“Exsolution of SrO during the Topochemical Conversion of LaSr3CoRuO8to the Oxyhydride LaSr3CoRuO4H4”. Jin L, Batuk M, Kirschner FKK, Lang F, Blundell SJ, Hadermann J, Hayward MA, Inorganic chemistry 58, 14863 (2019). http://doi.org/10.1021/acs.inorgchem.9b02552
Abstract: Reaction of the n = 1 Ruddlesden-Popper oxide LaSr3CoRuO8 with CaH2 yields the oxyhydride phase LaSr3CoRuO4H4 via topochemical anion-exchange. Close inspection of X-ray and neutron powder diffraction data in combination with HAADF-STEM images reveals that nanoparticles of SrO are exsolved from the system during the reaction, with the change in cation stoichiometry accommodated by the inclusion of n > 1 (Co/Ru)nOn+1H2n ‘perovskite’ layers into the Ruddlesden-Popper stacking sequence. This novel pseudo-topochemical process offers a new route for the formation of n > 1 Ruddlesden-Popper structured materials. Magnetization data are consistent with a LaSr3Co1+Ru2+O4H4 (Co1+, d8, S = 1; Ru2+, d6, S = 0) oxidation/spin state combination. Neutron diffraction and μ+SR data show no evidence for long-range magnetic order down to 2 K, suggesting the diamagnetic Ru2+ centers impede the Co-Co magnetic exchange interactions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 1
DOI: 10.1021/acs.inorgchem.9b02552
|
|
|
“Magnetic Ordering in the Layered Cr(II) Oxide Arsenides Sr2CrO2Cr2As2and Ba2CrO2Cr2As2”. Xu X, Jones MA, Cassidy SJ, Manuel P, Orlandi F, Batuk M, Hadermann J, Clarke SJ, Inorganic Chemistry 59, 15898 (2020). http://doi.org/10.1021/acs.inorgchem.0c02415
Abstract: Sr2CrO2Cr2As2 and Ba2CrO2Cr2As2 with Cr2+ ions in CrO2 sheets and in CrAs layers crystallize with the Sr2Mn3Sb2O2 structure (space group I4/mmm, Z = 2) and lattice parameters a = 4.00800(2) Å, c = 18.8214(1) Å (Sr2CrO2Cr2As2) and a = 4.05506(2) Å, c = 20.5637(1) Å (Ba2CrO2Cr2As2) at room temperature. Powder neutron diffraction reveals checkerboard-type antiferromagnetic ordering of the Cr2+ ions in the arsenide layers below TN1Sr, of 600(10) K (Sr2CrO2Cr2As2) and TN1Ba 465(5) K (Ba2CrO2Cr2As2) with the moments initially directed perpendicular to the layers in both compounds. Checkerboard-type antiferromagnetic ordering of the Cr2+ ions in the oxide layer below 230(5) K for Ba2CrO2Cr2As2 occurs with these moments also perpendicular to the layers, consistent with the orientation preferences of d4 moments in the two layers. In contrast, below 330(5) K in Sr2CrO2Cr2As2, the oxide layer Cr2+ moments are initially oriented in the CrO2 plane; but on further cooling, these moments rotate to become perpendicular to the CrO2 planes, while the moments in the arsenide layers rotate by 90° with the moments on the two sublattices remaining orthogonal throughout [behavior recently reported independently by Liu et al. [Liu et al. Phys. Rev. B 2018, 98, 134416]]. In Sr2CrO2Cr2As2, electron diffraction and high resolution powder X-ray diffraction data show no evidence for a structural distortion that would allow the two Cr2+ sublattices to couple, but high resolution neutron powder diffraction data suggest a small incommensurability between the magnetic structure and the crystal structure, which may account for the coupling of the two sublattices and the observed spin reorientation. The saturation values of the Cr2+ moments in the CrO2 layers (3.34(1) μB (for Sr2CrO2Cr2As2) and 3.30(1) μB (for Ba2CrO2Cr2As2)) are larger than those in the CrAs layers (2.68(1) μB for Sr2CrO2Cr2As2 and 2.298(8) μB for Ba2CrO2Cr2As2) reflecting greater covalency in the arsenide layers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
DOI: 10.1021/acs.inorgchem.0c02415
|
|
|
“Ambient and high pressure CuNiSb₂, : metal-ordered and metal-disordered NiAs-type derivative pnictides”. Skaggs CM, Kang C-J, Perez CJ, Hadermann J, Emge TJ, Frank CE, Pak C, Lapidus SH, Walker D, Kotliar G, Kauzlarich SM, Tan X, Greenblatt M, Inorganic Chemistry 59, 14058 (2020). http://doi.org/10.1021/ACS.INORGCHEM.0C01848
Abstract: The mineral Zlatogorite, CuNiSb2, was synthesized in the laboratory for the first time by annealing elements at ambient pressure (CuNiSb2-AP). Rietveld refinement of synchrotron powder X-ray diffraction data indicates that CuNiSb2-AP crystallizes in the NiAs-derived structure (P (3) over bar m1, #164) with Cu and Ni ordering. The structure consists of alternate NiSb6 and CuSb6 octahedral layers via face-sharing. The formation of such structure instead of metal disordered NiAs-type structure (P6(3)/mmc, #194) is validated by the lower energy of the ordered phase by first-principle calculations. Interatomic crystal orbital Hamilton population, electron localization function, and charge density analysis reveal strong Ni-Sb, Cu-Sb, and Cu-Ni bonding and long weak Sb-Sb interactions in CuNiSb2-AP. The magnetic measurement indicates that CuNiSb2-AP is Pauli paramagnetic. First-principle calculations and experimental electrical resistivity measurements reveal that CuNiSb2-AP is a metal. The low Seebeck coefficient and large thermal conductivity suggest that CuNiSb2 is not a potential thermoelectric material. Single crystals were grown by chemical vapor transport. The high pressure sample (CuNiSb2-8 GPa) was prepared by pressing CuNiSb2-AP at 700 degrees C and 8 GPa. However, the structures of single crystal and CuNiSb2-8 GPa are best fit with a disordered metal structure in the P (3) over bar m1 space group, corroborated by transmission electron microscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
DOI: 10.1021/ACS.INORGCHEM.0C01848
|
|
|
