“Monitoring oxygen production on mass-selected iridium–tantalum oxide electrocatalysts”. Zheng Y-R, Vernieres J, Wang Z, Zhang K, Hochfilzer D, Krempl K, Liao T-W, Presel F, Altantzis T, Fatermans J, Scott SB, Secher NM, Moon C, Liu P, Bals S, Van Aert S, Cao A, Anand M, Nørskov JK, Kibsgaard J, Chorkendorff I, Nature Energy (2021). http://doi.org/10.1038/s41560-021-00948-w
Abstract: Development of low-cost and high-performance oxygen evolution reaction catalysts is key to implementing polymer electrolyte membrane water electrolyzers for hydrogen production. Iridium-based oxides are the state-of-the-art acidic oxygen evolution reactio catalysts but still suffer from inadequate activity and stability, and iridium's scarcity motivates the discovery of catalysts with lower iridium loadings. Here we report a mass-selected iridium-tantalum oxide catalyst prepared by a magnetron-based cluster source with considerably reduced noble-metal loadings beyond a commercial IrO2 catalyst. A sensitive electrochemistry/mass-spectrometry instrument coupled with isotope labelling was employed to investigate the oxygen production rate under dynamic operating conditions to account for the occurrence of side reactions and quantify the number of surface active sites. Iridium-tantalum oxide nanoparticles smaller than 2 nm exhibit a mass activity of 1.2 ± 0.5 kA “g” _“Ir” ^“-1” and a turnover frequency of 2.3 ± 0.9 s-1 at 320 mV overpotential, which are two and four times higher than those of mass-selected IrO2, respectively. Density functional theory calculations reveal that special iridium coordinations and the lowered aqueous decomposition free energy might be responsible for the enhanced performance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Times cited: 95
DOI: 10.1038/s41560-021-00948-w
|
|
|
“Advanced electron tomography of nanoparticle assemblies”. Altantzis T, Zanaga D, Bals S, Europhysics letters 119, 38001 (2017). http://doi.org/10.1209/0295-5075/119/38001
Abstract: Nanoparticle assemblies have attracted enormous scientific interest during the last
years, due to their unique properties compared to those of their building blocks. To understand
the origin of these properties and to establish the connection with their structure, a detailed and
quantitative structural characterization is essential. Transmission electron microscopy has been
widely used to investigate nano-assemblies. However, TEM images only correspond to a twodimensional
projection of a three-dimensional object. Therefore, in order to obtain the necessary
3D structural information electron tomography has to be applied. By means of advanced electron
tomography, both qualitative and quantitative information can be obtained, which can be used
for detailed theoretical studies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 8
DOI: 10.1209/0295-5075/119/38001
|
|
|
“Composite Supraparticles with Tunable Light Emission”. Montanarella F, Altantzis T, Zanaga D, Rabouw FT, Bals S, Baesjou P, Vanmaekelbergh D, van Blaaderen A, ACS nano 11, 9136 (2017). http://doi.org/10.1021/acsnano.7b03975
Abstract: Robust luminophores emitting light with broadly tunable colors are desirable in many applications such as light-emitting diode (LED)-based lighting, displays, integrated optoelectronics and biology. Nanocrystalline quantum dots with multicolor emission, from core- and shell-localized excitons, as well as solid layers of mixed quantum dots that emit different colors have been proposed. Here, we report on colloidal supraparticles that are composed of three types of Cd(Se,ZnS) core/(Cd,Zn)S shell nanocrystals with emission in the red, green, and blue. The emission of the supraparticles can be varied from pure to composite colors over the entire visible region and finetuned into variable shades of white light by mixing the nanocrystals in controlled proportions. Our approach results in supraparticles with sizes spanning the colloidal domain and beyond that combine versatility and processability with a broad, stable, and tunable emission, promising applications in lighting devices and biological research.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 36
DOI: 10.1021/acsnano.7b03975
|
|
|
“Shape Control of Colloidal Cu2-x S Polyhedral Nanocrystals by Tuning the Nucleation Rates”. van der Stam W, Gradmann S, Altantzis T, Ke X, Baldus M, Bals S, de Mello Donega C, Chemistry of materials 28, 6705 (2016). http://doi.org/10.1021/acs.chemmater.6b03098
Abstract: Synthesis protocols for colloidal nanocrystals (NCs) with narrow size and shape distributions are of particular interest for the successful implementation of these nanocrystals into devices. Moreover, the preparation of NCs with well-defined crystal phases is of key importance. In this work, we show that Sn(IV)-thiolate complexes formed in situ strongly influence the nucleation and growth rates of colloidal Cu2-x S polyhedral NCs, thereby dictating their final size, shape, and crystal structure. This allowed us to successfully synthesize hexagonal bifrustums and hexagonal bipyramid NCs with low-chalcocite crystal structure, and hexagonal nanoplatelets with various thicknesses and aspect ratios with the djurleite crystal structure, by solely varying the concentration of Sn(IV)-additives (namely, SnBr4) in the reaction medium. Solution and solid-state 119Sn NMR measurements show that SnBr4 is converted in situ to Sn(IV)-thiolate complexes, which increase the Cu2-x S nucleation barrier without affecting the precursor conversion rates. This influences both the nucleation and growth rates in a concentration-dependent fashion and leads to a better separation between nucleation and growth. Our approach of tuning the nucleation and growth rates with in situ-generated Sn-thiolate complexes might have a more general impact due to the availability of various metal-thiolate complexes, possibly resulting in polyhedral NCs of a wide variety of metal-sulfide compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 27
DOI: 10.1021/acs.chemmater.6b03098
|
|
|
“Highly Emissive Divalent-Ion-Doped Colloidal CsPb1–xMxBr3Perovskite Nanocrystals through Cation Exchange”. van der Stam W, Geuchies JJ, Altantzis T, van den Bos KHW, Meeldijk JD, Van Aert S, Bals S, Vanmaekelbergh D, de Mello Donega C, Journal of the American Chemical Society 139, 4087 (2017). http://doi.org/10.1021/jacs.6b13079
