“Interfacial oxidation and photoluminescence of InP-Based core/shell quantum dots”. Tessier MD, Baquero EA, Dupont D, Grigel V, Bladt E, Bals S, Coppel Y, Hens Z, Nayral C, Delpech F, Chemistry of materials 30, 6877 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B03117
Abstract: Indium phosphide colloidal quantum dots (QDs) are emerging as an efficient cadmium-free alternative for optoelectronic applications. Recently, syntheses based on easy-to-implement aminophosphine precursors have been developed. We show by solid-state nuclear magnetic resonance spectroscopy that this new approach allows oxide-free indium phosphide core or core/shell quantum dots to be made. Importantly, the oxide-free core/shell interface does not help in achieving higher luminescence efficiencies. We demonstrate that in the case of InP/ZnS and InP/ZnSe QDs, a more pronounced oxidation concurs with a higher photoluminescence efficiency. This study suggests that a II-VI shell on a III-V core generates an interface prone to defects. The most efficient InP/ZnS or InP/ZnSe QDs are therefore made with an oxide buffer layer between the core and the shell: it passivates these interface defects but also results in a somewhat broader emission line width.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 74
DOI: 10.1021/ACS.CHEMMATER.8B03117
|
|
|
“Subtissue plasmonic heating monitored with CaF2:Nd3+,Y3+ nanothermometers in the second biological window”. Quintanilla M, Zhang Y, Liz-Marzan LM, Chemistry of materials 30, 2819 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B00806
Abstract: Measuring temperature in biological environments is an ambitious goal toward supporting medical treatment and diagnosis. Minimally invasive techniques based on optical probes require very specific properties that are difficult to combine within a single material. These include high chemical stability in aqueous environments, optical signal stability, low toxicity, high emission intensity, and, essential, working at wavelengths within the biological transparency windows so as to minimize invasiveness while maximizing penetration depth. We propose CaF2:Nd3+,Y3+ as a candidate for thermometry based on an intraband ratiometric approach, fully working within the biological windows (excitation at 808 nm; emission around 1050 nm). We optimized the thermal probes through the addition of Y3+ as a dopant to improve both emission intensity and thermal sensitivity. To define the conditions under which the proposed technique can be applied, gold nanorods were used to optically generate subtissue hot areas, while the resulting temperature variation was monitored with the new nanothermometers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 28
DOI: 10.1021/ACS.CHEMMATER.8B00806
|
|
|
“New solid electrolyte Na9Al(MoO4)6 : structure and Na+ ion conductivity”. Savina AA, Morozov VA, Buzlukov AL, Arapova IY, Stefanovich SY, Baklanova YV, Denisova TA, Medvedeva NI, Bardet M, Hadermann J, Lazoryak BI, Khaikina EG, Chemistry of materials 29, 8901 (2017). http://doi.org/10.1021/ACS.CHEMMATER.7B03989
Abstract: <script type='text/javascript'>document.write(unpmarked('Solid electrolytes are important materials with a wide range of technological applications. This work reports the crystal structure and electrical properties of a new solid electrolyte Na9Al(MoO4)(6). The monoclinic Na9Al(MoO4)(6) consists of isolated polyhedral, [Al(MoO4)(6)](9-) clusters composed of a central AlO6 octahedron sharing vertices with six MoO4 tetrahedra to form a three-dimensional framework. The AlO6 octahedron also shares edges with one NalO(6) octahedron and two Na2O(6) octahedra. Na3-Na5 atoms are located in the framework cavities. The structure is related to that of sodium ion conductor II-Na3Fe2(AsO4)(3). High-temperature conductivity measurements revealed that the conductivity (sigma) of Na9Al(MoO4)(6) at 803 K equals 1.63 X 10(-2) S cm(-1). The temperature behavior of the Na-23 and Al-27 nuclear magnetic resonance spectra and the spin-lattice relaxation rates of the Na-23 nuclei indicate the presence of fast Na+ ion diffusion in the studied compound. At T\u003C490 K, diffusion occurs by means of Na+ ion jumps exclusively through the sublattice of Na3-Na5 positions, whereas Na1 and Na2 become involved in the diffusion processes (through chemical exchange with the Na3-Na5 sublattice) only at higher temperatures.'));
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 13
DOI: 10.1021/ACS.CHEMMATER.7B03989
|
|
|
“Incommensurately modulated structures and luminescence properties of the AgxSm(2-x)/3WO4 (x=0.286, 0.2) scheelites as thermographic phosphors”. Morozov V, Deyneko D, Basoyich O, Khaikina EG, Spassky D, Morozov A, Chernyshev V, Abakumov A, Hadermann J, Chemistry of materials 30, 4788 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B02029
Abstract: Ag+ for Sm3+ substitution in the scheelite-type AgxSm(2-x)/3 square(1-2x)/3WO4 tungstates has been investigated for its influence on the cation-vacancy ordering and luminescence properties. A solid state method was used to synthesize the x = 0.286 and x = 0.2 compounds, which exhibited (3 + 1)D incommensurately modulated structures in the transmission electron microscopy study. Their structures were refined using high resolution synchrotron powder X-ray diffraction data. Under near-ultraviolet light, both compounds show the characteristic emission lines for (4)G(5/2) -> H-6(J) (J = 5/2, 7/2, 9/2, and 11/2) transitions of the Sm3+ ions in the range 550-720 nm, with the J = 9/2 transition at the similar to 648 nm region being dominant for all photoluminescence spectra. The intensities of the (4)G(5/2) -> H-6(9/2) and (4)G(5/2) -> H-6(7/2) bands have different temperature dependencies. The emission intensity ratios (R) for these bands vary reproducibly with temperature, allowing the use of these materials as thermographic phosphors.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 2
DOI: 10.1021/ACS.CHEMMATER.8B02029
|
|
|
“Postsynthetic high-alumina zeolite crystal engineering in organic free hyper-alkaline media”. Van Tendeloo L, Wangermez W, Vandekerkhove A, Willhammar T, Bals S, Maes A, Martens JA, Kirschhock CEA, Breynaert E, Chemistry of materials 29, 629 (2017). http://doi.org/10.1021/ACS.CHEMMATER.6B04052
