Abstract: In this work we present for the first time, to our knowledge, the CVD epitaxial growth of beta -SiC using an ion beam synthesized (IBS) beta -SiC layer as seed, which has been formed by multiple implantation into Si wafers at 500 degreesC. The ion beam synthesized continuous layer is constituted by beta -SiC nanocrystals that are well oriented relative to the silicon substrate. Comparison of the epitaxial growth on these samples with that on silicon test samples, both on and off-axis, is performed. The results show that the epitaxial growth can be achieved on the IBS samples without the need of the carbonization step and that the structural quality of the CVD layer is comparable to that obtained on a carbonized silicon sample. Improvement of the quality of the deposited layer is proposed.

Abstract: Multiwall carbon nanotubes are produced by decomposition of acetylene at 600 degreesC on metal catalysts supported on NaY zeolite. The support and the metal are eliminated by dissolving them in aqueous hydrofluoric acid (HF). Two methods were used to eliminate the pyrolitic carbon: oxidation in air at 500 degreesC and oxidation by potassium permanganate in acidic solution at 70 degreesC. The progress and efficacy of the purification methods are verified by TEM. The properties of the purified multiwalled carbon nanotubes are probed using C-13 and Xe-129 NMR spectroscopy under continuous-flow optical-pumping conditions. Xenon is shown to penetrate the interior of the nanotubes. A distribution of inner tube diameters gives rise to chemical shift dispersion. When the temperature is lowered, an increasing fraction of xenon resides inside the nanotubes and is not capable of exchanging with xenon in the interparticle space. In the case of the permanganate-oxidized sample, rapid xenon relaxation is attributed to interaction with residual MnO2 nanoparticles in the interior of the tubes.

Abstract: Rutherford backscattering and channeling spectrometry (RBS), photoluminescence (PL) spectroscopy and transmission electron microscopy (TEM) have been used to investigate macroscopic and microscopic segregation in MOCVD grown InGaN layers. The PL peak energy and In content (measured by RES) were mapped at a large number of distinct points on the samples. An indium concentration of 40%, the highest measured in this work, corresponds to a PL peak of 710 nn strongly suggesting that the light-emitting regions of the sample me very indium-rich compared to the average measured by RES. Cross-sectional TEM observations show distinctive layering of the InGaN films. The TEM study further reveals that these layers consist of amorphous pyramidal contrast features with sizes of order 10 nm The composition of these specific contrast features is shown to be In-rich compared to the nitride matrix.

Abstract: A two-step process for the formation of sensitivity centers different from earlier described two-step processes was found for sulfur sensitized emulsions. After deposition of sulfur in the first step, it was found that the second step does not consist of rearrangement of sulfur over the surface, but of the supply of silver interstitial ions towards the deposited sulfur clusters. The two processes could be separated by adsorbing and desorbing TAI (4-hydroxy-1, 3,3a, 7-tetraazaindene) at/from the silver halide surface. When 1.5 mmol TAI/mol Ag is added before the sulfur reaction, the silver interstitials are immobilized but sulfur still can be deposited at the same level. By lowering the pH to 2.50 after this sulfur reaction, TAI is desorbed from the surface and the released interstitials then cause a restoration of the properties of a sulfur system without TAI. These effects could be demonstrated via diffuse reflectance spectroscopy (DRS), sensitometry and dielectric loss measurements. We could also confirm the isolation of silver sulfide clusters by TAI from other chemicals in the solution, by adsorption of TAI on the clusters.

Abstract: Not much about the effect of thiocyanate addition on the sulphur ripening is known, although it is used for many applications in photographic practice. Via a combination of tracer analysis and diffuse reflectance spectroscopy the effect of thiocyanate addition on the sulphur and sulphur-plus-gold ripening could be unveiled. When thiocyanate is added prior to the sulphur addition, it appears to rearrange the silver halide surface in such way that the sulphur deposition rate is enhanced, but the supply of interstitials is limited. Addition of thiocyanate after the sulphur reaction results in the formation of thiocyanate complexes with silver, from which a silver ion is more easily deposited in a surface cell of the silver sulphide clusters thus enhancing the sensitization rate. For sulphur-plus-gold sensitized emulsions it was observed that part of the gold ions could be removed out of the Ag2-xAuxS clusters by addition of thiocyanate ions and subsequent washing. Hence, it was concluded that two different types of gold ions are present in the silver sulphide clusters; 1. gold ions which are substitutional for silver (bound between sulphur and bromide ions) 2. gold ions which bridge two or three sulphur atoms. Incorporation of gold ions into silver sulphide clusters suppresses their optical absorption in diffuse reflectance spectroscopy. Since the optical absorption at 505 nm can completely be restored by addition of thiocyanate, it is assumed that the entity absorbing at this wavelength is a monomer of silver sulphide.

Abstract: Multishell tabular grains have a higher speed than pure AgBr tabular grains. Usually the shells differ in size and iodide content, but also the precipitation method for the iodide containing shells has an influence on the iodide incorporation. A TEM investigation was performed to determine the defect structure of multishell AgBr (111) tabular crystals containing a shell with a low iodide concentration and one with a high iodide concentration. The twins that induce tabular growth and stacking fault contrast in the region of the iodide shells have been observed, similar to previously studied AgBr/Ag(Br,I) coreshell crystals. Moreover in some of the crystals dislocations have been observed, sometimes even an entire network. The number of dislocations formed varies for the different methods of iodide addition. Also variations in average thickness between the different iodide addition methods have been observed. A higher number of dislocations and thicker crystals point towards a higher local concentration of iodide. These observations allow deciding which iodide incorporation method is most useful for a preferred dislocation pattern.