“Well-organized zeolite nanocrystal aggregates with interconnected hierarchically micro-meso-macropore systems showing enhanced catalytic performance”. Yang X-Y, Tian G, Chen L-H, Li Y, Rooke JC, Wei Y-X, Liu Z-M, Deng Z, Van Tendeloo G, Su B-L, Chemistry: a European journal 17, 14987 (2011). http://doi.org/10.1002/chem.201101594
Abstract: Preparation and characterization of well-organized zeolitic nanocrystal aggregates with an interconnected hierarchically micromesomacro porous system are described. Amorphous nanoparticles in bimodal aluminosilicates were directly transformed into highly crystalline nanosized zeolites, as well as acting as scaffold template. All pores on three length scales incorporated in one solid body are interconnected with each other. These zeolitic nanocrystal aggregates with hierarchically micromesomacroporous structure were thoroughly characterized. TEM images and 29Si NMR spectra showed that the amorphous phase of the initial material had been completely replaced by nanocrystals to give a micromesomacroporous crystalline zeolitic structure. Catalytic testing demonstrated their superiority due to the highly active sites and the presence of interconnected micromesomacroporosity in the cracking of bulky 1,3,5-triisopropylbenzene (TIPB) compared to traditional zeolite catalysts. This synthesis strategy was extended to prepare various zeolitic nanocrystal aggregates (ZSM-5, Beta, TS-1, etc.) with well-organized hierarchical micromesomacroporous structures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 61
DOI: 10.1002/chem.201101594
|
|
|
“Anisotropic cation exchange in PbSe/CdSe core/shell nanocrystals of different geometry”. Casavola M, van Huis MA, Bals S, Lambert K, Hens Z, Vanmaekelbergh D, Chemistry of materials 24, 294 (2012). http://doi.org/10.1021/cm202796s
Abstract: We present a study of Cd2+-for-Pb2+ exchange in PbSe nanocrystals (NCs) with cube, star, and rod shapes. Prolonged temperature-activated cation exchange results in PbSe/CdSe heterostructured nanocrystals (HNCs) that preserve their specific overall shape, whereas the PbSe core is strongly faceted with dominance of {111} facets. Hence, cation exchange proceeds while the Se anion lattice is preserved, and well-defined {111}/{111} PbSe/CdSe interfaces develop. Interestingly, by quenching the reaction at different stages of the cation exchange new structures have been isolated, such as coreshell nanorods, CdSe rods that contain one or two separated PbSe dots and fully zinc blende CdSe nanorods. The crystallographically anisotropic cation exchange has been characterized by a combined HRTEM/HAADF-STEM study of heterointerface evolution over reaction time and temperature. Strikingly, Pb and Cd are only intermixed at the PbSe/CdSe interface. We propose a plausible model for the cation exchange based on a layer-by-layer replacement of Pb2+ by Cd2+ enabled by a vacancy-assisted cation migration mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 136
DOI: 10.1021/cm202796s
|
|
|
“Atomic scale electron vortices for nanoresearch”. Verbeeck J, Schattschneider P, Lazar S, Stöger-Pollach M, Löffler S, Steiger-Thirsfeld A, Van Tendeloo G, Applied physics letters 99, 203109 (2011). http://doi.org/10.1063/1.3662012
Abstract: Electron vortex beams were only recently discovered and their potential as a probe for magnetism in materials was shown. Here we demonstrate a method to produce electron vortex beams with a diameter of less than 1.2 Å. This unique way to prepare free electrons to a state resembling atomic orbitals is fascinating from a fundamental physics point of view and opens the road for magnetic mapping with atomic resolution in an electron microscope.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 90
DOI: 10.1063/1.3662012
|
|
|
“Electron tomography based on a total variation minimization reconstruction technique”. Goris B, van den Broek W, Batenburg KJ, Heidari Mezerji H, Bals S, Ultramicroscopy 113, 120 (2012). http://doi.org/10.1016/j.ultramic.2011.11.004
Abstract: The 3D reconstruction of a tilt series for electron tomography is mostly carried out using the weighted backprojection (WBP) algorithm or using one of the iterative algorithms such as the simultaneous iterative reconstruction technique (SIRT). However, it is known that these reconstruction algorithms cannot compensate for the missing wedge. Here, we apply a new reconstruction algorithm for electron tomography, which is based on compressive sensing. This is a field in image processing specialized in finding a sparse solution or a solution with a sparse gradient to a set of ill-posed linear equations. Therefore, it can be applied to electron tomography where the reconstructed objects often have a sparse gradient at the nanoscale. Using a combination of different simulated and experimental datasets, it is shown that missing wedge artefacts are reduced in the final reconstruction. Moreover, it seems that the reconstructed datasets have a higher fidelity and are easier to segment in comparison to reconstructions obtained by more conventional iterative algorithms.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 171
