“Electrodeposition of Highly Porous Pt Nanoparticles Studied by Quantitative 3D Electron Tomography: Influence of Growth Mechanisms and Potential Cycling on the Active Surface Area”. Ustarroz J, Geboes B, Vanrompay H, Sentosun K, Bals S, Breugelmans T, Hubin A, ACS applied materials and interfaces 9, 16168 (2017). http://doi.org/10.1021/acsami.7b01619
Abstract: Nanoporous Pt nanoparticles (NPs) are promising fuel cell catalysts due to their large surface area and increased electrocatalytic activity towards the oxygen reduction reaction (ORR). Herein, we report on the infuence of the growth mechanisms on the surface properties of electrodeposited Pt dendritic NPs with large surface areas. The electrochemically active surface was studied by hydrogen underpotential deposition (HUPD) and compared for the rst time to high angle annular dark eld scanning transmission electron microscopy (HAADF-STEM) quantitative 3D electron tomography of individual nanoparticles. Large nucleation overpotential leads to a large surface coverage of Pt roughened spheroids, which provide large roughness factor (Rf ) but low mass-specic electrochemically active surface area (EASA). Lowering the nucleation overpotential leads to highly porous Pt NPs with pores protruding to the center of the structure. At the expense of smaller Rf , the obtained EASA values of these structures are in the range of these of large surface area supported fuel cell catalysts. The active surface area of the Pt dendritic NPs was measured by electron tomography and it was found that the potential cycling in the H adsorption/desorption and Pt oxidation/reduction region, which is generally performed to determine the EASA, leads to a signicant reduction of that surface area due to a partial collapse of their dendritic and porous morphology. Interestingly, the extrapolation of the microscopic tomography results to macroscopic electrochemical parameters indicated that the surface properties measured by H UPD are comparable to the values measured on individual NPs by electron tomography after the degradation caused by the H UPD measurement. These results highlight that the combination of electrochemical and quantitative 3D surface analysis techniques is essential to provide insights into the surface properties, the electrochemical stability and, hence, the applicability of these materials. Moreover, it indicates that care must be taken with widely used electrochemical methods of surface area determination, especially in the case of large surface area and possibly unstable nanostructures, since the measured surface can be strongly aected by the measurement itself.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 7.504
Times cited: 24
DOI: 10.1021/acsami.7b01619
|
“Ligand-Induced Shape Transformation of PbSe Nanocrystals”. Peters JL, van den Bos KHW, Van Aert S, Goris B, Bals S, Vanmaekelbergh D, Chemistry of materials 29, 4122 (2017). http://doi.org/10.1021/acs.chemmater.7b01103
Abstract: We present a study of the relation between the surface chemistry and nanocrystal shape of PbSe nanocrystals with a variable Pb-to-Se stoichiometry and density of oleate ligands. The oleate ligand density and binding configuration are monitored by nuclear magnetic resonance and Fourier transform infrared absorbance spectroscopy, allowing us to quantify the number of surface-attached ligands per NC and the nature of the surface−Pb−oleate configuration. The three-dimensional shape of the PbSe nanocrystals is obtained from high-angle annular dark field scanning transmission electron microscopy combined with an atom counting method. We show that the enhanced oleate capping results in a stabilization and extension of the {111} facets, and a crystal shape transformation from a truncated nanocube to a truncated octahedron.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 45
DOI: 10.1021/acs.chemmater.7b01103
|
“Heterogeneous TiO2/V2O5/Carbon Nanotube Electrodes for Lithium-Ion Batteries”. Kurttepeli M, Deng S, Mattelaer F, Cott DJ, Vereecken P, Dendooven J, Detavernier C, Bals S, ACS applied materials and interfaces 9, 8055 (2017). http://doi.org/10.1021/acsami.6b12759
Abstract: Vanadium pentoxide (V2O5) is proposed and investigated as a cathode material for lithium-ion (Li-ion) batteries. However, the dissolution of V2O5 during the charge/discharge remains as an issue at the V2O5–electrolyte interface. In this work, we present a heterogeneous nanostructure with carbon nanotubes supported V2O5/titanium dioxide (TiO2) multilayers as electrodes for thin-film Li-ion batteries. Atomic layer deposition of V2O5 on carbon nanotubes provides enhanced Li storage capacity and high rate performance. An additional TiO2 layer leads to increased morphological stability and in return higher electrochemical cycling performance of V2O5/carbon nanotubes. The physical and chemical properties of TiO2/V2O5/carbon nanotubes are characterized by cyclic voltammetry and charge/discharge measurements as well as electron microscopy. The detailed mechanism of the protective TiO2 layer to improve the electrochemical cycling stability of the V2O5 is unveiled.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.504
Times cited: 28
DOI: 10.1021/acsami.6b12759
|
“Three-dimensional atomic models from a single projection using Z-contrast imaging: verification by electron tomography and opportunities”. De Backer A, Jones L, Lobato I, Altantzis T, Goris B, Nellist PD, Bals S, Van Aert S, Nanoscale 9, 8791 (2017). http://doi.org/10.1039/C7NR02656K
