“Barrier efficiency of sponge-like La2Zr2O7 buffer layers for YBCO-coated conductors”. Molina L, Tan H, Biermans E, Batenburg KJ, Verbeeck J, Bals S, Van Tendeloo G, Superconductor science and technology 24, 065019 (2011). http://doi.org/10.1088/0953-2048/24/6/065019
Abstract: Solution derived La2Zr2O7 films have drawn much attention for potential applications as thermal barriers or low-cost buffer layers for coated conductor technology. Annealing and coating parameters strongly affect the microstructure of La2Zr2O7, but different film processing methods can yield similar microstructural features such as nanovoids and nanometer-sized La2Zr2O7 grains. Nanoporosity is a typical feature found in such films and the implications for the functionality of the films are investigated by a combination of scanning transmission electron microscopy (STEM), electron energy-loss spectroscopy (EELS) and quantitative electron tomography. Chemical solution based La2Zr2O7 films deposited on flexible Ni5 at.%W substrates with a {100}lang001rang biaxial texture were prepared for an in-depth characterization. A sponge-like structure composed of nanometer-sized voids is revealed by high-angle annular dark-field scanning transmission electron microscopy in combination with electron tomography. A three-dimensional quantification of nanovoids in the La2Zr2O7 film is obtained on a local scale. Mostly non-interconnected highly faceted nanovoids compromise more than one-fifth of the investigated sample volume. The diffusion barrier efficiency of a 170 nm thick La2Zr2O7 film is investigated by STEM-EELS, yielding a 1.8 ± 0.2 nm oxide layer beyond which no significant nickel diffusion can be detected and intermixing is observed. This is of particular significance for the functionality of YBa2Cu3O7 − δ coated conductor architectures based on solution derived La2Zr2O7 films as diffusion barriers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.878
Times cited: 31
DOI: 10.1088/0953-2048/24/6/065019
|
|
|
“Defect controlled room temperature ferromagnetism in Co-doped barium titanate nanocrystals”. Ray S, Kolen'ko YV, Kovnir KA, Lebedev OI, Turner S, Chakraborty T, Erni R, Watanabe T, Van Tendeloo G, Yoshimura M, Itoh M, Nanotechnology 23, 025702 (2012). http://doi.org/10.1088/0957-4484/23/2/025702
Abstract: Defect mediated high temperature ferromagnetism in oxide nanocrystallites is the central feature of this work. Here, we report the development of room temperature ferromagnetism in nanosized Co-doped barium titanate particles with a size of around 14 nm, synthesized by a solvothermal drying method. A combination of x-ray diffraction with state-of-the-art electron microscopy techniques confirms the intrinsic doping of Co into BaTiO3. The development of the room temperature ferromagnetism was tracked down to the different donor defects, namely hydroxyl groups at the oxygen site (\mathrm {OH}\mathrm {(O)}
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 19
DOI: 10.1088/0957-4484/23/2/025702
|
|
|
“Electronic reconstruction at n-type SrTiO3/LaAlO3 interfaces”. Verbeeck J, Bals S, Lamoen D, Luysberg M, Huijben M, Rijnders G, Brinkman A, Hilgenkamp H, Blank DHA, Van Tendeloo G, Physical review : B : condensed matter and materials physics 81, 085113 (2010). http://doi.org/10.1103/PhysRevB.81.085113
Abstract: Electron-energy-loss spectroscopy (EELS) is used to investigate single layers of LaAlO3 grown on SrTiO3 having an n-type interface as well as multilayers of LaAlO3 and SrTiO3 in which both n- and p-type interfaces occur. Only minor changes in Ti valence at the n-type interface are observed. This finding seems to contradict earlier experiments for other SrTiO3/LaAlO3 systems where large deviations in Ti valency were assumed to be responsible for the conductivity of these interfaces. Ab initio calculations have been carried out in order to interpret our EELS results. Using the concept of Bader charges, it is demonstrated that the so-called polar discontinuity is mainly resolved by lattice distortions and to a far lesser extent by changes in valency for both single layer and multilayer geometries.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 25
DOI: 10.1103/PhysRevB.81.085113
|
|
|
“End-to-end assembly of shape-controlled nanocrystals via a nanowelding approach mediated by gold domains”. Figuerola A, Franchini IR, Fiore A, Mastria R, Falqui A, Bertoni G, Bals S, Van Tendeloo G, Kudera S, Cingolani R, Manna L, Advanced materials 21, 550 (2009). http://doi.org/10.1002/adma.200801928
Abstract: Welding nanocrystals for assembly: The welding of Au domains grown on the tips of shape-controlled cadmium chalcogenide colloidal nanocrystals is used as a strategy for their assembly. Iodine-induced coagulation of selectively grown Au domains leads to assemblies such as flowerlike structures based on bullet-shaped nanocrystals, linear and cross-linked chains of nanorods, and globular networks with tetrapods as building blocks.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 110
DOI: 10.1002/adma.200801928
|
|
|
“Nitrogen control in nanodiamond produced by detonation shock-wave-assisted synthesis”. Shenderova OA, Vlasov II, Turner S, Van Tendeloo G, Orlinskii SB, Shiryaev AA, Khomich AA, Sulyanov SN, Jelezko F, Wrachtrup J, The journal of physical chemistry: C : nanomaterials and interfaces 115, 14014 (2011). http://doi.org/10.1021/jp202057q
