Abstract: The changes induced by exposing multi-walled carbon nanotubes (CNTs) to atomic nitrogen were analysed by high-resolution transmission electron microscopy (HRTEM), x-ray and ultraviolet photoelectron spectroscopy. It was found that the atomic nitrogen generated by a microwave plasma effectively grafts chemical groups onto the CNT surface altering the density of valence electronic states. HRTEM showed that the exposure to atomic nitrogen does not significantly damage the CNT surface.

Abstract: Titanate nanotubes were prepared via a hydrothermal treatment of TiO2 powders (Riedel De Haen) in a basic solution. Morphology and structure of the prepared samples were characterized by high resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), XRD, FT-Raman spectroscopy, nitrogen sorption and DSC. The photocatalytic activity was evaluated by photocatalytic oxidation of rhodamine 6G. Trititanate nanotubes (TTNT) with inner pore diameters between 4 and 4.2 nm and surface areas up till 360 m(2)/g could be synthesized. The synthesis route was modified by introduction of a calcination step, by applying a lower hydrothermal temperature and microwave irradiation in order to increase the photocatalytic activity of the porous photoactive nanotubular materials. Calcination and a softer hydrothermal treatment led to the formation of anatase without affecting the surface area and nanotubular shape of the samples. In this way, the photocatalytic activity of the original trititanate nanotubes could be significantly increased. By making use of microwave assisted synthesis, the photocatalytic activity call also be increased due to the presence of anatase. However, by applying microwave synthesis, a different structure was obtained, nanoribbons (NR) instead of nanotubcs, resulting in a decrease in surface area and porosity.

Abstract: The effect of the oxygen plasma treatment on the electronic states of multi-wall carbon nanotubes (MWCNTs) is analyzed by X-ray photoemission measurements (XPS) and UPS, both using synchrotron radiation. It is found that the plasma treatment effectively grafts oxygen at the CNT-surface. Thereafter, the interaction between evaporated Pd and pristine or oxygen plasma-treated MWCNTs is investigated. Pd is found to nucleate at defective sites, whether initially present or introduced by oxygen plasma treatment. The plasma treatment induced a uniform dispersion of Pd clusters at the CNT-surface. The absence of additional features in the Pd 3d and C I s core levels spectra testifies that no Pd-C bond is formed. The shift of the Pd 3d core level towards high-binding energy for the smallest clusters is attributed to the Coulomb energy of the charged final state. (C) 2008 Elsevier Ltd. All rights reserved.

Abstract: Nanocrystalline titanium dioxide was prepared via aerosol pyrolysis of titanium alkoxide precursor at 200-580 degrees C in air and in nitrogen atmospheres. Powders were characterized by x-ray diffraction, thermogravimetric analysis, Brunauer-Emmett-Teller analysis, scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, x-ray fluorescence, Raman and infrared spectroscopy, and Berner-type low-pressure impactor. The anatase phase transition was initiated at 500 degrees C in nitrogen and at 580 degrees C in air. Under other conditions amorphous powders were observed and transformed to nanocrystalline TiO2 via thermal postannealing. In air, smooth and spherical particles with 2-4-mu m diameter were formed with an as-expected tendency to convert to rutile in the thermal postannealings. In nitrogen, a fraction of the titanium tetrabutoxide precursor evaporated and formed ultrafine particles via the gas-to-particle conversion. At 500 degrees C thermally stable anatase phase was formed in nitrogen. A specific surface area as high as 280 m(2) g(-1) was observed for an as-prepared powder.

Abstract: The incommensurately modulated scheelite-like KSm( MoO4)(2) structure has been refined in the monoclinic superspace group I2/b(alpha beta 0)00 by the Rietveld method on the basis of synchrotron radiation powder diffraction data. The systematic broadening of satellite reflections has been accounted for by applying anisotropic microstrain line-broadening. The microstructure has been studied by transmission electron microscopy (TEM). The partial disorder of the K and Sm cations in the A position is best approximated by a combination of harmonic and complex crenel functions with (0.952Sm + 0.048K) and (0.952K + 0.048Sm) atomic domains. This combination yields a compositional wave distribution from {KMoO4} to {SmMoO4} observed in the ab structure projection along q. The specific features of KSm(MoO4)(2) and degree of the A-cation ordering are discussed in comparison with the previously reported structure of KNd(MoO4)(2).

Abstract: Titania nanoparticles have been deposited on inert porous silica supports with high specific surface area. These materials have potential applications in paint and textile industry as the titania particles selectively deposited on the inner surface of the silica supports act as a photocatalyst. The inert external surface is necessary to avoid photodegradation of the textile material or the paint components. The photocatalytic activity of the catalysts has been evaluated with two catalytic setups. One setup in aqueous phase, for the degradation of dyes such as rhodamine-6G, is commonly used. The second setup is a continuous flow gaseous phase setup which was used for the mineralization of ethanol as a representative volatile organic compound (VOC). The influence of the porosity and the morphology of the silica supports on the photocatalytic activity are discussed.

