Abstract: Although it is well known that FeMnC TWIP steels exhibit high work-hardening rates, the elementary twinning mechanisms controlling the plastic deformation of these steels have still not been characterized. The aim of the present study is to analyse the extended defects related to the twinning occurrence using transmission electron microscopy. Based on these observations, the very early stage of twin nucleation can be attributed to the pole mechanism with deviation proposed by Cohen and Weertman or to the model of Miura, Takamura and Narita, while the twin growth is controlled by the pole mechanism proposed by Venables. High densities of sessile Frank dislocations are observed within the twins at the early stage of deformation, which can affect the growth and the stability of the twins, but also the strength of these twins and their interactions with the gliding dislocations present in the matrix. This experimental evidence is discussed and compared to recent results in order to relate the defects analysis to the macroscopic behaviour of this category of material.

Abstract: The influence of the stress state on the twinning rate and work hardening is studied in the case of an FeMnC TWIP steel strained in uniaxial tension, simple shear and rolling. The resulting stressstrain responses exhibit marked differences. The twinning rate, number of activated twinning systems in each grain, twin thickness and transmission of twins across grain boundaries are dependent on the imposed stress state during straining. Relationships between twin features and macroscopic work hardening rate are established.

Abstract: The size, shape and distribution of Ni4Ti3 precipitates in Ni51Ti49 single crystals annealed under stress-free and 〈1 1 1〉B2 compressive conditions are studied via focused ion beam/scanning electron microscopy slice-and-view. The precipitates in the stress-free material grow in autocatalytic pockets with larger size, lower number density, flatter shape and larger inter-particle distance than in the compressed material. Nevertheless, a new quantification method called water penetration reveals that, due to the precipitate alignment, martensite can grow more easily in the compressed material perpendicular to the compression direction.

Abstract: The three-dimensional size, morphology and distribution of Ni4Ti3 precipitates in a Ni50.8Ti49.2 polycrystalline shape memory alloy with a heterogeneous microstructure have been investigated using a focused ion beam/scanning electron microscopy slice-and-view procedure. The mean volume, central plane diameter, thickness, aspect ratio and sphericity of the precipitates in the grain interior as well as near to the grain boundary were measured and/or calculated. The morphology of the precipitates was quantified by determining the equivalent ellipsoids with the same moments of inertia and classified according to the Zingg scheme. Also, the pair distribution functions describing the three-dimensional distributions were obtained from the coordinates of the precipitate mass centres. Based on this new data it is suggested that the existence of the heterogeneous microstructure could be due to a very small concentration gradient in the grains of the homogenized material and that the resulting multistage martensitic transformation originates in strain effects related to the size of the precipitates and scale differences of the available B2 matrix in between the precipitates.

Abstract: Nb occupancy in the austenite B2-NiTi matrix and Ti2Ni phase in NiTiNb shape memory alloys was investigated by aberration-corrected scanning transmission electron microscopy and precession electron diffraction. In both cases, Nb atoms were found to prefer to occupy the Ti rather than Ni sites. A projector augmented wave method within density functional theory was used to calculate the atomic and electronic structures of the austenitic B2-NiTi matrix phase and the Ti2Ni precipitates both with and without addition of Nb. The obtained formation energies and analysis of structural and electronic characteristics explain the preference for Ti sites for Nb over Ni sites.

Abstract: Superelastic deformation of thin NiTi wires containing various nanograined microstructures was investigated by tensile cyclic loading with in situ evaluation of electric resistivity. Defects created by the superelastic cycling in these wires were analyzed by transmission electron microscopy. The role of dislocation slip in superelastic deformation is discussed. NiTi wires having finest microstructures (grain diameter <100 nm) are highly resistant against dislocation slip, while those with fully recrystallized microstructure and grain size exceeding 200 nm are prone to dislocation slip. The density of the observed dislocation defects increases significantly with increasing grain size. The upper plateau stress of the superelastic stressstrain curves is largely grain size independent from 10 up to 1000 nm. It is hence claimed that the HallPetch relationship fails for the stress-induced martensitic transformation in this grain size range. It is proposed that dislocation slip taking place during superelastic cycling is responsible for the accumulated irreversible strains, cyclic instability and degradation of functional properties. No residual martensite phase was found in the microstructures of superelastically cycled wires by TEM and results of the in situ electric resistance measurements during straining also indirectly suggest that none or very little martensite phase remains in the studied cycled superelastic wires after unloading. The accumulation of dislocation defects, however, does not prevent the superelasticity. It only affects the shape of the stressstrain response, makes it unstable upon cycling and changes the deformation mode from localized to homogeneous. The activity of dislocation slip during superelastic deformation of NiTi increases with increasing test temperature and ultimately destroys the superelasticity as the plateau stress approaches the yield stress for slip. Deformation twins in the austenite phase ({1 1 4} compound twins) were frequently found in cycled wires having largest grain size. It is proposed that they formed in the highly deformed B19′ martensite phase during forward loading and are retained in austenite after unloading. Such twinning would represent an additional deformation mechanism of NiTi yielding residual irrecoverable strains.

Abstract: Lanthanum carbonate is a new phosphate binder that is poorly absorbed from the gastrointestinal tract and eliminated largely by the liver. After oral treatment, we and others had noticed 23 fold higher lanthanum levels in the livers of rats with chronic renal failure compared to rats with normal renal function. Here we studied the kinetics and tissue distribution, absorption, and subcellular localization of lanthanum in the liver using transmission electron microscopy, electron energy loss spectrometry, and X-ray fluoresence. We found that in the liver lanthanum was located in lysosomes and in the biliary canal but not in any other cellular organelles. This suggests that lanthanum is transported and eliminated by the liver via a transcellular, endosomal-lysosomal-biliary canicular transport route. Feeding rats with chronic renal failure orally with lanthanum resulted in a doubling of the liver levels compared to rats with normal renal function, but the serum levels were similar in both animal groups. These levels plateaued after 6 weeks at a concentration below 3 g/g in both groups. When lanthanum was administered intravenously, thereby bypassing the gastrointestinal tract-portal vein pathway, no difference in liver levels was found between rats with and without renal failure. This suggests that there is an increased gastrointestinal permeability or absorption of oral lanthanum in uremia. Lanthanum levels in the brain and heart fluctuated near its detection limit with long-term treatment (20 weeks) having no effect on organ weight, liver enzyme activities, or liver histology. We suggest that the kinetics of lanthanum in the liver are consistent with a transcellular transport pathway, with higher levels in the liver of uremic rats due to higher intestinal absorption.

Abstract: Shape memory alloys inherit their macroscopic properties from their mesoscale microstructure originated from the martensitic phase transformation. In a cubic to orthorhombic transition, a single variant of martensite can have a compatible (exact) interface with the austenite for some special lattice parameters in contrast to conventional austenite/twinned martensite interface with a transition layer. Experimentally, the phase compatibility results in a dramatic drop in thermal hysteresis and gives rise to very stable functional properties over cycling. Here, we investigate the microstructures observed in Ti50Ni50-xPdx alloys that undergo a cubic to orthorhombic martensitic transformation using a three-dimensional phase field approach. We will show that the simulation results are in very good agreement with transmission electron microscopy observations. However, the understanding of the drop in thermal hysteresis requires the coupling of phase transformation with plastic activity. We will discuss this point within the framework of thermoelasticity, which is a generic feature of the martensitic transformation. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4712629]