Abstract: Development of efficient production methods of nanodiamond (ND) particles containing substitutional nitrogen and nitrogen-vacancy (NV) complexes remains an important goal in the nanodiamond community. ND synthesized from explosives is generally not among the preferred candidates for imaging applications owing to lack of optically active particles containing NV centers. In this paper, we have systematically studied representative classes of NDs produced by detonation shock wave conversion of different carbon precursor materials, namely, graphite and a graphite/hexogen mixture into ND, as well as ND produced from different combinations of explosives using different cooling methods (wet or dry cooling). We demonstrate that (i) the N content in nanodiamond particles can be controlled through a correct selection of the carbon precursor material (addition of graphite, explosives composition); (ii) particles larger than approximately 20 nm may contain in situ produced optically active NV centers, and (iii) in ND produced from explosives, NV centers are detected only in ND produced by wet synthesis. ND synthesized from a mixture of graphite/explosive contains the largest amount of NV centers formed during synthesis and thus deserves special attention.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 54
DOI: 10.1021/jp202057q
|
|
|
“Plasma-assisted synthesis of Ag/ZnO nanocomposites : first example of photo-induced H2 production and sensing”. Simon Q, Barreca D, Bekermann D, Gasparotto A, Maccato C, Comini E, Gombac V, Fornasiero P, Lebedev OI, Turner S, Devi A, Fischer RA, Van Tendeloo G, International journal of hydrogen energy 36, 15527 (2011). http://doi.org/10.1016/j.ijhydene.2011.09.045
Abstract: Ag/ZnO nanocomposites were developed by a plasma-assisted approach. The adopted strategy exploits the advantages of Plasma Enhanced-Chemical Vapor Deposition (PE-CVD) for the growth of columnar ZnO arrays on Si(100) and Al2O3 substrates, in synergy with the infiltration power of the Radio Frequency (RF)-sputtering technique for the subsequent dispersion of different amounts of Ag nanoparticles (NPs). The resulting composites, both as-prepared and after annealing in air, were thoroughly characterized with particular attention on their morphological organization, structure and composition. For the first time, the above systems have been used as catalysts in the production of hydrogen by photo-reforming of alcoholic solutions, yielding a stable H2 evolution even by the sole use of simulated solar radiation. In addition, Ag/ZnO nanocomposites presented an excellent response in the gas-phase detection of H2, opening attractive perspectives for advanced technological applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.582
Times cited: 62
DOI: 10.1016/j.ijhydene.2011.09.045
|
|
|
“A practical method to determine the effective resolution in incoherent experimental electron tomography”. Heidari Mezerji H, van den Broek W, Bals S, Ultramicroscopy 111, 330 (2011). http://doi.org/10.1016/j.ultramic.2011.01.021
Abstract: It is not straightforward to determine resolution for a 3D reconstruction when performing an electron tomography experiment. Different contributions such as missing wedge and misalignment add up and often influence the final resolution in an anisotropic manner. The conventional resolution measures can not be used for all of the reconstruction techniques, especially for iterative techniques which are more commonly used for electron tomography in materials science. Here we define a quantitative resolution measure that determines the resolution in three orthogonal directions of the reconstruction. As an application we use this measure to determine the optimum number of simultaneous iterative reconstruction technique (SIRT) iterations to reconstruct the gold nanoparticles, based on a high angle annular dark field STEM (HAADF-STEM) tilt series.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 26
DOI: 10.1016/j.ultramic.2011.01.021
|
|
|
“Production and application of electron vortex beams”. Verbeeck J, Tian H, Schattschneider P, Nature 467, 301 (2010). http://doi.org/10.1038/nature09366
Abstract: Vortex beams (also known as beams with a phase singularity) consist of spiralling wavefronts that give rise to angular momentum around the propagation direction. Vortex photon beams are widely used in applications such as optical tweezers to manipulate micrometre-sized particles and in micro-motors to provide angular momentum1, 2, improving channel capacity in optical3 and radio-wave4 information transfer, astrophysics5 and so on6. Very recently, an experimental realization of vortex beams formed of electrons was demonstrated7. Here we describe the creation of vortex electron beams, making use of a versatile holographic reconstruction technique in a transmission electron microscope. This technique is a reproducible method of creating vortex electron beams in a conventional electron microscope. We demonstrate how they may be used in electron energy-loss spectroscopy to detect the magnetic state of materials and describe their properties. Our results show that electron vortex beams hold promise for new applications, in particular for analysing and manipulating nanomaterials, and can be easily produced.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 40.137
Times cited: 626
DOI: 10.1038/nature09366
|
|
|
“Slicing the Perovskite structure with crystallographic shear planes : the AnBnO3n-2 homologous series”. Abakumov AM, Hadermann J, Batuk M, d' Hondt H, Tyablikov OA, Rozova MG, Pokholok KV, Filimonov DS, Sheptyakov DV, Tsirlin AA, Niermann D, Hemberger J, Van Tendeloo G, Antipov EV, Inorganic chemistry 49, 9508 (2010). http://doi.org/10.1021/ic101233s