DOI: 10.1016/j.ultramic.2011.11.004
|
|
|
“Nickel/carbon composite materials based on expanded graphite”. Afanasov IM, Lebedev OI, Kolozhvary BA, Smirnov AV, Van Tendeloo G, New carbon materials 26, 335 (2011). http://doi.org/10.1016/S1872-5805(11)60085-1
Abstract: Monolithic nickel/carbon (Ni/C) composites were prepared from coal tar pitch-impregnated compressed expanded graphite pre-decorated with NiO particles (EGNiO) by pyrolysis at 550 °C and subsequent steam activation at 800 °C. The microstructural arrangement of the Ni-comprising nanoparticles in the composites was investigated using transmission electron microscopy. The specific surface area and porosity of the composites were analyzed by nitrogen adsorption. The catalytic activity of the composites was compared with the material obtained by the conventional H2 treatment of EGNiO using hydrocracking of 2,2,3-trimethylpentane as a model reaction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1016/S1872-5805(11)60085-1
|
|
|
“Depth strain profile with sub-nm resolution in a thin silicon film using medium energy ion scattering”. Jalabert D, Pelloux-Gervais D, Béché, A, Hartmann JM, Gergaud P, Rouvière JL, Canut B, Physica Status Solidi A-Applications And Materials Science 209, 265 (2012). http://doi.org/10.1002/PSSA.201127502
Abstract: The depth strain profile in silicon from the Si (001) substrate to the surface of a 2 nm thick Si/12 nm thick SiGe/bulk Si heterostructure has been determined by medium energy ion scattering (MEIS). It shows with sub-nanometer resolution and high strain sensitivity that the thin Si cap presents residual compressive strain caused by Ge diffusion coming from the fully strained SiGe layer underneath. The strain state of the SiGe buffer have been checked by X-ray diffraction (XRD) and nano-beam electron diffraction (NBED) measurements.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.775
Times cited: 3
DOI: 10.1002/PSSA.201127502
|
|
|
“Iron catalysts for the growth of carbon nanofibers : Fe, Fe3C or both?”.He Z, Maurice J-L, Gohier A, Lee CS, Pribat D, Cojocaru CS, Chemistry of materials 23, 5379 (2011). http://doi.org/10.1021/cm202315j
Abstract: Iron is a widely used catalyst for the growth of carbon nanotubes (CNTs) or carbon nanofibers (CNFs) by catalytic chemical vapor deposition. However, both Fe and FeC compounds (generally, Fe3C) have been found to catalyze the growth of CNTs/CNFs, and a comparison study of their respective catalytic activities is still missing. Furthermore, the control of the crystal structure of iron-based catalysts, that is α-Fe or Fe3C, is still a challenge, which not only obscures our understanding of the growth mechanisms of CNTs/CNFs, but also complicates subsequent procedures, such as the removal of catalysts for better industrial applications. Here, we show a partial control of the phase of iron catalysts (α-Fe or Fe3C), obtained by varying the growth temperatures during the synthesis of carbon-based nanofibers/nanotubes in a plasma-enhanced chemical vapor deposition reactor. We also show that the structure of CNFs originating from Fe3C is bamboo-type, while that of CNFs originating from Fe is not. Moreover, we directly compare the growth rates of carbon-based nanofibers/nanotubes during the same experiments and find that CNFs/CNTs grown by α-Fe nanoparticles are longer than CNFs grown from Fe3C nanoparticles. The influence of the type of catalyst on the growth of CNFs is analyzed and the corresponding possible growth mechanisms, based on the different phases of the catalysts, are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 91
DOI: 10.1021/cm202315j
|
|
|
“Recent EM investigations on nano-and micro-defect structures in SMAs”. Schryvers D, Cao S, Pourbabak, Shi H, Lu, Journal of alloys and compounds 577, S705 (2013). http://doi.org/10.1016/j.jallcom.2011.10.112
Abstract: The present contribution reviews some recent electron microscopy investigations on different shape memory systems in which a variety of nano- and micro-defect structures play an essential role in the functional behaviour of the material. (NiTi3)-Ti-4 precipitates in Ni-Ti are a well-known example for which the focus is now on the 3D configurations, in Ni-Ti-Nb Nb-rich nanoprecipitates are thought to have a large impact on the hysteresis, in Co-Ni-Al an Al-enriched zone nearby the y'-precipitates yields a small sandwiched austenite while some first signs of quasidynamical lattice deformation in non-frozen Ni-Ti strain glass are measured by Cs-aberration-corrected transmission electron microscopy. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 7
DOI: 10.1016/j.jallcom.2011.10.112
|
|
|
“The reduction of the substitutional C content in annealed Si/SiGeC superlattices studied by dark-field electron holography”. Denneulin T, Rouvière JL, Béché, A, Py M, Barnes JP, Rochat N, Hartmann JM, Cooper D, Semiconductor science and technology 26, 1 (2011). http://doi.org/10.1088/0268-1242/26/12/125010
