“Transport, magnetic, and structural properties of La0.7Ce0.3MnO3 thin films: evidence for hole-doping”. Werner R, Raisch C, Leca V, Ion V, Bals S, Van Tendeloo G, Chasse T, Kleiner R, Koelle D, Physical review : B : solid state 79, 054416 (2009). http://doi.org/10.1103/PhysRevB.79.054416
Abstract: Cerium-doped manganite thin films were grown epitaxially by pulsed laser deposition at 720 °C and oxygen pressure pO2=125 Pa and were subjected to different annealing steps. According to x-ray diffraction (XRD) data, the formation of CeO2 as a secondary phase could be avoided for pO28 Pa. However, transmission electron microscopy shows the presence of CeO2 nanoclusters even in those films which appear to be single phase in XRD. With O2 annealing, the metal-to-insulator transition temperature increases, while the saturation magnetization decreases and stays well below the theoretical value for electron-doped La0.7Ce0.3MnO3 with mixed Mn3+/Mn2+ valences. The same trend is observed with decreasing film thickness from 100 to 20 nm, indicating a higher oxygen content for thinner films. Hall measurements on a film which shows a metal-to-insulator transition clearly reveal holes as dominating charge carriers. Combining data from x-ray photoemission spectroscopy, for determination of the oxygen content, and x-ray absorption spectroscopy (XAS), for determination of the hole concentration and cation valences, we find that with increasing oxygen content the hole concentration increases and Mn valences are shifted from 2+ to 4+. The dominating Mn valences in the films are Mn3+ and Mn4+, and only a small amount of Mn2+ ions can be observed by XAS. Mn2+ and Ce4+ XAS signals obtained in surface-sensitive total electron yield mode are strongly reduced in the bulk-sensitive fluorescence mode, which indicates hole-doping in the bulk for those films which do show a metal-to-insulator transition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 25
DOI: 10.1103/PhysRevB.79.054416
|
“Direct room-temperature synthesis of methyl-functionalized Ti-MCM-41 nanoparticles and their catalytic performance in epoxidation”. Lin K, Pescarmona PP, Houthoofd K, Liang D, Van Tendeloo G, Jacobs PA, Journal of catalysis 263, 75 (2009). http://doi.org/10.1016/j.jcat.2009.01.013
Abstract: Methyl-functionalized Ti-MCM-41 nanoparticles with a size of 80 to 160 nm (Me-Ti-MCM-41 NP) were directly prepared via a dilute solution route by the co-condensation of tetraethoxysilane and methylalkoxysilanes in sodium hydroxide medium at room temperature. The characterization results showed the existence of ordered hexagonal mesoporous structure and tetrahedral Ti species in the nanoparticles. In the epoxidation of cyclohexene with tert-butyl hydroperoxide and aqueous H2O2, Me-Ti-MCM-41 NP samples displayed higher turnover frequencies (TOFs) for cyclohexene and initial reaction rates compared to Ti-MCM-41 and methyl-functionalized Ti-MCM-41 with normal particle size and to non-functionalized Ti-MCM-41 nanoparticles. Simultaneously, a higher selectivity for cyclohexene epoxide was observed in the case of aqueous H2O2, suggesting that the hydrolysis of cyclohexene epoxide with water is reduced on Me-Ti-MCM-41 NP samples. The improved catalytic behavior of Me-Ti-MCM-41 NP is discussed both in terms of the nanosize and methylation of the surface of the catalyst particles. The regeneration of Me-Ti-MCM-41 NP with tert-butyl hydroperoxide solution was evaluated via washing and calcination approaches.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 89
DOI: 10.1016/j.jcat.2009.01.013
|
“A new mixed-valence ferrite with a cubic structure, YBaFe4O7: spin-glass-like behavior”. Caignaert V, Abakumov AM, Pelloquin D, Pralong V, Maignan A, Van Tendeloo G, Raveau B, Chemistry of materials 21, 1116 (2009). http://doi.org/10.1021/cm803312f
Abstract: A new mixed-valence ferrite, YBaFe4O7, has been synthesized. Its unique cubic structure, with a = 8.9595(2) Å, is closely related to that of the hexagonal 114 oxides YBaCo4O7 and CaBaFe4O7. It consists of corner-sharing FeO4 tetrahedra, forming triangular and kagome layers parallel to (111)C. In fact, the YBaFe4O7 and CaBaFe4O7 structures can be described as two different ccc and chch close packings of [BaO3]∞ and [O4]∞ layers, respectively, whose tetrahedral cavities are occupied by Fe2+/Fe3+ cations. The local structure of YBaFe4O7 is characterized by a large amount of stacking faults originating from the presence of hexagonal layers in the ccc cubic close-packed YBaFe4O7 structure. In this way, they belong to the large family of spinels and hexagonal ferrites studied for their magnetic properties. Differently from all the ferrites and especially from CaBaFe4O7, which are ferrimagnetic, YBaFe4O7 is an insulating spin glass with Tg = 50 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 39
DOI: 10.1021/cm803312f
|
“Spectroscopy and defect identification for fluorinated carbon nanotubes”. Bittencourt C, van Lier G, Ke X, Suarez-Martinez I, Felten A, Ghijsen J, Van Tendeloo G, Ewels CO, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 920 (2009). http://doi.org/10.1002/cphc.200800851
