Abstract: Defects in AgG tabular crystals with {111} surfaces are characterised by transmission electron microscopy (TEM) and their influence on the growth process is discussed. In the tabular crystals, twins parallel to the tabular face as well as dislocations along different directions are observed. The twins induce the tabular growth, while the dislocations do not influence the morphology. In 10 to 30% of the crystals that have been characterised, thickness growth is observed and it is shown that in all cases twins on other planes than the tabular ones are present. Two configurations occur more frequently and are analysed in detail. For the first group, twins parallel to the tabular face as well as a microtwin along a non-parallel {111} plane and ending inside the crystal are present. In the crystals of the second group only one extra non-parallel twin occurs giving rise to a bicrystal built up by a tetrahedral shaped part and a flat triangular or trapezoidal part. More complex twin configurations give rise to various, less characteristic morphologies.

Abstract: Transmission electron microscopy and X-ray diffraction proved chain/ladder incommensurate single crystal structure of investigated samples. The incommensurate ratio was determined from the X-ray and electron diffraction being equal to 0.704. Diffuse scattering intensities localised on the planes perpendicular to the c*-axis and passing through the spots originating from the periodicity of chain sublattice were detected. High-angle grain boundary or twinning formed by rotation of 33.3 degrees around [100] direction was observed. High-resolution electron microscopy images revealed the stacking faults in ac planes.

Abstract: In this work we present for the first time, to our knowledge, the CVD epitaxial growth of beta -SiC using an ion beam synthesized (IBS) beta -SiC layer as seed, which has been formed by multiple implantation into Si wafers at 500 degreesC. The ion beam synthesized continuous layer is constituted by beta -SiC nanocrystals that are well oriented relative to the silicon substrate. Comparison of the epitaxial growth on these samples with that on silicon test samples, both on and off-axis, is performed. The results show that the epitaxial growth can be achieved on the IBS samples without the need of the carbonization step and that the structural quality of the CVD layer is comparable to that obtained on a carbonized silicon sample. Improvement of the quality of the deposited layer is proposed.

Abstract: Not much about the effect of thiocyanate addition on the sulphur ripening is known, although it is used for many applications in photographic practice. Via a combination of tracer analysis and diffuse reflectance spectroscopy the effect of thiocyanate addition on the sulphur and sulphur-plus-gold ripening could be unveiled. When thiocyanate is added prior to the sulphur addition, it appears to rearrange the silver halide surface in such way that the sulphur deposition rate is enhanced, but the supply of interstitials is limited. Addition of thiocyanate after the sulphur reaction results in the formation of thiocyanate complexes with silver, from which a silver ion is more easily deposited in a surface cell of the silver sulphide clusters thus enhancing the sensitization rate. For sulphur-plus-gold sensitized emulsions it was observed that part of the gold ions could be removed out of the Ag2-xAuxS clusters by addition of thiocyanate ions and subsequent washing. Hence, it was concluded that two different types of gold ions are present in the silver sulphide clusters; 1. gold ions which are substitutional for silver (bound between sulphur and bromide ions) 2. gold ions which bridge two or three sulphur atoms. Incorporation of gold ions into silver sulphide clusters suppresses their optical absorption in diffuse reflectance spectroscopy. Since the optical absorption at 505 nm can completely be restored by addition of thiocyanate, it is assumed that the entity absorbing at this wavelength is a monomer of silver sulphide.