“Unravelling the solvent flux behaviour of ceramic nanofiltration and ultrafiltration membranes”. Buekenhoudt A, Bisignano F, De Luca G, Vandezande P, Wouters M, Verhulst K, Journal of membrane science 439, 36 (2013). http://doi.org/10.1016/j.memsci.2013.03.032
Abstract: In order to increase the understanding of the underlying processes in organic solvent nanofiltration (OSN), a study has been undertaken aimed at clarifying the solvent flux behaviour of ceramic nanofiltration and ultrafiltration membranes. Ceramic membranes were chosen for their non-swelling character. Pure water and a variation of 11 different organic solvents were measured on a series of different ceramic membranes with pore-size diameters ranging from 0.9 nm up to 100 nm. To avoid any historical effects, each flux measurement was carried out on a new membrane. The flux results were analysed in a phenomenological way, and a common very simple linear relationship was observed between the product of flux and viscosity of the solvent, and the total Hansen solubility parameter of the solvent. The linear relationship was found for all membranes, independent of the membrane pore size and the membrane material. The slope of the linear relationship was found to depend exponentially on the pore-size diameter and on the polarity of the membrane surface. This result emphasizes the importance of viscosity in the solvent transport, but also of the polarity difference between membrane surface and solvent. The very simple flux model deduced, allows a straightforward prediction of the flux of any solvent or solvent mixture, once the water flux of the membrane is known. At the high pore-size end, the phenomenological model naturally transforms into the viscous-flow or pore-flow behaviour as required. A tentative physical explanation of the model takes into account the presence and extension of a water layer adsorbed to the total pore surface of these membranes. This work also shows that the water flux of a hydrophilic membrane gives a good indication of its molecular weight cut-off (MWCO), and therefore of its separation performance in water. (C)0 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 6.035
Times cited: 55
DOI: 10.1016/j.memsci.2013.03.032
|
“The role of MOFs in Thin-Film Nanocomposite (TFN) membranes”. Van Goethem C, Verbeke R, Pfanmoeller M, Koschine T, Dickmann M, Timpel-Lindner T, Egger W, Bals S, Vankelecom IFJ, Journal of membrane science 563, 938 (2018). http://doi.org/10.1016/J.MEMSCI.2018.06.040
Abstract: Incorporation of MOFs in interfacially polymerized Thin-Film Nanocomposite (TFN) membranes has widely been shown to result in increased membrane performance. However, the exact functioning of these membranes is poorly understood as large variability in permeance increase, filler incorporation and rejection changes can be observed in literature. The synthesis and functioning of TFN membranes (herein exemplified by ZIF-8 filled polyamide (PA) membranes prepared via the EFP method) was investigated via targeted membrane synthesis and thorough characterization via STEM-EDX, XRD and PALS. It is hypothesized that the acid generated during the interfacial polymerization (IP) at least partially degrades the crystalline, acid-sensitive ZIF-8 and that this influences the membrane formation (through so-called secondary effects, i.e. not strictly linked to the pore morphology of the MOF). Nanoscale HAADF-STEM imaging and STEM-EDX Zn-mapping revealed no ZIF-8 particles but rather the presence of randomly shaped regions with elevated Zn-content. Also XRD failed to show the presence of crystalline areas in the composite PA films. As the addition of the acid-quenching TEA led to an increase in the diffraction signal observed in XRD, the role of the acid was confirmed. The separate addition of dissolved Zn2+ to the synthesis of regular TFC membranes showed an increase in permeance while losing some salt retention, similar to observations regularly made for TFN membranes. While the addition of a porous material to a TFC membrane is a straightforward concept, all obtained results indicate that the synthesis and performance of such composite membranes is often more complex than commonly accepted.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.035
Times cited: 84
DOI: 10.1016/J.MEMSCI.2018.06.040
|
“Development, performance and stability of sulfur-free, macrovoid-free BSCF capillaries for high temperature oxygen separation from air”. Buysse C, Kovalevsky A, Snijkers F, Buekenhoudt A, Mullens S, Luyten J, Kretzschmar J, Lenaerts S, Journal of membrane science 372, 239 (2011). http://doi.org/10.1016/J.MEMSCI.2011.02.011