Abstract: Colloidal CsPbX3 (X = Br, Cl, and I) perovskite nanocrystals (NCs) have emerged as promising phosphors and solar cell materials due to their remarkable optoelectronic properties. These properties can be tailored by not only controlling the size and shape of the NCs but also postsynthetic composition tuning through topotactic
anion exchange. In contrast, property control by cation exchange is still underdeveloped for colloidal CsPbX3 NCs. Here, we present a method that allows partial cation exchange in colloidal CsPbBr3 NCs, whereby Pb2+ is exchanged for several isovalent cations, resulting in doped CsPb1−xMxBr3 NCs (M= Sn2+, Cd2+, and Zn2+; 0 < x ≤ 0.1), with preservation of the original NC shape. The size of the parent NCs is also preserved in the product NCs, apart from a small (few
%) contraction of the unit cells upon incorporation of the guest cations. The partial Pb2+ for M2+ exchange leads to a blue-shift of the optical spectra, while maintaining the high photoluminescence quantum yields (>50%), sharp absorption features, and narrow emission of the parent CsPbBr3 NCs. The blue-shift in the optical spectra is attributed to the lattice contraction that accompanies the Pb2+ for M2+ cation exchange and is observed to scale linearly with the lattice contraction. This work opens up new possibilities to engineer the properties of halide perovskite NCs, which to date are demonstrated to be the only known
system where cation and anion exchange reactions can be sequentially combined while preserving the original NC shape, resulting in compositionally diverse perovskite NCs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 535
DOI: 10.1021/jacs.6b13079
|
|
|
“3D Atomic‐Scale Dynamics of Laser‐Light‐Induced Restructuring of Nanoparticles Unraveled by Electron Tomography”. Albrecht W, Arslan Irmak E, Altantzis T, Pedrazo‐Tardajos A, Skorikov A, Deng T‐S, van der Hoeven JES, van Blaaderen A, Van Aert S, Bals S, Advanced Materials , 2100972 (2021). http://doi.org/10.1002/adma.202100972
Abstract: Understanding light–matter interactions in nanomaterials is crucial for
optoelectronic, photonic, and plasmonic applications. Specifically, metal
nanoparticles (NPs) strongly interact with light and can undergo shape
transformations, fragmentation and ablation upon (pulsed) laser excitation.
Despite being vital for technological applications, experimental insight into
the underlying atomistic processes is still lacking due to the complexity of
such measurements. Herein, atomic resolution electron tomography is performed
on the same mesoporous-silica-coated gold nanorod, before and after
femtosecond laser irradiation, to assess the missing information. Combined
with molecular dynamics (MD) simulations based on the experimentally
determined 3D atomic-scale morphology, the complex atomistic rearrangements,
causing shape deformations and defect generation, are unraveled.
These rearrangements are simultaneously driven by surface diffusion, facet
restructuring, and strain formation, and are influenced by subtleties in the
atomic distribution at the surface.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 19.791
Times cited: 8
DOI: 10.1002/adma.202100972
|
|
|
“Enhanced electrochemical performance of Li-rich cathode materials through microstructural control”. Serrano-Sevillano J, Reynaud M, Saracibar A, Altantzis T, Bals S, van Tendeloo G, Casas-Cabanas M, Physical chemistry, chemical physics 20, 23112 (2018). http://doi.org/10.1039/C8CP04181D
Abstract: The microstructural complexity of Li-rich cathode materials has so far hampered understanding the critical link between size, morphology and structural defects with both capacity and voltage fadings that this family of materials exhibits. Li2MnO3 is used here as a model material to extract reliable structure–property
relationships that can be further exploited for the development of high-performing and long-lasting Li-rich oxides. A series of samples with microstructural variability have been prepared and thoroughly characterized using the FAULTS software, which allows quantification of planar defects and extraction of
average crystallite sizes. Together with transmission electron microscopy (TEM) and density functional theory (DFT) results, the successful application of FAULTS analysis to Li2MnO3 has allowed rationalizing the synthesis conditions and identifying the individual impact of concurrent microstructural features on
both voltage and capacity fadings, a necessary step for the development of high-capacity Li-ion cathode materials with enhanced cycle life.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.123
Times cited: 36
DOI: 10.1039/C8CP04181D
|
|
|
“Recent breakthroughs in scanning transmission electron microscopy of small species”. van den Bos KHW, Altantzis T, De Backer A, Van Aert S, Bals S, Advances in Physics: X 3, 1480420 (2018). http://doi.org/10.1080/23746149.2018.1480420
Abstract: Over the last decade, scanning transmission electron microscopy has become one of the most powerful tools to characterise nanomaterials at the atomic scale. Often, the ultimate goal is to retrieve the three-dimensional structure, which is very challenging since small species are typically sensitive to electron irradiation. Nevertheless, measuring individual atomic positions is crucial to understand the relation between the structure and physicochemical properties of these (nano)materials. In this review, we highlight the latest approaches that are available to reveal the 3D atomic structure of small species. Finally, we will provide an outlook and will describe future challenges where the limits of electron microscopy will be pushed even further.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 8
DOI: 10.1080/23746149.2018.1480420
|
|
|
“3D porous nanostructured platinum prepared using atomic layer deposition”. Pulinthanathu Sree S, Dendooven J, Geerts L, Ramachandran RK, Javon E, Ceyssens F, Breynaert E, Kirschhock CEA, Puers R, Altantzis T, Van Tendeloo G, Bals S, Detavernier C, Martens JA, Journal of materials chemistry A : materials for energy and sustainability 5, 19007 (2017). http://doi.org/10.1039/C7TA03257A
Abstract: A robust and easy to handle 3D porous platinum structure was created via replicating the 3D channel system
of an ordered mesoporous silica material using atomic layer deposition (ALD) over micrometer distances.
