“Synthesis of a 3D network of Pt nanowires by atomic layer deposition on a carbonaceous template”. Deng S, Kurttepeli M, Deheryan S, Cott DJ, Vereecken PM, Martens JA, Bals S, Van Tendeloo G, Detavernier C, Nanoscale 6, 6939 (2014). http://doi.org/10.1039/c4nr00982g
Abstract: The formation of a 3D network composed of free standing and interconnected Pt nanowires is achieved by a two-step method, consisting of conformal deposition of Pt by atomic layer deposition (ALD) on a forest of carbon nanotubes and subsequent removal of the carbonaceous template. Detailed characterization of this novel 3D nanostructure was carried out by transmission electron microscopy (TEM) and electrochemical impedance spectroscopy (EIS). The characterization showed that this pure 3D nanostructure of platinum is self-supported and offers an enhancement of the electrochemically active surface area by a factor of 50.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 14
DOI: 10.1039/c4nr00982g
|
“Synthesis of uniformly dispersed anatase nanoparticles inside mesoporous silica thin films via controlled breakup and crystallization of amorphous TiO2 deposited using atomic layer deposition”. Sree SP, Dendooven J, Masschaele K, Hamed HM, Deng S, Bals S, Detavernier C, Martens JA, Nanoscale 5, 5001 (2013). http://doi.org/10.1039/c3nr00594a
Abstract: Amorphous titanium dioxide was introduced into the pores of mesoporous silica thin films with 75% porosity and 12 nm average pore diameter via Atomic Layer Deposition (ALD) using alternating pulses of tetrakis(dimethylamino)titanium and water. Calcination provoked fragmentation of the deposited amorphous TiO2 phase and its crystallization into anatase nanoparticles inside the nanoporous film. The narrow particle size distribution of 4 ± 2 nm and the uniform dispersion of the particles over the mesoporous silica support were uniquely revealed using electron tomography. These anatase nanoparticle bearing films showed photocatalytic activity in methylene blue degradation. This new synthesis procedure of the anatase nanophase in mesoporous silica films using ALD is a convenient fabrication method of photocatalytic coatings amenable to application on very small as well as very large surfaces
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 22
DOI: 10.1039/c3nr00594a
|
“Thermodynamics at the nanoscale : phase diagrams of nickel-carbon nanoclusters and equilibrium constants for face transitions”. Engelmann Y, Bogaerts A, Neyts EC, Nanoscale 6, 11981 (2014). http://doi.org/10.1039/C4NR02354D
Abstract: Using reactive molecular dynamics simulations, the melting behavior of nickelcarbon nanoclusters is examined. The phase diagrams of icosahedral and Wulff polyhedron clusters are determined using both the Lindemann index and the potential energy. Formulae are derived for calculating the equilibrium constants and the solid and liquid fractions during a phase transition, allowing more rational determination of the melting temperature with respect to the arbitrary Lindemann value. These results give more insight into the properties of nickelcarbon nanoclusters in general and can specifically be very useful for a better understanding of the synthesis of carbon nanotubes using the catalytic chemical vapor deposition method.
Keywords: A1 Journal article; PLASMANT
Impact Factor: 7.367
Times cited: 20
DOI: 10.1039/C4NR02354D
|
“Thermodynamics at the nanoscale: phase diagrams of nickel-carbon nanoclusters and equilibrium constants for phase transitions”. Engelmann, Bogaerts A, Neyts EC, Nanoscale 6, 11981 (2014). http://doi.org/10.1039/c4nr02354d
Abstract: Using reactive molecular dynamics simulations, the melting behavior of nickel-carbon nanoclusters is examined. The phase diagrams of icosahedral and Wulff polyhedron clusters are determined using both the Lindemann index and the potential energy. Formulae are derived for calculating the equilibrium constants and the solid and liquid fractions during a phase transition, allowing more rational determination of the melting temperature with respect to the arbitrary Lindemann value. These results give more insight into the properties of nickel-carbon nanoclusters in general and can specifically be very useful for a better understanding of the synthesis of carbon nanotubes using the catalytic chemical vapor deposition method.