Abstract: In order to fully exploit structure–property relations of nanomaterials, three-dimensional (3D) characterization at the atomic scale is often required. In recent years, the resolution of electron tomography has reached the atomic scale. However, such tomography typically requires several projection images demanding substantial electron dose. A newly developed alternative circumvents this by counting the number of atoms across a single projection. These atom counts can be used to create an initial atomic model with which an energy minimization can be applied to obtain a relaxed 3D reconstruction of the nanoparticle. Here, we compare, at the atomic scale, this single projection reconstruction approach with tomography and find an excellent agreement. This new approach allows for the characterization of beam-sensitive materials or where the acquisition of a tilt series is impossible. As an example, the utility is illustrated by the 3D atomic scale characterization of a nanodumbbell on an in situ heating holder of limited tilt range.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 33
DOI: 10.1039/C7NR02656K
|
“Quantitative determination of residual silver distribution in nanoporous gold and its influence on structure and catalytic performance”. Mahr C, Kundu P, Lackmann A, Zanaga D, Thiel K, Schowalter M, Schwan M, Bals S, Wittstock A, Rosenauer A, Journal of catalysis 352, 52 (2017). http://doi.org/10.1016/j.jcat.2017.05.002
Abstract: Large efforts have been made trying to understand the origin of the high catalytic activity of dealloyed nanoporous gold as a green catalyst for the selective promotion of chemical reactions at low temperatures. Residual silver, left in the sample after dealloying of a gold-silver alloy, has been shown to have a strong influence on the activity of the catalyst. But the question of how the silver is distributed within the porous structure has not finally been answered yet. We show by quantitative energy dispersive X-ray tomography measurements that silver forms clusters that are distributed irregularly, both on the surface and inside the ligaments building up the porous structure. Furthermore, we find that the role of the residual silver is ambiguous. Whereas CO oxidation is supported by more residual silver, methanol oxidation to methyl formate is hindered. Structural characterisation reveals larger ligaments and pores for decreasing residual silver concentration.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 42
DOI: 10.1016/j.jcat.2017.05.002
|
“Nanorattles with tailored electric field enhancement”. Schnepf MJ, Mayer M, Kuttner C, Tebbe M, Wolf D, Dulle M, Altantzis T, Formanek P, Förster S, Bals S, König TAF, Fery A, Nanoscale 9, 9376 (2017). http://doi.org/10.1039/C7NR02952G
Abstract: Nanorattles are metallic core–shell particles with core and shell separated by a dielectric spacer. These
nanorattles have been identified as a promising class of nanoparticles, due to their extraordinary high
electric-field enhancement inside the cavity. Limiting factors are reproducibility and loss of axial symmetry
owing to the movable metal core; movement of the core results in fluctuation of the nanocavity dimensions
and commensurate variations in enhancement factor. We present a novel synthetic approach for
the robust fixation of the central gold rod within a well-defined box, which results in an axisymmetric
nanorattle. We determine the structure of the resulting axisymmetric nanorattles by advanced transmission
electron microscopy (TEM) and small-angle X-ray scattering (SAXS). Optical absorption and scattering
cross-sections obtained from UV-vis-NIR spectroscopy quantitatively agree with finite-difference
time-domain (FDTD) simulations based on the structural model derived from SAXS. The predictions of
high and homogenous field enhancement are evidenced by scanning TEM electron energy loss spectroscopy
(STEM-EELS) measurement on single-particle level. Thus, comprehensive understanding of
structural and optical properties is achieved for this class of nanoparticles, paving the way for photonic
applications where a defined and robust unit cell is crucial.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 69
DOI: 10.1039/C7NR02952G
|
“3D porous nanostructured platinum prepared using atomic layer deposition”. Pulinthanathu Sree S, Dendooven J, Geerts L, Ramachandran RK, Javon E, Ceyssens F, Breynaert E, Kirschhock CEA, Puers R, Altantzis T, Van Tendeloo G, Bals S, Detavernier C, Martens JA, Journal of materials chemistry A : materials for energy and sustainability 5, 19007 (2017). http://doi.org/10.1039/C7TA03257A
Abstract: A robust and easy to handle 3D porous platinum structure was created via replicating the 3D channel system
of an ordered mesoporous silica material using atomic layer deposition (ALD) over micrometer distances.
After ALD of Pt in the silica material, the host template was digested using hydrogen fluoride (HF). A fully
connected ordered Pt nanostructure was obtained with morphology and sizes corresponding to that of
the pores of the host matrix, as revealed with high-resolution scanning transmission electron
microscopy and electron tomography. The Pt nanostructure consisted of hexagonal Pt rods originating
from the straight mesopores (11 nm) of the host structure and linking features resulting from Pt
replication of the interconnecting mesopore segments (2–4 nm) present in the silica host structure.