“Chemistry, local molybdenum clustering, and electrochemistry in the Li2+xMo1-xO3 solid solutions”. Savina AA, Saiutina VV, Morozov AV, Boev AO, Aksyonov DA, Dejoie C, Batuk M, Bals S, Hadermann J, Abakumov AM, Inorganic chemistry 61, 5637 (2022). http://doi.org/10.1021/ACS.INORGCHEM.2C00420
Abstract: A broad range of cationic nonstoichiometry has been demonstratedfor the Li-rich layered rock-salt-type oxide Li2MoO3, which has generally been considered as a phase with a well-defined chemical composition. Li2+xMo1-xO3(-0.037 <= x <= 0.124) solid solutions were synthesized via hydrogen reduction ofLi2MoO4in the temperature range of 650-1100 degrees C, withxdecreasing with theincrease of the reduction temperature. The solid solutions adopt a monoclinicallydistorted O3-type layered average structure and demonstrate a robust localordering of the Li cations and Mo3triangular clusters within the mixed Li/Mocationic layers. The local structure was scrutinized in detail by electron diffractionand aberration-corrected scanning transmission electron microcopy (STEM),resulting in an ordering model comprising a uniform distribution of the Mo3clusters compatible with local electroneutrality and chemical composition. The geometry of the triangular clusters with their oxygenenvironment (Mo3O13groups) has been directly visualized using differential phase contrast STEM imaging. The established localstructure was used as input for density functional theory (DFT)-based calculations; they support the proposed atomic arrangementand provide a plausible explanation for the staircase galvanostatic charge profiles upon electrochemical Li+extraction fromLi2+xMo1-xO3in Li cells. According to DFT, all electrochemical capacity in Li2+xMo1-xO3solely originates from the cationic Moredox process, which proceeds via oxidation of the Mo3triangular clusters into bent Mo3chains where the electronic capacity of the clusters depends on the initial chemical composition and Mo oxidation state defining the width of the first charge low-voltageplateau. Further oxidation at the high-voltage plateau proceeds through decomposition of the Mo3chains into Mo2dimers and further into individual Mo6+cations
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
Times cited: 3
DOI: 10.1021/ACS.INORGCHEM.2C00420
|
|
|
“Structures and magnetic ordering in layered Cr oxide arsenides Sr₂CrO₂Cr₂OAs₂, and Sr₂CrO₃CrAs”. Sheath BC, Xu X, Manuel P, Hadermann J, Batuk M, O'Sullivan J, Bonilla RS, Clarke SJ, Inorganic chemistry 61, 10 (2022). http://doi.org/10.1021/ACS.INORGCHEM.2C01773
Abstract: Two novel chromium oxide arsenide materials have been synthesized, Sr2CrO2Cr2OAs2 (i.e., Sr2Cr3As2O3) and Sr2CrO3CrAs (i.e., Sr2Cr2AsO3), both of which contain chromium ions in two distinct layers. Sr2CrO2Cr2OAs2 was targeted following electron microscopy measurements on a related phase. It crystallizes in the space group P4/mmm and accommodates distorted CrO4As2 octahedra containing Cr2+ and distorted CrO(2)As(4 )octahedra containing Cr3+. In contrast, Sr2CrO3CrAs incorporates Cr3+ in CrO5 square-pyramidal coordination in [Sr2CrO3](+) layers and Cr2+ ions in CrAs(4 )tetrahedra in [CrAs](-) layers and crystallizes in the space group P4/nmm. Powder neutron diffraction data reveal antiferromagnetic ordering in both compounds. In Sr2CrO3CrAs the Cr2+ moments in the [CrAs](-) layers exhibit long-range ordering, while the Cr3+ moments in the [Sr2CrO3](+) layers only exhibit short-range ordering. However, in Sr2CrO2Cr2OAs2, both the Cr(2+ )moments in the CrO4As2 environments and the Cr3+ moments in the CrO2As4 polyhedra are long-range-ordered below 530(10) K. Above this temperature, only the Cr3+ moments are ordered with a Neel temperature slightly in excess of 600 K. A subtle structural change is evident in Sr2CrO2Cr2OAs2 below the magnetic ordering transitions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
DOI: 10.1021/ACS.INORGCHEM.2C01773
|
|
|
“Impact of anionic ordering on the iron site distribution and valence states in oxyfluoride Sr2FeO3+xF1-x(x=0.08, 0.2) with a layered Perovskite network”. Gamon J, Bassat J-M, Villesuzanne A, Duttine M, Batuk M, Vandemeulebroucke D, Hadermann J, Alassani F, Weill F, Durand E, Demourgues A, Inorganic chemistry 62, 10822 (2023). http://doi.org/10.1021/ACS.INORGCHEM.3C01455
Abstract: Sr2FeO3+x F1-x (x = 0.08, 0.2), an n = 1 Ruddlesden-Popperphase, was synthesized from the oxidationof Sr2FeO3F in air at high temperature followinga fluorine for oxygen substitution and Fe3+ to Fe4+ oxidation. A structural investigation of both compounds was performedusing complementary and high-resolution techniques (Synchrotron X-rayand electron diffraction, Mo''ssbauer spectroscopy, HR-STEM)coupled to DFT calculation. This study reveals that oxidation leadsto a high degree of apical anion disorder coupled to antiphase boundaries. Sr2FeO3F, an oxyfluoride compoundwith an n = 1 Ruddlesden-Popper structure,was identifiedas a potential interesting mixed ionic and electronic conductor (MIEC).The phase can be synthesized under a range of different pO(2) atmospheres, leading to various degrees of fluorinefor oxygen substitution and Fe4+ content. A structuralinvestigation and thorough comparison of both argon- and air-synthesizedcompounds were performed by combining high-resolution X-ray and electrondiffraction, high-resolution scanning transmission electron microscopy,Mo''ssbauer spectroscopy, and DFT calculations. While the argon-synthesizedphase shows a well-behaved O/F ordered structure, this study revealedthat oxidation leads to averaged large-scale anionic disorder on theapical site. In the more oxidized Sr2FeO3.2F0.8 oxyfluoride, containing 20% of Fe4+, two differentFe positions can be identified with a 32%/68% occupancy (P4/nmm space group). This originates due to the presenceof antiphase boundaries between ordered domains within the grains.Relations between site distortion and valence states as well as stabilityof apical anionic sites (O vs F) are discussed. This study paves theway for further studies on both ionic and electronic transport propertiesof Sr2FeO3.2F0.8 and its use in MIEC-baseddevices, such as solid oxide fuel cells.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