Abstract: Multi-wall carbon nanotubes (MWCNTs) were exposed to a CF4 radio-frequency (rf) plasma. High-resolution photoelectron spectroscopy shows that the treatment effectively grafts fluorine atoms onto the MWCNTs, altering the valence electronic states. Fluorine surface concentration can be tuned by varying the exposure time. Evaporation of gold onto MWCNTs is used to mark active site formation. High-resolution transmission electron microscopy coupled with density functional theory (DFT) modelling is used to characterise the surface defects formed, indicating that the plasma treatment does not etch the tube surface. We suggest that this combination of theory and microscopy of thermally evaporated gold atoms onto the CNT surface may be a powerful approach to characterise both surface defect density as well as defect type.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 14
DOI: 10.1002/cphc.200800851
|
“Quantitative three-dimensional modeling of zeotile through discrete electron tomography”. Bals S, Batenburg KJ, Liang D, Lebedev O, Van Tendeloo G, Aerts A, Martens JA, Kirschhock CE, Journal of the American Chemical Society 131, 4769 (2009). http://doi.org/10.1021/ja8089125
Abstract: Discrete electron tomography is a new approach for three-dimensional reconstruction of nanoscale objects. The technique exploits prior knowledge of the object to be reconstructed, which results in an improvement of the quality of the reconstructions. Through the combination of conventional transmission electron microscopy and discrete electron tomography with a model-based approach, quantitative structure determination becomes possible. In the present work, this approach is used to unravel the building scheme of Zeotile-4, a silica material with two levels of structural order. The layer sequence of slab-shaped building units could be identified. Successive layers were found to be related by a rotation of 120°, resulting in a hexagonal space group. The Zeotile-4 material is a demonstration of the concept of successive structuring of silica at two levels. At the first level, the colloid chemical properties of Silicalite-1 precursors are exploited to create building units with a slablike geometry. At the second level, the slablike units are tiled using a triblock copolymer to serve as a mesoscale structuring agent.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 13.858
Times cited: 58
DOI: 10.1021/ja8089125
|
“Rapid microwave-assisted synthesis of benzene bridged periodic mesoporous organosilicas”. Smeulders G, Meynen V, van Baelen G, Mertens M, Lebedev OI, Van Tendeloo G, Maes BUW, Cool P, Journal of materials chemistry 19, 3042 (2009). http://doi.org/10.1039/b820792e
Abstract: Following extended use in organic chemistry, microwave-assisted synthesis is gaining more importance in the field of inorganic chemistry, especially for the synthesis of nanoporous materials. It offers some major advantages such as a significant shortening of the synthesis time and an improved promotion of nucleation. In the research here reported, microwave technology is applied for the synthesis of benzene bridged PMOs (periodic mesoporous organosilicas). PMOs are one of the latest innovations in the field of hybrid ordered mesoporous materials and have attracted much attention because of their feasibility in electronics, catalysis, separation and sorption applications. The different synthesis steps (stirring, aging and extraction) of the classical PMO synthesis are replaced by microwave-assisted synthesis steps. The characteristics of the as-synthesized materials are evaluated by X-ray diffraction, N2-sorption, thermogravimetric analysis, scanning- and transmission electron microscopy. The microwave-assisted synthesis drastically reduces the synthesis time by more than 40 hours without any loss in structural properties, such as mesoscale and molecular ordering. The porosity of the PMO materials has even been improved by more than 25%. Moreover, the number of handling/transfer steps and amounts of chemicals and waste are drastically reduced. The study also shows that there is a clear time (1 to 3 hours) and temperature frame (373 K to 403 K) wherein synthesis of benzene bridged PMO is optimal. In conclusion, the microwave-assisted synthesis pathway allows an improved material to be obtained in a more economical way i.e. a much shorter time with fewer chemicals and less waste.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Times cited: 20
DOI: 10.1039/b820792e
|
“The benefits of statistical parameter estimation theory for quantitative interpretation of electron microscopy data”. Van Aert S, Bals S, Chang LY, den Dekker AJ, Kirkland AI, Van Dyck D, Van Tendeloo G Springer, Berlin, page 97 (2008).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT); Vision lab
DOI: 10.1007/978-3-540-85156-1_49
|