Electron tomography of partial replicas, made by incomplete infilling of Zeotile-4 material with Pt,
provided insight in the connectivity and formation mechanism of the Pt nanostructure by ALD. The Pt
replica was evaluated for its potential use as electrocatalyst for the hydrogen evolution reaction, one of
the half-reactions of water electrolysis, and as microelectrode for biomedical sensing. The Pt replica
showed high activity for the hydrogen evolution reaction and electrochemical characterization revealed
a large impedance improvement in comparison with reference Pt electrodes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 9
DOI: 10.1039/C7TA03257A
|
“Facile morphology-controlled synthesis of organolead iodide perovskite nanocrystals using binary capping agents”. Debroye E, Yuan H, Bladt E, Baekelant W, Van der Auweraer M, Hofkens J, Bals S, Roeffaers MBJ, ChemNanoMat : chemistry of nanomaterials for energy, biology and more 3, 223 (2017). http://doi.org/10.1002/CNMA.201700006
Abstract: Controlling the morphology of organolead halide perovskite crystals is crucial to a fundamental understanding of the materials and to tune their properties for device applications. Here, we report a facile solution-based method for morphology-controlled synthesis of rod-like and plate-like organolead halide perovskite nanocrystals using binary capping agents. The morphology control is likely due to an interplay between surface binding kinetics of the two capping agents at different crystal facets. By high-resolution scanning transmission electron microscopy, we show that the obtained nanocrystals are monocrystalline. Moreover, long photoluminescence decay times of the nanocrystals indicate long charge diffusion lengths and low trap/defect densities. Our results pave the way for large-scale solution synthesis of organolead halide perovskite nanocrystals with controlled morphology for future device applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.937
Times cited: 19
DOI: 10.1002/CNMA.201700006
|
“Tunable nitrogen-doped carbon nanoparticles from tannic acid and urea and their potential for sustainable soots”. Berthold T, Castro CR, Winter M, Hoerpel G, Kurttepeli M, Bals S, Antonietti M, Fechler N, ChemNanoMat : chemistry of nanomaterials for energy, biology and more 3, 311 (2017). http://doi.org/10.1002/CNMA.201700051
Abstract: Nano-sized nitrogen-doped carbon spheres are synthesized from two cheap, readily available and sustainable precursors: tannic acid and urea. In combination with a polymer structuring agent, nitrogen content, sphere size and the surface (up to 400 m(2)g(-1)) can be conveniently tuned by the precursor ratio, temperature and structuring agent content. Because the chosen precursors allow simple oven synthesis and avoid harsh conditions, this carbon nanosphere platform offers a more sustainable alternative to classical soots, for example, as printing pigments or conduction soots. The carbon spheres are demonstrated to be a promising as conductive carbon additive in anode materials for lithium ion batteries.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.937
Times cited: 14
DOI: 10.1002/CNMA.201700051
|
“Shape control in ZIF-8 nanocrystals and metal nanoparticles@ZIF-8 heterostructures”. Zheng G, Chen Z, Sentosun K, Pérez-Juste I, Bals S, Liz-Marzán LM, Pastoriza-Santos I, Pérez-Juste J, Hong M, Nanoscale 9, 16645 (2017). http://doi.org/10.1039/C7NR03739B
Abstract: Shape control in metal-organic frameworks still remains a challenge. We propose a strategy based on the capping agent modulator method to control the shape of ZIF-8 nanocrystals. This approach requires the use of a surfactant, cetyltrimethylammonium bromide (CTAB), and a second capping agent, tris(hydroxymethyl)aminomethane (TRIS), to obtain ZIF-8 nanocrystals with morphology control in aqueous media. Semiempirical computational simulations suggest that both shape-inducing agents adsorb onto different surface facets of ZIF-8, thereby slowing down their crystal growth rates. While CTAB molecules preferentially adsorb onto the {100} facets, leading to ZIF-8 particles with cubic morphology, TRIS preferentially stabilizes the {111} facets, inducing the formation of octahedral crystals. Interestingly, the presence of both capping agents leads to nanocrystals with irregular shapes and higher index facets, such as hexapods and burr puzzles. Additionally, the combination of ZIF-8 nanocrystals with other materials is expected to impart additional properties due to the hybrid nature of the resulting nanocomposites. In the present case, the presence of CTAB and TRIS molecules as capping agents facilitates the synthesis of metal nanoparticle@ZIF-8 nanocomposites, due to synergistic effects which could be of use in a number of applications such as catalysis, gas sensing and storage.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 109
DOI: 10.1039/C7NR03739B
|
“Bottom-Up Mechanical Nanometrology of Granular Ag Nanoparticles Thin Films”. Benetti G, Caddeo C, Melis C, Ferrini G, Giannetti C, Winckelmans N, Bals S, J Van Bael M, Cavaliere E, Gavioli L, Banfi F, The journal of physical chemistry: C : nanomaterials and interfaces 121, 22434 (2017). http://doi.org/10.1021/acs.jpcc.7b05795
Abstract: Ultrathin metal nanoparticles coatings, synthesized by gas-phase deposition, are emerging as go-to materials in a variety of fields ranging from pathogens control, sensing to energy storage. Predicting their morphology and mechanical properties beyond a trial-and-error approach is a crucial issue limiting their exploitation in real-life applications. The morphology and mechanical properties of Ag nanoparticles ultrathin films, synthesized by supersonic cluster beam deposition, are here assessed adopting a bottom-up, multi-technique approach. A virtual film model is proposed merging high resolution scanning transmission electron microscopy, supersonic cluster beam dynamics and molecular dynamics simulations. The model is validated against mechanical nanometrology measurements and is readily extendable to metals other than Ag. The virtual film is shown to be a flexible and reliable predictive tool to access morphology-dependent properties such as mesoscale gas-dynamics and elasticity of ultrathin films synthesized by gas-phase deposition.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 30
DOI: 10.1021/acs.jpcc.7b05795
|
“Vapor Phase Fabrication of Nanoheterostructures Based on ZnO for Photoelectrochemical Water Splitting”. Barreca D, Carraro G, Gasparotto A, Maccato C, Altantzis T, Sada C, Kaunisto K, Ruoko T-P, Bals S, Advanced Materials Interfaces 4, 1700161 (2017). http://doi.org/10.1002/admi.201700161
Abstract: Nanoheterostructures based on metal oxide semiconductors have emerged
as promising materials for the conversion of sunlight into chemical energy.