Abstract: Post-synthesis hydrothermal treatments have been used to improve the quality of MCM-41 materials. In our latest work, merging of surfactant-containing silica microspheres during the hydrothermal treatments was observed. Mechanistic insights and the different stages that are involved in the merging process can be summarized as follows. First, the surfaces of the starting microspheres open up due to the dissolution of silica. Then the dissolved silica species provide mass source for the formation of particle necks connecting two neighboring microspheres. Gradually, surfaces of the starting microspheres are flattened to meet the needs of further growth of the necks. Finally, some chain-like highly-ordered mesoporous structures up to several micrometers are formed. The observed merging of the surfactant-containing microspheres is a re-assembling process, which is under the control of electrostatic force between the dissolved silica species and the surfactant cations. The occluded surfactant cations in the precursor spheres play important roles in the merging process.

Abstract: Multi-wall carbon nanotubes (MWCNTs) were exposed to a CF4 rf-plasma. X-ray photoelectron spectroscopy analysis shows that the treatment effectively grafts fluorine atoms onto the MWCNTs. The fluorine atomic concentration and the nature of the CF bond (semi-ionic or covalent) can be tuned by varying the exposure time. Ultraviolet photoelectron spectroscopy analysis confirms that the valence electronic states are altered by the grafting of fluorine atoms. Characterization with high-resolution transmission electron microscopy reveals that while the plasma treatment does not induce significant etching impact on the CNT-surface, it does increase the number of active sites for gold cluster formation.

Abstract: Hysteretic resistance switching is observed in epitaxial Fe/Cr/MgO/Fe magnetic tunnel junctions under bias voltage cycling between negative and positive values of about 1 V. The junctions switch back and forth between high- and low-resistance states, both of which depend on the device bias history. A linear dependence is found between the magnitude of the tunnel magnetoresistance and the crafted resistance of the junctions. To explain these results, a model is proposed that considers electron transport both by elastic tunneling and by defect-assisted transmission. (c) 2008 American Institute of Physics.

Abstract: Two-ordered perovskites, Bi1/3Sr2/3FeO2.67 and Bi1/2Ca1/2FeO2.75, have been stabilized and characterized by transmission electron microscopy, Mössbauer spectroscopy and X-ray powder diffraction techniques. They both exhibit orthorhombic superstructures, one with a≈b≈2ap and c≈3ap (S.G.: Pb2n or Pbmn) for the Sr-based compound and one with a≈b≈2ap and c≈8ap (S.G.: B222, Bmm2, B2mm or Bmmm) for the Ca-based one. The high-resolution transmission electron microscopy (HRTEM) images evidence the existence of one deficient [FeOx]∞ layer, suggesting that Bi1/3Sr2/3FeO2.67 and Bi1/2Ca1/2FeO2.75 behave differently compared to their Ln-based homolog. The HAADF-STEM images allow to propose a model of cation ordering on the A sites of the perovskite. The Mössbauer analyses confirm the trivalent state of iron and its complex environment with three types of coordination. Both compounds exhibit a high value of resistivity and the inverse molar susceptibility versus temperature curves evidence a magnetic transition at about 730 K for the Bi1/3Sr2/3FeO2.67 and a smooth reversible transition between 590 and 650 K for Bi1/2Ca1/2FeO2.75.

Abstract: High quality epitaxial c axis oriented La2NiO4+ä thin films have been prepared by the pulsed injection metal organic chemical vapor deposition technique on different substrates. High-resolution electron microscopy/transmission electron microscopy has been used to confirm the high crystalline quality of the deposited films. The c-parameter evolution has been studied by XRD as a function of time and gas atmosphere. The high temperature transport properties along the basal a−b plane of epitaxial La2NiO4+ä films have been measured, and the total conductivity of the layers has been found to increase as the thickness is reduced. Layers of 50 nm and thinner have shown a maximum conductivity larger than that measured for single-crystals, in particular, the 33 nm thick films with a conductivity of 475 S/cm in oxygen correspond to the highest value measured to date for this material.

Abstract: We report the high temperature electronic transport properties of SrFeO3 − ä epitaxial thin films obtained by pulsed laser deposition on NdGaO3(110) substrates. The films show total conductivity higher than the bulk material and apparent activation energy of about 0.12 eV in O2, lower than reported values for SrFeO3 − ä films. The conductivity dependence with oxygen partial pressure shows a power dependence with an exponent close to + 1/4, in agreement with expected point defect equilibrium. For a given oxygen partial pressure, the temperature coefficient of resistance (TCR) shows a low positive value of about 1.52.5 10− 3 K− 1, which is still suitable for resistive oxygen sensing applications. The transport properties of the films are discussed in view of their particular microstructure.