Abstract: Postsynthetic modification of high -alumina zeolites in hyper alkaline media can be tailored toward alteration of framework topology, crystal size and morphology, or desired Si/A1 ratio. FAU, EMT, MAZ, KFI, HEU, and LTA starting materials were treated with 1.2 M MOH (M = Na, K, RE, or Cs), leading to systematic ordered porosity or fully transformed frameworks with new topology and adjustable Si/Al ratio. In addition to the versatility of this tool for zeolite crystal engineering, these alterations improve understanding of the crystal chemistry. Such knowledge can guide further development in zeolite crystal engineering. Postsynthetic alteration also provides insight on the long-term stability of aluminosilicate zeolites that are used as a sorption sink in concrete -based waste disposal facilities in harsh alkaline conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 16
DOI: 10.1021/ACS.CHEMMATER.6B04052
|
|
|
“Reduced Na2+xTi4O9 composite : a durable anode for sodium-ion batteries”. De Sloovere D, Safari M, Elen K, D'Haen J, Drozhzhin OA, Abakumov AM, Simenas M, Banys J, Bekaert J, Partoens B, Van Bael MK, Hardy A, Chemistry of materials 30, 8521 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B03301
Abstract: Sodium-ion batteries (SIBs) are potential cost-effective solutions for stationary energy storage applications. Unavailability of suitable anode materials, however, is one of the important barriers to the maturity of SIBs. Here, we report a Na2+xTi4O9/C composite as a promising anode candidate for SIBs with high capacity and cycling stability. This anode is characterized by a capacity of 124 mAh g(-1) (plus 11 mAh g(-1) contributed by carbon black), an average discharge potential of 0.9 V vs Na/Na+, a good rate capability and a high stability (89% capacity retention after 250 cycles at a rate of 1 degrees C). The mechanisms of sodium insertion/deinsertion and of the formation of Na2+xTi4O9/C are investigated with the aid of various ex/in situ characterization techniques. The in situ formed carbon is necessary for the formation of the reduced sodium titanate. This synthesis method may enable the convenient synthesis of other composites of crystalline phases with amorphous carbon.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 9.466
Times cited: 7
DOI: 10.1021/ACS.CHEMMATER.8B03301
|
|
|
“Chemical activity of the peroxide/oxide redox couple : case study of Ba5Ru2O11 in aqueous and organic solvents”. Grimaud A, Iadecola A, Batuk D, Saubanere M, Abakumov AM, Freeland JW, Cabana J, Li H, Doublet M-L, Rousse G, Tarascon J-M, Chemistry of materials 30, 3882 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B01372
Abstract: The finding that triggering the redox activity of oxygen ions within the lattice of transition metal oxides can boost the performances of materials used in energy storage and conversion devices such as Li-ion batteries or oxygen evolution electrocatalysts has recently spurred intensive and innovative research in the field of energy. While experimental and theoretical efforts have been critical in understanding the role of oxygen nonbonding states in the redox activity of oxygen ions, a clear picture of the redox chemistry of the oxygen species formed upon this oxidation process is still missing. This can be, in part, explained by the complexity in stabilizing and studying these species once electrochemically formed. In this work, we alleviate this difficulty by studying the phase Ba5Ru2O11, which contains peroxide O-2(2-) groups, as oxygen evolution reaction electrocatalyst and Li-ion battery material. Combining physical characterization and electrochemical measurements, we demonstrate that peroxide groups can easily be oxidized at relatively low potential, leading to the formation of gaseous dioxygen and to the instability of the oxide. Furthermore, we demonstrate that, owing to the stabilization at high energy of peroxide, the high-lying energy of the empty sigma* antibonding O-O states limits the reversibility of the electrochemical reactions when the O-2(2-)/O2- redox couple is used as redox center for Li-ion battery materials or as OER redox active sites. Overall, this work suggests that the formation of true peroxide O-2(2-) states are detrimental for transition metal oxides used as OER catalysts and Li-ion battery materials. Rather, oxygen species with O-O bond order lower than 1 would be preferred for these applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 2
DOI: 10.1021/ACS.CHEMMATER.8B01372
|
|
|
“Accelerated Discovery of Efficient Solar Cell Materials Using Quantum and Machine-Learning Methods”. Choudhary K, Bercx M, Jiang J, Pachter R, Lamoen D, Tavazza F, Chemistry of materials 31, 5900 (2019). http://doi.org/10.1021/acs.chemmater.9b02166
Abstract: Solar energy plays an important role in solving serious environmental
problems and meeting the high energy demand. However, the lack of suitable
materials hinders further progress of this technology. Here, we present the largest
inorganic solar cell material search till date using density functional theory (DFT) and
machine-learning approaches. We calculated the spectroscopic limited maximum
efficiency (SLME) using the Tran−Blaha-modified Becke−Johnson potential for 5097
nonmetallic materials and identified 1997 candidates with an SLME higher than 10%,
including 934 candidates with a suitable convex-hull stability and an effective carrier
mass. Screening for two-dimensional-layered cases, we found 58 potential materials
and performed G0W0 calculations on a subset to estimate the prediction uncertainty. As the above DFT methods are still computationally expensive, we developed a high accuracy machine-learning model to prescreen efficient materials and applied it to over a million materials. Our results provide a general framework and universal strategy for the design of high-efficiency solar
cell materials. The data and tools are publicly distributed at: https://www.ctcms.nist.gov/~knc6/JVASP.html, https://www.