After ALD of Pt in the silica material, the host template was digested using hydrogen fluoride (HF). A fully
connected ordered Pt nanostructure was obtained with morphology and sizes corresponding to that of
the pores of the host matrix, as revealed with high-resolution scanning transmission electron
microscopy and electron tomography. The Pt nanostructure consisted of hexagonal Pt rods originating
from the straight mesopores (11 nm) of the host structure and linking features resulting from Pt
replication of the interconnecting mesopore segments (2–4 nm) present in the silica host structure.
Electron tomography of partial replicas, made by incomplete infilling of Zeotile-4 material with Pt,
provided insight in the connectivity and formation mechanism of the Pt nanostructure by ALD. The Pt
replica was evaluated for its potential use as electrocatalyst for the hydrogen evolution reaction, one of
the half-reactions of water electrolysis, and as microelectrode for biomedical sensing. The Pt replica
showed high activity for the hydrogen evolution reaction and electrochemical characterization revealed
a large impedance improvement in comparison with reference Pt electrodes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 9
DOI: 10.1039/C7TA03257A
|
|
|
“Tunable porous nanoallotropes prepared by post-assembly etching of binary nanoparticle superlattices”. Udayabhaskararao T, Altantzis T, Houben L, Coronado-Puchau M, Langer J, Popovitz-Biro R, Liz-Marzán LM, Vuković, L, Král P, Bals S, Klajn R, Science 358, 514 (2017). http://doi.org/10.1126/science.aan6046
Abstract: Self-assembly of inorganic nanoparticles has been used to prepare hundreds of different colloidal crystals, but almost invariably with the restriction that the particles must be densely packed. Here,we show that non–close-packed nanoparticle arrays can be fabricated through the selective removal of one of two components comprising binary nanoparticle superlattices. First, a variety of binary nanoparticle superlattices were prepared at the liquid-air interface, including several arrangements that were previously unknown. Molecular dynamics simulations revealed the particular role of the liquid in templating the formation of superlattices not achievable through self-assembly in bulk solution. Second, upon stabilization, all of these binary superlattices could be transformed into distinct “nanoallotropes”—nanoporous materials having the same chemical composition but differing in their nanoscale architectures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 37.205
Times cited: 113
DOI: 10.1126/science.aan6046
|
|
|
“Optimized 3D Reconstruction of Large, Compact Assemblies of Metallic Nanoparticles”. Altantzis T, Wang D, Kadu A, van Blaaderen A, Bals S, Journal Of Physical Chemistry C 125, 26240 (2021). http://doi.org/10.1021/acs.jpcc.1c08478
Abstract: 3D characterization of assemblies of nanoparticles is of great importance to determine their structure-property connection. Such investigations become increasingly more challenging when the assemblies become larger and more compact. In this paper, we propose an optimized approach for electron tomography to minimize artefacts related to beam broadening in High Angle Annular Dark-Field Scanning Transmission Electron Microscopy mode. These artefacts are typically present at one side of the reconstructed 3D data set for thick nanoparticle assemblies. To overcome this problem, we propose a procedure in which two tomographic tilt series of the same sample are acquired. After acquiring the first series, the sample is flipped over 180o, and a second tilt series is acquired. By merging the two reconstructions, blurring in the reconstructed volume is minimized. Next, this approach is combined with an advanced three-dimensional reconstruction algorithm yielding quantitative structural information. Here, the approach is applied to a thick and compact assembly of spherical Au nanoparticles, but the methodology can we used to investigate a broad range of samples.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 4.536
Times cited: 4
DOI: 10.1021/acs.jpcc.1c08478
|
|
|
“Understanding the Effect of Iodide Ions on the Morphology of Gold Nanorods”. Amini MN, Altantzis T, Lobato I, Grzelczak M, Sánchez-Iglesias A, Van Aert S, Liz-Marzán LM, Partoens B, Bals S, Neyts EC, Particle and particle systems characterization 35, 1800051 (2018). http://doi.org/10.1002/ppsc.201800051
Abstract: The presence of iodide ions during the growth of gold nanorods strongly affects the shape of the final products, which is proposed to be due to selective iodide adsorption on certain crystallographic facets. Therefore, a detailed structural and morphological characterization of the starting rods is crucial toward understanding this effect. Electron tomography is used to determine the crystallographic indices of the lateral facets of gold nanorods, as well as those present at the tips. Based on this information, density functional theory calculations are used to determine the surface and interface energies of the observed facets and provide insight into the relationship between the amount of iodide ions in the growth solution and the final morphology of anisotropic gold nanoparticles.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.474
Times cited: 6
DOI: 10.1002/ppsc.201800051
|
|
|
“Three-Dimensional Quantification of the Facet Evolution of Pt Nanoparticles in a Variable Gaseous Environment”. Altantzis T, Lobato I, De Backer A, Béché, A, Zhang Y, Basak S, Porcu M, Xu Q, Sánchez-Iglesias A, Liz-Marzán LM, Van Tendeloo G, Van Aert S, Bals S, Nano letters 19, 477 (2019). http://doi.org/10.1021/acs.nanolett.8b04303
