“TEM investigation of the microstructure and defects of CuZr martensite: 2: planar defects”. Seo JW, Schryvers D, Acta materialia 46, 1177 (1998). http://doi.org/10.1016/S1359-6454(97)00334-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 21
DOI: 10.1016/S1359-6454(97)00334-0
|
|
|
“The study of carbon nanotubules produced by catalytic method”. Ivanov V, Nagy JB, Lambin P, Lucas A, Zhang XB, Zhang XF, Bernaerts D, Van Tendeloo G, Amelinckx S, van Landuyt J, Chemical physics letters 223, 329 (1994). http://doi.org/10.1016/0009-2614(94)00467-6
Abstract: Catalytic methods for the production of carbon nanotubules have been developed based on the decomposition of acetylene on well-dispersed metal particles strongly adsorbed on a support. Cobalt on silica was found to be the best catalyst-support combination for the production of graphitic tubules. The method for the catalyst preparation and the reaction conditions were optimized. Straight and coiled carbon tubules were obtained with inner and outer diameter of 3-7 and 15-20 nm, respectively, and up to 30 mum in length. These nanotubules were not coated by amorphous carbon. Traces of amorphous carbon could be removed by hydrogen. High resolution electron microscopy images and electron diffraction patterns of the straight nanotubules were similar to those obtained by the arc-discharge method. Coiled nanotubules were revealed by TEM to be regular polygonized helices where the bends are caused by pairs of pentagon-heptagon carbon rings among the hexagonal network.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 405
DOI: 10.1016/0009-2614(94)00467-6
|
|
|
“Transmission electron microscopy investigation of Bi-2223/Ag tapes”. Gottschalck Andersen L, Bals S, Van Tendeloo G, Poulsen HF, Liu YL, Physica: C : superconductivity 353, 251 (2001). http://doi.org/10.1016/S0921-4534(00)01755-X
Abstract: The microstructure of (Bi,Pb)2Sr2Ca2Cu3Ox (Bi-2223) tapes has been investigated by means of transmission electron microscopy (TEM) and high-resolution TEM. The emphasis has been placed on: (1) an examination of the grain morphology and size, (2) grain and colony boundary angles, which are formed during the tape processing, (3) a study of the grain boundaries on an atomic scale, including intergrowth investigations. Tapes with different process parameters have been compared with respect to the microstructure. A fully processed tape has on the average 50% thicker Bi-2223 grains than a tape after the first annealing. The angles of c-axis tilt grain boundaries are on average 14° and 26° for the fully processed tape and the tape after the first annealing, respectively. The intergrowth content (15%) and distribution are similar in these two tapes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 13
DOI: 10.1016/S0921-4534(00)01755-X
|
|
|
“Vortex states in a mescopic superconducting triangle”. Misko VR, Fomin VM, Devreese JT, Moshchalkov VV, Physica C-Superconductivity And Its Applications 369, 361 (2002). http://doi.org/10.1016/S0921-4534(01)01277-1
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 1.404
Times cited: 14
DOI: 10.1016/S0921-4534(01)01277-1
|
|
|
“Vortex states in a multi-conoid superconducting nanosized bridge”. Misko VR, Fomin VM, Devreese JT, Physica C-Superconductivity And Its Applications 369, 356 (2002). http://doi.org/10.1016/S0921-4534(01)01276-X
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 1.404
Times cited: 1
DOI: 10.1016/S0921-4534(01)01276-X
|
|
|
“Accurate infrared spectroscopy determination of interstitial and precipitated oxygen in highly doped Czochralski-grown silicon”. de Gryse O, Clauws P, Rossou L, van Landuyt J, Vanhellemont J, The review of scientific instruments 70, 3661 (1999). http://doi.org/10.1063/1.1149974