In the present study, ZnO-based nanocomposites have been developed by
a hybrid vapor phase route, consisting in the chemical vapor deposition
of ZnO systems on fluorine-doped tin oxide substrates, followed by the
functionalization with Fe2O3 or WO3 via radio frequency-sputtering. The
target systems are subjected to thermal treatment in air both prior and after
sputtering, and their properties, including structure, chemical composition,
morphology, and optical absorption, are investigated by a variety of characterization
methods. The obtained results evidence the formation of highly
porous ZnO nanocrystal arrays, conformally covered by an ultrathin Fe2O3
or WO3 overlayer. Photocurrent density measurements for solar-triggered
water splitting reveal in both cases a performance improvement with respect
to bare zinc oxide, that is mainly traced back to an enhanced separation of
photogenerated charge carriers thanks to the intimate contact between the
two oxides. This achievement can be regarded as a valuable result in view of
future optimization of similar nanoheterostructured photoanodes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
Times cited: 30
DOI: 10.1002/admi.201700161
|
“Composite Supraparticles with Tunable Light Emission”. Montanarella F, Altantzis T, Zanaga D, Rabouw FT, Bals S, Baesjou P, Vanmaekelbergh D, van Blaaderen A, ACS nano 11, 9136 (2017). http://doi.org/10.1021/acsnano.7b03975
Abstract: Robust luminophores emitting light with broadly tunable colors are desirable in many applications such as light-emitting diode (LED)-based lighting, displays, integrated optoelectronics and biology. Nanocrystalline quantum dots with multicolor emission, from core- and shell-localized excitons, as well as solid layers of mixed quantum dots that emit different colors have been proposed. Here, we report on colloidal supraparticles that are composed of three types of Cd(Se,ZnS) core/(Cd,Zn)S shell nanocrystals with emission in the red, green, and blue. The emission of the supraparticles can be varied from pure to composite colors over the entire visible region and finetuned into variable shades of white light by mixing the nanocrystals in controlled proportions. Our approach results in supraparticles with sizes spanning the colloidal domain and beyond that combine versatility and processability with a broad, stable, and tunable emission, promising applications in lighting devices and biological research.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 36
DOI: 10.1021/acsnano.7b03975
|
“Advanced electron tomography of nanoparticle assemblies”. Altantzis T, Zanaga D, Bals S, Europhysics letters 119, 38001 (2017). http://doi.org/10.1209/0295-5075/119/38001
Abstract: Nanoparticle assemblies have attracted enormous scientific interest during the last
years, due to their unique properties compared to those of their building blocks. To understand
the origin of these properties and to establish the connection with their structure, a detailed and
quantitative structural characterization is essential. Transmission electron microscopy has been
widely used to investigate nano-assemblies. However, TEM images only correspond to a twodimensional
projection of a three-dimensional object. Therefore, in order to obtain the necessary
3D structural information electron tomography has to be applied. By means of advanced electron
tomography, both qualitative and quantitative information can be obtained, which can be used
for detailed theoretical studies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 8
DOI: 10.1209/0295-5075/119/38001
|
“Disentangling the effect of seed size and crystal habit on gold nanoparticle seeded growth”. González-Rubio G, de Oliveira TM, Altantzis T, La Porta A, Guerrero-Martínez A, Bals S, Scarabelli L, Liz-Marzán LM, Chemical communications 53, 11360 (2017). http://doi.org/10.1039/C7CC06854A
Abstract: Oxidative etching was used to produce gold seeds of different sizes and crystal habits. Following detailed characterization, the seeds were grown under different conditions. Our results bring new insights toward understanding the effect of size and crystallinity on the growth of anisotropic particles, whilst identifying guidelines for the optimisation of new synthetic protocols of predesigned seeds.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 29
DOI: 10.1039/C7CC06854A
|
“Tunable porous nanoallotropes prepared by post-assembly etching of binary nanoparticle superlattices”. Udayabhaskararao T, Altantzis T, Houben L, Coronado-Puchau M, Langer J, Popovitz-Biro R, Liz-Marzán LM, Vuković, L, Král P, Bals S, Klajn R, Science 358, 514 (2017). http://doi.org/10.1126/science.aan6046
Abstract: Self-assembly of inorganic nanoparticles has been used to prepare hundreds of different colloidal crystals, but almost invariably with the restriction that the particles must be densely packed. Here,we show that non–close-packed nanoparticle arrays can be fabricated through the selective removal of one of two components comprising binary nanoparticle superlattices. First, a variety of binary nanoparticle superlattices were prepared at the liquid-air interface, including several arrangements that were previously unknown. Molecular dynamics simulations revealed the particular role of the liquid in templating the formation of superlattices not achievable through self-assembly in bulk solution. Second, upon stabilization, all of these binary superlattices could be transformed into distinct “nanoallotropes”—nanoporous materials having the same chemical composition but differing in their nanoscale architectures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 37.205
Times cited: 113
DOI: 10.1126/science.aan6046
|
“Mechanistic Insight into the Photocatalytic Working of Fluorinated Anatase {001} Nanosheets”. Kus M, Altantzis T, Vercauteren S, Caretti I, Leenaerts O, Batenburg KJ, Mertens M, Meynen V, Partoens B, Van Doorslaer S, Bals S, Cool P, The journal of physical chemistry: C : nanomaterials and interfaces 121, 26275 (2017). http://doi.org/10.1021/acs.jpcc.7b05586
Abstract: Anatase nanosheets with exposed {001} facets
have gained increasing interest for photocatalytic applications. To
fully understand the structure-to-activity relation, combined
experimental and computational methods have been exploited.