ctcms.nist.gov/jarvisml/, https://jarvis.nist.gov/, and https://github.com/usnistgov/jarvis.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/acs.chemmater.9b02166
|
|
|
“Locating and controlling the Zn content in In(Zn)P quantum dots”. Kirkwood N, De Backer A, Altantzis T, Winckelmans N, Longo A, Antolinez FV, Rabouw FT, De Trizio L, Geuchies JJ, Mulder JT, Renaud N, Bals S, Manna L, Houtepen AJ, Chemistry of materials 32, 557 (2019). http://doi.org/10.1021/acs.chemmater.9b04407
Abstract: Zinc is routinely employed in the synthesis of InP quantum dots (QDs) to improve the photoluminescence efficiency and carrier mobility of the resulting In(Zn)P alloy nanostructures. The exact location of Zn in the final structures and the mechanism by which it enhances the optoelectronic properties of the QDs is debated. We use synchrotron X-ray absorbance spectroscopy to show that the majority of Zn in In(Zn)P QDs is located at their surface as Zn-carboxylates. However, a small amount of Zn is present inside the bulk of the QDs with the consequent contraction of their lattice, as confirmed by combining high resolution high-angle annular dark-field imaging scanning transmission electron microscopy (HAADF-STEM) with statistical parameter estimation theory. We further demonstrate that the Zn content and its incorporation into the QDs can be tuned by the ligation of commonly employed Zn carboxylate precursors: the use of highly reactive Zn-acetate leads to the formation of undesired Zn3P2 and the final nanostructures being characterized by broad optical features, whereas Zn-carboxylates with longer carbon chains lead to InP crystals with much lower zinc content and narrow optical features. These results can explain the differences between structural and optical properties of In(Zn)P samples reported across the literature, and provide a rational method to tune the amount of Zn in InP nanocrystals and to drive the incorporation of Zn either as surface Zn-carboxylate, as a substitutional dopant inside the InP crystal lattice, or even predominantly as Zn3P2.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 39
DOI: 10.1021/acs.chemmater.9b04407
|
|
|
“Atomic resolution coordination mapping in Ca2FeCoO5 brownmillerite by spatially resolved electron energy-loss spectroscopy”. Turner S, Verbeeck J, Ramezanipour F, Greedan JE, Van Tendeloo G, Botton GA, Chemistry of materials 24, 1904 (2012). http://doi.org/10.1021/cm300640g
Abstract: Using a combination of high-angle annular dark field scanning transmission electron microscopy and atomically resolved electron energy-loss spectroscopy at high energy resolution in an aberration-corrected electron microscope, we demonstrate the capability of coordination mapping in complex oxides. Brownmillerite compound Ca2FeCoO5, consisting of repetitive octahedral and tetrahedral coordination layers with Fe and Co in a fixed 3+ valency, is selected to demonstrate the principle of atomic resolution coordination mapping. Analysis of the Co-L2,3 and the Fe-L2,3 edges shows small variations in the fine structure that can be specifically attributed to Co/Fe in tetrahedral or in octahedral coordination. Using internal reference spectra, we show that the coordination of the Fe and Co atoms in the compound can be mapped at atomic resolution.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 33
DOI: 10.1021/cm300640g
|
|
|
“Seeded growth combined with cation exchange for the synthesis of anisotropic Cu2-xS/ZnS, Cu2-xS, and CuInS2 nanorods”. Xia C, Pedrazo-Tardajos A, Wang D, Meeldijk JD, Gerritsen HC, Bals S, de Donega CM, Chemistry of materials 33, 102 (2021). http://doi.org/10.1021/ACS.CHEMMATER.0C02817
Abstract: Colloidal copper(I) sulfide (Cu2-xS) nanocrystals (NCs) have attracted much attention for a wide range of applications because of their unique optoelectronic properties, driving scientists to explore the potential of using Cu2-xS NCs as seeds in the synthesis of heteronanocrystals to achieve new multifunctional materials. Herein, we developed a multistep synthesis strategy toward Cu2-xS/ZnS heteronanorods. The Janus-type Cu2-xS/ZnS heteronanorods are obtained by the injection of hexagonal high-chalcocite Cu2-xS seed NCs in a hot zinc oleate solution in the presence of suitable surfactants, 20 s after the injection of sulfur precursors. The Cu2-xS seed NCs undergo rapid aggregation and coalescence in the first few seconds after the injection, forming larger NCs that act as the effective seeds for heteronucleation and growth of ZnS. The ZnS heteronucleation occurs on a single (100) facet of the Cu2-xS seed NCs and is followed by fast anisotropic growth along a direction that is perpendicular to the c-axis, thus leading to Cu2-xS/ZnS Janus-type heteronanorods with a sharp heterointerface. Interestingly, the high-chalcocite crystal structure of the injected Cu2-xS seed NCs is preserved in the Cu2-xS segments of the heteronanorods because of the highthermodynamic stability of this Cu2-xS phase. The Cu2-xS/ZnS heteronanorods are subsequently converted into single-component Cu2-xS and CuInS2 nanorods by postsynthetic topotactic cation exchange. This work expands the possibilities for the rational synthesis of colloidal multicomponent heteronanorods by allowing the design principles of postsynthetic heteroepitaxial seeded growth and nanoscale cation exchange to be combined, yielding access to a plethora of multicomponent heteronanorods with diameters in the quantum confinement regime.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 10
DOI: 10.1021/ACS.CHEMMATER.0C02817
|
|
|
“Frustrated octahedral tilting distortion in the incommensurately modulated Li3xNd2/3-xTiO3 perovskites”. Abakumov AM, Erni R, Tsirlin AA, Rossell MD, Batuk D, Nénert G, Van Tendeloo G, Chemistry of materials 25, 2670 (2013). http://doi.org/10.1021/cm4012052