Abstract: A new AnBnO3n−2 homologous series of anion-deficient perovskites has been evidenced by preparation of the members with n = 5 (Pb2.9Ba2.1Fe4TiO13) and n = 6 (Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16) in a single phase form. The crystal structures of these compounds were determined using a combination of transmission electron microscopy and X-ray and neutron powder diffraction (S.G. Ammm, a = 5.74313(7), b = 3.98402(4), c = 26.8378(4) Å, RI = 0.035, RP = 0.042 for Pb2.9Ba2.1Fe4TiO13 and S.G. Imma, a = 5.7199(1), b = 3.97066(7), c = 32.5245(8) Å, RI = 0.032, RP = 0.037 for Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16). The crystal structures of the AnBnO3n−2 homologues are formed by slicing the perovskite structure with (01)p crystallographic shear (CS) planes. The shear planes remove a layer of oxygen atoms and displace the perovskite blocks with respect to each other by the 1/2[110]p vector. The CS planes introduce edge-sharing connections of the transition metal−oxygen polyhedra at the interface between the perovskite blocks. This results in intrinsically frustrated magnetic couplings between the perovskite blocks due to a competition of the exchange interactions between the edge- and the corner-sharing metal−oxygen polyhedra. Despite the magnetic frustration, neutron powder diffraction and Mssbauer spectroscopy reveal that Pb2.9Ba2.1Fe4TiO13 and Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16 are antiferromagnetically ordered below TN = 407 and 343 K, respectively. The Pb2.9Ba2.1Fe4TiO13 and Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16 compounds are in a paraelectric state in the 5−300 K temperature range.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 23
DOI: 10.1021/ic101233s
|
|
|
“Surface chemistry and properties of ozone-purified detonation nanodiamonds”. Shenderova O, Koscheev A, Zaripov N, Petrov I, Skryabin Y, Detkov P, Turner S, Van Tendeloo G, The journal of physical chemistry: C : nanomaterials and interfaces 115, 9827 (2011). http://doi.org/10.1021/jp1102466
Abstract: Nanodiamond from ozone purification (NDO) demonstrates very distinctive properties within the class of detonation nanodiamonds, namely very high acidity and high colloidal stability in a broad pH range. To understand the origin of these unusual properties of NDO, the nature of the surface functional groups formed during detonation soot oxidation by ozone needs to be revealed. In this work, thermal desorption mass spectrometry (TDMS) and IR spectroscopy were used for the identification of surface groups and it was concluded that carboxylic anhydride groups prevail on the NDO surface. On the basis of the temperature profiles of the desorbed volatile products and their mass balance, it is hypothesized that decomposition of carboxylic anhydride groups from NDO during heating proceeds by two different mechanisms. Other distinctive features of NDO in comparison with air-treated nanodiamond are also reported.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 105
DOI: 10.1021/jp1102466
|
|
|
“Three-dimensional atomic imaging of colloidal core-shell nanocrystals”. Bals S, Casavola M, van Huis MA, Van Aert S, Batenburg KJ, Van Tendeloo G, Vanmaekelbergh D, Nano letters 11, 3420 (2011). http://doi.org/10.1021/nl201826e
Abstract: Colloidal coreshell semiconductor nanocrystals form an important class of optoelectronic materials, in which the exciton wave functions can be tailored by the atomic configuration of the core, the interfacial layers, and the shell. Here, we provide a trustful 3D characterization at the atomic scale of a free-standing PbSe(core)CdSe(shell) nanocrystal by combining electron microscopy and discrete tomography. Our results yield unique insights for understanding the process of cation exchange, which is widely employed in the synthesis of coreshell nanocrystals. The study that we present is generally applicable to the broad range of colloidal heteronanocrystals that currently emerge as a new class of materials with technological importance.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 12.712
Times cited: 121
DOI: 10.1021/nl201826e
|
|
|
“Three-dimensional characterization of helical silver nanochains mediated by protein assemblies”. Leroux F, Gysemans M, Bals S, Batenburg KJ, Snauwaert J, Verbiest T, van Haesendonck C, Van Tendeloo G, Advanced materials 22, 2193 (2010). http://doi.org/10.1002/adma.200903657
Abstract: Characterization methods for the structural investigation of biotemplates for nanodevices remain widely unexplored, despite the fact that biotemplating methods for nanodevice fabrication are becoming more widespread. In this study several techniques are used to characterize the morphology and 3D distribution of silver nanoparticles deposited on insulin fibrils.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 19.791
Times cited: 51
DOI: 10.1002/adma.200903657
|
|
|
“Transport, magnetic, and structural properties of La0.7Ce0.3MnO3 thin films: evidence for hole-doping”. Werner R, Raisch C, Leca V, Ion V, Bals S, Van Tendeloo G, Chasse T, Kleiner R, Koelle D, Physical review : B : solid state 79, 054416 (2009). http://doi.org/10.1103/PhysRevB.79.054416