DOI: 10.1021/ACS.INORGCHEM.3C01455
|
|
|
“Structural transformation in fluorinated LaACuGaO5 (A=Ca, Sr) brownmillerites”. Hadermann J, Van Tendeloo G, Abakumov AM, Pavlyuk BP, Rozova MG, Antipov EV, International journal of inorganic materials 2, 493 (2000). http://doi.org/10.1016/S1466-6049(00)00072-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 13
DOI: 10.1016/S1466-6049(00)00072-6
|
|
|
“Quantitative analysis of diffuse electron scattering in the lithium-ion battery cathode material Li1.2Ni0.13Mn0.54Co0.13O2”. Poppe R, Vandemeulebroucke D, Neder RB, Hadermann J, IUCrJ 9, 695 (2022). http://doi.org/10.1107/S2052252522007746
Abstract: In contrast to perfectly periodic crystals, materials with short-range order produce diffraction patterns that contain both Bragg reflections and diffuse scattering. To understand the influence of short-range order on material properties, current research focuses increasingly on the analysis of diffuse scattering. This article verifies the possibility to refine the short-range order parameters in submicrometre-sized crystals from diffuse scattering in single-crystal electron diffraction data. The approach was demonstrated on Li<sub>1.2</sub>Ni<sub>0.13</sub>Mn<sub>0.54</sub>Co<sub>0.13</sub>O<sub>2</sub>, which is a state-of-the-art cathode material for lithium-ion batteries. The intensity distribution of the 1D diffuse scattering in the electron diffraction patterns of Li<sub>1.2</sub>Ni<sub>0.13</sub>Mn<sub>0.54</sub>Co<sub>0.13</sub>O<sub>2</sub>depends on the number of stacking faults and twins in the crystal. A model of the disorder in Li<sub>1.2</sub>Ni<sub>0.13</sub>Mn<sub>0.54</sub>Co<sub>0.13</sub>O<sub>2</sub>was developed and both the stacking fault probability and the percentage of the different twins in the crystal were refined using an evolutionary algorithm in<italic>DISCUS</italic>. The approach was applied on reciprocal space sections reconstructed from 3D electron diffraction data since they exhibit less dynamical effects compared with in-zone electron diffraction patterns. A good agreement was achieved between the calculated and the experimental intensity distribution of the diffuse scattering. The short-range order parameters in submicrometre-sized crystals can thus successfully be refined from the diffuse scattering in single-crystal electron diffraction data using an evolutionary algorithm in<italic>DISCUS</italic>.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.9
DOI: 10.1107/S2052252522007746
|
|
|
“Refining short-range order parameters from the three-dimensional diffuse scattering in single-crystal electron diffraction data”. Poppe R, Roth N, Neder RB, Palatinus L, Iversen BB, Hadermann J, IUCrJ 11, 82 (2024). http://doi.org/10.1107/S2052252523010254
Abstract: Our study compares short-range order parameters refined from the diffuse scattering in single-crystal X-ray and single-crystal electron diffraction data. Nb0.84CoSb was chosen as a reference material. The correlations between neighbouring vacancies and the displacements of Sb and Co atoms were refined from the diffuse scattering using a Monte Carlo refinement in DISCUS. The difference between the Sb and Co displacements refined from the diffuse scattering and the Sb and Co displacements refined from the Bragg reflections in single-crystal X-ray diffraction data is 0.012 (7) angstrom for the refinement on diffuse scattering in single-crystal X-ray diffraction data and 0.03 (2) angstrom for the refinement on the diffuse scattering in single-crystal electron diffraction data. As electron diffraction requires much smaller crystals than X-ray diffraction, this opens up the possibility of refining short-range order parameters in many technologically relevant materials for which no crystals large enough for single-crystal X-ray diffraction are available.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.9
DOI: 10.1107/S2052252523010254
|
|
|
“A novel red Ca8.5Pb0.5Eu(PO4)7 phosphor for light emitting diodes application”. Deyneko DV, Morozov VA, Hadermann J, Savon AE, Spassky DA, Stefanovich SY, Belik AA, Lazoryak BI, Journal of alloys and compounds 647, 965 (2015). http://doi.org/10.1016/j.jallcom.2015.06.123
Abstract: Ca9-xPbxEu(PO4)(7) (0 <= x <= 1) solid solutions with a whitlockite-type (or beta-Ca-3(PO4)(2)-type) structure (sp.gr. R3c) were prepared by a standard solid-state method in air. Their luminescent properties under near-ultraviolet (n-UV) light were investigated. Excitation spectra of Ca9-xPbxEu(PO4)(7) showed the strongest absorption at about 395 nm, which matches well with commercially available n-UV-emitting GaN-based LED chips. Emission spectra indicated an intense red emission due to the D-5(0) -> F-7(2) transition of Eu3+, with a maximum in the intensity for Ca8.5Pb0.5Eu(PO4)(7). The emission intensity of Ca8.5Pb0.5Eu(PO4)(7) was about 1.8 times higher than that of a Ca9Eu(PO4)(7) phosphor. We suggest that the introduction of Pb2+ is an efficient approach to enhance luminescence properties of such phosphors. We clarified the influence of the Ca2+/Pb2+ substitution on intensities of three bands for the D-5(0) -> F-7(0) transition in excitation spectra of Ca9-xPbxEu(PO4)(7). In addition, we found a reversible first-order phase transition from R3c to R (3) over barc symmetry by second-harmonic generation in the range from 753 K (x = 1) to 846 K (x = 0). (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 18