Abstract: Perovskite-structured titanates with layered A-site ordering form remarkably complex superstructures. Using transmission electron microscopy, synchrotron X-ray and neutron powder diffraction, and ab initio structure relaxation, we present the structural solution of the incommensurately modulated Li3xNd2/3xTiO3 perovskites (x = 0.05, superspace group Pmmm(α1,1/2,0)000(1/2,β2 0)000, a = 3.831048(5) Å, b = 3.827977(4) Å, c = 7.724356(8) Å, q1 = 0.45131(8)a* + 1/2b*, q2 = 1/2a* + 0.41923(4)b*). In contrast to earlier conjectures on the nanoscale compositional phase separation in these materials, all peculiarities of the superstructure can be understood in terms of displacive modulations related to an intricate octahedral tilting pattern. It involves fragmenting the pattern of the out-of-phase tilted TiO6 octahedra around the a- and b-axes into antiphase domains, superimposed on the pattern of domains with either pronounced or suppressed in-phase tilt component around the c-axis. The octahedral tilting competes with the second order JahnTeller distortion of the TiO6 octahedra. This competition is considered as the primary driving force for the modulated structure. The A cations are suspected to play a role in this modulation affecting it mainly through the tolerance factor and the size variance. The reported crystal structure calls for a revision of the structure models proposed for the family of layered A-site ordered perovskites exhibiting a similar type of modulated structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 23
DOI: 10.1021/cm4012052
|
|
|
“Ligand-Induced Shape Transformation of PbSe Nanocrystals”. Peters JL, van den Bos KHW, Van Aert S, Goris B, Bals S, Vanmaekelbergh D, Chemistry of materials 29, 4122 (2017). http://doi.org/10.1021/acs.chemmater.7b01103
Abstract: We present a study of the relation between the surface chemistry and nanocrystal shape of PbSe nanocrystals with a variable Pb-to-Se stoichiometry and density of oleate ligands. The oleate ligand density and binding configuration are monitored by nuclear magnetic resonance and Fourier transform infrared absorbance spectroscopy, allowing us to quantify the number of surface-attached ligands per NC and the nature of the surface−Pb−oleate configuration. The three-dimensional shape of the PbSe nanocrystals is obtained from high-angle annular dark field scanning transmission electron microscopy combined with an atom counting method. We show that the enhanced oleate capping results in a stabilization and extension of the {111} facets, and a crystal shape transformation from a truncated nanocube to a truncated octahedron.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 45
DOI: 10.1021/acs.chemmater.7b01103
|
|
|
“Anisotropic cation exchange in PbSe/CdSe core/shell nanocrystals of different geometry”. Casavola M, van Huis MA, Bals S, Lambert K, Hens Z, Vanmaekelbergh D, Chemistry of materials 24, 294 (2012). http://doi.org/10.1021/cm202796s
Abstract: We present a study of Cd2+-for-Pb2+ exchange in PbSe nanocrystals (NCs) with cube, star, and rod shapes. Prolonged temperature-activated cation exchange results in PbSe/CdSe heterostructured nanocrystals (HNCs) that preserve their specific overall shape, whereas the PbSe core is strongly faceted with dominance of {111} facets. Hence, cation exchange proceeds while the Se anion lattice is preserved, and well-defined {111}/{111} PbSe/CdSe interfaces develop. Interestingly, by quenching the reaction at different stages of the cation exchange new structures have been isolated, such as coreshell nanorods, CdSe rods that contain one or two separated PbSe dots and fully zinc blende CdSe nanorods. The crystallographically anisotropic cation exchange has been characterized by a combined HRTEM/HAADF-STEM study of heterointerface evolution over reaction time and temperature. Strikingly, Pb and Cd are only intermixed at the PbSe/CdSe interface. We propose a plausible model for the cation exchange based on a layer-by-layer replacement of Pb2+ by Cd2+ enabled by a vacancy-assisted cation migration mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 136
DOI: 10.1021/cm202796s
|
|
|
“Au@ZIFs: stabilization and encapsulation of cavity-size matching gold clusters inside functionalized Zeolite Imidazolate Frameworks, ZIFs”. Esken D, Turner S, Lebedev OI, Van Tendeloo G, Fischer RA, Chemistry of materials 22, 6393 (2010). http://doi.org/10.1021/cm102529c
Abstract: The selective formation and stabilization of very small, naked metal particles inside the cavities of metal organic frameworks (MOFs) and the simultaneous realization of an even distribution of the particles throughout the crystalline MOF host matrix over a wide range of metal loading are challenging goals. MOFs reveal high specific surface areas, tunable pore sizes, and organic linkers, which are able to interact with guests. The chemically very robust zeolite imidazolate frameworks (ZIFs) are a subclass of MOFs. We chose the microporous sodalite-like ZIF-8 (Zn(MelM)(2); IM = imidazolate) and ZIF-90 (Zn(ICA)(2); ICA = imidazolate-2-carboxyaldehyde) as host matrices to influence the dispersion of imbedded gold nanoparticles (Au NPs). The metal loading was achieved via gas phase infiltration of [Au(CO)Cl] followed by a thermal hydrogenation step to form the Au NPs. Low-dose high-resolution transmission electron microscopy ((HR)TEM) and electron tomography reveal a homogeneous distribution of Au NPs throughout the ZIF matrix. The functional groups of ZIF-90 direct the anchoring of intermediate Au species and stabilize drastically smaller and quite monodisperse Au NPs in contrast to the parent not functionalized ZIF-8. The particles can be very small, match the cavity size and approach defined molecular clusters of magic numbers, i.e., Au(55), independently from the level of loading. Post-synthetic oxidation of the aldehyde groups to yield alkyl esters by the adjacent, catalytically active metal NPs is presented as a new concept of encapsulating nanoparticles inside MOFs and allows multiple steps of metal loadings without decomposition of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 194