Abstract: Pt nanoparticles play an essential role in a wide variety of catalytic reactions. The activity of the particles strongly depends on their three-dimensional (3D) structure and exposed facets, as well as on the reactive environment. High-resolution electron microscopy has often been used to characterize nanoparticle catalysts but unfortunately most observations so far have been either performed in vacuum and/or using conventional (2D) in situ microscopy. The latter however does not provide direct 3D morphological information. We have implemented a quantitative methodology to measure variations of the 3D atomic structure of nanoparticles under the flow of a selected gas. We were thereby able to quantify refaceting of Pt nanoparticles with atomic resolution during various oxidation−reduction cycles. In a H2 environment, a more faceted surface morphology of the particles was observed with {100} and {111} planes being dominant. On the other hand, in O2 the percentage of {100} and {111} facets decreased and a significant increase of higher order facets was found, resulting in a more rounded morphology. This methodology opens up new opportunities toward in situ characterization of catalytic nanoparticles because for the first time it enables one to directly measure 3D morphology variations at the atomic scale in a specific gaseous reaction environment.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 82
DOI: 10.1021/acs.nanolett.8b04303
|
|
|
“Restructuring of titanium oxide overlayers over nickel nanoparticles during catalysis”. Monai M, Jenkinson K, Melcherts AEM, Louwen JN, Irmak EA, Van Aert S, Altantzis T, Vogt C, van der Stam W, Duchon T, Smid B, Groeneveld E, Berben P, Bals S, Weckhuysen BM, Science 380, 644 (2023). http://doi.org/10.1126/SCIENCE.ADF6984
Abstract: Reducible supports can affect the performance of metal catalysts by the formation of suboxide overlayers upon reduction, a process referred to as the strong metal-support interaction (SMSI). A combination of operando electron microscopy and vibrational spectroscopy revealed that thin TiOx overlayers formed on nickel/titanium dioxide catalysts during 400 degrees C reduction were completely removed under carbon dioxide hydrogenation conditions. Conversely, after 600 degrees C reduction, exposure to carbon dioxide hydrogenation reaction conditions led to only partial reexposure of nickel, forming interfacial sites in contact with TiOx and favoring carbon-carbon coupling by providing a carbon species reservoir. Our findings challenge the conventional understanding of SMSIs and call for more-detailed operando investigations of nanocatalysts at the single-particle level to revisit static models of structure-activity relationships.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 56.9
Times cited: 29
DOI: 10.1126/SCIENCE.ADF6984
|
|
|
“Disentangling the effect of seed size and crystal habit on gold nanoparticle seeded growth”. González-Rubio G, de Oliveira TM, Altantzis T, La Porta A, Guerrero-Martínez A, Bals S, Scarabelli L, Liz-Marzán LM, Chemical communications 53, 11360 (2017). http://doi.org/10.1039/C7CC06854A
Abstract: Oxidative etching was used to produce gold seeds of different sizes and crystal habits. Following detailed characterization, the seeds were grown under different conditions. Our results bring new insights toward understanding the effect of size and crystallinity on the growth of anisotropic particles, whilst identifying guidelines for the optimisation of new synthetic protocols of predesigned seeds.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 29
DOI: 10.1039/C7CC06854A
|
|
|
“Controlled Surface Modification of ZnO Nanostructures with Amorphous TiO2for Photoelectrochemical Water Splitting”. Gasparotto A, Maccato C, Sada C, Carraro G, Kondarides DI, Bebelis S, Petala A, La Porta A, Altantzis T, Barreca D, Advanced Sustainable Systems , 1900046 (2019). http://doi.org/10.1002/adsu.201900046
Abstract: The utilization of solar radiation to trigger photoelectrochemical (PEC) water splitting has gained interest for sustainable energy production. In this study, attention is focused on the development of ZnO–TiO2 nanocomposite photoanodes. The target systems are obtained by growing porous arrays of highly crystalline, elongated ZnO nanostructures on indium tin oxide (ITO) by chemical vapor deposition. Subsequently, the obtained nanodeposits are functionalized with TiO2 via radio frequency-sputtering for different process durations, and subjected to final annealing in air. Characterization results demonstrate the successful formation of high purity composite systems in which the surface of ZnO nanostructures is decorated by ultra-small amounts of amorphous titania, whose content can be conveniently tailored as a function of deposition time. Photocurrent density measurements in sunlight triggered water splitting highlight a remarkable performance enhancement with respect to single-phase zinc and titanium oxides, with up to a threefold photocurrent increase compared to bare ZnO. These results, mainly traced back to the formation of ZnO/TiO2 heterojunctions yielding an improved photocarrier separation, show that the target nanocomposites are attractive photoanodes for efficient PEC water splitting.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
DOI: 10.1002/adsu.201900046
|
|
|
“Stabilization effects in binary colloidal Cu and Ag nanoparticle electrodes under electrochemical CO₂, reduction conditions”. Wu L, Kolmeijer KE, Zhang Y, An H, Arnouts S, Bals S, Altantzis T, Hofmann JP, Costa Figueiredo M, Hensen EJM, Weckhuysen BM, van der Stam W, Nanoscale 13, 4835 (2021). http://doi.org/10.1039/D0NR09040A