Abstract: A method has been developed to determine the interstitial and precipitated oxygen concentration in highly doped n- and p-type silicon. 10-30-mu m-thin silicon samples in a mechanical stress-free state and without alteration of the thermal history are prepared and measured with Fourier transform infrared spectroscopy at 5.5-6 K. The measured oxygen contents in the as-grown Si samples agree well with those obtained with gas fusion analysis. In the highly boron-doped samples, the interstitial oxygen can be determined down to 10(17) cm(-3). (C) 1999 American Institute of Physics. [S0034-6748(99)04909-6].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.515
Times cited: 5
DOI: 10.1063/1.1149974
|
|
|
“Adsorption of potassium and oxygen on graphite: a theoretical study”. Lamoen D, Persson BNJ, Journal Of Chemical Physics 108, 3332 (1998). http://doi.org/10.1063/1.475732
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 2.965
Times cited: 91
DOI: 10.1063/1.475732
|
|
|
“Barium-based manganites Ln1-xBaxMnO3 with Ln = {Pr, La}: phase transitions and magnetoresistance properties”. Barnabé, A, Millange F, Maignan A, Hervieu M, Raveau B, Van Tendeloo G, Laffez P, Chem. mater. 10, 252 (1998). http://doi.org/10.1021/cm9704084
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 48
DOI: 10.1021/cm9704084
|
|
|
“Chemical, structural and electrical characterizations in the BIZNVOX family”. Vernochet C, Vannier R-N, Huvé, M, Pirovano C, Nowogrocki G, Mairesse G, Van Tendeloo G, Journal of materials chemistry 10, 2811 (2000). http://doi.org/10.1039/b006157n
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 13
DOI: 10.1039/b006157n
|
|
|
“The colour of silver stained glass : analytical investigations carried out with XRF, SEM/EDX, TEM and IBA”. Jembrih-Simbürger D, Neelmeijer C, Schalm O, Fredrickx P, Schreiner M, De Vis K, Mäder M, Schryvers D, Caen J, Journal of analytical atomic spectrometry 17, 321 (2002). http://doi.org/10.1039/b111024c
Abstract: Glass treated on its surface with silver compounds and an aluminosilicate, such as ochre or clay, at higher temperatures (between 550 and 650 °C) accepts a wide variety of a yellow colour. It is the aim of this study to investigate the parameters of the manufacturing process affecting the final colour of silver stained glass and to correlate them with the final colour and colour intensity. Therefore, defined mixtures of ochre and a silver compound (AgCl, AgNO3, Ag2SO4, Ag3PO4, Ag2O) were prepared and applied on soda-lime glass. The firing process was modified within the range from 563 to 630 °C and glass samples were analysed after treatment with energy dispersive X-ray fluorescence analysis (EDXRF), scanning electron microscopy (SEM/EDX), transmission electron microscopy (TEM), as well as ion beam analysis (IBA) with an external beam. Within the scope of IBA simultaneous measurements using particle-induced X-ray emission (PIXE), particle-induced gamma-ray emission (PIGE), and Rutherford backscattering spectrometry (RBS) were carried out in order to obtain the thickness of the Ag-rich surface layer and the depth distribution of Ag. By means of TEM the microstructure of the silver particles was visualised. XRF results show that the lowest amount of Ag could be detected on glass samples treated with silver stain mixtures containing AgCl and Ag2O. A low kiln temperature (e.g. 563 °C) results in a higher silver concentration at the surface and lower penetration depths. Furthermore, the results obtained with SEM/EDX at cross-sections of the glass samples could be confirmed by PIXE, PIGE, RBS, and TEM.