Abstract: Si/Si(1 − x − y)GexCy superlattices are used in the construction of new microelectronic architectures such as multichannel transistors. The introduction of carbon in SiGe allows for compensation of the strain and to avoid plastic relaxation. However, the formation of incoherent β-SiC clusters during annealing limits the processability of SiGeC. This precipitation leads to a modification of the strain in the alloy due to the reduction of the substitutional carbon content. Here, we investigated the strain in annealed Si/Si0.744Ge0.244C0.012 superlattices grown by reduced pressure chemical vapour deposition using dark-field electron holography. The variation of the substitutional C content was calculated by correlating the results with finite-element simulations. The obtained values were then compared with Fourier-transformed infrared spectrometry measurements. It was shown that after annealing for 2 min at 1050 °C carbon no longer has any influence on strain in the superlattice, which behaves like pure SiGe. However, a significant proportion of substitutional C atoms remain in a third-nearest neighbour (3nn) configuration. It was deduced that the influence of 3nn C on strain is negligible and that only isolated atoms have a significant contribution. It was also proposed that the 3nn configuration is an intermediary step during the formation of SiC clusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.305
DOI: 10.1088/0268-1242/26/12/125010
|
|
|
“Imaging from atomic structure to electronic structure”. Xu Q, Zandbergen HW, van Dyck D, Micron 43, 524 (2012). http://doi.org/10.1016/j.micron.2011.10.024
Abstract: This paper discusses the possibility of retrieving the electron distribution (with highlighted valence electron distribution information) of materials from recorded HREM images. This process can be achieved by solving two inverse problems: reconstruction of the exit wave and reconstruction of the electron distribution from exit waves. The first inverse problem can be solved using a focal series reconstruction method. We show that the second inverse problem can be solved by combining a series of exit waves recorded at different thickness conditions. This process is designed based on an improved understanding of the dynamical scattering process. It also explains the fundamental difficulty of obtaining the valence electron distribution information and the basis of our solution.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.98
DOI: 10.1016/j.micron.2011.10.024
|
|
|
“F-doped Co3O4 photocatalysts for sustainable H2 generation from water/ethanol”. Gasparotto A, Barreca D, Bekermann D, Devi A, Fischer RA, Fornasiero P, Gombac V, Lebedev OI, Maccato C, Montini T, Van Tendeloo G, Tondello E, Journal of the American Chemical Society 133, 19362 (2011). http://doi.org/10.1021/ja210078d
Abstract: p-Type Co3O4 nanostructured films are synthesized by a plasma-assisted process and tested in the photocatalytic production of H2 from water/ethanol solutions under both near-UV and solar irradiation. It is demonstrated that the introduction of fluorine into p-type Co3O4 results in a remarkable performance improvement with respect to the corresponding undoped oxide, highlighting F-doped Co3O4 films as highly promising systems for hydrogen generation. Notably, the obtained yields were among the best ever reported for similar semiconductor-based photocatalytic processes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 114
DOI: 10.1021/ja210078d
|
|
|
“Model-based electron microscopy : from images toward precise numbers for unknown structure parameters”. Van Aert S, van den Broek W, Goos P, van Dyck D, Micron 43, 509 (2012). http://doi.org/10.1016/j.micron.2011.10.019
Abstract: Statistical parameter estimation theory is proposed as a method to quantify electron microscopy images. It aims at obtaining precise and accurate values for the unknown structure parameters including, for example, atomic column positions and types. In this theory, observations are purely considered as data planes, from which structure parameters have to be determined using a parametric model describing the images. The method enables us to measure positions of atomic columns with a precision of the order of a few picometers even though the resolution of the electron microscope is one or two orders of magnitude larger. Moreover, small differences in averaged atomic number, which cannot be distinguished visually, can be quantified using high-angle annular dark field scanning transmission electron microscopy images. Finally, it is shown how to optimize the experimental design so as to attain the highest precision. As an example, the optimization of the probe size for nanoparticle radius measurements is considered. It is also shown how to quantitatively balance signal-to-noise ratio and resolution by adjusting the probe size.