Abstract: Nanoparticle modified electrodes constitute an attractive way to tailor-make efficient carbon dioxide (CO2) reduction catalysts. However, the restructuring and sintering processes of nanoparticles under electrochemical reaction conditions not only impedes the widespread application of nanoparticle catalysts, but also misleads the interpretation of the selectivity of the nanocatalysts. Here, we colloidally synthesized metallic copper (Cu) and silver (Ag) nanoparticles with a narrow size distribution (<10%) and utilized them in electrochemical CO2 reduction reactions. Monometallic Cu and Ag nanoparticle electrodes showed severe nanoparticle sintering already at low overpotential of -0.8 V vs. RHE, as evidenced by ex situ SEM investigations, and potential-dependent variations in product selectivity that resemble bulk Cu (14% for ethylene at -1.3 V vs. RHE) and Ag (69% for carbon monoxide at -1.0 V vs. RHE). However, by co-deposition of Cu and Ag nanoparticles, a nanoparticle stabilization effect was observed between Cu and Ag, and the sintering process was greatly suppressed at CO2 reducing potentials (-0.8 V vs. RHE). Furthermore, by varying the Cu/Ag nanoparticle ratio, the CO2 reduction reaction (CO2RR) selectivity towards methane (maximum of 20.6% for dense Cu-2.5-Ag-1 electrodes) and C-2 products (maximum of 15.7% for dense Cu-1-Ag-1 electrodes) can be tuned, which is attributed to a synergistic effect between neighbouring Ag and Cu nanoparticles. We attribute the stabilization of the nanoparticles to the positive enthalpies of Cu-Ag solid solutions, which prevents the dissolution-redeposition induced particle growth under CO2RR conditions. The observed nanoparticle stabilization effect enables the design and fabrication of active CO2 reduction nanocatalysts with high durability.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 7.367
Times cited: 24
DOI: 10.1039/D0NR09040A
|
|
|
“Controlled Growth of Supported ZnO Inverted Nanopyramids with Downward Pointing Tips”. Barreca D, Carraro G, Maccato C, Altantzis T, Kaunisto K, Gasparotto A, Crystal growth &, design , acs.cgd.8b00198 (2018). http://doi.org/10.1021/acs.cgd.8b00198
Abstract: High purity porous ZnO nanopyramids with controllable properties are grown on their tips on
Si(100) substrates by means of a catalyst-free vapor phase deposition route in a wet oxygen
reaction environment. The system degree of preferential [001] orientation, as well as
nanopyramid size, geometrical shape and density distribution, can be finely tuned by varying the
growth temperature between 300 and 400°C, whereas higher temperatures lead to more compact
systems with a three-dimensional (3D) morphology. A growth mechanism of the obtained ZnO
nanostructures based on a self-catalytic vapor-solid (VS) mode is proposed, in order to explain
the evolution of nanostructure morphologies as a function of the adopted process conditions. The
results obtained by a thorough chemico-physical characterization enable to get an improved
control over the properties of ZnO nanopyramids grown by this technique. Taken together, they
are of noticeable importance not only for fundamental research on ZnO nanomaterials with
controlled nano-organization, but also to tailor ZnO functionalities in view of various potential
applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 6
DOI: 10.1021/acs.cgd.8b00198
|
|
|
“Femtosecond Laser-Controlled Tip-to-Tip Assembly and Welding of Gold Nanorods”. Gonzalez-Rubio G, Gonzalez-Izquierdo J, Banares L, Tardajos G, Rivera A, Altantzis T, Bals S, Pena-Rodriguez O, Guerrero-Martinez A, Liz-Marzan LM, Nano letters 15, 8282 (2015). http://doi.org/10.1021/acs.nanolett.5b03844
Abstract: Directed assembly of gold nanorods through the use of dithiolated molecular linkers is one of the most efficient methodologies for the morphologically controlled tip-to-tip assembly of this type of anisotropic nanocrystals. However, in a direct analogy to molecular polymerization synthesis, this process is characterized by difficulties in chain-growth control over nanoparticle oligomers. In particular, it is nearly impossible to favor the formation of one type of oligomer, making the methodology hard to use for actual applications in nanoplasmonics. We propose here a light-controlled synthetic procedure that allows obtaining selected plasmonic oligomers in high yield and with reaction times in the scale of minutes by irradiation with low fluence near-infrared (NIR) femtosecond laser pulses. Selective inhibition of the formation of gold nanorod n-mers (trimers) with a longitudinal localized surface plasmon in resonance with a 800 nm Ti:sapphire laser, allowed efficient trapping of the (n – 1)-mers (dimers) by hot spot mediated photothermal decomposition of the interparticle molecular linkers. Laser irradiation at higher energies produced near-field enhancement at the interparticle gaps, which is large enough to melt gold nanorod tips, offering a new pathway toward tip-to-tip welding of gold nanorod oligomers with a plasmonic response at the NIR. Thorough optical and electron microscopy characterization indicates that plasmonic oligomers can be selectively trapped and welded, which has been analyzed in terms of a model that predicts with reasonable accuracy the relative concentrations of the main plasmonic species.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 101
DOI: 10.1021/acs.nanolett.5b03844
|
|
|
“Galvanic Replacement Coupled to Seeded Growth as a Route for Shape-Controlled Synthesis of Plasmonic Nanorattles”. Polavarapu L, Zanaga D, Altantzis T, Rodal-Cedeira S, Pastoriza-Santos I, Pérez-Juste J, Bals S, Liz-Marzán LM, Journal of the American Chemical Society 138, 11453 (2016). http://doi.org/10.1021/jacs.6b06706