Keywords: A1 Journal article; Art; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 42
DOI: 10.1039/b111024c
|
|
|
“Crystal structure of Bi6Sr8-xCa3+xO22(-0.5\leq x\leq1.7): a mixed valence bismuth oxide related to perovskite”. Luhrs CC, Molins E, Van Tendeloo G, Beltran-Porter D, Fuertes A, Chemistry of materials 10, 1875 (1998). http://doi.org/10.1021/cm9800377
Abstract: The crystal structure of BiSr8-xCa3+xO22 has been determined by single-crystal X-ray diffraction. This phase is the same as Bi9Sr11Ca5Oy that was previously studied by several authors as a secondary phase in the Bi-Sr-Ca-Cu-O system and coexists in thermodynamic equilibrium with the superconductors Bi2Sr2CuO6 and Bi2Sr2CaCu2O8 It crystallizes in the monoclinic space group P2(1)/c, with cell parameters a 11.037(3) Angstrom, b = 5.971(2) Angstrom, c = 19.703(7) Angstrom, beta = 101.46(3)degrees Z = 2. The structure was solved by direct methods and full-matrix least-squares refinement. It is built up by perovskite-related blocks of composition [Sr8-xBi2Ca3+xO16] that intergrow with double rows [Bi4O6] running along b. The perovskite blocks are formed by groups of five octahedra that are shifted from each other 3/2 root 2a(p) along [110](p) (a(p) being the parameter of the cubic perovskite subcell) in a zigzag configuration and are aligned with this direction parallel to the one forming an angle of 25" with the c axis. In turn, the perovskite blocks [Sr8-xBi2Ca3+xO16] are shifted from each other 1/2 of both a(p) and root 2a(p) along [100](p) and [110](p), respectively. In the double rows, two trivalent bismuth atoms are placed, forming dimeric anion complexes [Bi2O6].(6-).6- The oxygen atoms around bismuth in these dimers are placed in the vertexes of a distorted trigonal bipyramid, with one vacant position that would be occupied by the lone pairs characteristic for the electronic configuration of Bi(III). The B sites in the perovskite blocks are occupied by pentavalent bismuth atoms and calcium atoms; the remaining Sr and Ca ions occupy the A sites of the perovskite blocks with coordination numbers with oxygen ranging from 10 to 12. The mean valence for Bi is +3.67 [33.3% of Bi(V) and 66.7% of Bi(III)]. The oxygen vacancies are located in the boundaries between domains having the two possible configurations of the perovskite subcell as in the anionic superconductor Bi3BaO5.5. The oxidation of Bi6Sr8-xCa3+xO22 at 650 degrees C allows the complete filling of the oxygen vacancies to form the double perovskite (Sr2-xCax)Bi1.4Ca0.6O6 that shows 92.5% of bismuth in +5 oxidation state. The experimental high-resolution electon microscopy image and the electron diffraction pattern of powder samples along the [010]* zone axis are in good agreement with those calculated from the structural model obtained by single-crystal X-ray diffraction. The material is almost free of defects and the occurrence of planar defects is very exceptional.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/cm9800377
|
|
|
“Crystal-structure of the double-hg-layer copper-oxide superconductor (Hg,Pr)2Ba2(Y,Ca)Cu2O8-\deltaas a function of doping”. Radaelli PG, Marezio M, Tholence JL, Debrion S, Santoro A, Huang Q, Capponi JJ, Chaillout C, Krekels T, Van Tendeloo G, The journal of physics and chemistry of solids 56, 1471 (1995). http://doi.org/10.1016/0022-3697(95)00084-4
Abstract: The crystal structure of the newly discovered double-Hg-layer copper oxide superconductor (Hg, Pr)(2)Ba-2(Y, Ca)Cu2O8-delta was studied as a function of chemical doping using neutron and electron diffraction and high-resolution transmission electron microscopy (HREM). Rietveld refinements of the structural parameters from neutron powder diffraction data indicate that the oxygen site O3 on the mercury plane is highly defective, being both partially occupied and displaced from the high-symmetry position. The variable concentration of oxygen vacancies partially compensates for the cation doping and, together with the O3 displacement field, makes some of the Hg atoms acquire an unusual pyramidal coordination. HREM images confirm that the structure is of the '2212' type, with very few defects. In some grains, faint superstructure reflections were evidenced by electron diffraction, suggesting that both the oxygen vacancies and the O3 displacement field may order at least on a local scale.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.853