Abstract: Cerium-doped manganite thin films were grown epitaxially by pulsed laser deposition at 720 °C and oxygen pressure pO2=125 Pa and were subjected to different annealing steps. According to x-ray diffraction (XRD) data, the formation of CeO2 as a secondary phase could be avoided for pO28 Pa. However, transmission electron microscopy shows the presence of CeO2 nanoclusters even in those films which appear to be single phase in XRD. With O2 annealing, the metal-to-insulator transition temperature increases, while the saturation magnetization decreases and stays well below the theoretical value for electron-doped La0.7Ce0.3MnO3 with mixed Mn3+/Mn2+ valences. The same trend is observed with decreasing film thickness from 100 to 20 nm, indicating a higher oxygen content for thinner films. Hall measurements on a film which shows a metal-to-insulator transition clearly reveal holes as dominating charge carriers. Combining data from x-ray photoemission spectroscopy, for determination of the oxygen content, and x-ray absorption spectroscopy (XAS), for determination of the hole concentration and cation valences, we find that with increasing oxygen content the hole concentration increases and Mn valences are shifted from 2+ to 4+. The dominating Mn valences in the films are Mn3+ and Mn4+, and only a small amount of Mn2+ ions can be observed by XAS. Mn2+ and Ce4+ XAS signals obtained in surface-sensitive total electron yield mode are strongly reduced in the bulk-sensitive fluorescence mode, which indicates hole-doping in the bulk for those films which do show a metal-to-insulator transition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 25
DOI: 10.1103/PhysRevB.79.054416
|
|
|
“Adsorption of sulfur onto a surface of silver nanoparticles stabilized with sago starch biopolymer”. Djoković, V, Krsmanović, R, Božanić, DK, McPherson M, Van Tendeloo G, Nair PS, Georges MK, Radhakrishnan T, Colloids and surfaces: B : biointerfaces 73, 30 (2009). http://doi.org/10.1016/j.colsurfb.2009.04.022
Abstract: Adsorption of sulfide ions onto a surface of starch capped silver nanoparticles upon addition of thioacetamide was investigated. UVvis absorption spectroscopy revealed that the adsorption of the sulfide ion on the surface of the silver nanoparticles induced damping as well as blue shift of the silver surface plasmon resonance band. Further increase in thioacetamide concentration led to shift of the resonance band toward higher wavelengths indicating the formation of the continuous Ag2S layer on the silver surface. Thus fabricated nanoparticles were investigated using electron microscopy techniques (TEM, HRTEM, and HAADF-STEM) and X-ray photoelectron spectroscopy (XPS), which confirmed their coreshell structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.887
Times cited: 41
DOI: 10.1016/j.colsurfb.2009.04.022
|
|
|
“Anisotropic cation exchange in PbSe/CdSe core/shell nanocrystals of different geometry”. Casavola M, van Huis MA, Bals S, Lambert K, Hens Z, Vanmaekelbergh D, Chemistry of materials 24, 294 (2012). http://doi.org/10.1021/cm202796s
Abstract: We present a study of Cd2+-for-Pb2+ exchange in PbSe nanocrystals (NCs) with cube, star, and rod shapes. Prolonged temperature-activated cation exchange results in PbSe/CdSe heterostructured nanocrystals (HNCs) that preserve their specific overall shape, whereas the PbSe core is strongly faceted with dominance of {111} facets. Hence, cation exchange proceeds while the Se anion lattice is preserved, and well-defined {111}/{111} PbSe/CdSe interfaces develop. Interestingly, by quenching the reaction at different stages of the cation exchange new structures have been isolated, such as coreshell nanorods, CdSe rods that contain one or two separated PbSe dots and fully zinc blende CdSe nanorods. The crystallographically anisotropic cation exchange has been characterized by a combined HRTEM/HAADF-STEM study of heterointerface evolution over reaction time and temperature. Strikingly, Pb and Cd are only intermixed at the PbSe/CdSe interface. We propose a plausible model for the cation exchange based on a layer-by-layer replacement of Pb2+ by Cd2+ enabled by a vacancy-assisted cation migration mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 136
DOI: 10.1021/cm202796s
|
|
|
“Assisted spray pyrolysis production and characterisation of ZnO nanoparticles with narrow size distribution”. Turner S, Tavernier SMF, Huyberechts G, Bals S, Batenburg KJ, Van Tendeloo G, Journal of nanoparticle research 12, 615 (2010). http://doi.org/10.1007/s11051-009-9630-1
Abstract: Nano-sized ZnO particles with a narrow size distribution and high crystallinity were prepared from aqueous solutions with high concentrations of Zn2+ containing salts and citric acid in a conventional spray pyrolysis setup. Structure, morphology and size of the produced material were compared to ZnO material produced by simple spray pyrolysis of zinc nitrates in the same experimental setup. Using transmission electron microscopy and electron tomography it has been shown that citric acid-assisted spray pyrolysed material is made up of micron sized secondary particles comprising a shell of lightly agglomerated, monocrystalline primary ZnO nanoparticles with sizes in the 2030 nm range, separable by a simple ultrasonic treatment step.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.02
Times cited: 27
DOI: 10.1007/s11051-009-9630-1
|
|
|
“Au@ZIFs: stabilization and encapsulation of cavity-size matching gold clusters inside functionalized Zeolite Imidazolate Frameworks, ZIFs”. Esken D, Turner S, Lebedev OI, Van Tendeloo G, Fischer RA, Chemistry of materials 22, 6393 (2010). http://doi.org/10.1021/cm102529c