DOI: 10.1016/j.jallcom.2015.06.123
|
|
|
“Effect of cation vacancies on the crystal structure and luminescent properties of Ca(0.85-1.5x)Gd(x)Eu(0.1)_(0.05+0.5x)WO(4) (0<x<0.567) scheelite-based red phosphors”. Batuk D, Batuk M, Morozov VA, Meert KW, Smet PF, Poelman D, Abakumov AM, Hadermann J, Journal of alloys and compounds 706, 358 (2017). http://doi.org/10.1016/j.jallcom.2017.02.154
Abstract: The Ca0.85-1.5xGdxEu0.1_0.05-0.5xWO4 (0 < x < 0.567) series of cation-deficient scheelites is investigated to unveil the influence of the cation vacancies on the crystal structure and luminescent properties. The concentration of the vacancies is varied by the heterovalent substitution of Gd3+ for Ca2+, keeping the concentration of the Eu3+ luminescent centers constant in all compounds of the series. The crystal structure of the materials is studied using a combination of transmission electron microscopy and synchrotron X-ray powder diffraction. At low vacancy concentration (x = 0.1, 0.2), cations and cation vacancies are randomly distributed in the structure, and the materials preserve the I41/a symmetry of the parent scheelite structure [x = 0.1: a = 5.25151(1) Å, c = 11.39479(2) Å; x = 0.2: a = 5.25042(1) Å, c = 11.41335(2) Å]. At higher concentration, the cation-vacancy ordering gives rise to incommensurately modulated structures. The x = 0.3 structure has a (3 + 2)D tetragonal symmetry [superspace group I41/a(a,b,0)00(-b,a,0)00, a = 5.24700(1) Å, c = 11.45514(3) Å, q1 = 0.51637(14)a* + 0.80761(13)b*, q2 = -0.80761a* + 0.51637b*]. At x = 0.4, the scheelite basic cell undergoes a monoclinic distortion with the formation of the (3 + 1)D structure [superspace group I2/b(a,b,0)00, a = 5.23757(1) Å, b = 5.25035(1) Å, c = 11.45750(2) Å, g = 90.5120(2) o, q = 0.54206(8)a* + 0.79330(8)b*]. In both structures, the antiphase Ca and (Gd,Eu) occupancy modulations indicate that the ordering between the A cations and vacancies also induces partial Ca/(Gd,Eu) cation ordering. Further increase of the Gd3þ content up to x = 0.567 leads to the formation of a monoclinic phase (space group C2/c) with the Eu2/3WO4-type structure. Despite the difference in the cation-vacancy ordering patterns, all materials in the series demonstrate very similar quantum efficiency and luminescence decay lifetimes. However, the difference in the local coordination environment of the A cation species noticeably affects the line width and the multiplet splitting of the 4f6-4f6 transitions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 2
DOI: 10.1016/j.jallcom.2017.02.154
|
|
|
“Cobalt location in p -CoO x / n -SnO 2 nanocomposites: Correlation with gas sensor performances”. Vladimirova SA, Rumyantseva MN, Filatova DG, Chizhov AS, Khmelevsky NO, Konstantinova EA, Kozlovsky VF, Marchevsky AV, Karakulina OM, Hadermann J, Gaskov AM, Journal Of Alloys And Compounds 721, 249 (2017). http://doi.org/10.1016/j.jallcom.2017.05.332
Abstract: Nanocomposites CoOx/SnO2 based on tin oxide powders with different crystallinity have been prepared by wet chemical synthesis and characterized in detail by ICP-MS, XPS, EPR, XRD, HAADF-STEM imaging and EDX-STEM mapping. It was shown that cobalt is distributed differently between the bulk and surface of SnO2 nanocrystals, which depends on the crystallinity of the SnO2 matrix. The measurements of gas sensor properties have been carried out during exposure to CO (10 ppm), and H2S (2 ppm) in dry air. The decrease of sensor signal toward CO was attributed to high catalytic activity of Co3O4 leading to oxidation of carbon monoxide entirely on the surface of catalyst particles. The formation of a p-CoOx/n-SnO2 heterojunction results in high sensitivity of nanocomposites in H2S detection. The conductance significantly changed in the presence of H2S, which was attributed to the formation of metallic cobalt sulfide and removal of the p – n junction.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 3.133
DOI: 10.1016/j.jallcom.2017.05.332
|
|
|
“Cobalt location in p-CoOxIn-SnO2 nanocomposites : correlation with gas sensor performances”. Vladimirova SA, Rumyantseva MN, Filatova DG, Chizhov AS, Khmelevsky NO, Konstantinova EA, Kozlovsky VF, Marchevsky AV, Karakulina OM, Hadermann J, Gaskov AM, Journal of alloys and compounds 721, 249 (2017). http://doi.org/10.1016/JJALLCOM.2017.05.332
Abstract: Nanocomposites CoOx/SnO2 based on tin oxide powders with different crystallinity have been prepared by wet chemical synthesis and characterized in detail by ICP-MS, XPS, EPR, XRD, HAADF-STEM imaging and EDX-STEM mapping. It was shown that cobalt is distributed differently between the bulk and surface of SnO2 nanocrystals, which depends on the crystallinity of the SnO2 matrix. The measurements of gas sensor properties have been carried out during exposure to CO (10 ppm), and H2S (2 ppm) in dry air. The decrease of sensor signal toward CO was attributed to high catalytic activity of Co3O4 leading to oxidation of carbon monoxide entirely on the surface of catalyst particles. The formation of a p-CoOx/n-SnO2 heterojunction results in high sensitivity of nanocomposites in H2S detection. The conductance significantly changed in the presence of H2S, which was attributed to the formation of metallic cobalt sulfide and removal of the p – n junction. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