Times cited: 16
DOI: 10.1016/0022-3697(95)00084-4
|
|
|
“Direct evidence of spontaneous quantum dot formation in a thick InGaN epilayer”. Nistor L, Bender H, Vantomme A, Wu MF, van Landuyt J, O'Donnell KP, Martin R, Jacobs K, Moerman I, Applied physics letters 77, 507 (2000). http://doi.org/10.1063/1.127026
Abstract: We report a direct observation of quantum dots formed spontaneously in a thick InGaN epilayer by high resolution transmission electron microscopy. Investigation of a (280 nm thick) In0.22Ga0.78N single layer, emitting in the blue/green spectral region, reveals quantum dots with estimated sizes in the range of 1.5-3 nm. Such sizes are in very good agreement with calculations based on the luminescence spectra of this specimen. (C) 2000 American Institute of Physics. [S0003-6951(00)00930-X].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 44
DOI: 10.1063/1.127026
|
|
|
“Distribution of fields and charge carriers in cylindrical nanosize silicon-based metal-oxide-semiconductor structures”. Pokatilov EP, Fomin VM, Balaban SN, Gladilin VN, Klimin SN, Devreese JT, Magnus W, Schoenmaker W, Collaert N, van Rossum M, de Meyer K, Journal Of Applied Physics 85, 6625 (1999). http://doi.org/10.1063/1.370171
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 2.068
Times cited: 16
DOI: 10.1063/1.370171
|
|
|
“Doubling the critical temperature of La1.9Sr0.1CuO4 using epitaxial strain”. Loquet J-P, Perret J, Fompeyrine J, Mächler E, Seo JW, Van Tendeloo G, Nature 394, 453 (1998). http://doi.org/10.1038/28810
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 40.137
Times cited: 404
DOI: 10.1038/28810
|
|
|
“Electron energy-loss spectroscopy study of a (LaMnO3)8(SrMnO3)4 heterostructure”. Verbeeck J, Lebedev OI, Van Tendeloo G, Silcox J, Mercey B, Hervieu M, Haghiri-Gosnet AM, Applied physics letters 79, 2037 (2001). http://doi.org/10.1063/1.1403316
Abstract: An epitaxially grown heterostructure consisting of alternating layers of LaMnO3 (8 unit cells) and SrMnO3 (4 unit cells) on a SrTiO3 substrate has been studied by a combination of electron energy-loss spectroscopy (EELS) and high-resolution transmission electron microscopy (HRTEM) on an atomic scale. Excitation edges of all elements are captured with subnanometer spatial accuracy, and parametrized to obtain chemical profiles. The fine-edge structure of O K and Mn L-2,L-3 edges are interpreted as signatures of the local electronic structure and show a spatial modulation of the concentration of holes with O 2p character. The chemical concentration is found to be different for the bottom and top interface of a SrMnO3 layer. HRTEM complements the EELS results and confirms the asymmetry of the interfaces. (C) 2001 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 19
DOI: 10.1063/1.1403316
|
|
|
“An electron microscopic study of highly oriented undoped and FeCl3-doped poly (p-phenylenevinylene)”. Zhang XB, Van Tendeloo G, van Landuyt J, van Dyck D, Briers J, Bao Y, Geise HJ, Macromolecules 29, 1554 (1996). http://doi.org/10.1021/ma9513067
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 5.8
Times cited: 10
DOI: 10.1021/ma9513067
|
|
|
“Electron microscopy and Rutherford backscattering spectrometry characterisation of 6H SiC samples implanted with He+”. Frangis N, van Landuyt J, Grimaldi MG, Calcagno L, Nuclear instruments and methods in physics research: B: beam interactions with materials and atoms
