Abstract: The structure and defect structure of Bi2-xPbxSr3.5Cu2 (CO3)O8-delta compounds with 0 less-than-or-equal-to x less-than-or-equal-to 0.75 are carefully investigated by electron diffraction and high-resolution electron microscopy. All compounds have an orthorhombic structure with a almost-equal-to b almost-equal-to 5.4 angstrom and c almost-equal-to 39.5 angstrom. The length of the b-axis decreases monotonically with increasing x. The space group for the basic structure is Abm2. The structure can be considered as an intergrowth of Bi2Sr2CuO6 lamellae with Sr2CuO2 (CO3) lamellae along the c-axis. CO3 groups behave as bridges connecting the CuO6 octahedra. In the x = 0 compound the carbon atoms are shifted away from their symmetry positions; the orientational ordering of the CO3 groups (or the carbon shift) in successive CO planes alternates along +b and -b. Typical Bi-type and Pb-type modulations are found along the b-axis up to a Pb content x = 0.5. Electron beam irradiation destroys the ordering of the CO3 groups and alters the modulated structure. (C) 1994 Academic press, inc.

Abstract: The ternary oxides Ba8Ta4Ti3O24 and Ba10Ta7.04Ti1.2O30 were synthesized and their crystal structures and defects were studied by means of X-ray powder diffraction, electron diffraction, and high resolution electron microscopy. The crystal structure of Ba8Ta4Ti3O24 is based on the 8H (cchc)(2) close-packed stacking (a 10.0314 Angstrom, c = 18.869 Angstrom, SG P6(3)/mcm, Z = 3) and that of Ba10Ta7.04Ti1.2O30 and on the 10H (cchcc)(2) close-packed stacking (a = 5.7981 Angstrom, c = 23.755 Angstrom, SG P6(3)/mmc, Z = 1) of BaO3 layers. The structural refinements gave the following values for the R factors for Ba8Ta4Ti3O24 (Ba10Ta7.04Ti1.2O30) R(I) = 0.041 (0.039), R(P) = 0.108 (0.118), and R(wP) = 0.094 (0.099). The main feature of both structures is the presence of two types of face-sharing octahedra (FSO) with different occupancies by Ta atoms, Ti atoms, and vacancies, which results in the formation of a superstructure. It was shown that in the Ba8Ta4Ti3O24 structure these pairs of FSO occur in an ordered fashion and in the Ba10Ta7.04Ti1.2O30 structure in a disordered fashion. The existence of the wide range of solid solutions was shown to be also a consequence of the presence of one of the two types of face-sharing octahedra. (C) 1995 Academic Press, Inc,

Abstract: Tetrahedral chain ordering in the Sr2MnGaO5 structure is studied using electron diffraction (ED) and high-resolution electron microscopy. The ED patterns show the presence of satellite reflections, which indicate a commensurately modulated structure with a = 5.4056(8) Angstrom b 16.171(3) Angstrom, c = 5.5592(7) Angstrom, q – 1/2c*, superspace group Immma(00gamma,)s00. The Superstructure arises due to ordering of the two types of symmetry related tetrahedral chains (L and R) according to a ... LRLR ... sequence, where L and R chains alternate along the c-axis within the same (GaO) layer. Numerous defects at different structural levels were observed, comprising interleaving L and R chains, violation of the ... LRLR ... chain sequence within one layer, different stacking modes of the ... LRLR ... ordered layers with subsequent alternation of blocks of different width along the h-axis of the brownmillerite subcell and island fragmentation of the modulated superstructure. By in situ heating ED experiments it is found that the long-range ordering of the tetrahedral chains is stable tip to 665degreesC and is completely suppressed at 905degreesC. (C) 2003 Elsevier Inc. All rights reserved.