DOI: 10.1016/JJALLCOM.2017.05.332
|
|
|
“Spinel nanoparticles on stick-like Freudenbergite nanocomposites as effective smart-removal photocatalysts for the degradation of organic pollutants under visible light”. Ciocarlan R-G, Seftel EM, Gavrila R, Suchea M, Batuk M, Mertens M, Hadermann J, Cool P, Journal Of Alloys And Compounds 820, 153403 (2020). http://doi.org/10.1016/j.jallcom.2019.153403
Abstract: A series of mixed nanocomposite materials was synthetized, containing a Ferrite phase type Zn1-xNixFe2O4 and a Freudenbergite phase type Na2Fe2Ti6O16, where x = 0; 0.2; 0.4; 0.6; 0.8; 1. The choice for this combination is based on the good adsorption properties of Freudenbergite for dye molecules, and the small bandgap energy of Ferrite spinel, allowing activation of the catalysts under visible light irradiation. A two steps synthesis protocol was used to obtain the smart-removal nanocomposites. Firstly, the spinel structure was obtained via the co-precipitation route followed by the addition of the Ti-source and formation of the Freudenbergite system. The role of cations on the formation mechanism and an interesting interchange of cations between spinel and Freudenbergite structures was clarified by a TEM study. Part of the Ti4+ penetrated the spinel structure and, at the same time, part of the Fe3+ formed the Freudenbergite system. The photocatalytic activity was studied under visible light, reaching for the best catalysts a 67% and 40% mineralization degree for methylene blue and rhodamine 6G respectively, after 6 h of irradiation. In the same conditions, the well-known commercial P25 (Degussa) managed to mineralize only 12% and 3% of methylene blue and rhodamine 6G, respectively. Due to the remarkable magnetic properties of Ferrites, a convenient recovery and reuse of the catalysts is possible after the photocatalytic tests. Based on the excellent catalytic performance of the nanocomposites under visible light and their ease of separation out of the solution after the catalytic reaction, the newly developed composite catalysts are considered very effective for wastewater treatment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 6.2
DOI: 10.1016/j.jallcom.2019.153403
|
|
|
“Antiferroelectric properties and site occupations ofR3+ cations in Ca8MgR(PO4)7 luminescent host materials”. Belik AA, Morozov VA, Deyneko DV, Savon AE, Baryshnikova OV, Zhukovskaya ES, Dorbakov NG, Katsuya Y, Tanaka M, Stefanovich SY, Hadermann J, Lazoryak BI, Journal of alloys and compounds 699, 928 (2017). http://doi.org/10.1016/J.JALLCOM.2016.12.288
Abstract: Ca8MgR(PO4)(7) = La, Pr, Nd, Sm-Lu, and Y) phosphates with a beta-Ca-3(PO4)(2) related structure were prepared by a standard solid-state method in air. Second-harmonic generation, differential scanning calorimetry, and dielectric measurements led to the conclusion that all Ca8MgR(PO4)(7) are centrosymmetric and go to another centrosymmetric phase in the course of a first-order antiferroelectric phase transition well above room temperature (RT). High-temperature electron diffraction showed that the symmetry changes from R (3) over barc to R (3) over barm during the phase transition. Structures of Ca8MgR(PO4)(7) at RT were refined by the Rietveld method in centrosymmetric space group R (3) over barc. Mg2+ cations occupy the M5 site; the occupancy of the M1 site by R3+ cations increases monotonically from 0.0389 for R = La to 0.1667 for R = Er-Lu, whereas the occupancy of the M3 site by R3+ cations decreases monotonically from 0.1278 for R = La to 0 for R = Er-Lu. In the case of R = Er-Lu, the M3 site is occupied only by Ca2+ cations. P1O(4) tetrahedra and cations at the M3 site are disordered in the R (3) over barc structure of Ca8MgEu(PO4)(7). Using synchrotron X-ray powder diffraction, we found that annealing conditions do not significantly affect the distribution of Ca2+ and Eu3+ cations between the structure positions of Ca8MgEu(PO4)(7). Luminescent properties of CasMgEu(PO4)(7) powder samples were investigated under near-ultraviolet (n-UV) light. Excitation spectra of CasMgEu(PO4)(7) show the strongest absorption at about 395 nm that matches with commercially available n-UV-emitting GaN-based LED chips. Emission spectra show an intense red emission due to the D-5(0) -> F-7(2) transition of Eu3+. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.JALLCOM.2016.12.288
|
|
|
“Anisotropic magnetism and spin-dependent transport in Co nanoparticle embedded ZnO thin films”. Li DY, Zeng YJ, Pereira LMC, Batuk D, Hadermann J, Zhang YZ, Ye ZZ, Temst K, Vantomme A, Van Bael MJ, Van Haesendonck C;, Journal of applied physics 114, 033909 (2013). http://doi.org/10.1063/1.4815877
Abstract: Oriented Co nanoparticles were obtained by Co ion implantation in crystalline ZnO thin films grown by pulsed laser deposition. Transmission electron microscopy revealed the presence of elliptically shaped Co precipitates with nanometer size, which are embedded in the ZnO thin films, resulting in anisotropic magnetic behavior. The low-temperature resistance of the Co-implanted ZnO thin films follows the Efros-Shklovskii type variable-range-hopping. Large negative magnetoresistance (MR) exceeding 10% is observed in a magnetic field of 1 T at 2.5K and the negative MR survives up to 250K (0.3%). The negative MR reveals hysteresis as well as anisotropy that correlate well with the magnetic properties, clearly demonstrating the presence of spin-dependent transport. (C) 2013 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 10