“Electrical nonlinearity in colossal magnetoresistance manganite films: relevance of correlated polarons”. Moshnyaga V, Gehrke K, Sudheendra L, Belenchuk A, Raabe S, Shapoval O, Verbeeck J, Van Tendeloo G, Samwer K, Physical review : B : solid state 79, 134413 (2009). http://doi.org/10.1103/PhysRevB.79.134413
Abstract: The metal-insulator (MI) transition in epitaxial thin films of La0.75Ca0.25MnO3 (LCMO) is accompanied by the appearance of an intrinsic electrical nonlinearity. The latter, probed by electrical third harmonic voltage, U3, or resistance, R3=dU3/dJ, is drastically enhanced in the vicinity of the MI transition, TMI=267 K. Applied magnetic field, B=5 T, suppresses the nonlinearity, resulting in a huge nonlinear CMR3(TMI)~105%. R3 shows a peculiar low-frequency (1 kHz) dependence, R3~(-0)n, with exponent, n, changing across the MI transition from n~1,52 for TTMI to n=1 (T<TMI). The observed electrical nonlinearity in LCMO reflects the behavior of correlated polarons, the number of which dramatically enhances in the vicinity of TMI. We argued that correlated polarons, considered as electric-elastic quadrupoles, provide a nonlinear (quadratic) coupling to the electric field, yielding a third harmonic electric nonlinearity in LCMO. The reference film of La0.7Sr0.3MnO3 (LSMO), a prototypic double exchange system with second-order phase transition, is characterized as a linear metallic material in the whole range of temperatures (T=10400 K), magnetic fields (B=05 T), and frequencies (=11000 Hz).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 28
DOI: 10.1103/PhysRevB.79.134413
|
“Assisted spray pyrolysis production and characterisation of ZnO nanoparticles with narrow size distribution”. Turner S, Tavernier SMF, Huyberechts G, Bals S, Batenburg KJ, Van Tendeloo G, Journal of nanoparticle research 12, 615 (2010). http://doi.org/10.1007/s11051-009-9630-1
Abstract: Nano-sized ZnO particles with a narrow size distribution and high crystallinity were prepared from aqueous solutions with high concentrations of Zn2+ containing salts and citric acid in a conventional spray pyrolysis setup. Structure, morphology and size of the produced material were compared to ZnO material produced by simple spray pyrolysis of zinc nitrates in the same experimental setup. Using transmission electron microscopy and electron tomography it has been shown that citric acid-assisted spray pyrolysed material is made up of micron sized secondary particles comprising a shell of lightly agglomerated, monocrystalline primary ZnO nanoparticles with sizes in the 2030 nm range, separable by a simple ultrasonic treatment step.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.02
Times cited: 27
DOI: 10.1007/s11051-009-9630-1
|
“Multiwalled carbon nanotubes functionalized with 7-octenyltrichlorosilane and n-octyltrichlorosilane: dispersion in Sylgard®184 silicone and Youngs modulus”. Vast L, Carpentier L, Lallemand F, Colomer J-F, Van Tendeloo G, Fonseca A, Nagy JB, Mekhalif Z, Delhalle J, Journal of materials science 44, 3476 (2009). http://doi.org/10.1007/s10853-009-3464-1
Abstract: Sylgard®184/multiwalled carbon nanotube (MWNT) composites have been prepared by in situ polymerization using purified and functionalized multiwalled carbon nanotubes (f-MWNTs) as fillers. Surface modification of the MWNTs has been carried out by silanization with 7-octenyltrichlorosilane (7OTCS) and n-octyltrichlorosilane (nOTCS). The modification and dispersion of the carbon nanotubes in composites were characterized by X-ray photoelectron spectroscopy (XPS), transmission electron spectroscopy (TEM), and high-resolution transmission electron spectroscopy (HRTEM). Youngs modulus results were derived from indentation testing. It is shown that the terminal-vinyl group of 7OTCS molecules plays an essential role for both the dispersion of the f-MWNTs in the composite and its mechanical properties. At loading as low as 0.2 wt%, the Youngs modulus is shown to increase up to 50%. This is interpreted as resulting from a combination of the good compatibility in the forming silicone matrix of the MWNTs coated with a siloxane network, on the one hand, and the covalent links created between the terminal-vinyl groups and the host matrix in formation, on the other hand.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 16
DOI: 10.1007/s10853-009-3464-1
|
“Rational synthesis of a nanocrystalline calcium phosphate cement exhibiting rapid conversion to hydroxyapatite”. Neira IS, Kolen'ko YV, Lebedev OI, Van Tendeloo G, Gupta HS, Matsushita N, Yoshimura M, Guitian F, Materials science and engineering: part C: biomimetic materials 29, 2124 (2009). http://doi.org/10.1016/j.msec.2009.04.011
