patterns and energy-loss spectra, are only obtained after post-oxidation of SnO films at temperatures T ≥ 673 K in 105 Pa O2. Preparation of GeOx films inevitably results in amorphous films with a composition close to GeO2, which cannot be crystallized by annealing treatments in oxygen or hydrogen at temperatures comparable to SnO/SnO2. Similarities and differences to neighbouring oxides relevant for selective MSR in the third group of the periodic system (In2O3 and Ga2O3) are also discussed with the aim of cross-correlation in formation of nanomaterials, and ultimately, also catalytic properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.084
Times cited: 15
DOI: 10.1016/j.matchemphys.2010.03.057
|
|
|
“Gaining new insight into low-temperature aqueous photochemical solution deposited ferroelectric PbTiO3 films”. De Dobbelaere C, Lourdes Calzada M, Bretos I, Jimenez R, Ricote J, Hadermann J, Hardy A, Van Bael MK, Materials chemistry and physics 174, 28 (2016). http://doi.org/10.1016/J.MATCHEMPHYS.2016.02.047
Abstract: The nature of the low-temperature photochemical assisted formation process of ferroelectric lead titanate (PbTiO3) films is studied in the present work. Films are obtained by the deposition of an aqueous solution containing citric acid based (citrato) metal ion complexes with intrinsic UV activity. This UV activity is crucial for the aqueous photochemical solution deposition (aqueous PCSD) route being used. UV irradiation enhances the early decomposition of organics and results in improved electrical properties for the crystalline oxide film, even if the film is crystallized at low temperature. GATR-FTIR shows that UV irradiation promotes the decomposition of organic precursor components, resulting in homogeneous films if applied in the right temperature window during film processing. The organic content, morphology and crystallinity of the irradiated films, achieved at different processing atmospheres and temperatures, is studied and eventually correlated to the functional behavior of the obtained films. This is an important issue, as crystalline films obtained at low temperatures often lack ferroelectric responses. In this work, the film prepared in pure oxygen at the very low temperature of 400 degrees C and after an optimized UV treatment presents a significant remanent polarization value of P-r = 8.8 mu C cm(-2). This value is attributed to the better crystallinity, the larger grain size and the reduced porosity obtained thanks to the early film crystallization effectively achieved through the UV treatment in oxygen. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.084
Times cited: 4
DOI: 10.1016/J.MATCHEMPHYS.2016.02.047
|
|
|
“Microstructure of adiabatic shear bands in Ti6Al4V”. Peirs J, Tirry W, Amin-Ahmadi B, Coghe F, Verleysen P, Rabet L, Schryvers D, Degrieck J, Materials characterization 75, 79 (2013). http://doi.org/10.1016/j.matchar.2012.10.009
Abstract: Microstructural deformation mechanisms in adiabatic shear bands in Ti6Al4V are studied using traditional TEM and selected area diffraction, and more advanced microstructural characterisation techniques such as energy dispersive X-ray spectroscopy, high angle annular dark field STEM and conical dark field TEM. The shear bands under investigation are induced in Ti6Al4V samples by high strain rate compression of cylindrical and hat-shaped specimens in a split Hopkinson pressure bar setup. Samples from experiments interrupted at different levels of deformation are used to study the evolution of the microstructure in and nearby the shear bands. From the early stages of adiabatic shear band formation, TEM revealed strongly elongated equiaxed grains in the shear band. These band-like grains become narrower towards the centre of the band and start to fraction even further along their elongated direction to finally result in a nano-crystalline region in the core. In fully developed shear bands, twins and a needle-like martensite morphology are observed near the shear band.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 56
DOI: 10.1016/j.matchar.2012.10.009
|
|
|
“Quantitative study of particle size distribution in an in-situ grown Al-TiB2 composite by synchrotron X-ray diffraction and electron microscopy”. Tang Y, Chen Z, Borbely A, Ji G, Zhong SY, Schryvers D, Ji V, Wang HW, Materials characterization 102, 131 (2015). http://doi.org/10.1016/j.matchar.2015.03.003
Abstract: Synchrotron X-ray diffraction and transmission electron microscopy (TEM) were applied to quantitatively characterize the average particle size and size distribution of free-standing TiB2 particles and TiB2 particles in an insitu grown Al–TiB2 composite. The detailed evaluations were carried out by X-ray line profile analysis using the restrictedmoment method and multiplewhole profile fitting procedure (MWP). Both numericalmethods indicate that the formed TiB2 particles are well crystallized and free of crystal defects. The average particle size determined from different Bragg reflections by the restricted moment method ranges between 25 and 55 nm, where the smallest particle size is determined using the 110 reflection suggesting the highest lateral-growth velocity of (110) facets. TheMWP method has shown that the in-situ grown TiB2 particles have a very low dislocation density (~1011 m−2) and their size distribution can be described by a log-normal distribution. Good agreement was found between the results obtained from the restricted moment and MWP methods, which was further confirmed by TEM.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 41
DOI: 10.1016/j.matchar.2015.03.003
|
|