DOI: 10.1063/1.4815877
|
|
|
“(Ba0.85Ca0.15)(Ti0.9Zr0.1)O3 thin films prepared by PLD : relaxor properties and complex microstructure”. Piorra A, Hrkac V, Wolff N, Zamponi C, Duppel V, Hadermann J, Kienle L, Quandt E, Journal of applied physics 125, 244103 (2019). http://doi.org/10.1063/1.5063428
Abstract: Ferroelectric lead-free thin films of the composition (Ba0.85Ca0.15)(Ti0.9Zr0.1)O-3 (BCZT) were deposited by pulsed laser deposition on Pt/TiO2/SiO2/Si substrates using a ceramic BCZT target prepared by a conventional solid state reaction. The target material itself shows a piezoelectric coefficient of d(33)=640pm/V. The (111) textured thin films possess a thickness of up to 1.1 mu m and exhibit a clamped piezoelectric response f of up to 190pm/V, a dielectric coefficient of (r)=2000 at room temperature, and a pronounced relaxor behavior. As indicated by transmission electron microscopy, the thin films are composed of longitudinal micrometersized columns with similar to 100nm lateral dimension that are separated at twin- and antiphase boundaries. The superposition phenomena according to this columnar growth were simulated based on suitable supercells. The major structural component is described as a tetragonal distorted variant of the perovskite parent type; however, frequently coherently intergrown nanodomains were observed indicating a much more complex structure that is characterized by a 7-layer modulation along the growth direction of the films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
DOI: 10.1063/1.5063428
|
|
|
“Grain-boundary engineering for aging and slow-crack-growth resistant zirconia”. Zhang F, Chevalier J, Olagnon C, Batuk M, Hadermann J, Van Meerbeek B, Vleugels J, Journal of dental research 96, 774 (2017). http://doi.org/10.1177/0022034517698661
Abstract: Ceramic materials are prone to slow crack growth, resulting in strength degradation over time. Although yttria-stabilized zirconia (Y-TZP) ceramics have higher crack resistance than other dental ceramics, their aging susceptibility threatens their long-term performance in aqueous environments such as the oral cavity. Unfortunately, increasing the aging resistance of Y-TZP ceramics normally reduces their crack resistance. Our recently conducted systematic study of doping 3Y-TZP with various trivalent cations revealed that lanthanum oxide (La2O3) and aluminum oxide (Al2O3) have the most potent effect to retard the aging kinetics of 3Y-TZP. In this study, the crack-propagation behavior of La2O3 and Al2O3 co-doped 3Y-TZP ceramics was investigated by double-torsion methods. The grain boundaries were examined using scanning transmission electron microscopy and energy-dispersive spectroscopy (STEM-EDS). Correlating these analytic data with hydrothermal aging studies using different doping systems, a strategy to strongly bind the segregated dopant cations with the oxygen vacancies at the zirconia-grain boundary was found to improve effectively the aging resistance of Y-TZP ceramics without affecting the resistance to crack propagation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.755
Times cited: 3
DOI: 10.1177/0022034517698661
|
|
|
“The (3 + 2)D structure of oxygen deficient LaSrCuO3.52”. Hadermann J, Pérez O, Créon N, Michel C, Hervieu M, Journal of materials chemistry 17, 2344 (2007). http://doi.org/10.1039/b701449j
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1039/b701449j
|
|
|
“Advanced electron microscopy and its possibilities to solve complex structures: application to transition metal oxides”. Van Tendeloo G, Hadermann J, Abakumov AM, Antipov EV, Journal of materials chemistry 19, 2660 (2009). http://doi.org/10.1039/b817914j
Abstract: Design and optimization of materials properties can only be performed through a thorough knowledge of the structure of the compound. In this feature article we illustrate the possibilities of advanced electron microscopy in materials science and solid state chemistry. The different techniques are briefly discussed and several examples are given where the structures of complex oxides, often with a modulated structure, have been solved using electron microscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 9
DOI: 10.1039/b817914j
|
|
|
“Synthesis and charactreization of the new Ln(2)FeMoO(7) (Ln = Y, Dy, Ho) compounds”. Veith GM, Lobanov MV, Emge TJ, Greenblatt M, Croft M, Stowasser F, Hadermann J, Van Tendeloo G, Journal of materials chemistry 14, 1623 (2004). http://doi.org/10.1039/b315028c
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 17
DOI: 10.1039/b315028c
|
|
|
“Synthesis and crystal structure of the Sr2Al1.07Mn0.93O5 brownmillerite”. Hadermann J, Abakumov AM, d' Hondt H, Kalyuzhnaya AS, Rozova MG, Markina MM, Mikheev MG, Tristan N, Klingeler R, Büchner B, Antipov EV, Journal of materials chemistry 17, 692 (2007). http://doi.org/10.1039/b614168d
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 31
DOI: 10.1039/b614168d
|
|
|
“Synthesis and structure determination of ferromagnetic semiconductors LaAMnSnO6(A = Sr, Ba)”. Yang T, Perkisas T, Hadermann J, Croft M, Ignatov A, Van Tendeloo G, Greenblatt M, Journal of materials chemistry 21, 199 (2011). http://doi.org/10.1039/c0jm02614j