Keywords: A1 Journal article; Engineering Management (ENM); Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.98
Times cited: 7
DOI: 10.1016/j.micron.2011.10.019
|
|
|
“A new way of producing electron vortex probes for STEM”. Verbeeck J, Tian H, Béché, A, Ultramicroscopy 113, 83 (2012). http://doi.org/10.1016/j.ultramic.2011.10.008
Abstract: A spiral holographic aperture is used in the condensor plane of a scanning transmission electron microscope to produce a focussed electron vortex probe carrying a topological charge of either −1, 0 or +1. The spiral aperture design has a major advantage over the previously used forked aperture in that the three beams with topological charge m=−1, 0, and 1 are not side by side in the specimen plane, but rather on top of each other, focussed at different heights. This allows us to have only one selected beam in focus on the sample while the others contribute only to a background signal. In this paper we describe the working principle as well as first experimental results demonstrating atomic resolution HAADF STEM images obtained with electron vortex probes. These results pave the way for atomic resolution magnetic information when combined with electron energy loss spectroscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 62
DOI: 10.1016/j.ultramic.2011.10.008
|
|
|
“Point defect clusters and dislocations in FIB irradiated nanocrystalline aluminum films : an electron tomography and aberration-corrected high-resolution ADF-STEM study”. Idrissi H, Turner S, Mitsuhara M, Wang B, Hata S, Coulombier M, Raskin J-P, Pardoen T, Van Tendeloo G, Schryvers D, Microscopy and microanalysis 17, 983 (2011). http://doi.org/10.1017/S143192761101213X
Abstract: Focused ion beam (FIB) induced damage in nanocrystalline Al thin films has been characterized using advanced transmission electron microscopy techniques. Electron tomography was used to analyze the three-dimensional distribution of point defect clusters induced by FIB milling, as well as their interaction with preexisting dislocations generated by internal stresses in the Al films. The atomic structure of interstitial Frank loops induced by irradiation, as well as the core structure of Frank dislocations, has been resolved with aberration-corrected high-resolution annular dark-field scanning TEM. The combination of both techniques constitutes a powerful tool for the study of the intrinsic structural properties of point defect clusters as well as the interaction of these defects with preexisting or deformation dislocations in irradiated bulk or nanostructured materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 25
DOI: 10.1017/S143192761101213X
|
|
|
“Two-fold emission from the S-shell of PbSe/CdSe core/shell quantum dots”. Grodzińska D, Evers WH, Dorland R, van Rijssel J, van Huis MA, Meijerink A, de Mello Donegá, C, Vanmaekelbergh D, Small 7, 3493 (2011). http://doi.org/10.1002/smll.201101819
Abstract: The optical properties of PbSe/CdSe core/shell quantum dots with core sizes smaller than 4 nm in the 5300 K range are reported. The photoluminescence spectra show two peaks, which become increasingly separated in energy as the core diameter is reduced below 4 nm. It is shown that these peaks are due to intrinsic exciton transitions in each quantum dot, rather than emission from different quantum dot sub-ensembles. Most likely, the energy separation between the peaks is due to inter-valley coupling between the L-points of PbSe. The temperature dependence of the relative intensities of the peaks implies that the two emitting states are not in thermal equilibrium and that dark exciton states must play an important role.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 23
DOI: 10.1002/smll.201101819
|
|
|
“Synthesis, crystal structure and physico-chemical properties of the new quaternary oxide Sr5BiNi2O9.6”. Novitskaya M, Makhnach L, Ivashkevich L, Pankov V, Klein H, Regeau A, David J, Gemmi M, Hadermann J, Strobel P, Journal of solid state chemistry 184, 3262 (2011). http://doi.org/10.1016/j.jssc.2011.10.020