DOI: 10.1021/cm102529c
|
|
|
“Competing magnetic structures and the evolution of copper ion/vacancy ordering with composition in the manganite oxide chalcogenides Sr2MnO2Cu1.5(S1-xSex)2”. Adamson P, Hadermann J, Smura CF, Rutt OJ, Hyett G, Free DG, Clarke SJ, Chemistry of materials 24, 2802 (2012). http://doi.org/10.1021/cm301486v
Abstract: The series Sr2MnO2Cu1.5(S1-xSex)(2) (0 <= x <= 1) contains mixed-valent Mn ions (Mn2+/Mn3+) in MnO2 sheets which are separated by copper-deficient antifluorite-type Cu(2-delta)Ch(2) layers with delta similar to 0.5. The compounds crystallize in the structure type first described for Sr2Mn3Sb2O2 and are described in the I4/mmm space group at ambient temperatures. Below about 250 K, ordering between Cu+ ions and tetrahedral vacancies occurs which is long-range and close to complete in the sulfide-containing end member of the series Sr2MnO2Cu1.5S2 but which occurs over shorter length scales as the selenide content increases. The superstructure is an orthorhombic 2 root 2a x root 2a x c expansion in Ibam of the room temperature cell. For x > 0.3 there are no superstructure reflections evident in the X-ray or neutron diffraction patterns, and the I4/mmm description is valid for the average structure at all temperatures. However, in the pure selenide end member, Sr2MnO2Cu1.5Se2, diffuse scattering in electron diffractograms and modulation in high resolution lattice image profiles may arise from short-range Cu/vacancy order. All members of the series exhibit long-range magnetic order. In the sulfide-rich end member and in compounds with x < 0.1 in the formula Sr2MnO2Cu1.5(S1-xSex)(2), which show well developed superstructures due to long-range Cu/vacancy order, the magnetic structure has a (1/4 1/4 0) propagation vector in which ferromagnetic zigzag chains of Mn moments in the MnO2 sheets are coupled antiferromagnetically in an arrangement described as the CE-type magnetic structure and found in many mixed-valent perovskite and Ruddlesden-Popper type oxide manganites. In these cases the magnetic cell is an a x 2b x c expansion of the low temperature Ibam structural cell. For x >= 0.2 in the formula Sr2MnO2Cu1.5(S1-xSex)(2) the magnetic structure has a (0 0 0) propagation vector and is similar to the A-type structure, also commonly adopted by some perovskite-related manganites, in which the Mn moments in the MnO2 sheets are coupled ferromagnetically and long-range antiferromagnetic order results from antiferromagnetic coupling between planes. In the region of the transition between the two different structural and magnetic long-range ordering schemes (0.1 < x < 0.2) the two magnetic structures coexist in the same sample. The evolution of the competition between magnetic ordering schemes and the length scale of the structural order with composition in Sr2MnO2Cu1.5(S1-xSex)(2) suggest that the changes in magnetic and structural order are related consequences of the introduction of chemical disorder.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 11
DOI: 10.1021/cm301486v
|
|
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
|
|
“Incommensurate crystallographic shear structures and magnetic properties of the cation deficient perovskite (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29”. Malo S, Lepoittevin C, Pérez O, Hébert S, Van Tendeloo G, Hervieu M, Chemistry of materials 22, 1788 (2010). http://doi.org/10.1021/cm903288s
Abstract: The origin of the incommensurability in the crystallographic shear (CS) structure of the ferri-Manganite (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29, related to the cation deficient perovskite, has been determined by careful analysis of the boundaries between the two variants constituting the phasoid. High Resolution Electron Microscopy/HAADF-STEM images allow the structural mechanisms to be understood through the presence of structural units common to both phases, responsible of the incommensurate character observed in the electron diffraction patterns. The structural analysis allows for identifying different types of CS phases in the Pb−Sr−Fe(Mn)−O diagram and shows that the stabilization of the six-sided tunnels requires a higher A/B cationic ratio. A description of these phases is proposed through simple structural building units (SBU), based on chains of octahedra bordered by two pyramids. The (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29 CS compound exhibits a strong antiferromagnetic and insulating behavior, similar to the Fe-2201 and terrace ferrites but differs by the presence of a hysteresis, with a small coercive field.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/cm903288s
|
|
|
“A new mixed-valence ferrite with a cubic structure, YBaFe4O7: spin-glass-like behavior”. Caignaert V, Abakumov AM, Pelloquin D, Pralong V, Maignan A, Van Tendeloo G, Raveau B, Chemistry of materials 21, 1116 (2009). http://doi.org/10.1021/cm803312f
Abstract: A new mixed-valence ferrite, YBaFe4O7, has been synthesized. Its unique cubic structure, with a = 8.9595(2) Å, is closely related to that of the hexagonal 114 oxides YBaCo4O7 and CaBaFe4O7. It consists of corner-sharing FeO4 tetrahedra, forming triangular and kagome layers parallel to (111)C. In fact, the YBaFe4O7 and CaBaFe4O7 structures can be described as two different ccc and chch close packings of [BaO3]∞ and [O4]∞ layers, respectively, whose tetrahedral cavities are occupied by Fe2+/Fe3+ cations. The local structure of YBaFe4O7 is characterized by a large amount of stacking faults originating from the presence of hexagonal layers in the ccc cubic close-packed YBaFe4O7 structure. In this way, they belong to the large family of spinels and hexagonal ferrites studied for their magnetic properties. Differently from all the ferrites and especially from CaBaFe4O7, which are ferrimagnetic, YBaFe4O7 is an insulating spin glass with Tg = 50 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 39