Abstract: The rational synthesis, comprehensive characterization, and mechanical and micromechanical properties of a calcium phosphate cement are presented. Hydroxyapatite cement biomaterial was synthesized from reactive sub-micrometer-sized dicalcium phosphate dihydrate and tetracalcium phosphate via a dissolution-precipitation reaction using water as the liquid phase. As a result nanostructured, Ca-deficient and carbonated B-type hydroxyapatite is formed. The cement shows good processibility, sets in 22 ± 2 min and entirely transforms to the end product after 6 h of setting reaction, one of the highest conversion rates among previously reported for calcium phosphate cements based on dicalcium and tetracalcium phosphates. The combination of all elucidated physical-chemical traits leads to an essential bioactivity and biocompatibility of the cement, as revealed by in vitro acellular simulated body fluid and cell culture studies. The compressive strength of the produced cement biomaterial was established to be 25 ± 3 MPa. Furthermore, nanoindentation tests were performed directly on the cement to probe its local elasticity and plasticity at sub-micrometer/micrometer level. The measured elastic modulus and hardness were established to be Es = 23 ± 3.5 and H = 0.7 ± 0.2 GPa, respectively. These values are in close agreement with those reported in literature for trabecular and cortical bones, reflecting good elastic and plastic coherence between synthesized cement biomaterial and human bones.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.164
Times cited: 18
DOI: 10.1016/j.msec.2009.04.011
|
“La2MnVO6 double perovskite: a structural, magnetic and X-ray absorption investigation”. Mandal TK, Croft M, Hadermann J, Van Tendeloo G, Stephens PW, Greenblatt M, Journal of materials chemistry 19, 4382 (2009). http://doi.org/10.1039/b823513a
Abstract: The synthesis, electron diffraction (ED), synchrotron X-ray and neutron structure, X-ray absorption spectroscopy (XAS) and magnetic property studies of La2MnVO6 double perovskite are described. Analysis of the synchrotron powder X-ray diffraction data for La2MnVO6 indicates a disordered arrangement of Mn and V at the B-site of the perovskite structure. Absence of super-lattice reflections in the ED patterns for La2MnVO6 supports the disordered cation arrangement. Room temperature time-of-flight (TOF) neutron powder diffraction (NPD) data show no evidence of cation ordering, in corroboration with the ED and synchrotron studies (orthorhombic Pnma, a = 5.6097(3), b = 7.8837(5) and c = 5.5668(3) ; 295 K, NPD). A comparison of XAS analyses of La2TVO6 with T = Ni and Co shows T2+ formal oxidation state while the T = Mn material evidences a Mn3+ admixture into a dominantly Mn2+ ground state. V-K edge measurements manifest a mirror image behavior with a V4+ state for T = Ni and Co with a V3+ admixture arising in the T = Mn material. The magnetic susceptibility data for La2MnVO6 show ferromagnetic correlations; the observed effective moment, µeff (5.72 µB) is much smaller than the calculated moment (6.16 µB) based on the spin-only formula for Mn2+ (d5, HS) /V4+ (d1), supportive of the partly oxidized Mn and reduced V scenario (Mn3+/V3+).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 10
DOI: 10.1039/b823513a
|
“Addition of yttrium into HfO2 films: microstructure and electrical properties”. Dubourdieu C, Rauwel E, Roussel H, Ducroquet F, Hollaender B, Rossell M, Van Tendeloo G, Lhostis S, Rushworth S, Journal of vacuum science and technology: A: vacuum surfaces and films 27, 503 (2009). http://doi.org/10.1116/1.3106627
Abstract: The cubic phase of HfO2 was stabilized by addition of yttrium in thin films grown on Si/SiO2 by metal-organic chemical vapor deposition. The cubic phase was obtained for contents of 6.5 at. % Y or higher at a temperature as low as 470 °C. The complete compositional range (from 1.5 to 99.5 at. % Y) was investigated. The crystalline structure of HfO2 was determined from x-ray diffraction, electron diffraction, and attenuated total-reflection infrared spectroscopy. For cubic films, the continuous increase in the lattice parameter indicates the formation of a solid-solution HfO2Y2O3. As shown by x-ray photoelectron spectroscopy, yttrium silicate is formed at the interface with silicon; the interfacial layer thickness increases with increasing yttrium content and increasing film thickness. The dependence of the intrinsic relative permittivity r as a function of Y content was determined. It exhibits a maximum of ~30 for ~8.8 at. % Y. The cubic phase is stable upon postdeposition high-temperature annealing at 900 °C under NH3.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.374
Times cited: 29
DOI: 10.1116/1.3106627
|
“Adsorption of sulfur onto a surface of silver nanoparticles stabilized with sago starch biopolymer”. Djoković, V, Krsmanović, R, Božanić, DK, McPherson M, Van Tendeloo G, Nair PS, Georges MK, Radhakrishnan T, Colloids and surfaces: B : biointerfaces 73, 30 (2009). http://doi.org/10.1016/j.colsurfb.2009.04.022