Keywords: A1 Journal article; Engineering sciences. Technology; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 7.367
Times cited: 20
DOI: 10.1039/c4nr02354d
|
“Engineering excitonic dynamics and environmental stability of post-transition metal chalcogenides by pyridine functionalization technique”. Meng X, Pant A, Cai H, Kang J, Sahin H, Chen B, Wu K, Yang S, Suslu A, Peeters FM, Tongay S;, Nanoscale 7, 17109 (2015). http://doi.org/10.1039/c5nr04879f
Abstract: http://cmt.ua.ac.be/hsahin/publishedpapers/46.pdf
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 7.367
Times cited: 11
DOI: 10.1039/c5nr04879f
|
“Morphological and chemical transformations of single silica-coated CdSe/CdS nanorods upon fs-laser excitation”. Albrecht W, Goris B, Bals S, Hutter EM, Vanmaekelbergh D, van Huis MA, van Blaaderen A, Nanoscale 9, 4810 (2017). http://doi.org/10.1039/C6NR09879G
Abstract: Radiation-induced modifications of nanostructures are of fundamental interest and constitute a viable out-of-equilibrium approach to the development of novel nanomaterials. Herein, we investigated the structural transformation of silica-coated CdSe/CdS nanorods (NRs) under femtosecond (fs) illumination. By comparing the same nanorods before and after illumination with different fluences we found that the silica-shell did not only enhance the stability of the NRs but that the confinement of the NRs also led to novel morphological and chemical transformations. Whereas uncoated CdSe/CdS nanorods were found to sublimate under such excitations the silica-coated nanorods broke into fragments which deformed towards a more spherical shape. Furthermore, CdS decomposed which led to the formation of metallic Cd, confirmed by high-resolution electron microscopy and energy dispersive X-ray spectrometry (EDX), whereby an epitaxial interface with the remaining CdS lattice was formed. Under electron beam exposure similar transformations were found to take place which we followed in situ.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 4
DOI: 10.1039/C6NR09879G
|
“Gold nanoclusters with bright near-infrared photoluminescence”. Pramanik G, Humpolickova J, Valenta J, Kundu P, Bals S, Bour P, Dracinsky M, Cigler P, Nanoscale 10, 3792 (2018). http://doi.org/10.1039/C7NR06050E
Abstract: The increase in nonradiative pathways with decreasing emission energy reduces the luminescence quantum yield (QY) of near-infrared photoluminescent (NIR PL) metal nanoclusters. Efficient surface ligand chemistry can significantly improve the luminescence QY of NIR PL metal nanoclusters. In contrast to the widely reported but modestly effective thiolate ligand-to-metal core charge transfer, we show that metal-to-ligand charge transfer (MLCT) can be used to greatly enhance the luminescence QY of NIR PL gold nanoclusters (AuNCs). We synthesized water-soluble and colloidally stable NIR PL AuNCs with unprecedentedly high QY (similar to 25%) upon introduction of triphenylphosphonium moieties into the surface capping layer. By using a combination of spectroscopic and theoretical methods, we provide evidence for gold core-to-ligand charge transfer occurring in AuNCs. We envision that this work can stimulate the development of these unusually bright AuNCs for promising optoelectronic, bioimaging, and other applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 97
DOI: 10.1039/C7NR06050E
|
“In situ tailoring of superconducting junctions via electro-annealing”. Lombardo J, Jelić, ŽL, Baumans XDA, Scheerder JE, Nacenta JP, Moshchalkov VV, Van de Vondel J, Kramer RBG, Milošević, MV, Silhanek AV, Nanoscale 10, 1987 (2018). http://doi.org/10.1039/C7NR08571K
Abstract: We demonstrate the in situ engineering of superconducting nanocircuitry by targeted modulation of material properties through high applied current densities. We show that the sequential repetition of such customized electro-annealing in a niobium (Nb) nanoconstriction can broadly tune the superconducting critical temperature T-c and the normal-state resistance R-n in the targeted area. Once a sizable R-n is reached, clear magneto-resistance oscillations are detected along with a Fraunhofer-like field dependence of the critical current, indicating the formation of a weak link but with further adjustable characteristics. Advanced Ginzburg-Landau simulations fully corroborate this picture, employing the detailed parametrization from the electrical characterization and high resolution electron microscope images of the region within the constriction where the material has undergone amorphization by electro-annealing.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 7.367