Abstract: The selective formation and stabilization of very small, naked metal particles inside the cavities of metal organic frameworks (MOFs) and the simultaneous realization of an even distribution of the particles throughout the crystalline MOF host matrix over a wide range of metal loading are challenging goals. MOFs reveal high specific surface areas, tunable pore sizes, and organic linkers, which are able to interact with guests. The chemically very robust zeolite imidazolate frameworks (ZIFs) are a subclass of MOFs. We chose the microporous sodalite-like ZIF-8 (Zn(MelM)(2); IM = imidazolate) and ZIF-90 (Zn(ICA)(2); ICA = imidazolate-2-carboxyaldehyde) as host matrices to influence the dispersion of imbedded gold nanoparticles (Au NPs). The metal loading was achieved via gas phase infiltration of [Au(CO)Cl] followed by a thermal hydrogenation step to form the Au NPs. Low-dose high-resolution transmission electron microscopy ((HR)TEM) and electron tomography reveal a homogeneous distribution of Au NPs throughout the ZIF matrix. The functional groups of ZIF-90 direct the anchoring of intermediate Au species and stabilize drastically smaller and quite monodisperse Au NPs in contrast to the parent not functionalized ZIF-8. The particles can be very small, match the cavity size and approach defined molecular clusters of magic numbers, i.e., Au(55), independently from the level of loading. Post-synthetic oxidation of the aldehyde groups to yield alkyl esters by the adjacent, catalytically active metal NPs is presented as a new concept of encapsulating nanoparticles inside MOFs and allows multiple steps of metal loadings without decomposition of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 194
DOI: 10.1021/cm102529c
|
|
|
“B-site ordered perovskite LaSrMnNbO6 : synthesis, structure and antiferromagnetism”. Yang T, Perkisas T, Hadermann J, Croft M, Ignatov A, Greenblatt M, Journal of solid state chemistry 183, 2689 (2010). http://doi.org/10.1016/j.jssc.2010.08.041
Abstract: LaSrMnNbO6 has been synthesized by high temperature solid state reaction under 1% H2/Ar dynamic flow. The structure is determined by Rietveld refinement of the powder X-ray diffraction data. It crystallizes in the monoclinic space group P21/n with the unit cell parameters: a=5.69187(12), b=5.74732(10), c=8.07018(15) Å and β=90.0504(29)°, which were also confirmed by electron diffraction. The Mn2+ and Nb5+ ions, whose valence states are confirmed by X-ray absorption near-edge spectroscopy, are almost completely ordered over the B-site (<1% inversion) of the perovskite structure due to the large differences of both cationic size (0.19 Å) and charge. The octahedral framework displays significant tilting distortion according to Glazers tilt system a−b−c+. Upon heating, LaSrMnNbO6 decomposes at 690 °C under O2 flow or at 775 °C in air. The magnetic susceptibility data indicate the presence of long-range antiferromagnetic ordering at TN=8 K; the experimentally observed effective paramagnetic moment, μeff=5.76 μB for high spin Mn2+ (3d5, S=5/2) is in good agreement with the calculated value (μcalcd=5.92 μB).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 13
DOI: 10.1016/j.jssc.2010.08.041
|
|
|
“Catalytic characterization of pure SnO2 and GeO2 in methanol steam reforming”. Zhao Q, Lorenz H, Turner S, Lebedev OI, Van Tendeloo G, Rameshan C, Klötzer B, Konzett J, Penner S, Applied catalysis : A : general 375, 188 (2010). http://doi.org/10.1016/j.apcata.2009.12.027
Abstract: Structural changes of a variety of different SnO, SnO2 and GeO2 catalysts upon reduction in hydrogen were correlated with associated catalytic changes in methanol steam reforming. Studied systems include SnO, SnO2 and GeO2 thin film model catalysts prepared by vapour phase deposition and growth on polycrystalline NaCl surfaces and, for comparison, the corresponding pure oxide powder catalysts. Reduction of both the SnO2 thin film and powder at around 673 K in 1 bar hydrogen leads to a substantial reduction of the bulk structure and yields a mixture of SnO2 and metallic β-Sn. On the powder catalyst this transformation is fully reversible upon oxidation in 1 bar O2 at 673 K. Strongly reduced thin films, however, can only be re-transformed to SnO2 if the reduction temperature did not exceed 573 K. For GeO2, the situation is more complex due to its polymorphism. Whereas the tetragonal phase is structurally stable during reduction, oxidation or catalytic reaction, a small part of the hexagonal phase is always transformed into the tetragonal at 673 K independent of the gas phase used. SnO2 is highly active and CO2 selective in methanol steam reforming, but the initial high activity drops considerably upon reduction between 373 and 573 K and almost complete catalyst deactivation is observed after reduction at 673 K, which is associated with the parallel formation of β-Sn. In close correlation to the structural results, the catalytic activity and selectivity can be restored upon an oxidative catalyst regeneration at 673 K. Tetragonal GeO2 exhibits only a small activity and no pronounced selectivity to either CO or CO2, at least after reduction. In its fully oxidized state release of surface/lattice oxygen results in a non-catalytic formation of CO2 by oxidation of CO originating from catalytic dehydrogenation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 20
DOI: 10.1016/j.apcata.2009.12.027
|
|
|
“Competing magnetic structures and the evolution of copper ion/vacancy ordering with composition in the manganite oxide chalcogenides Sr2MnO2Cu1.5(S1-xSex)2”. Adamson P, Hadermann J, Smura CF, Rutt OJ, Hyett G, Free DG, Clarke SJ, Chemistry of materials 24, 2802 (2012). http://doi.org/10.1021/cm301486v