Abstract: Adsorption of sulfide ions onto a surface of starch capped silver nanoparticles upon addition of thioacetamide was investigated. UVvis absorption spectroscopy revealed that the adsorption of the sulfide ion on the surface of the silver nanoparticles induced damping as well as blue shift of the silver surface plasmon resonance band. Further increase in thioacetamide concentration led to shift of the resonance band toward higher wavelengths indicating the formation of the continuous Ag2S layer on the silver surface. Thus fabricated nanoparticles were investigated using electron microscopy techniques (TEM, HRTEM, and HAADF-STEM) and X-ray photoelectron spectroscopy (XPS), which confirmed their coreshell structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.887
Times cited: 41
DOI: 10.1016/j.colsurfb.2009.04.022
|
“CVD of copper oxides from a \beta-diketonate diamine precursor: tailoring the nano-organization”. Barreca D, Gasparotto A, Maccato C, Tondello E, Lebedev OI, Van Tendeloo G, Crystal growth &, design 9, 2470 (2009). http://doi.org/10.1021/cg801378x
Abstract: A copper(II) hexafluoroacetylacetonate (1,1,1,5,5,5-hexafluoro-2,4-pentanedionate, hfa) adduct with N,N,N¡ä,N¡ä-tetramethylethylenediamine (TMEDA) [Cu(hfa)2¡¤TMEDA] is used for the first time as precursor for the chemical vapor deposition (CVD) of copper oxide nanosystems. The syntheses are carried out under both O2 and O2+H2O reaction atmospheres on Si(100) substrates, at temperatures ranging between 250 and 550 ¡ãC. Subsequently, the interrelations between the preparative conditions and the system composition, nanostructure, and morphology are elucidated by means of complementary analytical techniques [Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron and X-ray excited auger electron spectroscopies (XPS and XE-AES), glancing incidence X-ray diffraction (GIXRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM)]. The obtained data revealed a gradual transformation from Cu2O, to Cu2O + CuO, to CuO nanosystems upon increasing the deposition temperature from 250 to 550 ¡ãC under both growth atmospheres. Such a phenomenon was accompanied by a progressive morphological evolution from continuous films to 1D hyperbranched nanostructures. Water vapor introduction in the deposition environment enabled to lower the deposition temperature and resulted in a higher aggregate interconnection, attributed to a higher density of nucleation centers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 60
DOI: 10.1021/cg801378x
|
“Determination of size, morphology, and nitrogen impurity location in treated detonation nanodiamond by transmission electron microscopy”. Turner S, Lebedev OI, Shenderova O, Vlasov II, Verbeeck J, Van Tendeloo G, Advanced functional materials 19, 2116 (2009). http://doi.org/10.1002/adfm.200801872
Abstract: Size, morphology, and nitrogen impurity location, all of which are all thought to be related to the luminescent properties of detonation nanodiamonds, are determined in several detonation nanodiamond samples using a combination of transmission electron microscopy techniques. Results obtained from annealed and cleaned detonation nanodiamond samples are compared to results from conventionally purified detonation nanodiamond. Detailed electron energy loss spectroscopy combined with model-based quantification provides direct evidence for the sp3 like embedding of nitrogen impurities into the diamond cores of all the studied nanodiamond samples. Simultaneously, the structure and morphology of the cleaned detonation nanodiamond particles are studied using high resolution transmission electron microscopy. The results show that the size and morphology of detonation nanodiamonds can be modified by temperature treatment and that by applying a special cleaning procedure after temperature treatment, nanodiamond particles with clean facets almost free from sp2 carbon can be prepared. These clean facets are clear evidence that nanodiamond cores are not necessarily in coexistence with a graphitic shell of non-diamond carbon.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 100
DOI: 10.1002/adfm.200801872
|
“The remarkable and intriguing resistance to oxidation of 2D ordered hcp Co nanocrystals: a new intrinsic property”. Lisiecki I, Turner S, Bals S, Pileni MP, Van Tendeloo G, Chemistry of materials 21, 2335 (2009). http://doi.org/10.1021/cm900284u
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 28
DOI: 10.1021/cm900284u
|
“The role of oxygen at the interface between titanium and carbon nanotubes”. Felten A, Suarez-Martinez I, Ke X, Van Tendeloo G, Ghijsen J, Pireaux J-J, Drube W, Bittencourt C, Ewels CP, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 1799 (2009). http://doi.org/10.1002/cphc.200900193
Abstract: We study the interface between carbon nanotubes (CNTs) and surface-deposited titanium using electron microscopy and photoemission spectroscopy, supported by density functional calculations. Charge transfer from the Ti atoms to the nanotube and carbide formation is observed at the interface which indicates strong interaction. Nevertheless, the presence of oxygen between the Ti and the CNTs significantly weakens the Ti-CNT interaction. Ti atoms at the surface will preferentially bond to oxygenated sites. Potential sources of oxygen impurities are examined, namely oxygen from any residual atmosphere and pre-existing oxygen impurities on the nanotube surface, which we enhance through oxygen plasma surface pre-treatment. Variation in literature data concerning Ohmic contacts between Ti and carbon nanotubes is explained via sample pre-treatment and differing vacuum levels, and we suggest improved treatment routes for reliable Schottky barrier-free Ti-nanotube contact formation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 38