Anatase nanosheets were prepared under hydrothermal conditions
in the presence of fluorine ions. High resolution scanning
transmission electron microscopy was used to fully characterize
the synthesized material, confirming the TiO2 nanosheet
morphology. Moreover, the surface structure and composition
of a single nanosheet could be determined by annular bright-field
scanning transmission electron microscopy (ABF-STEM) and
STEM electron energy loss spectroscopy (STEM-EELS). The photocatalytic activity was tested for the decomposition of organic
dyes rhodamine 6G and methyl orange and compared to a reference TiO2 anatase sample. The anatase nanosheets with exposed
{001} facets revealed a significantly lower photocatalytic activity compared to the reference. In order to understand the
mechanism for the catalytic performance, and to investigate the role of the presence of F−, light-induced electron paramagnetic
resonance (EPR) experiments were performed. The EPR results are in agreement with TEM, proving the presence of Ti3+
species close to the surface of the sample and allowing the analysis of the photoinduced formation of paramagnetic species.
Further, ab initio calculations of the anisotropic effective mass of electrons and electron holes in anatase show a very high effective
mass of electrons in the [001] direction, having a negative impact on the mobility of electrons toward the {001} surface and thus
the photocatalysis. Finally, motivated by the experimental results that indicate the presence of fluorine atoms at the surface, we
performed ab initio calculations to determine the position of the band edges in anatase slabs with different terminations of the
{001} surface. The presence of fluorine atoms near the surface is shown to strongly shift down the band edges, which indicates
another reason why it can be expected that the prepared samples with a large amount of {001} surface, but with fluorine atoms
near the surface, show only a low photocatalytic activity.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 4.536
Times cited: 20
DOI: 10.1021/acs.jpcc.7b05586
|
“TiO2 Films Modified with Au Nanoclusters as Self-Cleaning Surfaces under Visible Light”. Liao T-W, Verbruggen S, Claes N, Yadav A, Grandjean D, Bals S, Lievens P, Nanomaterials 8, 30 (2018). http://doi.org/10.3390/nano8010030
Abstract: In this study, we applied cluster beam deposition (CBD) as a new approach for fabricating efficient plasmon-based photocatalytic materials. Au nanoclusters (AuNCs) produced in the gas phase were deposited on TiO2 P25-coated silicon wafers with coverage ranging from 2 to 8 atomic monolayer (ML) equivalents. Scanning Electron Microscopy (SEM) images of the AuNCs modified TiO2 P25 films show that the surface is uniformly covered by the AuNCs that remain isolated at low coverage (2 ML, 4 ML) and aggregate at higher coverage (8 ML). A clear relationship between AuNCs coverage and photocatalytic activity towards stearic acid photo-oxidation was measured, both under ultraviolet and green light illumination. TiO2 P25 covered with 4 ML AuNCs showed the best stearic acid photo-oxidation performance under green light illumination (Formal Quantum Efficiency 1.6 x 10-6 over a period of 93 h). These results demonstrate the large potential of gas-phase AuNCs beam deposition technology for the fabrication of visible light active plasmonic photocatalysts.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 3.553
Times cited: 29
DOI: 10.3390/nano8010030
|
“Independent tuning of size and coverage of supported Pt nanoparticles using atomic layer deposition”. Dendooven J, Ramachandran RK, Solano E, Kurttepeli M, Geerts L, Heremans G, Ronge J, Minjauw MM, Dobbelaere T, Devloo-Casier K, Martens JA, Vantomme A, Bals S, Portale G, Coati A, Detavernier C, Nature communications 8, 1074 (2017). http://doi.org/10.1038/S41467-017-01140-Z
Abstract: Synthetic methods that allow for the controlled design of well-defined Pt nanoparticles are highly desirable for fundamental catalysis research. In this work, we propose a strategy that allows precise and independent control of the Pt particle size and coverage. Our approach exploits the versatility of the atomic layer deposition (ALD) technique by combining two ALD processes for Pt using different reactants. The particle areal density is controlled by tailoring the number of ALD cycles using trimethyl(methylcyclopentadienyl) platinum and oxygen, while subsequent growth using the same Pt precursor in combination with nitrogen plasma allows for tuning of the particle size at the atomic level. The excellent control over the particle morphology is clearly demonstrated by means of in situ and ex situ X-ray fluorescence and grazing incidence small angle X-ray scattering experiments, providing information about the Pt loading, average particle dimensions, and mean center-to-center particle distance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 88
DOI: 10.1038/S41467-017-01140-Z
|
“Artifact Reduction Based on Sinogram Interpolation for the 3D Reconstruction of Nanoparticles Using Electron Tomography”. Sentosun K, Lobato I, Bladt E, Zhang Y, Palenstijn WJ, Batenburg KJ, Van Dyck D, Bals S, Particle and particle systems characterization 34, 1700287 (2017). http://doi.org/10.1002/ppsc.201700287