Abstract: The series Sr2MnO2Cu1.5(S1-xSex)(2) (0 <= x <= 1) contains mixed-valent Mn ions (Mn2+/Mn3+) in MnO2 sheets which are separated by copper-deficient antifluorite-type Cu(2-delta)Ch(2) layers with delta similar to 0.5. The compounds crystallize in the structure type first described for Sr2Mn3Sb2O2 and are described in the I4/mmm space group at ambient temperatures. Below about 250 K, ordering between Cu+ ions and tetrahedral vacancies occurs which is long-range and close to complete in the sulfide-containing end member of the series Sr2MnO2Cu1.5S2 but which occurs over shorter length scales as the selenide content increases. The superstructure is an orthorhombic 2 root 2a x root 2a x c expansion in Ibam of the room temperature cell. For x > 0.3 there are no superstructure reflections evident in the X-ray or neutron diffraction patterns, and the I4/mmm description is valid for the average structure at all temperatures. However, in the pure selenide end member, Sr2MnO2Cu1.5Se2, diffuse scattering in electron diffractograms and modulation in high resolution lattice image profiles may arise from short-range Cu/vacancy order. All members of the series exhibit long-range magnetic order. In the sulfide-rich end member and in compounds with x < 0.1 in the formula Sr2MnO2Cu1.5(S1-xSex)(2), which show well developed superstructures due to long-range Cu/vacancy order, the magnetic structure has a (1/4 1/4 0) propagation vector in which ferromagnetic zigzag chains of Mn moments in the MnO2 sheets are coupled antiferromagnetically in an arrangement described as the CE-type magnetic structure and found in many mixed-valent perovskite and Ruddlesden-Popper type oxide manganites. In these cases the magnetic cell is an a x 2b x c expansion of the low temperature Ibam structural cell. For x >= 0.2 in the formula Sr2MnO2Cu1.5(S1-xSex)(2) the magnetic structure has a (0 0 0) propagation vector and is similar to the A-type structure, also commonly adopted by some perovskite-related manganites, in which the Mn moments in the MnO2 sheets are coupled ferromagnetically and long-range antiferromagnetic order results from antiferromagnetic coupling between planes. In the region of the transition between the two different structural and magnetic long-range ordering schemes (0.1 < x < 0.2) the two magnetic structures coexist in the same sample. The evolution of the competition between magnetic ordering schemes and the length scale of the structural order with composition in Sr2MnO2Cu1.5(S1-xSex)(2) suggest that the changes in magnetic and structural order are related consequences of the introduction of chemical disorder.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 11
DOI: 10.1021/cm301486v
|
|
|
“Crystal fields, disorder, and antiferromagnetic short-range order in Yb0.24Sn0.76Ru”. Klimczuk T, Wang CH, Lawrence JM, Xu Q, Durakiewicz T, Ronning F, Llobet A, Trouw F, Kurita N, Tokiwa Y, Lee Ho, Booth CH, Gardner JS, Bauer ED, Joyce JJ, Zandbergen HW, Movshovich R, Cava RJ, Thompson JD;, Physical review : B : condensed matter and materials physics 84, 075152 (2011). http://doi.org/10.1103/PhysRevB.84.075152
Abstract: We report extensive measurements on a new compound (Yb0.24Sn0.76)Ru that crystallizes in the cubic CsCl structure. Valence-band photoemission (PES) and L3 x-ray absorption show no divalent component in the 4f configuration of Yb. Inelastic neutron scattering (INS) indicates that the eight-fold degenerate J-multiplet of Yb3+ is split by the crystalline electric field (CEF) into a Γ7-doublet ground state and a Γ8 quartet at an excitation energy 20 meV. The magnetic susceptibility can be fit very well by this CEF scheme under the assumption that a Γ6-excited state resides at 32 meV; however, the Γ8/Γ6 transition expected at 12 meV was not observed in the INS. The resistivity follows a Bloch-Grüneisen law shunted by a parallel resistor, as is typical of systems subject to phonon scattering with no apparent magnetic scattering. All of these properties can be understood as representing simple local moment behavior of the trivalent Yb ion. At 1 K there is a peak in specific heat that is too broad to represent a magnetic-phase transition, consistent with absence of magnetic reflections in neutron diffraction. On the other hand this peak also is too narrow to represent the Kondo effect in the Γ7-doublet ground state. On the basis of the field dependence of the specific heat, we argue that antiferromagnetic (AF) short-range order (SRO) (possibly coexisting with Kondo physics) occurs at low temperatures. The long-range magnetic order is suppressed because the Yb site occupancy is below the percolation threshold for this disordered compound.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 8
DOI: 10.1103/PhysRevB.84.075152
|
|
|
“Crystal growth of CsCl-type Yb0.24Sn0.76Ru”. Klimczuk T, Wang CH, Xu Q, Lawrence J, Durakiewicz T, Ronning F, Llobet A, Bauer ED, Griveau J-C, Sadowski W, Zandbergen HW, Thompson JD, Cava RJ, Journal of crystal growth 318, 1005 (2011). http://doi.org/10.1016/j.jcrysgro.2010.10.045
Abstract: The YbRuSn ternary system was investigated and a new material, Yb0.24Sn0.76Ru, with a simple cubic crystal structure, was discovered. Yb0.24Sn0.76Ru has a smaller lattice parameter a=3.217(4) Å, than its isostructural YbRu analogue (a=3.360 Å). Both X-ray diffraction and electron microscopy techniques were used to refine the crystal structure of Yb0.24Sn0.76Ru. It was found that a new compound forms in the CsCl structure, with Ru on the 1a site and a (Yb, Sn) mixture on site 1b. The XRD Rietveld analysis provides the occupation of Yb equal to 0.24, in agreement with the single crystal nano-electron diffraction refinement, which gives the occupation 0.21.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.751
Times cited: 1
DOI: 10.1016/j.jcrysgro.2010.10.045
|
|
|
“CVD of copper oxides from a \beta-diketonate diamine precursor: tailoring the nano-organization”. Barreca D, Gasparotto A, Maccato C, Tondello E, Lebedev OI, Van Tendeloo G, Crystal growth &, design 9, 2470 (2009). http://doi.org/10.1021/cg801378x
