Abstract: YCuO2 delafossite crystallizes into two stacking variants; hexagonal 2H or rhombohedral 3R, depending on the preparation conditions. The structure of the fully oxygenated material YCuO2.50 has been determined as orthorhombic (a(O) = 6.1961 Angstrom; b(O) = 11.2158 Angstrom; c(O) = 7.1505 Angstrom; space group Pnma). The structure is based on the hexagonal 2H structure (a(O) = a(H)root3; b(O) = c(H); c(O) = 2a(H)). Upon incomplete oxidation, a different YCuOZ phase with ideal composition YCuO2.33 and lattice parameters a(H root)3, a(H)root3, c(H) is also formed. Diffraction patterns are often very complex because of the presence of planar defects and intergrowth of both phases. Under electron beam irradiation, oxygen is released from the structure and one phase gradually transforms into the other. (C) 2001 Academic Press.

Abstract: The morphology and structure of hexagonal graphitic BN (h-BN) powders with graphitization indices GI <5, used as precursors for the synthesis of cubic BN (c-BN) crystals, has been investigated by transmission electron microscopy in diffraction contrast and high resolution. We show that besides the GI, which is a general parameter for controlling the structural quality of h-EN ponders, some other microstructural features strongly influence the synthesis of c-BN. In our opinion, the high reactivity of some h-BN powders results from the presence of some nucleation centers for c-BN, observed at the edges of the h-BN particles. They are formed by a rearrangement of the graphitic (0002) planes by bending back, joining in pairs and forming locally nanoarches (half nanotubes). In these particular places, the nature of bonding locally turns towards sp(3), as in the case of c-BN, (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: Infrared absorption spectra of polyhedral and platelet oxygen precipitates are analyzed using a modified Day-Thorpe approach (J. Phys.: Condens. Matter 11 (1999) 2551). The aspect ratio has been determined by TEM measurements. The reduced spectral function and the stoichiometry are extracted from the absorption spectra and the concentration of precipitated interstitial oxygen. One set of spectra reveal a Frohlich frequency around 1100 cm(-1) and another around 1110-1120 cm(-1). It is shown that the shift in the Frohlich frequency is not due to a different stoichiometry, but due to the detailed structure in the reduced spectral function. The oxygen precipitates consist of SiO. with gammaapproximate to1.1-1.2+/-0.1. (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: The problem of the epitaxial growth of the high temperature superconducting R1+xBa2xCu3O7δ (R = Y or rare earth except Ce and Tb) films has been addressed. Using in situ ultra high vacuum Scanning Tunneling Microscopy (UHV-STM) we have studied the role of cationic substitution and substrate mismatch on the growth mode of stoichiometric and Nd-rich Nd1+xBa2xCu3O7δ thin films. The results are compared to the growth of Y1Ba2Cu3O7δ, Dy1Ba2Cu3O7δ and Gd1Ba2Cu3O7δ epitaxial films. Two main phenomena are investigated: a) the first stage of the direct nucleation on the substrate and b) the crossover between 2D and 3D growth upon increasing the film thickness. At the first stage of the growth, pseudo-cubic perovskite (Re,Ba)CuO3 nuclei are formed. While they disappear after the growth of a few nm in stoichiometric films, they persist on the surface of Nd-rich films of up to 110 nm thickness. Stoichiometric R1+xBa2xCu3O7δ films exhibit a rough morphology with increasing thickness due to island growth mode, whereas Nd-rich films remain smooth and continue to grow layer by layer. It is proposed that linear defects (like anti-phase boundaries), which are formed due to the misalignment of growth fronts, are the source of screw dislocations in stoichiometric films. In Nd-rich films, linear defects are eliminated through the insertion of (Nd,Ba)CuO3 extra layers without introduction of any screw dislocations.