T2 –, Symposium 1 on New Trends in Ion Beam Processing of Materials, at the, E-MRS 96 Spring Meeting, June 04-07, 1996, Strasbourg, France 120, 186 (1996). http://doi.org/10.1016/S0168-583X(96)00506-X
Abstract: 6H SiC single crystals were implanted al room temperature with 1 MeV He+ up to a fluence of 2 x 10(17) at./cm(2) RBS-channeling analysis with a 2 MeV He+ beam indicated the formation of extended defects or the generation of point defects at a constant concentration over a depth of about 1 mu m. Electron microscopy characterisation revealed the presence of two amorphous buried layers at depths of about 1,75 and 4.8 mu m. They an due to the implantation and to the analysing RES beam, respectively, No extended planar or linear faults were found in the region between the surface and the first amorphous layer. However, at the surface, a 50 nm thick amorphous layer was observed in which crystalline inclusions were embedded. Electron diffraction and HREM data of the inclusions were typical for diamond, These inclusions were even found in the crystalline SiC material below this layer, however at a reduced density.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.124
Times cited: 2
DOI: 10.1016/S0168-583X(96)00506-X
|
|
|
“Epitaxial Ni-Al thin films on NaCl using a Ag buffer layer”. Yandouzi M, Toth L, Vasudevan V, Cannaerts M, van Haesendonck C, Schryvers D, Philosophical magazine letters 80, 719 (2000). http://doi.org/10.1080/09500830050192936
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.941
Times cited: 2
DOI: 10.1080/09500830050192936
|
|
|
“Epitaxial strain induced metal insulator transition in La0.9Sr0.1MnO3 and La0.88Sr0.1MnO3 thin films”. Razavi FS, Gross G, Habermeier H-U, Lebedev O, Amelinckx S, Van Tendeloo G, Vigliante A, Applied physics letters 76, 155 (2000). http://doi.org/10.1063/1.125687
Abstract: We are reporting an unexpected metal insulator transition at the ferromagnetic phase-transition temperature for thin films of La0.9Sr0.1MnO3 (< 50 nm), grown on a (100) face of SrTiO3 substrate. For the thicker films (> 50 nm), similar to the single crystal, no such transition is observed below T-C. Additionally, we observe the suppression of the features associated with charge or orbital ordering in intentionally La-deficient thin films of La0.88Sr0.1MnO3 (< 75 nm). In thin films, transmission electron microscopy reveals a compressive strain due to the epitaxial growth, that is, lattice parameters adopt those of the cubic lattice of SrTiO3. As the film thickness increases, coherent microtwinning is observed in the films and the films relax to a orthorhombic structure. (C) 2000 American Institute of Physics. [S0003-6951(00)00402-2].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 91
DOI: 10.1063/1.125687
|
|
|
“Extracellular matrix protein 1 (ECM1) has angiogenic properties and is expressed by breast tumor cells”. Han Z, Ni J, Smits P, Underhill C, Xie B, Chen Y, Liu N, Tylzanowski P, Parmelee D, Feng P, Ding I, Gao F, Gentz R, Huylebroeck D, Merregaert J, Zhang L, The FASEB journal 15, 988 (2001). http://doi.org/10.1096/fj.99-0934com
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 94
DOI: 10.1096/fj.99-0934com
|
|
|
“Ferromagnetism and magnetoresistance in monolayered manganites Ca2-xLnxMnO4”. Maignan A, Martin C, Van Tendeloo G, Hervieu M, Raveau B, Journal of materials chemistry 8, 2411 (1998). http://doi.org/10.1039/a805393f
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 30
DOI: 10.1039/a805393f
|
|
|
“Growth kinetic of MgO film on r-plane of sapphire: microstructural study”. Lei CH, Van Tendeloo G, Lisoni JG, Siegert M, Schubert J, Journal of crystal growth 226, 419 (2001). http://doi.org/10.1016/S0022-0248(01)01396-3
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.751
Times cited: 7
DOI: 10.1016/S0022-0248(01)01396-3
|
|
|