Abstract: A new black quaternary oxide Sr5BiNi2O9.6 was synthesized by solid state reaction at 1200 °C. Its structure was solved by electron crystallography and X-ray powder refinement, yielding a tetragonal structure with space group I4/mmm, a=5.3637 (2) Å, c=17.5541(5) Å, Z=4. The structure can be described as a stacking of (Bi,Sr)O rocksalt slabs and SrNiO3−δ perovskite slabs. The initial nickel valence is close to +3.1. Thermogravimetry and high-temperature oxygen coulometry showed that this compound has variable oxygen content as a function of temperature and oxygen pressure, and ultimately decomposes when heated in low oxygen pressure above 800 °C. It is a metallic conductor with n-type conduction. Its thermoelectric power was determined and found to be −20 and −38 μV/K at 300 and 650 °C, respectively. Magnetic measurements confirm the nickel valence close to +3 and show evidence of magnetic ordering at 20 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 4
DOI: 10.1016/j.jssc.2011.10.020
|
|
|
“Effect of heat-treatment on luminescence and structure of Ag nanoclusters doped oxyfluoride glasses and implication for fiber drawing”. Kuznetsov AS, Cuong NT, Tikhomirov VK, Jivanescu M, Stesmans A, Chibotaru LF, Velázquez JJ, Rodríguez VD, Kirilenko D, Van Tendeloo G, Moshchalkov VV, Optical materials 34, 616 (2012). http://doi.org/10.1016/j.optmat.2011.09.007
Abstract: The effect of heat treatment on the structure and luminescence of Ag nanoclusters doped oxyfluoride glasses was studied and the implication for drawing the corresponding fibers doped with luminescent Ag nanoclusters has been proposed. The heat treatment results, first, in condensation of the Ag nanoclusters into larger Ag nanoparticles and loss of Ag luminescence, and further heat treatment results in precipitation of a luminescent-loss nano- and microcrystalline Ag phases onto the surface of the glass. Thus, the oxyfluoride fiber doped with luminescent Ag nanoclusters was pulled from the viscous glass melt and its attenuation loss was 0.19 dB/cm in the red part of the spectrum; i.e. near to the maximum of Ag nanoclusters luminescence band. The nucleation centers for the Ag nanoclusters in oxyfluoride glasses have been suggested to be the fluorine vacancies and their nanoclusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.238
Times cited: 25
DOI: 10.1016/j.optmat.2011.09.007
|
|
|
“Mn(I) in an extended oxide : the synthesis and characterization of La1-xCaxMnO2+\delta (0.6\leq x\leq1)”. Dixon E, Hadermann J, Ramos S, Goodwin AL, Hayward MA, Journal of the American Chemical Society 133, 18397 (2011). http://doi.org/10.1021/ja207616c
Abstract: Reduction of La1xCaxMnO3 (0.6 ≤ x ≤ 1) perovskite phases with sodium hydride yields materials of composition La1xCaxMnO2+δ. The calcium-rich phases (x = 0.9, 1) adopt (La0.9Ca0.1)0.5Mn0.5O disordered rocksalt structures. However local structure analysis using reverse Monte Carlo refinement of models against pair distribution functions obtained from neutron total scattering data reveals lanthanum-rich La1xCaxMnO2+δ (x = 0.6, 0.67, 0.7) phases adopt disordered structures consisting of an intergrowth of sheets of MnO6 octahedra and sheets of MnO4 tetrahedra. X-ray absorption data confirm the presence of Mn(I) centers in La1xCaxMnO2+δ phases with x < 1. Low-temperature neutron diffraction data reveal La1xCaxMnO2+δ (x = 0.6, 0.67, 0.7) phases become antiferromagnetically ordered at low temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 33
DOI: 10.1021/ja207616c
|
|
|
“Plasma-assisted synthesis of Ag/ZnO nanocomposites : first example of photo-induced H2 production and sensing”. Simon Q, Barreca D, Bekermann D, Gasparotto A, Maccato C, Comini E, Gombac V, Fornasiero P, Lebedev OI, Turner S, Devi A, Fischer RA, Van Tendeloo G, International journal of hydrogen energy 36, 15527 (2011). http://doi.org/10.1016/j.ijhydene.2011.09.045
Abstract: Ag/ZnO nanocomposites were developed by a plasma-assisted approach. The adopted strategy exploits the advantages of Plasma Enhanced-Chemical Vapor Deposition (PE-CVD) for the growth of columnar ZnO arrays on Si(100) and Al2O3 substrates, in synergy with the infiltration power of the Radio Frequency (RF)-sputtering technique for the subsequent dispersion of different amounts of Ag nanoparticles (NPs). The resulting composites, both as-prepared and after annealing in air, were thoroughly characterized with particular attention on their morphological organization, structure and composition. For the first time, the above systems have been used as catalysts in the production of hydrogen by photo-reforming of alcoholic solutions, yielding a stable H2 evolution even by the sole use of simulated solar radiation. In addition, Ag/ZnO nanocomposites presented an excellent response in the gas-phase detection of H2, opening attractive perspectives for advanced technological applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.582
