Abstract: We report a microstructural and compositional study of a 90% Pb(Mg1/3Nb2/3)O-3 – 10% PbTiO3 ceramic sample. High resolution transmission electron microscopy (HRTEM) revealed the presence of compositional ordered nano-domains (1 – 4 mn), observable in two specific orientations, [0 (1) over bar 1] and [1 1 (2) over bar]. However, the visibility and the ordering degree of the nano-domains on the HRTEM images are not at all obvious. Fourier filtering of the images clearly revealed the ordered domains. Antiphase boundaries lying in the (111) planes separate them, while (100) and (111) facets separate the ordered domains from the disordered matrix. Their shape is plate-like, not uniformly spread in the disordered matrix. Their average size varies in different regions of the sample, most probably due to a non-uniform distribution of Ti, as observed by energy dispersive X-ray spectroscopy. (c) 2007 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim.

Abstract: Nanocrystalline diamond (NCD) thin films were produced by chemical vapor deposition (CVD) and doped by the addition of phosphine to the gas mixture. The characterization of the films focused on probing the incorporation and distribution of the phosphorus (P) dopants. Electron microscopy evaluated the overall film morphology and revealed the interior structure of the nanosized grains. The homogeneous films with distinct diamond grains featured a notably low sp(2):sp(3)-ratio as confirmed by Raman spectroscopy. High resolution spectroscopy methods demonstrated a homogeneous P-incorporation, both in-depth and in-plane. The P concentration in the films was determined to be in the order of 10(19) cm(-3) with a significant fraction integrated at substitutional donor sites. (C) 2014 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim

Abstract: Transmission electron microscopy has been applied to study Ti and Al/Ti contacts on GaN and AlGaN/GaN as a function of annealing temperature. This has lead to a profound understanding of the role of Al, both in the contact formation on n-GaN and on AlGaN/GaN. Al in the AlGaN decreases the N-extraction by Ti out of the nitride, because of the strong Al-N bond. Al in the metal bilayer also reduces the N-extraction by Ti due to a preferential alloy mixing.

Abstract: Solution derived La2Zr2O7 films have drawn much attention for potential applications as thermal barriers or low-cost buffer layers for coated conductor technology. Annealing and coating parameters strongly affect the microstructure of La2Zr2O7, but different film processing methods can yield similar microstructural features such as nanovoids and nanometer-sized La2Zr2O7 grains. Nanoporosity is a typical feature found in such films and the implications for the functionality of the films are investigated by a combination of scanning transmission electron microscopy (STEM), electron energy-loss spectroscopy (EELS) and quantitative electron tomography. Chemical solution based La2Zr2O7 films deposited on flexible Ni5 at.%W substrates with a {100}lang001rang biaxial texture were prepared for an in-depth characterization. A sponge-like structure composed of nanometer-sized voids is revealed by high-angle annular dark-field scanning transmission electron microscopy in combination with electron tomography. A three-dimensional quantification of nanovoids in the La2Zr2O7 film is obtained on a local scale. Mostly non-interconnected highly faceted nanovoids compromise more than one-fifth of the investigated sample volume. The diffusion barrier efficiency of a 170 nm thick La2Zr2O7 film is investigated by STEM-EELS, yielding a 1.8 ± 0.2 nm oxide layer beyond which no significant nickel diffusion can be detected and intermixing is observed. This is of particular significance for the functionality of YBa2Cu3O7 − δ coated conductor architectures based on solution derived La2Zr2O7 films as diffusion barriers.