Abstract: Shape-controlled synthesis of metal nanoparticles (NPs) requires mechanistic understanding toward the development of modern nanoscience and nanotechnology. We demonstrate here an unconventional shape transformation of Au@Ag core−shell NPs (nanorods and nanocubes) into octahedral nanorattles via roomtemperature galvanic replacement coupled with seeded growth. The corresponding morphological and chemical transformations were investigated in three dimensions, using state-of-the-art X-ray energy-dispersive spectroscopy (XEDS) tomography. The addition of a reducing agent (ascorbic acid) plays a key role in this unconventional mechanistic path, in which galvanic replacement is found to dominate initially when the shell is made of Ag, while seeded growth suppresses transmetalation when a composition of Au:Ag (∼60:40) is reached in the shell, as revealed by quantitative XEDS tomography. This work not only opens new avenues toward the shape control of hollow NPs beyond the morphology of sacrificial templates, but also expands our understanding of chemical transformations in nanoscale galvanic replacement reactions. The XEDS electron tomography study presented here can be generally applied to investigate a wide range of nanoscale morphological and chemical transformations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 75
DOI: 10.1021/jacs.6b06706
|
|
|
“Nanorattles with tailored electric field enhancement”. Schnepf MJ, Mayer M, Kuttner C, Tebbe M, Wolf D, Dulle M, Altantzis T, Formanek P, Förster S, Bals S, König TAF, Fery A, Nanoscale 9, 9376 (2017). http://doi.org/10.1039/C7NR02952G
Abstract: Nanorattles are metallic core–shell particles with core and shell separated by a dielectric spacer. These
nanorattles have been identified as a promising class of nanoparticles, due to their extraordinary high
electric-field enhancement inside the cavity. Limiting factors are reproducibility and loss of axial symmetry
owing to the movable metal core; movement of the core results in fluctuation of the nanocavity dimensions
and commensurate variations in enhancement factor. We present a novel synthetic approach for
the robust fixation of the central gold rod within a well-defined box, which results in an axisymmetric
nanorattle. We determine the structure of the resulting axisymmetric nanorattles by advanced transmission
electron microscopy (TEM) and small-angle X-ray scattering (SAXS). Optical absorption and scattering
cross-sections obtained from UV-vis-NIR spectroscopy quantitatively agree with finite-difference
time-domain (FDTD) simulations based on the structural model derived from SAXS. The predictions of
high and homogenous field enhancement are evidenced by scanning TEM electron energy loss spectroscopy
(STEM-EELS) measurement on single-particle level. Thus, comprehensive understanding of
structural and optical properties is achieved for this class of nanoparticles, paving the way for photonic
applications where a defined and robust unit cell is crucial.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 69
DOI: 10.1039/C7NR02952G
|
|
|
“Chemical and Structural Configuration of Pt Doped Metal Oxide Thin Films Prepared by Atomic Layer Deposition”. Ramachandran RK, Filez M, Solano E, Poelman H, Minjauw MM, Van Daele M, Feng J-Y, La Porta A, Altantzis T, Fonda E, Coati A, Garreau Y, Bals S, Marin GB, Detavernier C, Dendooven J, Chemistry of materials 31, 9673 (2019). http://doi.org/10.1021/acs.chemmater.9b03066
Abstract: Pt doped semiconducting metal oxides and Pt metal clusters embedded in an oxide matrix are of interest for applications such as catalysis and gas sensing, energy storage and memory devices. Accurate tuning of the dopant level is crucial for adjusting the properties of these materials. Here, a novel atomic layer deposition (ALD) based method for doping Pt into In2O3 in specific, and metals in metal oxides in general, is demonstrated. This approach combines alternating exposures of Pt and In2O3 ALD processes in a single ‘supercycle’, followed by supercycle repetition leading to multilayered nanocomposites. The atomic level control of ALD and its conformal nature make the method suitable for accurate dopant control even on high surface area supports. Oxidation state, local structural environment and crystalline phase of the embedded Pt dopants were obtained by means of X-ray characterization methods and high angle annular dark-field scanning transmission electron microscopy (HAADF-STEM). In addition, this approach allows characterization of the nucleation stages of metal ALD processes, by stacking those states multiple times in an oxide matrix. Regardless of experimental conditions, a few Pt ALD cycles leads to the formation of oxidized Pt species due to their highly dispersed nature, as proven by X-ray absorption spectroscopy (XAS). Grazing-incidence small-angle X-ray scattering (GISAXS) and highresolution scanning transmission electron microscopy, combined with energy dispersive X-ray spectroscopy (HR-STEM/EDXS) show that Pt is evenly distributed in the In2O3 metal oxide matrix without the formation of clusters. For a larger number of Pt ALD
cycles, typ. > 10, the oxidation state gradually evolves towards fully metallic, and metallic Pt clusters are obtained within the In2O3 metal oxide matrix. This work reveals how tuning of the ALD supercycle approach for Pt doping allows controlled engineering of the Pt compositional and structural configuration within a metal oxide matrix.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/acs.chemmater.9b03066
|
|
|