Times cited: 62
DOI: 10.1016/j.ijhydene.2011.09.045
|
|
|
“Letter Chemical transformation of Au-tipped CdS nanorods into AuS/Cd core/shell particles by electron beam irradiation”. van Huis MA, Figuerola A, Fang C, Béché, A, Zandbergen HW, Manna L, Nano letters 11, 4555 (2011). http://doi.org/10.1021/nl2030823
Abstract: We demonstrate that electron irradiation of colloidal CdS nanorods carrying Au domains causes their evolution into AuS/Cd core/shell nanoparticles as a result of a concurrent chemical and morphological transformation. The shrinkage of the CdS nanorods and the growth of the Cd shell around the Au tips are imaged in real time, while the displacement of S atoms from the CdS nanorod to the Au domains is evidenced by high-sensitivity energy-dispersive X-ray (EDX) spectroscopy. The various nanodomains display different susceptibility to the irradiation, which results in nanoconfigurations that are very different from those obtained after thermal annealing. Such physical manipulations of colloidal nanocrystals can be exploited as a tool to access novel nanocrystal heterostructures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 25
DOI: 10.1021/nl2030823
|
|
|
“Smart heating profiles for the synthesis of benzene bridged periodic mesoporous organosilicas”. Smeulders G, van Oers C, Van Havenbergh K, Houthoofd K, Mertens M, Martens JA, Bals S, Maes BUW, Meynen V, Cool P, Chemical engineering journal 175, 585 (2011). http://doi.org/10.1016/j.cej.2011.09.116
Abstract: In this study the effects of the heating rate and heating time on the formation of crystal-like benzene bridged periodic mesoporous organosilicas (PMOs) are investigated. The time needed to heat up an autoclave during the hydrothermal treatment has shown to be crucial in the synthesis of PMOs, while the total duration of heating gave rise to only minor differences. By choosing a smart heating profile, superior PMO materials can be obtained in a short time. Different heating profiles in a range from one minute to one hour are adopted by microwave equipment and compared with conventional heating methods. The heating rate has a large influence on the porosity characteristics and the uniformity of the obtained particles. Moreover, two new alternative synthetic strategies to adopt the smart heating profile are presented, in order to give some possible solutions for the expensive microwave equipment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Impact Factor: 6.216
Times cited: 7
DOI: 10.1016/j.cej.2011.09.116
|
|
|
“Ultra-high resolution electron tomography for materials science : a roadmap”. Batenburg KJ, Bals S, Van Aert S, Roelandts T, Sijbers J, Microscopy and microanalysis 17, 934 (2011). http://doi.org/10.1017/S143192761100554X
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.891
DOI: 10.1017/S143192761100554X
|
|
|
“Field mapping with nanometer-scale resolution for the next generation of electronic devices”. Cooper D, de la Peña F, Béché, A, Rouvière J-L, Servanton G, Pantel R, Morin P, Nano letters 11, 4585 (2011). http://doi.org/10.1021/NL201813W
Abstract: In order to improve the performance of todays nanoscaled semiconductor devices, characterization techniques that can provide information about the position and activity of dopant atoms and the strain fields are essential. Here we demonstrate that by using a modern transmission electron microscope it is possible to apply multiple techniques to advanced materials systems in order to provide information about the structure, fields, and composition with nanometer-scale resolution. Off-axis electron holography has been used to map the active dopant potentials in state-of-the-art semiconductor devices with 1 nm resolution. These dopant maps have been compared to electron energy loss spectroscopy maps that show the positions of the dopant atoms. The strain fields in the devices have been measured by both dark field electron holography and nanobeam electron diffraction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 12
DOI: 10.1021/NL201813W
|
|
|
“Atomic oxygen functionalization of vertically aligned carbon nanotubes”. Bittencourt C, Navio C, Nicolay A, Ruelle B, Godfroid T, Snyders R, Colomer J-F, Lagos MJ, Ke X, Van Tendeloo G, Suarez-Martinez I, Ewels CP, The journal of physical chemistry: C : nanomaterials and interfaces 115, 20412 (2011). http://doi.org/10.1021/jp2057699