Abstract: Electron tomography is a well-known technique providing a 3D characterization of the morphology and chemical composition of nanoparticles. However, several reasons hamper the acquisition of tilt series with a large number of projection images, which deteriorate the quality of the 3D reconstruction. Here, an inpainting method that is based on sinogram interpolation is proposed, which enables one to reduce artifacts in the reconstruction related to a limited tilt series of projection images. The advantages of the approach will be demonstrated for the 3D characterization of nanoparticles using phantoms and several case studies.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Vision lab
Times cited: 2
DOI: 10.1002/ppsc.201700287
|
“Exploring the Optical and Morphological Properties of Ag and Ag/TiO2 Nanocomposites Grown by Supersonic Cluster Beam Deposition”. Cavaliere E, Benetti G, Van Bael M, Winckelmans N, Bals S, Gavioli L, Nanomaterials 7, 442 (2017). http://doi.org/10.3390/nano7120442
Abstract: Nanocomposite systems and nanoparticle (NP) films are crucial for many applications and research fields. The structure-properties correlation raises complex questions due to the collective structure of these systems, often granular and porous, a crucial factor impacting their effectiveness and performance. In this framework, we investigate the optical and morphological properties of Ag nanoparticles (NPs) films and of Ag NPs/TiO₂ porous matrix films, one-step grown by supersonic cluster beam deposition. Morphology and structure of the Ag NPs film and of the Ag/TiO₂ (Ag/Ti 50-50) nanocomposite are related to the optical properties of the film employing spectroscopic ellipsometry (SE). We employ a simple Bruggeman effective medium approximation model, corrected by finite size effects of the nano-objects in the film structure to gather information on the structure and morphology of the nanocomposites, in particular porosity and average NPs size for the Ag/TiO₂ NP film. Our results suggest that SE is a simple, quick and effective method to measure porosity of nanoscale films and systems, where standard methods for measuring pore sizes might not be applicable.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.553
Times cited: 19
DOI: 10.3390/nano7120442
|
“Plasmonic Near-Field Localization of Silver Core–Shell Nanoparticle Assemblies via Wet Chemistry Nanogap Engineering”. Asapu R, Ciocarlan R-G, Claes N, Blommaerts N, Minjauw M, Ahmad T, Dendooven J, Cool P, Bals S, Denys S, Detavernier C, Lenaerts S, Verbruggen SW, ACS applied materials and interfaces 9, 41577 (2017). http://doi.org/10.1021/acsami.7b13965
Abstract: Silver nanoparticles are widely used in the field of plasmonics because of their unique optical properties. The wavelength-dependent surface plasmon resonance gives rise to a strongly enhanced electromagnetic field, especially at so-called hot spots located in the nanogap in-between metal nanoparticle assemblies. Therefore, the interparticle distance is a decisive factor in plasmonic applications, such as surface-enhanced Raman spectroscopy (SERS). In this study, the aim is to engineer this interparticle distance for silver nanospheres using a convenient wet-chemical approach and to predict and quantify the corresponding enhancement factor using both theoretical and experimental tools. This was done by building a tunable ultrathin polymer shell around the nanoparticles using the layer-by-layer method, in which the polymer shell acts as the separating interparticle spacer layer. Comparison of different theoretical approaches and corroborating the results with SERS analytical experiments using silver and silver−polymer core−shell nanoparticle clusters as SERS substrates was also done. Herewith, an approach is provided to estimate the extent of plasmonic near-field enhancement both theoretically as well as experimentally.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 7.504
Times cited: 29
DOI: 10.1021/acsami.7b13965
|
“Multimode Electron Tomography as a Tool to Characterize the Internal Structure and Morphology of Gold Nanoparticles”. Winckelmans N, Altantzis T, Grzelczak M, Sánchez-Iglesias A, Liz-Marzán LM, Bals S, The journal of physical chemistry: C : nanomaterials and interfaces 122, 13522 (2018). http://doi.org/10.1021/acs.jpcc.7b12379
Abstract: Three dimensional (3D) characterization of structural defects in nanoparticles by transmission electron microscopy is far from straightforward. We propose the use of a dose-efficient approach, so-called multimode tomography, during which tilt series of low and high angle annular dark field scanning transmission electron microscopy projection images are acquired simultaneously. In this manner, not only reliable information can be obtained concerning the shape of the nanoparticles, but also the twin planes can be clearly visualized in 3D. As an example, we demonstrate the application of this approach to identify the position of the seeds with respect to the twinning planes in anisotropic gold nanoparticles synthesized using a seed mediated growth approach.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 23
DOI: 10.1021/acs.jpcc.7b12379
|
“Do Binary Supracrystals Enhance the Crystal Stability?”.Yang Z, Altantzis T, Bals S, Tendeloo GV, Pileni M-P, The journal of physical chemistry: C : nanomaterials and interfaces 122, 13515 (2018). http://doi.org/10.1021/acs.jpcc.7b12373
Abstract: We study the oxygen thermal stability of two binary
systems. The larger particles are magnetic amorphous Co (7.2 nm) or
Fe3O4 (7.5 nm) nanocrystals, whereas the smaller ones (3.7 nm) are
Au nanocrystals. The nanocrystal ordering as well as the choice of the
magnetic nanoparticles very much influence the stability of the binary
system. A perfect crystalline structure is obtained with the Fe3O4/Au
binary supracrystals. For the Co/Au binary system, oxidation of Co
results in the chemical transformation from Co to CoO, where the size