“High resolution electron microscopy and X-ray photoelectron spectroscopy studies of heteroepitaxial SixGe1-x alloys produced through laser induced processing”. Frangis N, van Landuyt J, Lartiprete R, Martelli S, Borsella E, Chiussi S, Castro J, Leon B, Applied physics letters 72, 2877 (1998). http://doi.org/10.1063/1.121487
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 16
DOI: 10.1063/1.121487
|
|
|
“High resolution electron microscopy in materials research”. Van Tendeloo G, Journal of materials chemistry 8, 797 (1998). http://doi.org/10.1039/a708240a
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 8
DOI: 10.1039/a708240a
|
|
|
“High resolution electron microscopy study of molecular beam epitaxy grown CoSi2/Si1-xGex/Si(100) heterostructurs”. Buschmann V, Rodewald M, Fuess H, Van Tendeloo G, Schäffer C, Journal of applied physics 85, 2119 (1999). http://doi.org/10.1063/1.369512
Abstract: Two CoSi2/Si1-xGex/Si(100) heterostructures, with different Ge content, made by molecular beam epitaxy are characterized by high resolution electron microscopy. In general, the interface between the CoSi2 thin film and the Si1-xGex layer is of a high structural quality and the strained Si1-xGex layer exhibits few defects. For both samples, different interface structures are present, although the dominant interfacial configuration is similar to the unreconstructed interface present at the CoSi2/Si(100) interface. Only occasionally (2x1) reconstructed interface regions are found which are just a few nanometers in length. Phenomena such as Ge segregation and the introduction of defects are also observed in the Si1-xGex layer. We attribute the minimal presence of the reconstructed interface to both the (2x8):Si1-xGex(100) surface reconstruction and the Ge segregation that takes place. (C) 1999 American Institute of Physics. [S0021-8979(99)02104-0].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 6
DOI: 10.1063/1.369512
|
|
|
“Holotomography: quantitative phase tomography with micrometer resolution using hard synchrotron radiation X-rays”. Cloetens P, Ludwig W, Baruchel J, van Dyck D, van Landuyt J, Guigay JP, Schlenker M, Applied physics letters 75, 2912 (1999). http://doi.org/10.1063/1.125225
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 3.411
Times cited: 481
DOI: 10.1063/1.125225
|
|
|
“HREM investigation of martensite precursor effects and stacking sequences in Ni-Mn-Ti alloys”. Schryvers D, Lahjouji DE, Slootmaekers B, Potapov PL, Scripta metallurgica et materialia 35, 1235 (1996). http://doi.org/10.1016/1359-6462(96)00271-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.224
Times cited: 2
DOI: 10.1016/1359-6462(96)00271-0
|
|
|
“In situ transmission electron microscopy study of Ni silicide phases formed on (001) Si active lines”. Teodorescu V, Nistor L, Bender H, Steegen A, Lauwers A, Maex K, van Landuyt J, Journal of applied physics 90, 167 (2001). http://doi.org/10.1063/1.1378812
Abstract: The formation of Ni silicides is studied by transmission electron microscopy during in situ heating experiments of 12 nm Ni layers on blanket silicon, or in patterned structures covered with a thin chemical oxide. It is shown that the first phase formed is the NiSi2 which grows epitaxially in pyramidal crystals. The formation of NiSi occurs quite abruptly around 400 degreesC when a monosilicide layer covers the disilicide grains and the silicon in between. The NiSi phase remains stable up to 800 degreesC, at which temperature the layer finally fully transforms to NiSi2. The monosilicide grains show different epitaxial relationships with the Si substrate. Ni2Si is never observed. (C) 2001 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 97
DOI: 10.1063/1.1378812
|
|
|
“InAs p-n diodes grown on GaAs and GaAs-coated Si by molecular beam epitaxy”. Dobbelaere W, de Boeck J, Heremans P, Mertens R, Borghs G, Luyten W, van Landuyt J, Applied physics letters 60, 868 (1992). http://doi.org/10.1063/1.106490
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.302
Times cited: 20
DOI: 10.1063/1.106490
|
|