DOI: 10.1002/cphc.200900193
|
“Quantitative atomic resolution mapping using high-angle annular dark field scanning transmission electron microscopy”. Van Aert S, Verbeeck J, Erni R, Bals S, Luysberg M, van Dyck D, Van Tendeloo G, Ultramicroscopy 109, 1236 (2009). http://doi.org/10.1016/j.ultramic.2009.05.010
Abstract: A model-based method is proposed to relatively quantify the chemical composition of atomic columns using high angle annular dark field (HAADF) scanning transmission electron microscopy (STEM) images. The method is based on a quantification of the total intensity of the scattered electrons for the individual atomic columns using statistical parameter estimation theory. In order to apply this theory, a model is required describing the image contrast of the HAADF STEM images. Therefore, a simple, effective incoherent model has been assumed which takes the probe intensity profile into account. The scattered intensities can then be estimated by fitting this model to an experimental HAADF STEM image. These estimates are used as a performance measure to distinguish between different atomic column types and to identify the nature of unknown columns with good accuracy and precision using statistical hypothesis testing. The reliability of the method is supported by means of simulated HAADF STEM images as well as a combination of experimental images and electron energy-loss spectra. It is experimentally shown that statistically meaningful information on the composition of individual columns can be obtained even if the difference in averaged atomic number Z is only 3. Using this method, quantitative mapping at atomic resolution using HAADF STEM images only has become possible without the need of simultaneously recorded electron energy loss spectra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 166
DOI: 10.1016/j.ultramic.2009.05.010
|
“Effects of nanocracks on the magnetic and electrical properties of La0.8Sr0.2MnO3 single crystals”. Dominiczak M, Ruyter A, Limelette P, Monot-Laffez I, Giovannelli F, Rossell MD, Van Tendeloo G, Solid state communications 149, 1543 (2009). http://doi.org/10.1016/j.ssc.2009.06.001
Abstract: An investigation of the physical properties of La0.8Sr0.2MnO3 single crystals grown by the molten zone technique is realized close to the metal-to-insulator transition temperature (TMI). In this paper, we review the effect of the structural defects through magnetotransport and local magnetic microstructures. From electron microscopy observations, some nanocrack defects (i.e. defects at a nanometer scale) were found, essentially in the center part of the single crystals. At room temperature, magnetic force microscopy measurements have shown that the absence of defects allowed a magnetic ordering of the domains at the crystal edge, which is the best-crystallized region. In addition, the magnetization loops have permitted us to verify that the crystal was ferromagnetically weaker in the center. On analyzing the electrical resistivity data, we observed in the linear current regime a sensitive variation of the resistivity due to defects, by comparing the center and the edge of the material at TMI. Additionally, at strong current, non-linearity phenomena have been supposed to be related to local heating. Finally, we discuss the structural disorder effect on the relaxation of the ferromagnetic domains.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.554
Times cited: 3
DOI: 10.1016/j.ssc.2009.06.001
|
“Synthesis of highly stable pure-silica thin-walled hexagonally ordered mesoporous material”. Verlooy P, Aerts A, Lebedev OI, Van Tendeloo G, Kirschhock C, Martens JA, Chemical communications , 4287 (2009). http://doi.org/10.1039/b901796h
Abstract: Hexagonally ordered mesoporous silica with a very narrow mesopore size distribution and exceptionally high stability paired with unusually thin pore walls was prepared using piperidine and cetyltrimethylammonium bromide.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 17
DOI: 10.1039/b901796h
|
“Role of substrate on nucleation and morphology of gold nanoparticles produced by pulsed laser deposition”. Resta V, Afonso CN, Piscopiello E, Van Tendeloo G, Physical review : B : solid state 79, 235409 (2009). http://doi.org/10.1103/PhysRevB.79.235409