Abstract: LaAMnSnO(6) (A = Sr, Ba) have been synthesized by high temperature solid-state reactions under dynamic 1% H(2)/Ar flow. Rietveld refinements on room temperature powder X-ray diffraction data indicate that LaSrMnSnO(6) crystallizes in the GdFeO(3)-structure, with space group Pnma and, combined with transmission electron microscopy, LaBaMnSnO(6) in Imma. Both space groups are common in disordered double-perovskites. The Mn(3+) and Sn(4+) ions whose valence states were confirmed by X-ray absorption spectroscopy, are completely disordered over the B-sites and the BO(6) octahedra are slightly distorted. LaAMnSnO(6) are ferromagnetic semiconductors with a T(C) = 83 K for the Sr- and 66 K for the Ba-compound. The title compounds, together with the previously reported LaCaMnSnO(6) provide an interesting example of progression from Pnma to Imma as the tolerance factor increases. An analysis of the relationship between space group and tolerance factor for the series LaAMnMO(6) (A = Ca, Sr, Ba; M = Sn, Ru) provides a better understanding of the symmetry determination for double perovskites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.1039/c0jm02614j
|
|
|
“La2MnVO6 double perovskite: a structural, magnetic and X-ray absorption investigation”. Mandal TK, Croft M, Hadermann J, Van Tendeloo G, Stephens PW, Greenblatt M, Journal of materials chemistry 19, 4382 (2009). http://doi.org/10.1039/b823513a
Abstract: The synthesis, electron diffraction (ED), synchrotron X-ray and neutron structure, X-ray absorption spectroscopy (XAS) and magnetic property studies of La2MnVO6 double perovskite are described. Analysis of the synchrotron powder X-ray diffraction data for La2MnVO6 indicates a disordered arrangement of Mn and V at the B-site of the perovskite structure. Absence of super-lattice reflections in the ED patterns for La2MnVO6 supports the disordered cation arrangement. Room temperature time-of-flight (TOF) neutron powder diffraction (NPD) data show no evidence of cation ordering, in corroboration with the ED and synchrotron studies (orthorhombic Pnma, a = 5.6097(3), b = 7.8837(5) and c = 5.5668(3) ; 295 K, NPD). A comparison of XAS analyses of La2TVO6 with T = Ni and Co shows T2+ formal oxidation state while the T = Mn material evidences a Mn3+ admixture into a dominantly Mn2+ ground state. V-K edge measurements manifest a mirror image behavior with a V4+ state for T = Ni and Co with a V3+ admixture arising in the T = Mn material. The magnetic susceptibility data for La2MnVO6 show ferromagnetic correlations; the observed effective moment, µeff (5.72 µB) is much smaller than the calculated moment (6.16 µB) based on the spin-only formula for Mn2+ (d5, HS) /V4+ (d1), supportive of the partly oxidized Mn and reduced V scenario (Mn3+/V3+).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 10
DOI: 10.1039/b823513a
|
|
|
“Topotactic redox cycling in SrFeO2.5+&delta, explored by 3D electron diffraction in different gas atmospheres”. Batuk M, Vandemeulebroucke D, Ceretti M, Paulus W, Hadermann J, Journal of materials chemistry A : materials for energy and sustainability (2022). http://doi.org/10.1039/D2TA03247C
Abstract: For oxygen conducting materials applied in solid oxide fuel cells and chemical-looping processes, the understanding of the oxygen diffusion mechanism and the materials’ crystal structure at different stages of the redox reactions is a key parameter to control their performance. In this paper we report the first ever in situ 3D ED experiment in a gas environment and with it uncover the structure evolution of SrFeO2.5 as notably different from that reported from in situ X-ray and in situ neutron powder diffraction studies in gas environments. Using in situ 3D ED on submicron sized single crystals obtained from a high quality monodomain SrFeO2.5 single crystal , we observe the transformation under O2 flow of SrFeO2.5 with an intra- and interlayer ordering of the left and right twisted (FeO4) tetrahedral chains (space group Pcmb) into consecutively SrFeO2.75 with space group Cmmm (at 350°C, 33% O2) and SrFeO3-δ with space group Pm3 ̅m (at 400°C, 100% O2). Upon reduction in H2 flow, the crystals return to the brownmillerite structure with intralayer order, but without regaining the interlayer order of the pristine crystals. Therefore, redox cycling of SrFeO2.5 crystals in O2 and H2 introduces stacking faults into the structure, resulting in an I2/m(0βγ)0s symmetry with variable β.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 11.9
DOI: 10.1039/D2TA03247C
|
|
|
“Can surface reactivity of mixed crystals be predicted from their counterparts? A case study of (Bi1-xSbx)2Te3 topological insulators”. Volykhov AA, Sanchez-Barriga J, Batuk M, Callaert C, Hadermann J, Sirotina AP, Neudachina VS, Belova AI, Vladimirova NV, Tamm ME, Khmelevsky NO, Escudero C, Perez-Dieste V, Knop-Gericke A, Yashina LV, Journal of materials chemistry C : materials for optical and electronic devices 6, 8941 (2018). http://doi.org/10.1039/C8TC02235F
