Abstract: The structure and surface morphology of aluminum and silver mirrors covered with protective dielectric oxide layer were studied by means of TEM and SEM. The presence of needle-like pores throughout the thickness of the ZrO(2) film and bubble-like pores in Al(2)O(3) was observed. The test for resistivity to deuterium ion bombardment shows that the exposition to a fluence of similar to 2 x 10(20) ions/cm(2) with the ion energy of 40-50 eV results in appearance of blisters on the surface of mirrors covered wit h Al(2)O(3). For the mirrors protected with ZrO(2) no noticeable changes in surface morphology and reflectivity were found even after order of magnitude higher ion fluence. The effect of different porous structures on blistering phenomena is discussed. (C) 2010 Elsevier B.V. All rights reserved.

Abstract: Neutron and high resolution X-ray diffraction investigations on perfect single crystals of RbH2PO4 (RDP), a hydrogen bonded ferroelectric of KDP type are reported. The results of crystal structure analysis from diffraction data, below and above the paraelectric – ferroelectric phase transition, support a disorder – order character Of [PO4H2](-)-groups. The tetragonal symmetry of the paraelectric phase with the double well potential of the hydrogen atoms obtained by diffraction, results simply from a time-space average of orthorhombic symmetry. According to the group – subgroup relation between the tetragonal space group 142d and the orthorhombic Fdd2 a short range order of ferroelectric clusters in the tetragonal phase is observed. With decreasing temperature the ferroelectric clusters increase and the long range interaction between their local polarisation vectors leads to the formation of lamellar ferroelectric domains with alternating polarisation directions at T-C = 147 K. From the high resolution X-ray data it is concluded that below T-C the ferroelastic strain in the (a,b)-plane leads to micro-angle grain boundaries at the domain walls. The tilt angle is enhanced by an applied electric field parallel to the ferroelectric axis. The resulting dislocations at the domain walls persist in the paraelectric phase leading to a memory effect for the arrangement of twin lamellae. With increased electric field the phase transition temperature T-C is decreased.

Abstract: The crystal structures of the three high-temperature polymorphs of K3AlF6 have been solved from neutron powder diffraction, synchrotron X-ray powder diffraction, and electron diffraction data. The β-phase (stable between 132 and 153 °C) and γ-phase (stable between 153 to 306 °C) can be described as unusually complex superstructures of the double-perovskite structure (K2KAlF6) which result from noncooperative tilting of the AlF6 octahedra. The β-phase is tetragonal, space group I4/m, with lattice parameters of a = 13.3862(5) Å and c = 8.5617(3) Å (at 143 °C) and Z = 10. In this phase, one-fifth of the AlF6 octahedra are rotated about the c-axis by 45° while the other four-fifths remain untilted. The large 45° rotations result in edge sharing between these AlF6 octahedra and the neighboring K-centered polyhedra, resulting in pentagonal bipyramidal coordination for four-fifths of the K+ ions that reside on the B-sites of the perovskite structure. The remaining one-fifth of the K+ ions on the B-sites retain octahedral coordination. The γ-phase is orthorhombic, space group Fddd, with lattice parameters of a = 36.1276(4) Å, b = 17.1133(2) Å, and c = 12.0562(1) Å (at 225 °C) and Z = 48. In the γ-phase, one-sixth of the AlF6 octahedra are randomly rotated about one of two directions by 45° while the other five-sixths remain essentially untilted. These rotations result in two-thirds of the K+ ions on the B-site obtaining 7-fold coordination while the other one-third remain in octahedral coordination. The δ-phase adopts the ideal cubic double-perovskite structure, space group Fmm, with a = 8.5943(1) Å at 400 °C. However, pair distribution function analysis shows that locally the δ-phase is quite different from its long-range average crystal structure. The AlF6 octahedra undergo large-amplitude rotations which are accompanied by off-center displacements of the K+ ions that occupy the 12-coordinate A-sites.