Abstract: Over the past years a number of studies have described the instability of the pigment cadmium yellow (CdS). In a previous paper we have shown how cadmium sulfide on paintings by James Ensor oxidizes to CdSO4 center dot H2O. The degradation process gives rise to the fading of the bright yellow color and the formation of disfiguring white crystals that are present on the paint surface in approximately 50 mu m sized globular agglomerations. Here, we study cadmium yellow in the painting “Flowers in a blue vase” by Vincent van Gogh. This painting differs from the Ensor case in the fact that (a) a varnish was superimposed onto the degraded paint surface and (b) the CdS paint area is entirely covered with an opaque crust. The latter obscures the yellow color completely and thus presents a seemingly more advanced state of degradation. Analysis of a cross-sectioned and a crushed sample by combining scanning microscopic X-ray diffraction (mu-XRD), microscopic X-ray absorption near-edge spectroscopy (mu-XANES), microscopic X-ray fluorescence (mu-XRF) based chemical state mapping and scanning microscopic Fourier transform infrared (mu-FT-IR) spectrometry allowed unravelling the complex alteration pathway. Although no crystalline CdSO4 compounds were identified on the Van Gogh paint samples, we conclude that the observed degradation was initially caused by oxidation of the original CdS pigment, similar as for the previous Ensor case. However, due to the presence of an overlying varnish containing lead-based driers and oxalate ions, secondary reactions took place. In particular, it appears that upon the photoinduced oxidation of its sulfidic counterion, the Cd2+ ions reprecipitated at the paint/varnish interface after having formed a complex with oxalate ions that themselves are considered to be degradation products of the resin and/or oil in the varnish. The SO42- anions, for their part, found a suitable reaction partner in Pb2+ ions stemming from a dissolved lead-based siccative that was added to the varnish to promote its drying. The resulting opaque anglesite compound in the varnish, in combination with the underlying CdC2O4 layer at the paint/varnish interface, account for the orange-gray crust that is disfiguring the painting on a macroscopic level. In this way, the results presented in this paper demonstrate how, through a judicious combined use of several microanalytical methods with speciation capabilities, many new insights can be obtained from two minute, but highly complex and heterogeneous paint samples.

Abstract: A hundred 18th-century glass fragments were recovered at the Clairefontaine monastery in the Belgian province of Luxembourg. They were analysed by a combination of SEM-EDX and LA-ICP-MS in order to determine their major composition as well as their trace element signature. Multivariate statistical methods such as hierarchical clustering and principal component analysis were used to divide the glass fragments into four main groups: potassium-rich glass, sodium-rich glass, potassium/lime-rich glass and high-lime-low-alkali glass. Within every group, not only a similarity in composition is observed, but also in colour, morphology and deterioration patterns. Potash glass fragments are the most abundant and show extensive deterioration; two classes of potash glass were identified: one similar to certain Central European glass compositions, while the other one, characterised by large variations in potash: lime ratio, may be attributed to local (regional) glass production. (C) 2014 Elsevier Ltd. All rights reserved.

Abstract: A set of ca. 500 window glass fragments originating from different historical sites in Belgium and covering the period 12(th)- 18(th) century was analyzed by rneans of electron probe microanalysis. Most samples are archaeological finds deriving from non-figurative windows in secular buildings. However. the analyzed set also contains glass sampled from still existing non-figurative windows in secular buildings and stained-glass windows in religious buildings. A sudden compositional change at the end of the 14(th) century can be noticed among the series of glass compositions that were obtained. These changes could be related to the use of different glassmaker recipes and to the introduction of new raw materials for glass making. (c) 2007 Elsevier B.V All rights reserved.

Abstract: Focused narrow-band beam of the synchrotron radiation was used for in-depth analysis of historic and modern paint layers. The fluorescent radiation induced by 21 keV impact radiation was detected by a Si(Li) detector equipped with a polycapillary X-ray lens in con-focal geometry. Scanning of the sample was performed by a motorized xyz stage. Space resolution of 30 ìm was achieved. The procedure of evaluation of concentrations was based on the independent parameter method and included absorption of radiation in the outer layers and secondary fluorescence enhancement induced by hard X-rays of the same and neighboring layers.

Abstract: Combined mu-XRF, mu-XAFS, and mu-XRD investigations of a uranium-rich tertiary sediment, from a nuclear repository natural analogue site, and a fractured granite bore core section after a column tracer experiment using a Np(V) containing cocktail have been performed. Most mu-XRF/mu-XAFS measurements are recorded in a confocal geometry to provide added depth information. The U-rich sediment results show uranium to be present as a tetravalent phosphate and that U(IV) is associated with As(V). Arsenic present is either As(V) or As(0). The As(0) form thin coatings on the surface of pyrite nodules. A hypothesis for the mechanism of uranium immobilization is proposed, where arsenopyrite acted as reductant of ground water dissolved U(VI) leading to precipitation of less soluble U(IV) and thereby forming As(V). Results for the granite sample show the immobilized Np to be tetravalent and associated with facture material.