Abstract: In situ HREM irradiation of (110) FZ-Si crystals covered with thin Si3N4 films was carried out in a JEOL-4000EX microscope, operated at 400 keV at room temperature. It is found that clustering of vacancies on (113) planes is realised in a Si layer close to the Si-Si3N4 interface at the initial stage of irradiation. Further aggregation of self-interstitials inside vacancy clusters is considered as an alternative way of point defect recombination in extended shape, to be accomplished with the formation of the extended defects of interstitial type upon interstitial supersaturation.

Abstract: Rutherford backscattering and channeling spectrometry (RBS), photoluminescence (PL) spectroscopy and transmission electron microscopy (TEM) have been used to investigate macroscopic and microscopic segregation in MOCVD grown InGaN layers. The PL peak energy and In content (measured by RES) were mapped at a large number of distinct points on the samples. An indium concentration of 40%, the highest measured in this work, corresponds to a PL peak of 710 nn strongly suggesting that the light-emitting regions of the sample me very indium-rich compared to the average measured by RES. Cross-sectional TEM observations show distinctive layering of the InGaN films. The TEM study further reveals that these layers consist of amorphous pyramidal contrast features with sizes of order 10 nm The composition of these specific contrast features is shown to be In-rich compared to the nitride matrix.

Abstract: Defects in AgG tabular crystals with {111} surfaces are characterised by transmission electron microscopy (TEM) and their influence on the growth process is discussed. In the tabular crystals, twins parallel to the tabular face as well as dislocations along different directions are observed. The twins induce the tabular growth, while the dislocations do not influence the morphology. In 10 to 30% of the crystals that have been characterised, thickness growth is observed and it is shown that in all cases twins on other planes than the tabular ones are present. Two configurations occur more frequently and are analysed in detail. For the first group, twins parallel to the tabular face as well as a microtwin along a non-parallel {111} plane and ending inside the crystal are present. In the crystals of the second group only one extra non-parallel twin occurs giving rise to a bicrystal built up by a tetrahedral shaped part and a flat triangular or trapezoidal part. More complex twin configurations give rise to various, less characteristic morphologies.

Abstract: Materials with low dielectric constant ("low-k'') in combination with Cu metallization are replacing the oxide based dielectrics with Al metallization in future generations of micro-electronic devices. In this work, a carbon doped oxide low-k dielectric material is studied after different kinds of etch/strip steps in single damascene Cu. filled line structures. Interline capacitance measurements indicate a dependence of the dielectric constant on the strip conditions. EFTEM is used to study the composition of the dielectric material and the modification of the low-k material at the sidewall of the etched structures for the various treatment conditions.