Times cited: 23
DOI: 10.1039/C7NR08571K
|
“Pushing the limits of applicability of REBCO coated conductor films through fine chemical tuning and nanoengineering of inclusions”. Rizzo F, Augieri A, Kursumovic A, Bianchetti M, Opherden L, Sieger M, Huehne R, Haenisch J, Meledin A, Van Tendeloo G, MacManus-Driscoll JL, Celentano G, Nanoscale 10, 8187 (2018). http://doi.org/10.1039/C7NR09428K
Abstract: An outstanding current carrying performance (namely critical current density, J(c)) over a broad temperature range of 10-77 K for magnetic fields up to 12 T is reported for films of YBa2Cu3O7-x with Ba2Y(Nb,Ta)O-6 inclusion pinning centres (YBCO-BYNTO) and thicknesses in the range of 220-500 nm. J(c) values of 10 MA cm(-2) were measured at 30 K – 5 T and 10 K – 9 T with a corresponding maximum of the pinning force density at 10 K close to 1 TN m(-3). The system is very flexible regarding properties and microstructure tuning, and the growth window for achieving a particular microstructure is wide, which is very important for industrial processing. Hence, the dependence of J(c) on the magnetic field angle was readily controlled by fine tuning the pinning microstructure. Transmission electron microscopy (TEM) analysis highlighted that higher growth rates induce more splayed and denser BYNTO nanocolumns with a matching field as high as 5.2 T. Correspondingly, a strong peak at the B||c-axis is noticed when the density of vortices is lower than the nanocolumn density. YBCO-BYNTO is a very robust and reproducible composite system for high-current coated conductors over an extended range of magnetic fields and temperatures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 9
DOI: 10.1039/C7NR09428K
|
“Quantum anomalous Hall effect in a stable 1T-YN2 monolayer with a large nontrivial bandgap and a high Chern number”. Kong X, Li L, Leenaerts O, Wang W, Liu X-J, Peeters FM, Nanoscale 10, 8153 (2018). http://doi.org/10.1039/C8NR00571K
Abstract: The quantum anomalous Hall (QAH) effect is a topologically nontrivial phase, characterized by a non-zero Chern number defined in the bulk and chiral edge states in the boundary. Using first-principles calculations, we demonstrate the presence of the QAH effect in a 1T-YN2 monolayer, which was recently predicted to be a Dirac half metal without spin-orbit coupling (SOC). We show that the inclusion of SOC opens up a large nontrivial bandgap of nearly 0.1 eV in the electronic band structure. This results in the nontrivial bulk topology, which is confirmed by the calculation of Berry curvature, anomalous Hall conductance and the presence of chiral edge states. Remarkably, a QAH phase of high Chern number C = 3 is found, and there are three corresponding gapless chiral edge states emerging inside the bulk gap. Different substrates are also chosen to study the possible experimental realization of the 1T-YN2 monolayer, while retaining its nontrivial topological properties. Our results open a new avenue in searching for QAH insulators with high temperature and high Chern numbers, which can have nontrivial practical applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 7.367
Times cited: 28
DOI: 10.1039/C8NR00571K
|
“Topological confinement in an antisymmetric potential in bilayer graphene in the presence of a magnetic field”. Zarenia M, Pereira JM, Peeters FM, Farias G de A, Nanoscale research letters 6, 452 (2011). http://doi.org/10.1186/1556-276X-6-452
Abstract: We investigate the effect of an external magnetic field on the carrier states that are localized at a potential kink and a kink-antikink in bilayer graphene. These chiral states are localized at the interface between two potential regions with opposite signs.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.833
Times cited: 4
DOI: 10.1186/1556-276X-6-452
|