Abstract: Vertically aligned multiwalled carbon nanotubes (v-MWCNTs) are functionalized using atomic oxygen generated in a microwave plasma. X-ray photoelectron spectroscopy depth profile analysis shows that the plasma treatment effectively grafts oxygen exclusively at the v-MWCNT tips. Electron microscopy shows that neither the vertical alignment nor the structure of v-MWCNTs were affected by the plasma treatment. Density functional calculations suggest assignment of XPS C 1s peaks at 286.6 and 287.5 eV, to epoxy and carbonyl functional groups, respectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 31
DOI: 10.1021/jp2057699
|
|
|
“Pb2.85Ba2.15Fe4SnO13 : a new member of the AnBnO3n-2 anion-deficient perovskite-based homologous series”. Korneychik OE, Batuk M, Abakumov AM, Hadermann J, Rozova MG, Sheptyakov DV, Pokholok KV, Filimonov DS, Antipov EV, Journal of solid state chemistry 184, 3150 (2011). http://doi.org/10.1016/j.jssc.2011.09.029
Abstract: Pb2.85Ba2.15Fe4SnO13, a new n=5 member of the anion-deficient perovskite based AnBnO3n−2 (A=Pb, Ba, B=Fe, Sn) homologous series, was synthesized by the solid state method. The crystal structure of Pb2.85Ba2.15Fe4SnO13 was investigated using a combination of neutron powder diffraction, electron diffraction, high angle annular dark field scanning transmission electron microscopy and Mössbauer spectroscopy. It crystallizes in the Ammm space group with unit cell parameters a=5.7990(1) Å, b=4.04293(7) Å and c=26.9561(5) Å. The Pb2.85Ba2.15Fe4SnO13 structure consists of quasi two-dimensional perovskite blocks separated by 1/2[110](1̄01)p crystallographic shear (CS) planes. The corner-sharing FeO6 octahedra at the CS planes are transformed into edge-sharing FeO5 distorted tetragonal pyramids. The octahedral positions in the perovskite blocks between the CS planes are jointly taken up by Fe and Sn, with a preference of Sn towards the position at the center of the perovskite block. The chains of FeO5 pyramids and (Fe,Sn)O6 octahedra of the perovskite blocks delimit six-sided tunnels at the CS planes occupied by double chains of Pb atoms. The compound is antiferromagnetically ordered below TN=368±15 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 7
DOI: 10.1016/j.jssc.2011.09.029
|
|
|
“Article Structure and magnetic properties of BiFe0.75Mn0.25O3 perovskite prepared at ambient and high pressure”. Belik AA, Abakumov AM, Tsirlin AA, Hadermann J, Kim J, Van Tendeloo G, Takayama-Muromachi E, Chemistry of materials 23, 4505 (2011). http://doi.org/10.1021/cm201774y
Abstract: Solid solutions of BiFe1xMnxO3 (0.0 ≤ x ≤ 0.4) were prepared at ambient pressure and at 6 GPa. The ambient-pressure (AP) phases crystallize in space group R3c similarly to BiFeO3. The high-pressure (HP) phases crystallize in space group R3c for x = 0.05 and in space group Pnma for 0.15 ≤ x ≤ 0.4. The structure of HP-BiFe0.75Mn0.25O3 was investigated using synchrotron X-ray powder diffraction, electron diffraction, and transmission electron microscopy. HP-BiFe0.75Mn0.25O3 has a PbZrO3-related √2ap × 4ap × 2√2ap (ap is the parameter of the cubic perovskite subcell) superstructure with a = 5.60125(9) Å, b = 15.6610(2) Å, and c = 11.2515(2) Å similar to that of Bi0.82La0.18FeO3. A remarkable feature of this structure is the unconventional octahedral tilt system, with the primary ab0a tilt superimposed on pairwise clockwise and counterclockwise rotations around the b-axis according to the oioi sequence (o stands for out-of-phase tilt, and i stands for in-phase tilt). The (FeMn)O6 octahedra are distorted, with one longer metaloxygen bond (2.222.23 Å) that can be attributed to a compensation for covalent BiO bonding. Such bonding results in the localization of the lone electron pair on Bi3+ cations, as confirmed by electron localization function analysis. The relationship between HP-BiFe0.75Mn0.25O3 and antiferroelectric structures of PbZrO3 and NaNbO3 is discussed. On heating in air, HP-BiFe0.75Mn0.25O3 irreversibly transforms to AP-BiFe0.75Mn0.25O3 starting from about 600 K. Both AP and HP phases undergo an antiferromagnetic ordering at TN ≈ 485 and 520 K, respectively, and develop a weak net magnetic moment at low temperatures. Additionally, ceramic samples of AP-BiFe0.75Mn0.25O3 show a peculiar phenomenon of magnetization reversal.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 57
DOI: 10.1021/cm201774y
|
|
|
“Characterization of NbC and (Nb, Ti)N nanoprecipitates in TRIP assisted multiphase steels”. Tirumalasetty GK, van Huis MA, Fang CM, Xu Q, Tichelaar FD, Hanlon DN, Sietsma J, Zandbergen HW, Acta materialia 59, 7406 (2011). http://doi.org/10.1016/j.actamat.2011.08.012