of the amorphous Co nanoparticles increases from 7.2 to 9.8 nm in
diameter. During the volume expansion of the Co nanoparticles, Au
nanoparticles within the binary assemblies coalesce and are at the
origin of the instability of the binary nanoparticle supracrystals. On the
other hand, for the Fe3O4/Au binary system, the oxidation of Fe3O4 to
γ-Fe2O3 does not lead to a size change of the nanoparticles, which
maintains the stability of the binary nanoparticle supracrystals. A similar behavior is observed for an AlB2-type Co−Ag binary
system: The crystalline structure is maintained, whereas in disordered assemblies, coalescence of Ag nanocrystals is observed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 5
DOI: 10.1021/acs.jpcc.7b12373
|
“Highly selective gas separation membrane using in situ amorphised metal-organic frameworks”. Kertik A, Wee LH, Pfannmöller M, Bals S, Martens JA, Vankelecom IFJ, Energy &, environmental science 10, 2342 (2017). http://doi.org/10.1039/C7EE01872J
Abstract: Conventional carbon dioxide (CO2) separation in the petrochemical industry via cryogenic distillation is energy intensive and environmentally unfriendly. Alternatively, polymer membrane-based separations are of significant interest owing to low production cost, low-energy consumption and ease of upscaling. However, the implementation of commercial polymeric membranes is limited by their permeability and selectivity trade-off and the insufficient thermal and chemical stability. Herein, a novel type of amorphous mixed matrix membrane (MMM) able to separate CO2/CH4 mixtures with the highest selectivities ever reported for MOF based MMMs is presented. The MMM consists of an amorphised metal-organic framework (MOF) dispersed in an oxidatively cross-linked matrix achieved by fine tuning of the thermal treatment temperature in air up to 350 degrees C which drastically boosts the separation properties of the MMM. Thanks to the protection of the surrounding polymer, full oxidation of this MOF (i.e. ZIF-8) is prevented, and amorphisation of the MOF is realized instead, thus in situ creating a molecular sieve network. In addition, the treatment also improves the filler-polymer adhesion and induces an oxidative cross-linking of the polyimide matrix, resulting in MMMs with increased stability or plasticization resistance at high pressure up to 40 bar, marking a new milestone as new molecular sieve MOF MMMs for challenging natural gas purification applications. A new field for the use of amorphised MOFs and a variety of separation opportunities for such MMMs are thus opened.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 29.518
Times cited: 122
DOI: 10.1039/C7EE01872J
|
“Reversible Clustering of Gold Nanoparticles under Confinement”. Sánchez-Iglesias A, Claes N, Solís DM, Taboada JM, Bals S, Liz-Marzán LM, Grzelczak M, Angewandte Chemie: international edition in English 57, 3183 (2018). http://doi.org/10.1002/anie.201800736
Abstract: A limiting factor of solvent-induced nanoparticle self-assembly is the need for constant sample dilution in assembly/disassembly cycles. Changes in the nanoparticle concentration alter the kinetics of the subsequent assembly process, limiting optical signal recovery. Herein, we show that upon confining hydrophobic nanoparticles in permeable silica nanocapsules, the number of nanoparticles participating in cyclic aggregation remains constant despite bulk changes in solution, leading to highly reproducible plasmon band shifts at different solvent compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 53
DOI: 10.1002/anie.201800736
|
“Near-Infrared-Emitting CuInS2/ZnS Dot-in-Rod Colloidal Heteronanorods by Seeded Growth”. Xia C, Winckelmans N, Prins PT, Bals S, Gerritsen HC, de Mello Donegá, C, Journal of the American Chemical Society 140, 5755 (2018). http://doi.org/10.1021/jacs.8b01412
Abstract: Synthesis protocols for anisotropic CuInX2 (X = S, Se, Te)-based heteronanocrystals (HNCs) are scarce due to the difficulty in balancing the reactivities of multiple precursors and the high solid-state diffusion rates of the cations involved in the CuInX2 lattice. In this work, we report a multistep seeded growth synthesis protocol that yields colloidal wurtzite CuInS2/ZnS dot core/rod shell HNCs with photoluminescence in the NIR (∼800 nm). The wurtzite CuInS2 NCs used as seeds are obtained by topotactic partial Cu+ for In3+ cation exchange in template Cu2–xS NCs. The seed NCs are injected in a hot solution of zinc oleate and hexadecylamine in octadecene, 20 s after the injection of sulfur in octadecene. This results in heteroepitaxial growth of wurtzite ZnS primarily on the Sulfur-terminated polar facet of the CuInS2 seed NCs, the other facets being overcoated only by a thin (∼1 monolayer) shell. The fast (∼21 nm/min) asymmetric axial growth of the nanorod proceeds by addition of [ZnS] monomer units, so that the polarity of the terminal (002) facet is preserved throughout the growth. The delayed injection of the CuInS2 seed NCs is crucial to allow the concentration of [ZnS] monomers to build up, thereby maximizing the anisotropic heteroepitaxial growth rates while minimizing the rates of competing processes (etching, cation exchange, alloying). Nevertheless, a mild etching still occurred, likely prior to the onset of heteroepitaxial overgrowth, shrinking the core size from 5.5 to ∼4 nm. The insights provided by this work open up new possibilities in designing multifunctional Cu-chalcogenide based colloidal heteronanocrystals.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 43
DOI: 10.1021/jacs.8b01412
|