“Breaking structure sensitivity in CO2 hydrogenation by tuning metal–oxide interfaces in supported cobalt nanoparticles”. Parastaev A, Muravev V, Osta EH, Kimpel TF, Simons JFM, van Hoof AJF, Uslamin E, Zhang L, Struijs JJC, Burueva DB, Pokochueva EV, Kovtunov KV, Koptyug IV, Villar-Garcia IJ, Escudero C, Altantzis T, Liu P, Béché, A, Bals S, Kosinov N, Hensen EJM, Nature Catalysis 5, 1051 (2022). http://doi.org/10.1038/s41929-022-00874-4
Abstract: A high dispersion of the active metal phase of transition metals on oxide supports is important when designing efficient heterogeneous catalysts. Besides nanoparticles, clusters and even single metal atoms can be attractive for a wide range of reactions. However, many industrially relevant catalytic transformations suffer from structure sensitivity, where reducing the size of the metal particles below a certain size substantially lowers catalytic performance. A case in point is the low activity of small cobalt nanoparticles in the hydrogenation of CO and CO2. Here we show how engineering of catalytic sites at the metal–oxide interface in cerium oxide–zirconium dioxide (ceria–zirconia)-supported cobalt can overcome this structure sensitivity. Few-atom cobalt clusters dispersed on 3 nm cobalt(II)-oxide particles stabilized by ceria–zirconia yielded a highly active CO2 methanation catalyst with a specific activity higher than that of larger particles under the same conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 37.8
Times cited: 32
DOI: 10.1038/s41929-022-00874-4
|
|
|
“3D Characterization and Plasmon Mapping of Gold Nanorods Welded by Femtosecond Laser Irradiation”. Milagres de Oliveira T, Albrecht W, González-Rubio G, Altantzis T, Lobato Hoyos IP, Béché, A, Van Aert S, Guerrero-Martínez A, Liz-Marzán LM, Bals S, Acs Nano 14, acsnano.0c02610 (2020). http://doi.org/10.1021/acsnano.0c02610
Abstract: Ultrafast laser irradiation can induce morphological and structural changes in plasmonic nanoparticles. Gold nanorods (Au NRs), in particular, can be welded together upon irradiation with femtosecond laser pulses, leading to dimers and trimers through the formation of necks between individual nanorods. We used electron tomography to determine the 3D (atomic) structure at such necks for representative welding geometries and to characterize the induced defects. The spatial distribution of localized surface plasmon modes for different welding configurations was assessed by electron energy loss spectroscopy. Additionally, we were able to directly compare the plasmon line width of single-crystalline and welded Au NRs with single defects at the same resonance energy, thus making a direct link between the structural and plasmonic properties. In this manner, we show that the occurrence of (single) defects results in significant plasmon broadening.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 17.1
Times cited: 25
DOI: 10.1021/acsnano.0c02610
|
|
|
“Preparation and study of 2-D semiconductors with Dirac type bands due to the honeycomb nanogeometry”. Kalesaki E, Boneschanscher MP, Geuchies JJ, Delerue C, Morais Smith C, Evers WH, Allan G, Altantzis T, Bals S, Vanmaekelbergh D, Proceedings of the Society of Photo-optical Instrumentation Engineers
T2 –, Proceedings of SPIE 8981, 898107 (2014). http://doi.org/10.1117/12.2042882
Abstract: The interest in 2-dimensional systems with a honeycomb lattice and related Dirac-type electronic bands has exceeded the prototype graphene1. Currently, 2-dimensional atomic2,3 and nanoscale4-8 systems are extensively investigated in the search for materials with novel electronic properties that can be tailored by geometry. The immediate question that arises is how to fabricate 2-D semiconductors that have a honeycomb nanogeometry, and as a consequence of that, display a Dirac-type band structure? Here, we show that atomically coherent honeycomb superlattices of rocksalt (PbSe, PbTe) and zincblende (CdSe, CdTe) semiconductors can be obtained by nanocrystal self-assembly and facet-to-facet atomic bonding, and subsequent cation exchange. We present a extended structural analysis of atomically coherent 2-D honeycomb structures that were recently obtained with self-assembly and facet-to-facet bonding9. We show that this process may in principle lead to three different types of honeycomb structures, one with a graphene type-, and two others with a silicene-type structure. Using TEM, electron diffraction, STM and GISAXS it is convincingly shown that the structures are from the silicene-type. In the second part of this work, we describe the electronic structure of graphene-type and silicene type honeycomb semiconductors. We present the results of advanced electronic structure calculations using the sp3d5s* atomistic tight-binding method10. For simplicity, we focus on semiconductors with a simple and single conduction band for the native bulk semiconductor. When the 3-D geometry is changed into 2-D honeycomb, a conduction band structure transformation to two types of Dirac cones, one for S- and one for P-orbitals, is observed. The width of the bands depends on the honeycomb period and the coupling between the nanocrystals. Furthermore, there is a dispersionless P-orbital band, which also forms a landmark of the honeycomb structure. The effects of considerable intrinsic spin-orbit coupling are briefly considered. For heavy-element compounds such as CdTe, strong intrinsic spin-‐orbit coupling opens a non-trivial gap at the P-orbital Dirac point, leading to a quantum Spin Hall effect10-12. Our work shows that well known semiconductor crystals, known for centuries, can lead to systems with entirely new electronic properties, by the simple action of nanogeometry. It can be foreseen that such structures will play a key role in future opto-electronic applications, provided that they can be fabricated in a straightforward way.