Abstract: Multiphase steels utilising composite strengthening may be further strengthened via grain refinement or precipitation by the addition of microalloying elements. In this study a Nb microalloyed steel comprising martensite, bainite and retained austenite has been studied. By means of transmission electron microscopy (TEM) we have investigated the size distribution and the structural properties of (Nb, Ti)N and NbC precipitates, their occurrence in the various steel phases, and their relationship with the Fe matrix. (Nb, Ti)N precipitates were found in ferrite, martensite, and bainite, while NbC precipitates were found only in ferrite. All NbC precipitates were found to be small (520 nm in size) and to have a face centred cubic (fcc) crystal structure with lattice parameter a = 4.36 ± 0.05 Å. In contrast, the (Nb, Ti)N precipitates were found to have a broader size range (5150 nm) and to have a fcc crystal structure with lattice parameter a = 8.09 ± 0.05 Å. While the NbC precipitates were found to be randomly oriented, the (Nb, Ti)N precipitates have a well-defined NishiyamaWasserman orientation relationship with the ferrite matrix. An analysis of the lattice mismatch suggests that the latter precipitates have a high potential for effective strengthening. Density functional theory calculations were performed for various stoichiometries of NbCx and NbxTiyNz phases and the comparison with experimental data indicates that both the carbides and nitrides are deficient in C and N content.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 58
DOI: 10.1016/j.actamat.2011.08.012
|
|
|
“Resistive switching at manganite/manganite interfaces”. Kalkert C, Krisponeit J-O, Esseling M, Lebedev OI, Moshnyaga V, Damaschke B, Van Tendeloo G, Samwer K, Applied physics letters 99, 132512 (2011). http://doi.org/10.1063/1.3643425
Abstract: We report bipolar resistive switching between the interfaces of manganite nanocolumns. La0.7Sr0.3MnO3 films were prepared on Al2O3 substrates, where the films grow in nanocolumns from the substrate to the surface. Conductive atomic force microscopy directly detects that the resistive switching is located at the boundaries of the grains. Furthermore, mesoscopic transport measurements reveal a tunnel magnetoresistance. In combination with the resistive switching, this leads to a total of four different resistive states.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 10
DOI: 10.1063/1.3643425
|
|
|
“A cyclic catalyst pretreatment in CO2 for high yield production of Carbon nanofibers with narrow diameter distribution”. Corthals S, van Noyen J, Liang D, Ke X, Van Tendeloo G, Jacobs P, Sels B, Catalysis letters 141, 1621 (2011). http://doi.org/10.1007/s10562-011-0690-3
Abstract: This paper presents a cyclic catalyst pretreatment process to improve the CNF yield with narrow size distribution by sequentially feeding the CVD reactor with CH4/CO2 mixtures (carbon deposition) and CO2 (carbon removal) prior to the actual growth process. A mechanism based on a break-up of large Ni particles tentatively explains the beneficial effect of the cyclic carbon deposition/removal CVD procedure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.799
Times cited: 1
DOI: 10.1007/s10562-011-0690-3
|
|
|
“Unity quantum yield of photogenerated charges and band-like transport in quantum-dot solids”. Talgorn E, Gao Y, Aerts M, Kunneman LT, Schins JM, Savenije TJ, van Huis MA, van der Zant HSJ, Houtepen AJ, Siebbeles LDA, Nature nanotechnology 6, 733 (2011). http://doi.org/10.1038/NNANO.2011.159
Abstract: Solid films of colloidal quantum dots show promise in the manufacture of photodetectors and solar cells. These devices require high yields of photogenerated charges and high carrier mobilities, which are difficult to achieve in quantum-dot films owing to a strong electronhole interaction and quantum confinement. Here, we show that the quantum yield of photogenerated charges in strongly coupled PbSe quantum-dot films is unity over a large temperature range. At high photoexcitation density, a transition takes place from hopping between localized states to band-like transport. These strongly coupled quantum-dot films have electrical properties that approach those of crystalline bulk semiconductors, while retaining the size tunability and cheap processing properties of colloidal quantum dots.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 38.986
Times cited: 129
DOI: 10.1038/NNANO.2011.159
|
|