Abstract: A copper(II) hexafluoroacetylacetonate (1,1,1,5,5,5-hexafluoro-2,4-pentanedionate, hfa) adduct with N,N,N¡ä,N¡ä-tetramethylethylenediamine (TMEDA) [Cu(hfa)2¡¤TMEDA] is used for the first time as precursor for the chemical vapor deposition (CVD) of copper oxide nanosystems. The syntheses are carried out under both O2 and O2+H2O reaction atmospheres on Si(100) substrates, at temperatures ranging between 250 and 550 ¡ãC. Subsequently, the interrelations between the preparative conditions and the system composition, nanostructure, and morphology are elucidated by means of complementary analytical techniques [Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron and X-ray excited auger electron spectroscopies (XPS and XE-AES), glancing incidence X-ray diffraction (GIXRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM)]. The obtained data revealed a gradual transformation from Cu2O, to Cu2O + CuO, to CuO nanosystems upon increasing the deposition temperature from 250 to 550 ¡ãC under both growth atmospheres. Such a phenomenon was accompanied by a progressive morphological evolution from continuous films to 1D hyperbranched nanostructures. Water vapor introduction in the deposition environment enabled to lower the deposition temperature and resulted in a higher aggregate interconnection, attributed to a higher density of nucleation centers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 60
DOI: 10.1021/cg801378x
|
|
|
“Determination of size, morphology, and nitrogen impurity location in treated detonation nanodiamond by transmission electron microscopy”. Turner S, Lebedev OI, Shenderova O, Vlasov II, Verbeeck J, Van Tendeloo G, Advanced functional materials 19, 2116 (2009). http://doi.org/10.1002/adfm.200801872
Abstract: Size, morphology, and nitrogen impurity location, all of which are all thought to be related to the luminescent properties of detonation nanodiamonds, are determined in several detonation nanodiamond samples using a combination of transmission electron microscopy techniques. Results obtained from annealed and cleaned detonation nanodiamond samples are compared to results from conventionally purified detonation nanodiamond. Detailed electron energy loss spectroscopy combined with model-based quantification provides direct evidence for the sp3 like embedding of nitrogen impurities into the diamond cores of all the studied nanodiamond samples. Simultaneously, the structure and morphology of the cleaned detonation nanodiamond particles are studied using high resolution transmission electron microscopy. The results show that the size and morphology of detonation nanodiamonds can be modified by temperature treatment and that by applying a special cleaning procedure after temperature treatment, nanodiamond particles with clean facets almost free from sp2 carbon can be prepared. These clean facets are clear evidence that nanodiamond cores are not necessarily in coexistence with a graphitic shell of non-diamond carbon.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 100
DOI: 10.1002/adfm.200801872
|
|
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
|
|
“An effective morphology control of hydroxyapatite crystals via hydrothermal synthesis”. Neira IS, Kolen'ko YV, Lebedev OI, Van Tendeloo G, Gupta HS, Guitián F, Yoshimura M, Crystal growth &, design 9, 466 (2009). http://doi.org/10.1021/cg800738a
Abstract: A facile urea-assisted hydrothermal synthesis and systematic characterization of hydroxyapatite (HA) with calcium nitrate tetrahydrate and diammonium hydrogen phosphate as precursors are reported. The advantage of the proposed technique over previously reported synthetic approaches is the simple but precise control of the HA crystals morphology, which is achieved by employing an intensive, stepwise, and slow thermal decomposition of urea as well as varying initial concentrations of starting reagents. Whereas the plate-, hexagonal prism- and needle-like HA particles preferentially growth along the c-axis, the smaller and fine-plate-like HA crystals demonstrate crystal growth along the (102) and (211) directions, uncommon for HA. Furthermore, it was established that the hydrothermally derived powdered products are phase-pure HA containing CO32− anions in the crystal lattice, that is, AB-type carbonated hydroxyapatite. Transmission electron microscopy (TEM) and electron diffraction (ED) of selected samples reveal that the as-prepared HA crystals are single-crystalline and exhibit a nearly defect-free microstructure. The hardness and elastic modulus of the hexagonal prism-like HA crystals have been investigated on a nanoscale using the nanoindentation technique; the observed trends are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 183
DOI: 10.1021/cg800738a
|
|
|
“Electrical nonlinearity in colossal magnetoresistance manganite films: relevance of correlated polarons”. Moshnyaga V, Gehrke K, Sudheendra L, Belenchuk A, Raabe S, Shapoval O, Verbeeck J, Van Tendeloo G, Samwer K, Physical review : B : solid state 79, 134413 (2009). http://doi.org/10.1103/PhysRevB.79.134413
Abstract: The metal-insulator (MI) transition in epitaxial thin films of La0.75Ca0.25MnO3 (LCMO) is accompanied by the appearance of an intrinsic electrical nonlinearity. The latter, probed by electrical third harmonic voltage, U3, or resistance, R3=dU3/dJ, is drastically enhanced in the vicinity of the MI transition, TMI=267 K. Applied magnetic field, B=5 T, suppresses the nonlinearity, resulting in a huge nonlinear CMR3(TMI)~105%. R3 shows a peculiar low-frequency (1 kHz) dependence, R3~(-0)n, with exponent, n, changing across the MI transition from n~1,52 for TTMI to n=1 (T<TMI). The observed electrical nonlinearity in LCMO reflects the behavior of correlated polarons, the number of which dramatically enhances in the vicinity of TMI. We argued that correlated polarons, considered as electric-elastic quadrupoles, provide a nonlinear (quadratic) coupling to the electric field, yielding a third harmonic electric nonlinearity in LCMO. The reference film of La0.7Sr0.3MnO3 (LSMO), a prototypic double exchange system with second-order phase transition, is characterized as a linear metallic material in the whole range of temperatures (T=10400 K), magnetic fields (B=05 T), and frequencies (=11000 Hz).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 28