DOI: 10.1021/cm803312f
|
|
|
“Short-range layered A-site ordering in double perovskites NaLaBB'O6 (B = Mn, Fe, B' = Nb, Ta)”. Dachraoui W, Yang T, Liu C, Ling G, Hadermann J, Van Tendeloo G, Llobet A, Greenblatt M, Chemistry of materials 23, 2398 (2011). http://doi.org/10.1021/cm200226u
Abstract: The new compounds NaLaFeTaO6, NaLaFeNbO6, NaLaMnTaO6, and NaLaMnNbO6 have been synthesized and characterized with a combination of transmission electron microscopy, X-ray powder diffraction (XRPD), neutron powder diffraction (NPD), and magnetization measurements. Through electron microscopy study, a local layered order of the A-cations has been detected without the typical occurrence of rock salt order at the B-cation site. Satellite reflections in the electron diffraction related to the local layered order are not visible on the XRPD or NPD patterns. The occurrence of local layered order is supported by pair distribution function analysis, which also reveals the presence of uncorrelated displacements of the Nb and Ta cations. The octahedra are tilted according to the system a−b+a−, and the coordinates were refined from XRPD and NPD with a disordered cation distribution in the space group Pnma. The magnetic exchange interactions in NaLaFeTaO6 and NaLaFeNbO6 are antiferromagnetic, while they are ferromagnetic in NaLaMnTaO6 and NaLaMnNbO6. Long-range magnetic ordering is not observed down to 4 K for any of the compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 14
DOI: 10.1021/cm200226u
|
|
|
“Structures and magnetism of La1-xSrxMnO3-(0.5+x)/2 (0.67\leq x\leq1) phases”. Dixon E, Hadermann J, Hayward MA, Chemistry of materials 24, 1486 (2012). http://doi.org/10.1021/cm300199b
Abstract: Topotactic reduction of La1-xSrxMnO3 (0.67 <= x <= 1) phases with sodium hydride yields a series of isoelectronic materials of composition La1-xSrxMnO3-(0.5+x)/2. Lanthanum rich members of the series (0.67 <= x <= 0.83) adopt anion deficient perovskite structures with a 6-layer -OTOOT'O- stacking sequence of sheets of octahedra/square-based pyramids (O) and sheets of tetrahedra (T). The strontium rich members of the series (0.83 <= x <= 1) incorporate “step defects” into this 6-layer structure in which the OTOOT'O stacking sequence is converted into either OOTOOT' or TOOT'OO at a defect plane which runs perpendicular to the [201] lattice plane. The step defects appear to provide a mechanism to relieve lattice strain and accommodate additional anion deficiency in phases with x > 0.83. Magnetization and neutron diffraction data indicate La1-xSrxMnO3-(0.5+x)/2 phases adopt antiferromagnetically ordered states at low-temperature in which the ordered arrangement of magnetic spins is incommensurate with the crystallographic lattice.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 13
DOI: 10.1021/cm300199b
|
|
|
“Transmission electron microscopy study of BA0.5Sr0.5CO0.8Fe0.2O3-\delta Perovskite decomposition at intermediate temperatures”. Efimov K, Xu Q, Feldhoff A, Chemistry of materials 22, 5866 (2010). http://doi.org/10.1021/cm101745v
Abstract: The cubic perovskite Ba(0.5)Sr(0.5)Co(0.8)Fe(0.2)O(3-delta) (denoted BSCF) is the state-of-the-art ceramic membrane material used for oxygen separation technologies above 1150 K. BSCF is a mixed oxygen-ion and electron conductor (MIEC) and exhibits one of the highest oxygen permeabilities reported so far for dense oxides. Additionally, it has excellent phase stability above 1150 K. In the intermediate temperature range (750-1100 K), however, BSCF suffers from a slow decomposition of the cubic perovskite into variants with hexagonal stacking that are barriers to oxygen transport. To elucidate details of the decomposition process, both sintered BSCF ceramic and powder were annealed for 180-240 h in ambient air at temperatures below 1123 K and analyzed by different transmission electron microscopy techniques. Aside from hexagonal perovskite Ba(0.5)Sr(0.5)CoO(3-delta) , the formation of lamellar noncubic phases was observed in the quenched samples. The structure of the lamellae with the previously unknown composition Ba(1-x)Sr(x)Co(2-y)Fe(y)O(5-delta) was found to be related to the 15R hexagonal perovskite polytype. The valence and spin-state transition of cobalt leading to a considerable diminution of its ionic radius can be considered a reason for BSCF's inherent phase instability at intermediate temperatures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 117
DOI: 10.1021/cm101745v
|
|
|
“Alloy CsCdxPb1–xBr3Perovskite Nanocrystals: The Role of Surface Passivation in Preserving Composition and Blue Emission”. Imran M, Ramade J, Di Stasio F, De Franco M, Buha J, Van Aert S, Goldoni L, Lauciello S, Prato M, Infante I, Bals S, Manna L, Chemistry Of Materials 32, acs.chemmater.0c03825 (2020). http://doi.org/10.1021/acs.chemmater.0c03825