Abstract: The behavior of ternary mixed crystals or solid solutions and its correlation with the properties of their binary constituents is of fundamental interest. Due to their unique potential for application in future information technology, mixed crystals of topological insulators with the spin-locked, gapless states on their surfaces attract huge attention of physicists, chemists and material scientists. (Bi1-xSbx)(2)Te-3 solid solutions are among the best candidates for spintronic applications since the bulk carrier concentration can be tuned by varying x to obtain truly bulk-insulating samples, where the topological surface states largely contribute to the transport and the realization of the surface quantum Hall effect. As this ternary compound will be evidently used in the form of thin-film devices its chemical stability is an important practical issue. Based on the atomic resolution HAADF-TEM and EDX data together with the XPS results obtained both ex situ and in situ, we propose an atomistic picture of the mixed crystal reactivity compared to that of its binary constituents. We find that the surface reactivity is determined by the probability of oxygen attack on the Te-Sb bonds, which is directly proportional to the number of Te atoms bonded to at least one Sb atom. The oxidation mechanism includes formation of an amorphous antimony oxide at the very surface due to Sb diffusion from the first two quintuple layers, electron tunneling from the Fermi level of the crystal to oxygen, oxygen ion diffusion to the crystal, and finally, slow Te oxidation to the +4 oxidation state. The oxide layer thickness is limited by the electron transport, and the overall process resembles the Cabrera-Mott mechanism in metals. These observations are critical not only for current understanding of the chemical reactivity of complex crystals, but also to improve the performance of future spintronic devices based on topological materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.256
Times cited: 3
DOI: 10.1039/C8TC02235F
|
|
|
“MnFe0.5Ru0.5O3 : an above-room-temperature antiferromagnetic semiconductor”. Tan X, McCabe EE, Orlandi F, Manuel P, Batuk M, Hadermann J, Deng Z, Jin C, Nowik I, Herber R, Segre CU, Liu S, Croft M, Kang C-J, Lapidus S, Frank CE, Padmanabhan H, Gopalan V, Wu M, Li M-R, Kotliar G, Walker D, Greenblatt M, Journal of materials chemistry C : materials for optical and electronic devices 7, 509 (2019). http://doi.org/10.1039/C8TC05059G
Abstract: A transition-metal-only MnFe0.5Ru0.5O3 polycrystalline oxide was prepared by a reaction of starting materials MnO, MnO2, Fe2O3, RuO2 at 6 GPa and 1873 K for 30 minutes. A combination of X-ray and neutron powder diffraction refinements indicated that MnFe0.5Ru0.5O3 adopts the corundum (alpha-Fe2O3) structure type with space group R (3) over barc, in which all metal ions are disordered. The centrosymmetric nature of the MnFe0.5Ru0.5O3 structure is corroborated by transmission electron microscopy, lack of optical second harmonic generation, X-ray absorption near edge spectroscopy, and Mossbauer spectroscopy. X-ray absorption near edge spectroscopy of MnFe0.5Ru0.5O3 showed the oxidation states of Mn, Fe, and Ru to be 2+/3+, 3+, and similar to 4+, respectively. Resistivity measurements revealed that MnFe0.5Ru0.5O3 is a semiconductor. Magnetic measurements and magnetic structure refinements indicated that MnFe0.5Ru0.5O3 orders antiferromagnetically around 400 K, with magnetic moments slightly canted away from the c axis. Fe-57 Mossbauer confirmed the magnetic ordering and Fe3+ (S = 5/2) magnetic hyperfine splitting. First principles calculations are provided to understand the electronic structure more thoroughly. A comparison of synthesis and properties of MnFe0.5Ru0.5O3 and related corundum Mn2BB'O-6 derivatives is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.256
Times cited: 1
DOI: 10.1039/C8TC05059G
|
|
|
“Composition and crystal structure of resorbable calcium phosphate thin films”. Tuck L, Sayer M, Mackenzie M, Hadermann J, Dunfield D, Pietak A, Reid JW, Stratilatov AD, Journal of materials science 41, 4273 (2006). http://doi.org/10.1007/s10853-005-5532-5
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 2
DOI: 10.1007/s10853-005-5532-5
|
|
|
“Hydrothermal processing of barium strontium titanate sol-gel composite thin films”. Zelonka K, Sayer M, Freundorfer AP, Hadermann J, Journal of materials science 41, 3885 (2006). http://doi.org/10.1007/s10853-005-5525-4
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 10
DOI: 10.1007/s10853-005-5525-4
|
|
|
“Increasing the solubility limit for tetrahedral aluminium in ZnO:Al nanorods by variation in synthesis parameters”. Kelchtermans A, Adriaensens P, Slocombe D, Kuznetsov VL, Hadermann J, Riskin A, Elen K, Edwards PP, Hardy A, Van Bael MK, Journal of nanomaterials 2015, 1 (2015). http://doi.org/10.1155/2015/546041
Abstract: Nanocrystalline ZnO:Al nanoparticles are suitable building blocks for transparent conductive layers. As the concentration of substitutional tetrahedral Al is an important factor for improving conductivity, here we aim to increase the fraction of substitutional Al. To this end, synthesis parameters of a solvothermal reaction yielding ZnO:Al nanorods were varied. A unique set of complementary techniques was combined to reveal the exact position of the aluminium ions in the ZnO lattice and demonstrated its importance in order to evaluate the potential of ZnO:Al nanocrystals as optimal building blocks for solution deposited transparent conductive oxide layers. Both an extension of the solvothermal reaction time and stirring during solvothermal treatment result in a higher total tetrahedral aluminium content in the ZnO lattice. However, only the longer solvothermal treatment effectively results in an increase of the substitutional positions aimed for.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.871
Times cited: 2
DOI: 10.1155/2015/546041
|
|