Abstract: This work compares the morphology of gold nanoparticles (NPs) produced at room temperature on single-crystalline (MgO nanocubes and plates) and amorphous (carbon/glass plates) substrates by pulsed laser deposition (PLD). The results show that similar deposition and nucleation rates (>5×1013 cm−2 s−1) are achieved irrespective of the nature of the substrate. Instead, the shape of NPs is substrate dependent, i.e., quasispheres and faceted NPs in amorphous and single-crystalline substrates, respectively. The shape of the latter is octahedral for small NPs and truncated octahedral for large ones, with the degree of truncation being well explained using the Wulff-Kaichew theorem. Furthermore, epitaxial growth at room temperature is demonstrated for single-crystalline substrate. The large fraction of ions having energies higher than 200 eV and the large flux of species arriving to the substrate (1016 at. cm−2 s−1) involved in the PLD process are, respectively, found to be responsible for the high nucleation rates and epitaxial growth at room temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 16
DOI: 10.1103/PhysRevB.79.235409
|
“Topotactic transformation of the cationic conductor Li4Mo5O17 into a rock salt type oxide Li12Mo5O17”. Pop N, Pralong V, Caignaert V, Colin JF, Malo S, Van Tendeloo G, Raveau B, Chemistry of materials 21, 3242 (2009). http://doi.org/10.1021/cm900767m
Abstract: Intercalation of lithium in the ribbon structure Li4Mo5O17 has been achieved, using both electrochemistry and soft chemistry. The ab initio structure determination of the ¡°Mo−O¡± framework of Li12Mo5O17 shows that the [Mo5O17]¡Þ ribbons keep the same arrangement of edge sharing MoO6 octahedra and the same orientation as in the parent structure but that a topotactic antidistortion of the ribbons appears, as a result of the larger size of Mo4+ in ¡°Li12¡± compared to Mo6+ in ¡°Li4¡±. On the basis of bond valence calculations, it is observed that 12 octahedral sites are available for Li+ in the new structure so that an ordered hypothetical rock salt type structure can be proposed for Li12Mo5O17. After the first Li insertion, a stable reversible capacity of 100 mA¡¤h/g is maintained after 20 cycles. A complete structural reversibility leading back to the ribbon type Li4Mo5O17 structure is obtained using a very low rate of C/100. The exploration of the Li mobility in those oxides shows that Li4Mo5O17 is a cationic conductor with ¦Ò = 10−3.5 S/cm at 500 ¡ãC and Ea = 0.35 eV.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 18
DOI: 10.1021/cm900767m
|
“TEM sample preparation by FIB for carbon nanotube interconnects”. Ke X, Bals S, Romo Negreira A, Hantschel T, Bender H, Van Tendeloo G, Ultramicroscopy 109, 1353 (2009). http://doi.org/10.1016/j.ultramic.2009.06.011
Abstract: A powerful method to study carbon nanotubes (CNTs) grown in patterned substrates for potential interconnects applications is transmission electron microscopy (TEM). However, high-quality TEM samples are necessary for such a study. Here, TEM specimen preparation by focused ion beam (FIB) has been used to obtain lamellae of patterned samples containing CNTs grown inside contact holes. A dual-cap Pt protection layer and an extensive 5 kV cleaning procedure are applied in order to preserve the CNTs and avoid deterioration during milling. TEM results show that the inner shell structure of the carbon nanotubes has been preserved, which proves that focused ion beam is a useful technique to prepare TEM samples of CNT interconnects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 21
DOI: 10.1016/j.ultramic.2009.06.011
|
“Two variants of the 1/2[110]p(203)p crystallographic shear structures: the phasoid Sr0.61Pb0.18(Fe0.75Mn0.25)O2.29”. Lepoittevin C, Hadermann J, Malo S, Pérez O, Van Tendeloo G, Hervieu M, Inorganic chemistry 48, 8257 (2009). http://doi.org/10.1021/ic900762s
Abstract: For the composition (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29, a new modulated crystallographic shear structure, related to perovskite, has been synthesized and structurally characterized by transmission electron microscopy. The structure can be described using a monoclinic supercell with cell parameters am = 27.595(2) Å, bm = 3.8786(2) Å, cm = 13.3453(9) Å, and βm = 100.126(5)°, refined from powder X-ray diffraction data. The incommensurate crystallographic shear phases require an alternative approach using the superspace formalism. This allows a unified description of the incommensurate phases from a monoclinically distorted perovskite unit cell and a modulation wave vector. The structure deduced from the high-resolution transmission electron microscopy and high-angle annular dark-field−scanning transmission electron microscopy images is that of a 1/2[110]p(203)p crystallographic shear structure. The structure follows the concept of a phasoid, with two coexisting variants with the same unit cell. The difference is situated at the translational interface, with the local formation of double (phase 2) or single (phase 1) tunnels, where the Pb cations are likely located.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 11
DOI: 10.1021/ic900762s
|