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1117/12.2042882
|
|
|
“Surface Functionalization of Grown-on-Tip ZnO Nanopyramids: From Fabrication to Light-Triggered Applications”. Gasparotto A, Maccato C, Carraro G, Sada C, Štangar UL, Alessi B, Rocks C, Mariotti D, La Porta A, Altantzis T, Barreca D, Acs Applied Materials &, Interfaces 11, 15881 (2019). http://doi.org/10.1021/acsami.8b22744
Abstract: We report on a combined chemical vapor deposition (CVD)/radio frequency (RF) sputtering synthetic strategy for the controlled surface modification of ZnO nanostructures by Ti-containing species. Specifically, the proposed approach consists in the CVD of grown-on-tip ZnO nanopyramids, followed by titanium RF sputtering under mild conditions. The results obtained by a thorough characterization demonstrate the successful ZnO surface functionalization with dispersed Ti-containing species in low amounts. This phenomenon, in turn, yields a remarkable enhancement of photoactivated superhydrophilic behavior, self-cleaning ability, and photocatalytic performances in comparison to bare ZnO. The reasons accounting for such an improvement are unravelled by a multitechnique analysis, elucidating the interplay between material chemico-physical properties and the corresponding functional behavior. Overall, the proposed strategy stands as an amenable tool for the mastering of semiconductor-based functional nanoarchitectures through ad hoc engineering of the system surface.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 7.504
Times cited: 1
DOI: 10.1021/acsami.8b22744
|
|
|
“Thermal Stability of CoAu13Binary Nanoparticle Superlattices under the Electron Beam”. Altantzis T, Yang Z, Bals S, Van Tendeloo G, Pileni M-P, Chemistry of materials 28, 716 (2016). http://doi.org/10.1021/acs.chemmater.5b04898
Abstract: One primary goal of self-assembly in nanoscale regime is to implement multifunctional binary nanoparticle superlattices into practical use. In the last decade, considerable effort has been put into the fabrication of binary nanoparticle superlattices with controllable structure and stoichiometry. However, limited effort has been made in order to improve the stability of these binary nanoparticle superlattices, which is a prerequisite for their potential application. In this work, we demonstrate that the carbon deposition from specimen contamination can play an auxiliary role during the heat treatment of binary nanoparticle superlattices. With the in-situ carbon matrix formation, the thermal stability of CoAu 13 binary nanoparticle superlattices is unambiguously enhanced.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 10
DOI: 10.1021/acs.chemmater.5b04898
|
|
|
“Supracrystalline Colloidal Eggs: Epitaxial Growth and Freestanding Three-Dimensional Supracrystals in Nanoscaled Colloidosomes”. Yang Z, Altantzis T, Zanaga D, Bals S, Van Tendeloo G, Pileni M-P, Journal of the American Chemical Society 138, 3493 (2016). http://doi.org/10.1021/jacs.5b13235
Abstract: The concept of template-confined chemical reactions allows the synthesis of complex molecules that would hardly be producible through conventional method. This idea was developed to produce high quality nanocrystals more than 20 years ago. However, template-mediated assembly of colloidal nanocrystals is still at an elementary level, not only because of the limited templates suitable for colloidal assemblies, but also because of the poor control over the assembly of nanocrystals within a confined space. Here, we report the design of a new system called “supracrystalline colloidal eggs” formed by controlled assembly of nanocrystals into complex colloidal supracrystals through superlattice-matched epitaxial overgrowth along the existing colloidosomes. Then, with this concept, we extend the supracrystalline growth to lattice-mismatched binary nanocrystal superlattices, in order to reach anisotropic superlattice growths, yielding freestanding binary nanocrystal supracrystals that could not be produced previously.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 57
DOI: 10.1021/jacs.5b13235
|
|
|
“Do Binary Supracrystals Enhance the Crystal Stability?”.Yang Z, Altantzis T, Bals S, Tendeloo GV, Pileni M-P, The journal of physical chemistry: C : nanomaterials and interfaces 122, 13515 (2018). http://doi.org/10.1021/acs.jpcc.7b12373
Abstract: We study the oxygen thermal stability of two binary
systems. The larger particles are magnetic amorphous Co (7.2 nm) or
Fe3O4 (7.5 nm) nanocrystals, whereas the smaller ones (3.7 nm) are
Au nanocrystals. The nanocrystal ordering as well as the choice of the
magnetic nanoparticles very much influence the stability of the binary
system. A perfect crystalline structure is obtained with the Fe3O4/Au
binary supracrystals. For the Co/Au binary system, oxidation of Co
results in the chemical transformation from Co to CoO, where the size
of the amorphous Co nanoparticles increases from 7.2 to 9.8 nm in
diameter. During the volume expansion of the Co nanoparticles, Au
nanoparticles within the binary assemblies coalesce and are at the
origin of the instability of the binary nanoparticle supracrystals. On the
other hand, for the Fe3O4/Au binary system, the oxidation of Fe3O4 to
γ-Fe2O3 does not lead to a size change of the nanoparticles, which
maintains the stability of the binary nanoparticle supracrystals. A similar behavior is observed for an AlB2-type Co−Ag binary
system: The crystalline structure is maintained, whereas in disordered assemblies, coalescence of Ag nanocrystals is observed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 5
DOI: 10.1021/acs.jpcc.7b12373
|
|
|
“Insights into the Plasma-Assisted Fabrication and Nanoscopic Investigation of Tailored MnO2Nanomaterials”. Barreca D, Gri F, Gasparotto A, Altantzis T, Gombac V, Fornasiero P, Maccato C, Inorganic Chemistry 57, 14564 (2018). http://doi.org/10.1021/acs.inorgchem.8b02108
Abstract: Among transition metal oxides, MnO2 is of considerable importance for various technological end-uses,from heterogeneous catalysis to gas sensing, owing to its
structural flexibility and unique properties at the nanoscale. In this work, we demonstrate the successful fabrication of supported MnO2 nanomaterials by a catalyst-free, plasmaassisted process starting from a fluorinated manganese(II)
molecular source in Ar/O2 plasmas. A thorough multitechnique characterization aimed at the systematic investigation of material structure, chemical composition, and
morphology revealed the formation of F-doped, oxygendeficient, MnO2-based nanomaterials, with a fluorine content tunable as a function of growth temperature (TG). Whereas phase-pure β-MnO2 was obtained for 100 °C ≤ TG ≤ 300 °C, the formation of mixed phase MnO2 + Mn2O3 nanosystems took place at 400 °C. In addition, the system nano-organization could be finely tailored, resulting in a controllable evolution from wheat-ear columnar arrays to high aspect ratio pointed-tip nanorod assemblies. Concomitantly, magnetic force microscopy analyses suggested the formation of spin domains with features dependent on material morphology. Preliminary tests in Vislight activated photocatalytic degradation of rhodamine B aqueous solutions pave the way to possible applications of the target materials in wastewater purification.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 4.857
DOI: 10.1021/acs.inorgchem.8b02108
|
|