Abstract: We measured the electrical resistivity R(T) and specific heat C-p(T) between room temperature (RT) and 4.2 K as well as the microstructure by transmission electron microscopy (TEM) of a Ni-52 Ti-48 SMA quenched from 1000degreesC (B2-Phase range) to RT and then annealed for 1h at T=380degreesC, 550degreesC and 650degreesC. In the “as quenched” and the “650degreesC annealed” state no martensitic transformations (MT's) occur. The diffraction patterns show faint reflections originating from coherent Ni4Ti3 precipitates in an early state of formation. Additional reflections of the type 1/2 <110>, 1/2 <111> and 1/3 <110> result from various lattice displacement waves, which are precursors of the MT's to the B19' and R-phase, respectively. Indeed, high resolution TEM micrographs of the [001] zone of the “as quenched” sample reveal transverse 1/2 <110> <110> lattice displacement waves, precursors of the B19' martensite. The coherent Ni4Ti3 precipitates, homogeneously distributed on a small length scale, binder the MT's in the “as quenched” and the “650degreesC annealed” state, and thus only the precursors appear. When annealed at T=380degreesC, however, coherent Ni4Ti3 precipitates with a length of 10nm are clearly visible in TEM. These precipitates trigger the NIT from the B2 to the R-phase on cooling, as evidenced also by anomalies in R(T) and C-p(T). Annealing at T-550degreesC leads to the well known two step MT's from the B2 to the R-phase and then into the B19'-phase. These martensitic transitions are clearly seen as additional peaks in the specific heat and anomalies in the resistance, while the “as quenched” and 650degreesC annealed samples show weak features in R(T) and C-p(T).

Abstract: We present a theoretical study of macrotwins arising in cubic to tetragonal martensitic transformations. The results help to explain some features of such macrotwins observed in Ni65Al35.

Abstract: Glass treated on its surface with silver compounds and an aluminosilicate, such as ochre or clay, at higher temperatures (between 550 and 650 °C) accepts a wide variety of a yellow colour. It is the aim of this study to investigate the parameters of the manufacturing process affecting the final colour of silver stained glass and to correlate them with the final colour and colour intensity. Therefore, defined mixtures of ochre and a silver compound (AgCl, AgNO3, Ag2SO4, Ag3PO4, Ag2O) were prepared and applied on soda-lime glass. The firing process was modified within the range from 563 to 630 °C and glass samples were analysed after treatment with energy dispersive X-ray fluorescence analysis (EDXRF), scanning electron microscopy (SEM/EDX), transmission electron microscopy (TEM), as well as ion beam analysis (IBA) with an external beam. Within the scope of IBA simultaneous measurements using particle-induced X-ray emission (PIXE), particle-induced gamma-ray emission (PIGE), and Rutherford backscattering spectrometry (RBS) were carried out in order to obtain the thickness of the Ag-rich surface layer and the depth distribution of Ag. By means of TEM the microstructure of the silver particles was visualised. XRF results show that the lowest amount of Ag could be detected on glass samples treated with silver stain mixtures containing AgCl and Ag2O. A low kiln temperature (e.g. 563 °C) results in a higher silver concentration at the surface and lower penetration depths. Furthermore, the results obtained with SEM/EDX at cross-sections of the glass samples could be confirmed by PIXE, PIGE, RBS, and TEM.

Abstract: The structure of the metastable Ni2Al phase, which has long been a matter of controversy, has been carefully re-examined by means of high-resolution transmission electron microscopy (HREM) and electron microdiffraction. First, it is concluded that theas-quenched NixAl100-x(60 less-than-or-equal-to x less-than-or-equal-to 65) material already exhibits a partial omega-type collapse in a one-dimensional fashion which and is consistent with the anomalous dip in the phonon dispersion curve. Ni2Al precipitates are formed on annealing by thermal decomposition of the high-temperature NixAl100-xB2 phase and still retain the small omega-type shuffle. The amount of displacement in the well developed Ni2Al phase was estimated to be between 20 and 50% of the ideal omega collapse; this was determined by means of a combined technique of HREM and microdiffraction together with dynamical calculations of HREM images and diffraction intensities.

Abstract: Investigating domain boundaries and their effects on the behaviour of materials automatically implies the need for detailed knowledge on the structural aspects of the atomic configurations at these interfaces. Not only in view of nearest neighbour interactions but also at a larger scale, often surpassing the unit cell, the boundaries can contain structural elements that do not exist in the bulk. In the present contribution, a number of special boundaries resulting from phase transformations or crystal growth and those recently investigated by advanced transmission electron microscopy techniques in different systems will be reviewed. These include macrotwins between microtwinned martensite plates in NiAl, austenite-single variant martensite habit planes in low hysteresis NiTiPd, nanotwins in non-textured nanostructured Pd and ferroelastic domain boundaries in CaTiO3. In all discussed cases these boundaries play an essential role in the properties of the respective materials.