“Atomic resolution mapping using quantitative high-angle annular dark field scanning transmission electron microscopy”. Van Aert S, Verbeeck J, Bals S, Erni R, van Dyck D, Van Tendeloo G, Microscopy and microanalysis 15, 464 (2009). http://doi.org/10.1017/S1431927609093957
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.891
Times cited: 1
DOI: 10.1017/S1431927609093957
|
“Crystal structure of the group of optical materials Ln2MeGe4O12 (Me = Ca, Mn)”. Tarakina NV, Zubkov VG, Leonidov II, Tyutunnik AP, Surat LL, Hadermann J, Van Tendeloo G, Zeitschrift für Kristallographie , 401 (2009). http://doi.org/10.1524/zksu.2009.0059
Abstract: The crystal structure of the group of optical materials Ln2MeGe4O12, Ln = Eu, Gd, Dy-Lu, Y; Me = Ca, Mn and of the solid solution (Y1-xErx)2CaGe4O12 (x = 0 – 1), promising materials for photonics, has been studied in detail. The crystal structure of all compounds exhibit two alternating layers: one formed by Ln and Me atoms and another by cyclic [Ge4O12]8- anions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1524/zksu.2009.0059
|
“Investigation of stacking disorder in Li2SnO3”. Tarakina NV, Denisova TA, Maksimova LG, Baklanova YV, Tyutyunnik AP, Berger IF, Zubkov VG, Van Tendeloo G, Zeitschrift für Kristallographie , 375 (2009). http://doi.org/10.1524/zksu.2009.0055
Abstract: A crystal structure investigation of the low temperature Li2SnO3 modification has been carried out. X-ray, neutron powder and electron diffraction data showed that this compound crystallizes in a monoclinic unit cell with parameters: a = 5.3033(2)Å, b = 9.1738(3)Å, c = 10.0195(2)Å, β ~ 100.042(2)º and has stacking disorder along the c-axis. Simulation of diffraction patterns with different stacking faults mainly reveal the presence of rotational stacking faults with a probability of about 40% .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 16
DOI: 10.1524/zksu.2009.0055
|
“Preparation of sulfonated ordered mesoporous carbon and its use for the esterification of fatty acids”. Peng L, Philippaerts A, Ke X, van Noyen J, de Cleppel F, Van Tendeloo G, Jacobs PA, Sels BF, Catalysis today 150, 140 (2010). http://doi.org/10.1016/j.cattod.2009.07.066
Abstract: Mesoporous carbon, which can be replicated from mesoporous silica and whose surface is hydrophobic, can be an ideal catalyst for the esterification of fatty acids. Here we report an easy and low cost way to prepare sulfonic acid group-functionalized mesoporous carbon. A sample of calcined mesoporous silica SBA-15 was added to an aqueous sucrose solution followed by drying and calcination at different temperatures. In contrast to existing procedures, the obtained hybrid Si/C material was then first sulfonated in H2SO4, before the final removal of the silica template in order to stabilize the porous structure towards the liquid phase sulfonation treatment. Thus the silicacarbon composites, instead of the mesoporous carbon, were successfully sulfonated to introduce SO3H groups, while keeping the ordered mesoporous structure intact. The influence of carbonization temperature was investigated, suggesting an optimum temperature of 873 K. The SO3H group-functionalized mesoporous carbon, denoted as CMK-3-873-SO3H, was characterized by means of XRD, N2 physisorption, SEM, FT-IR, elemental analysis and TEM. It followed that a uniform mesoporous carbon was obtained with an average pore size of 3.89 nm, a specific surface of 807 m2/g and a SO3H group loading of 0.39 meq/g of dry material. Compared with other solid acid catalysts, the resulting material shows enhanced activity in the acid-catalyzed esterification of oleic acid with methanol, and can be used repeatedly. The increased catalytic performance is attributed to the hydrophobic surface and larger pore size of the new catalyst. It can effectively accommodate long chain fatty acids and reject formed water, making the active sites easily accessible.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.636
Times cited: 132
DOI: 10.1016/j.cattod.2009.07.066
|
“Compositional changes of Pd-Au bimetallic nanoclusters upon hydrogenation”. di Vece M, Bals S, Lievens P, Van Tendeloo G, Physical review : B : solid state 80, 125420 (2009). http://doi.org/10.1103/PhysRevB.80.125420
Abstract: Changes in the size distribution and composition of bimetallic Pd-Au nanoclusters have been observed after hydrogen exposure. This effect is caused by hydrogen-induced Ostwald ripening whereby the hydrogen reduces the binding energy of the cluster atoms leading to their detachment from the cluster. The composition changes due to a difference in mobility of the detached palladium and gold atoms on the surface. Fast palladium atoms contribute to the formation of larger nanoclusters, while the slower gold atoms are confined to the smaller nanoclusters. These transformations in the Pd-Au nanocluster size and composition set a limit for chemical reactions in which such nanoclusters are involved together with hydrogen.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 28
DOI: 10.1103/PhysRevB.80.125420
|