“Detection of amyloid fibrils in Parkinson’s disease using plasmonic chirality”. Kumar J, Eraña H, López-Martínez E, Claes N, Martín VF, Solís DM, Bals S, Cortajarena AL, Castilla J, Liz-Marzán LM, Proceedings of the National Academy of Sciences of the United States of America 115, 3225 (2018). http://doi.org/10.1073/pnas.1721690115
Abstract: Amyloid fibrils, which are closely associated with various neurodegenerative
diseases, are the final products in many protein aggregation pathways. The identification of fibrils at low concentration is, therefore, pivotal in disease diagnosis and development of therapeutic strategies. We report a methodology for the specific identification of amyloid fibrils using chiroptical effects in plasmonic nanoparticles. The formation of amyloid fibrils based on α-synuclein was probed using gold nanorods, which showed no
apparent interaction with monomeric proteins but effective adsorption onto fibril structures via noncovalent interactions. The amyloid structure drives a helical nanorod arrangement, resulting in intense optical activity at the surface plasmon resonance wavelengths. This sensing technique was successfully applied to human brain homogenates of patients affected by Parkinson’s disease,
wherein protein fibrils related to the disease were identified through chiral signals from Au nanorods in the visible and near IR, whereas healthy brain samples did not exhibit any meaningful optical activity. The technique was additionally extended to the specific detection of infectious amyloids formed by prion proteins, thereby confirming the wide potential of the technique. The intense chiral response driven by strong dipolar coupling in helical Au nanorod arrangements allowed us to detect amyloid fibrils down to nanomolar concentrations.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.661
Times cited: 187
DOI: 10.1073/pnas.1721690115
|
“Interplay of interfacial layers and blend composition to reduce thermal degradation of polymer solar cells at high temperature”. Ben Dkhil S, Pfannmöller M, Schroeder RR, Alkarsifi R, Gaceur M, Koentges W, Heidari H, Bals S, Margeat O, Ackermann J, Videlot-Ackermann C, ACS applied materials and interfaces 10, 3874 (2018). http://doi.org/10.1021/ACSAMI.7B17021
Abstract: The thermal stability of printed polymer solar cells at elevated temperatures needs to be improved to achieve high-throughput fabrication including annealing steps as well as long-term stability. During device processing, thermal annealing impacts both the organic photoactive layer, and the two interfacial layers make detailed studies of degradation mechanism delicate. A recently identified thermally stable poly[[4,8-bis[(2-ethylhexyl)oxy]benzo[1,2-b:4,5-b'-dithiopherie-2,6-diyl] [3-fluoro-2-[(2-ethylhexyl) carbonyl] thieno [3,4-b]thiophenediyl]] : [6,6]-phenyl- C-71-butyric acid methyl ester (PTB7:PC70BM) blend as photoactive layer in combination with poly(3,4-ethylenedioxythiophene) polystyrene sulfonate as hole extraction layer is used here to focus on the impact of electron extraction layer (EEL) on the thermal stability of solar cells. Solar cells processed with densely packed ZnO nanoparticle layers still show 92% of the initial efficiency after constant annealing during 1 day at 140 degrees C, whereas partially covering ZnO layers as well as an evaporated calcium layer leads to performance losses of up to 30%. This demonstrates that the nature and morphology of EELs highly influence the thermal stability of the device. We extend our study to thermally unstable PTB7:[6,6]-phenyl-C-61-butyric acid methyl ester (PC60BM) blends to highlight the impact of ZnO on the device degradation during annealing. Importantly, only 12% loss in photocurrent density is observed after annealing at 140 degrees C during 1 day when using closely packed ZnO. This is in stark contrast to literature and addressed here to the use of a stable double-sided confinement during thermal annealing. The underlying mechanism of the inhibition of photocurrent losses is revealed by electron microscopy imaging and spatially resolved spectroscopy. We found that the double-sided confinement suppresses extensive fullerene diffusion during the annealing step, but with still an increase in size and distance of the enriched donor and acceptor domains inside the photoactive layer by an average factor of 5. The later result in combination with comparably small photocurrent density losses indicates the existence of an efficient transport of minority charge carriers inside the donor and acceptor enriched phases in PTB7:PC60BM blends.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.504
Times cited: 9
DOI: 10.1021/ACSAMI.7B17021
|
“Characterization of silver-polymer core–shell nanoparticles using electron microscopy”. Claes N, Asapu R, Blommaerts N, Verbruggen SW, Lenaerts S, Bals S, Nanoscale 10, 9186 (2018). http://doi.org/10.1039/C7NR09517A
Abstract: Silver-polymer core–shell nanoparticles show interesting optical properties, making them widely applicable in the field of plasmonics. The uniformity, thickness and homogeneity of the polymer shell will affect the properties of the system which makes a thorough structural characterization of these core–shell silver-polymer nanoparticles of great importance. However, visualizing the shell and the particle simultaneously is far from straightforward due to the sensitivity of the polymer shell towards the electron beam. In this study, we use different 2D and 3D electron microscopy techniques to investigate different structural aspects of the polymer coating.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 7.367
Times cited: 11
DOI: 10.1039/C7NR09517A
|