Abstract: Various strategies have been proposed to engineer the band gap of metal halide perovskite nanocrystals (NCs) while preserving their structure and composition and thus ensuring spectral stability of the emission color. An aspect that has only been marginally investigated is how the type of surface passivation influences the structural/color stability of AMX3 perovskite NCs composed of two different M2+ cations. Here, we report the synthesis of blue-emitting Cs-oleate capped CsCdxPb1–xBr3 NCs, which exhibit a cubic perovskite phase containing Cd-rich domains of Ruddlesden–Popper phases (RP phases). The RP domains spontaneously transform into pure orthorhombic perovskite ones upon NC aging, and the emission color of the NCs shifts from blue to green over days. On the other hand, postsynthesis ligand exchange with various Cs-carboxylate or ammonium bromide salts, right after NC synthesis, provides monocrystalline NCs with cubic phase, highlighting the metastability of RP domains. When NCs are treated with Cs-carboxylates (including Cs-oleate), most of the Cd2+ ions are expelled from NCs upon aging, and the NCs phase evolves from cubic to orthorhombic and their emission color changes from blue to green. Instead, when NCs are coated with ammonium bromides, the loss of Cd2+ ions is suppressed and the NCs tend to retain their blue emission (both in colloidal dispersions and in electroluminescent devices), as well as their cubic phase, over time. The improved compositional and structural stability in the latter cases is ascribed to the saturation of surface vacancies, which may act as channels for the expulsion of Cd2+ ions from NCs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.6
Times cited: 44
DOI: 10.1021/acs.chemmater.0c03825
|
|
|
“Plasmonic Au@Pd Nanorods with Boosted Refractive Index Susceptibility and SERS Efficiency: A Multifunctional Platform for Hydrogen Sensing and Monitoring of Catalytic Reactions”. Rodal-Cedeira S, Montes-García V, Polavarapu L, Solís DM, Heidari H, La Porta A, Angiola M, Martucci A, Taboada JM, Obelleiro F, Bals S, Pérez-Juste J, Pastoriza-Santos I, Chemistry of materials 28, 9169 (2016). http://doi.org/10.1021/acs.chemmater.6b04941
Abstract: Palladium nanoparticles (NPs) have received tremendous attention over the years due to their high catalytic activity for various chemical reactions. However, unlike other noble metal nanoparticles such as Au and Ag NPs, they exhibit poor plasmonic properties with broad extinction spectra and less scattering efficiency, and thus limiting their applications in the field of plasmonics. Therefore, it has been challenging to integrate tunable and strong plasmonic properties into catalytic Pd nanoparticles. Here we show that plasmonic Au@Pd nanorods (NRs) with relatively narrow and remarkably tunable optical responses in the NIR region can be obtained by directional growth of Pd on penta-twinned Au NR seeds. We found the presence of bromide ions facilitates the stabilization of facets for the directional growth of Pd shell to obtain Au@Pd nanorods (NR) with controlled length scales. Interestingly, it turns out the Au NR supported Pd NRs exhibit much narrow extinction compared to pure Pd NRs, which makes them suitable for plasmonic sensing applications. Moreover, these nanostructures display, to the best of our knowledge, one of the highest ensemble refractive index sensitivity values reported to date (1067 nm per refractive index unit, RIU). Additionally, we showed the application of such plasmonic Au@Pd NRs for localized surface plasmon resonance (LSPR)-based sensing of hydrogen both in solution as well as on substrate. Finally, we demonstrate the integration of excellent plasmonic properties in catalytic palladium enables the in situ monitoring of a reaction progress by surface-enhanced Raman scattering. We postulate the proposed approach to boost the plasmonic properties of Pd nanoparticles will ignite the design of complex shaped plasmonic Pd NPs to be used in various plasmonic applications such as sensing and in situ monitoring of various chemical reactions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 80
DOI: 10.1021/acs.chemmater.6b04941
|
|
|
“Highly disordered crystal structure and thermoelectric properties of Sn3P4”. Zaikina JV, Kovnir KA, Sobolev AN, Presniakov IA, Kytin VG, Kulbachinskii VA, Olenev AV, Lebedev OI, Van Tendeloo G, Dikarev EV, Shevelkov AV, Chemistry of materials 20, 2476 (2008). http://doi.org/10.1021/cm702655g
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 33
DOI: 10.1021/cm702655g
|
|
|
“Seedless synthesis of single crystalline Au nanoparticles with unusual shapes and tunable LSPR in the near-IR”. Angelomé, PC, Heidari Mezerji H, Goris B, Pastoriza-Santos I, Pérez-Juste J, Bals S, Liz-Marzán LM, Chemistry of materials 24, 1393 (2012). http://doi.org/10.1021/cm3004479
Abstract: The plasmonic properties of metal nanoparticles have acquired great importance because of their potential applications in very diverse fields. Metal nanoparticles with localized surface plasmon resonances (LSPR) in the near-infrared (NIR, 7501300 nm) are of particular interest because tissues, blood, and water display low absorption in this spectral range, thus facilitating biomedical applications. Cetyltrimethylammonium chloride (CTAC) was used to induce the seedless formation of highly anisotropic, twisted single crystalline Au nanoparticles in a single step. The LSPR of the obtained particles can be tuned from 600 nm up to 1400 nm by simply changing the reaction temperature or the reagents concentrations. The tunability of the LSPR is closely associated with significant changes in the final particle morphology, which was studied by advanced electron microscopy techniques (3D Tomography and HAADF-STEM). Kinetic experiments were carried out to establish the growth mechanism, suggesting that slow kinetics together with the complexation of the gold salt precursor to CTAC are key factors favoring the formation of these anisotropic particles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 42
DOI: 10.1021/cm3004479
|
|
|
“Tuning the pore size of ink-bottle mesopores by atomic layer deposition”. Dendooven J, Goris B, Devloo-Casier K, Levrau E, Biermans E, Baklanov MR, Ludwig KF, van der Voort P, Bals S, Detavernier C, Chemistry of materials 24, 1992 (2012). http://doi.org/10.1021/cm203754a
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 52
DOI: 10.1021/cm203754a
|
|
|
“Influence of the structure on the properties of NaxEuy(MoO4)z red phosphors”. Morozov VA, Lazoryak BI, Shmurak SZ, Kiselev AP, Lebedev OI, Gauquelin N, Verbeeck J, Hadermann J, Van Tendeloo G, Chemistry of materials 26, 3238 (2014). http://doi.org/10.1021/cm500966g