DOI: 10.1103/PhysRevB.79.134413
|
|
|
“Gas-phase loading of [Zn4O(btb)2] (MOF-177) with organometallic CVD-precursors: inclusion compounds of the type [LnM]a@MOF-177 and the formation of Cu and Pd nanoparticles inside MOF-177”. Müller M, Lebedev OI, Fischer RA, Journal of materials chemistry 18, 5274 (2008). http://doi.org/10.1039/b810989c
Abstract: The highly porous and desolvated (activated) coordination polymer [Zn4O(btb)2] (btb = benzene-1,3,5-tribenzoate; MOF-177) was loaded with the organometallic compounds [Cp2Fe], [Cp*2Zn], [Cu(OCHMeCH2NMe2)2], [CpCuL] (L = PMe3, CNtBu) and [CpPd(3-C3H5)] via solvent-free adsorption from the gas-phase. The inclusion compounds of the type [LnM]a@MOF-177, where [LnM] indicates the respective compound and the parameter a denotes the number of molecules per formula unit of the MOF-177, were characterised by elemental analysis, FT-IR, solid-state NMR spectroscopy and by powder X-ray diffraction (PXRD). Remarkably high effective loadings of up to 11 molecules [Cp2Fe] and 10 molecules [CpPd(3-C3H5)] per cavity were determined. The analytical data prove that the host lattice and the guest molecules interact only by weak van-der-Waals forces without any significant change of the framework or the chemical nature of the included molecules. Cu nanoparticles showing the typical surface plasmon resonance at 580 nm and Pd nanoparticles of about 2.6 nm in size were formed inside the cavities of MOF-177 by the thermally activated hydrogenolysis of the inclusion compounds [CpCuCNtBu]2@MOF-177 and by photolysis of [CpPd(3-C3H5)]10@MOF-177 in an inert atmosphere (Ar). PXRD, FT-IR and NMR studies revealed that the MOF-177 matrix remained unchanged during the decomposition process of the precursors. N2 adsorption studies of the obtained materials Cu@MOF-177 (e.g. 10.6 wt.% Cu, 2309 m2 g-1) and Pd@MOF-177 (e.g. 32.5 wt.%, 1063 m2 g-1) reveal high remaining specific surface areas (Langmuir model).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 65
DOI: 10.1039/b810989c
|
|
|
“Highly oriented ZnO nanorod arrays by a novel plasma chemical vapor deposition process”. Bekermann D, Gasparotto A, Barreca D, Bovo L, Devi A, Fischer RA, Lebedev OI, Maccato C, Tondello E, Van Tendeloo G, Crystal growth &, design 10, 2011 (2010). http://doi.org/10.1021/cg1002012
Abstract: Strongly c-axis oriented ZnO nanorod arrays were grown on Si(100) by plasma enhanced-chemical vapor deposition (PE-CVD) starting from two volatile bis(ketoiminato) zinc(II) compounds Zn[(R′)NC(CH3)═C(H)C(CH3)═O]2, with R′ = -(CH2)xOCH3 (x = 2, 3). A systematic investigation of process parameters enabled us to obtain the selective formation of ZnO nanorods with tailored features, and provided an important insight into their growth mechanism. The morphology, structure, and composition of the synthesized ZnO nanosystems were thoroughly analyzed by field emission-scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDXS), glancing incidence X-ray diffraction (GIXRD), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). Photoluminescence (PL) measurements were carried out to gain information on the optical properties. Specifically, one-dimensional (1D) ZnO architectures could be grown on Si(100) substrates at temperatures as low as 200−300 °C and radio frequency (RF)-power values of 20 W, provided that a sufficiently high mass supply to the growth surface was maintained. To the best of our knowledge, the present work reports the mildest preparation conditions ever appeared in the literature for the PE-CVD of ZnO nanorods, a key result in view of potential large-scale technological applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 75
DOI: 10.1021/cg1002012
|
|
|
“HRTEM and neutron diffraction study of LixMo5O17 : from the ribbon (x=5) structure to the rock salt (x=12) structure”. Lebedev OI, Caignaert V, Raveau B, Pop N, Gozzo F, Van Tendeloo G, Pralong V, Journal of solid state chemistry 184, 790 (2011). http://doi.org/10.1016/j.jssc.2011.02.001
Abstract: Structure determination of the fully intercalated phase Li12Mo5O17 and of the deintercalated oxide Li5Mo5O17 has been carried out by electron microscopy and neutron powder diffraction. The reversible topotactic transformation between the ordered rock salt structure of the former and the ribbon structure of the latter (closely related to that of Li4Mo5O17) is explained on the following basis: both structures can be described as strips built up as an assembly of infinite ribbons of MoO6 octahedra that are five octahedra thick, and that differ by slight displacements of the octahedral ribbons. We show that the electrochemical behavior of the LixMo5O17 system is based on two sorts of Li+ sites; those that are located within the strips between the ribbons, and those that are located at the border of the strips. The high rate of Li intercalation in this oxide and its reversibility are discussed in terms of its peculiar structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 1
DOI: 10.1016/j.jssc.2011.02.001
|
|