Abstract: Capture and storage of CO2 (CCS) from fossil-fuel power plants is vital in order to counteract a pending anthropogenic global warming. High temperature oxygen transport perovskite membranes can fulfill an important role in the separation of oxygen from air needed in the oxy-fuel technologies for CCS. In this study we present the development, performance and stability of gastight, macrovoid-free and sulfur-free Ba0.5Sr0.5Co0.8Fe0.2O3 − δ (BSCF) mixed conductor capillary membranes prepared by phase-inversion spinning and sintering. A sulfur-free phase-inversion polymer was chosen in order to obtain a phase-pure BSCF crystal phase. Special attention was given to the polymer solution and ceramic spinning suspension in order to avoid macrovoids and achieve gastight membranes. The sulfur-free BSCF capillaries showed an average 4-point bending strength of 64 ± 8 MPa and a maximum oxygen flux of not, vert, similar5.3 Nml/(cm2 min) at 950 °C for an argon sweep flow rate of 125 Nml/min. The comparison of the performance of sulfur-free and sulfur-containing BSCF capillaries with similar dimensions revealed a profound impact of the sulfur contamination on both the oxygen flux and the activation energy of the overall oxygen transport mechanism. Both long-term oxygen permeation at different temperatures and post-operation analysis of a sulfur-free BSCF capillary were performed and discussed.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 6.035
Times cited: 32
DOI: 10.1016/J.MEMSCI.2011.02.011
|
“Fabrication and oxygen permeability of gastight, macrovoid-free Ba0.5Sr0.5Co0.8Fe0.2O3-\delta capillaries for high temperature gas separation”. Buysse C, Kovalevsky A, Snijkers F, Buekenhoudt A, Mullens S, Luyten J, Kretzschmar J, Lenaerts S, Journal of membrane science 359, 86 (2010). http://doi.org/10.1016/J.MEMSCI.2009.10.030
Abstract: Oxygen-permeable perovskites with mixed ionic-electronic conducting properties can play an important role in the separation of oxygen from air which is needed in the oxy-fuel and pre-combustion technologies for the removal and capture of CO2. In this work, gastight, macrovoid-free Ba0.5Sr0.5Co0.8Fe0.2O3−δ (BSCF) capillaries were successfully shaped by a phase-inversion spinning technique, followed by calcination and sintering. It was found that both the rheology of the ceramic suspension and the composition of bore liquid and coagulation bath are key factors for making macrovoid-free green capillaries. Gastight BSCF capillaries were obtained by sintering for 5 h at 1100 °C. The sintered BSCF capillaries contained a significant amount of BaSO4 due to a reaction with the polysulfone binder during calcination. The oxygen permeation flux through the BSCF capillaries was measured and compared to literature data on BSCF disk and hollow fiber membranes measured in similar conditions.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 6.035
Times cited: 38
DOI: 10.1016/J.MEMSCI.2009.10.030
|
“Oxygen exchange-limited transport and surface activation of Ba0.5Sr0.5Co0.8Fe0.2O3-\delta capillary membranes”. Kovalevsky A, Buysse C, Snijkers F, Buekenhoudt A, Luyten J, Kretzschmar J, Lenaerts S, Journal of membrane science 368, 223 (2011). http://doi.org/10.1016/J.MEMSCI.2010.11.034
Abstract: Analysis of oxygen permeation fluxes through Ba0.5Sr0.5Co0.8Fe0.2O3−δ (BSCF) capillary membranes, fabricated via a phase-inversion spinning technique using polysulfone as binder, showed a significant limiting role of the surface-oxygen exchange kinetics. Within the studied temperature and oxygen partial pressure ranges, the activation of core and shell sides of the BSCF capillary with praseodymium oxide (PrOx) resulted in an increase in permeation rate of about 300%. At 11231223 K the activated BSCF membranes demonstrate almost 3-times lower activation energies for the overall oxygen transport (not, vert, similar35 kJ/mol) than the non-activated capillaries, indicating that the mechanism of oxygen transport through the activated capillaries becomes significantly controlled by bulk diffusion limitations, allowing further improvement of the overall performance by decreasing the wall thickness. XRD, EDS and EPMA studies revealed the formation of (Pr,Ba,Sr)(Co,Fe)O3−δ perovskite-type oxides on the surface of the PrOx-modified membranes, which may be responsible for the drastic increase in oxygen exchange rate. At T > 1123 K both non-activated and activated Ba0.5Sr0.5Co0.8Fe0.2O3−δ membranes demonstrate stable performance with time, while at 1073 K only a small initial decrease in permeation was observed.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 6.035
Times cited: 21
DOI: 10.1016/J.MEMSCI.2010.11.034
|