Abstract: Scheelite related compounds (A',A '')(n)[(B',B '')O-4](m) with B', B '' = W and/or Mo are promising new materials for red phosphors in pc-WLEDs (phosphor-converted white-light-emitting-diode) and solid-state lasers. Cation substitution in CaMoO4 of Ca2+ by the combination of Na+ and Eu3+, with the creation of A cation vacancies, has been investigated as a factor for controlling the scheelite-type structure and the luminescent properties. Na5Eu(MoO4)(4) and NaxEu(2-x)/33+square(2-x)/3MoO4 (0.138 <= x <= 0.5) phases with a scheelite-type structure were synthesized by the solid state method; their structural characteristics were investigated using transmission electron microscopy. Contrary to powder synchrotron X-ray diffraction before, the study by electron diffraction and high resolution transmission electron microscopy in this paper revealed that Na0.286Eu0.571MoO4 has a (3 + 2)D incommensurately modulated structure and that (3 + 2)D incommensurately modulated domains are present in Na0.200Eu0.600MoO4. It also confirmed the (3 + 1)D incommensurately modulated character of Na(0.138)Eu(0.621)Mo04. The luminescent properties of all phases under near-ultraviolet (n-UV) light have been investigated. The excitation spectra of these phosphors show the strongest absorption at about 395 nm, which matches well with the commercially available n-UV-emitting GaN-based LED chip. The emission spectra indicate an intense red emission due to the D-5(0) -> F-7(2) transition of Eu3+, with local minima in the intensity at Na0.286Eu0.571MoO4 and Na0.200Eu0.600MoO4 for similar to 613 nm and similar to 616 nm bands. The phosphor Na5Eu(MoO4)(4) shows the brightest red light emission among the phosphors in the Na2MoO4-Eu2/3MoO4 system and the maximum luminescence intensity of Na5Eu(MoO4)(4) (lambda(ex) = 395 nm) in the D-5(0) -> F-7(2) transition region is close to that of the commercially used red phosphor YVO4:Eu3+ (lambda(ex) = 326 nm). Electron energy loss spectroscopy measurements revealed the influence of the structure and Na/Eu cation distribution on the number and positions of bands in the UV-optical-infrared regions of the EELS spectrum.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 53
DOI: 10.1021/cm500966g
|
|
|
“Crystal Structure and Luminescent Properties of R2-xEux(MoO4)(3) (R = Gd, Sm) Red Phosphors”. Morozov VA, Raskina MV, Lazoryak BI, Meert KW, Korthout K, Smet PF, Poelman D, Gauquelin N, Verbeeck J, Abakumov AM, Hadermann J;, Chemistry of materials 26, 7124 (2014). http://doi.org/10.1021/cm503720s
Abstract: The R-2(MoO4)(3) (R = rare earth elements) molybdates doped with Eu3+ cations are interesting red-emitting materials for display and solid-state lighting applications. The structure and luminescent properties of the R2-xEux(MoO4)(3) (R = Gd, Sm) solid solutions have been investigated as a function of chemical composition and preparation conditions. Monoclinic (alpha) and orthorhombic (beta') R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) modifications were prepared by solid-state reaction, and their structures were investigated using synchrotron powder X-ray diffraction and transmission electron microscopy. The pure orthorhombic beta'-phases could be synthesized only by quenching from high temperature to room temperature for Gd2-xEux(MoO4)(3) in the Eu3+-rich part (x > 1) and for all Sm2-xEux(MoO4)(3) solid solutions. The transformation from the alpha-phase to the beta'-phase results in a notable increase (similar to 24%) of the unit cell volume for all R2-xEux(MoO4)(3) (R = Sm, Gd) solid solutions. The luminescent properties of all R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) solid solutions were measured, and their optical properties were related to their structural properties. All R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) phosphors emit intense red light dominated by the D-5(0)-> F-7(2) transition at similar to 616 nm. However, a change in the multiplet splitting is observed when switching from the monoclinic to the orthorhombic structure, as a consequence of the change in coordination polyhedron of the luminescent ion from RO8 to RO7 for the alpha- and beta'-modification, respectively. The Gd2-xEux(MoO4)(3) solid solutions are the most efficient emitters in the range of 0 < x < 1.5, but their emission intensity is comparable to or even significantly lower than that of Sm2-xEux(MoO4)(3) for higher Eu3+ concentrations (1.5 <= x <= 1.75). Electron energy loss spectroscopy (EELS) measurements revealed the influence of the structure and element content on the number and positions of bands in the ultraviolet-visible-infrared regions of the EELS spectrum.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 24
DOI: 10.1021/cm503720s
|
|
|
“Solving the structure of Li ion battery materials with precession electron diffraction : application to Li2CoPo4F”. Hadermann J, Abakumov AM, Turner S, Hafideddine Z, Khasanova NR, Antipov EV, Van Tendeloo G, Chemistry of materials 23, 3540 (2011). http://doi.org/10.1021/cm201257b
Abstract: The crystal structure of the Li2CoPO4F high-voltage cathode for Li ion rechargeable batteries has been completely solved from precession electron diffraction (PED) data, including the location of the Li atoms. The crystal structure consists of infinite chains of CoO4F2 octahedra sharing common edges and linked into a 3D framework by PO4 tetrahedra. The chains and phosphate anions together delimit tunnels filled with the Li atoms. This investigation demonstrates that PED can be successfully applied for obtaining structural information on a variety of Li-containing electrode materials even from single micrometer-sized crystallites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 46
DOI: 10.1021/cm201257b
|
|