“A new way of synthesis and characterization of superconducting oxyfluoride Sr2Cu(O,F)4+\delta”. Ardashnikova EI, Lubarsky SV, Denisenko DI, Shpanchenko RV, Antipov EV, Van Tendeloo G, Physica: C : superconductivity 253, 259 (1995)
Abstract: Superconducting Cu mixed oxyfluoride, Sr,Cu(O, F)(4+delta), was Obtained via fluorination of Sr2CuO3 by XeF2 in the 100-250 degrees C temperature range in a closed Ni container. The prepared samples exhibited a lower T-c in comparison with earlier reported values. Different samples in the Sr-Cu-O-F system were prepared by a solid-state reaction at 220-400 degrees C, but no formation of the oxyfluoride was detected even with an addition of xenon difluoride. These data allow one to draw conclusions on the metastability of the oxyfluoride under the conditions used, Electron microscopy and X-ray powder diffraction studies revealed large amounts of badly crystallized SrF2; this could be a reason for the small superconducting volume fraction as well as for the inhomogeneous distribution of the anions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 29
|
|
|
“Ordering of tetrahedral chains in the Sr2MnGaO5 brownmillerite”. Abakumov AM, Alekseeva AM, Rozova MG, Antipov EV, Lebedev OI, Van Tendeloo G, Journal of solid state chemistry 174, 319 (2003). http://doi.org/10.1016/S0022-4596(03)00226-3
Abstract: Tetrahedral chain ordering in the Sr2MnGaO5 structure is studied using electron diffraction (ED) and high-resolution electron microscopy. The ED patterns show the presence of satellite reflections, which indicate a commensurately modulated structure with a = 5.4056(8) Angstrom b 16.171(3) Angstrom, c = 5.5592(7) Angstrom, q – 1/2c*, superspace group Immma(00gamma,)s00. The Superstructure arises due to ordering of the two types of symmetry related tetrahedral chains (L and R) according to a ... LRLR ... sequence, where L and R chains alternate along the c-axis within the same (GaO) layer. Numerous defects at different structural levels were observed, comprising interleaving L and R chains, violation of the ... LRLR ... chain sequence within one layer, different stacking modes of the ... LRLR ... ordered layers with subsequent alternation of blocks of different width along the h-axis of the brownmillerite subcell and island fragmentation of the modulated superstructure. By in situ heating ED experiments it is found that the long-range ordering of the tetrahedral chains is stable tip to 665degreesC and is completely suppressed at 905degreesC. (C) 2003 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 34
DOI: 10.1016/S0022-4596(03)00226-3
|
|
|
“Oxygen and fluorine doping in Sr2MnGaO5 brownmillerite”. Antipov EV, Abakumov AM, Alekseeva AM, Rozova MG, Hadermann J, Lebedev OI, Van Tendeloo G, Physica status solidi: A: applied research 201, 1403 (2004). http://doi.org/10.1002/pssa.200304428
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 9
DOI: 10.1002/pssa.200304428
|
|
|
“The phase transition and crystal structures of Ba3RM2O7.5 complex oxides (R=rare-earth elements, M = Al,Ga)”. Abakumov AM, Shpanchenko RV, Lebedev OI, Van Tendeloo G, Amelinckx S, Antipov EV, Acta crystallographica: section A: foundations of crystallography 55, 828 (1999). http://doi.org/10.1107/S0108767399002068
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.725
Times cited: 7
DOI: 10.1107/S0108767399002068
|
|
|
“Phase transitions in K3AlF6”. Abakumov AM, Rossell MD, Alekseeva AM, Vassiliev SY, Mudrezova SN, Van Tendeloo G, Antipov EV, Journal of solid state chemistry 179, 421 (2006). http://doi.org/10.1016/j.jssc.2005.10.044
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 18
DOI: 10.1016/j.jssc.2005.10.044
|
|
|
“Spatial separation of covalent, ionic, and metallic interactions in Mg11Rh18B8 and Mg3Rh5B3”. Alekseeva AM, Abakumov AM, Leither-Jasper A, Schnelle W, Prots Y, Van Tendeloo G, Antipov EV, Grin Y, Chemistry: a European journal 19, 17860 (2013). http://doi.org/10.1002/chem.201301512
Abstract: The crystal structures of Mg11Rh18B8 and Mg3Rh5B3 have been investigated by using single-crystal X-ray diffraction. Mg11Rh18B8: space group P4/mbm; a=17.9949(7), c=2.9271(1)angstrom; Z=2. Mg3Rh5B3: space group Pmma; a=8.450(2), b=2.8644(6), c=11.602(2)angstrom; Z=2. Both crystal structures are characterized by trigonal prismatic coordination of the boron atoms by rhodium atoms. The [BRh6] trigonal prisms form arrangements with different connectivity patterns. Analysis of the chemical bonding by means of the electron-localizability/electron-density approach reveals covalent BRh interactions in these arrangements and the formation of BRh polyanions. The magnesium atoms that are located inside the polyanions interact ionically with their environment, whereas, in the structure parts, which are mainly formed by Mg and Rh atoms, multicenter (metallic) interactions are observed. Diamagnetic behavior and metallic electron transport of the Mg11Rh18B8 and Mg3Rh5B3 phases are in agreement with the bonding picture and the band structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 5
DOI: 10.1002/chem.201301512
|
|
|
“Spin ladder compound Pb0.55Cd0.45V2O5: synthesis and investigation”. Tsirlin AA, Shpanchenko RV, Antipov EV, Bougerol C, Hadermann J, Van Tendeloo G, Schnelle W, Rosner H, Physical review : B : condensed matter and materials physics 76, 104429 (2007). http://doi.org/10.1103/PhysRevB.76.104429
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 1
DOI: 10.1103/PhysRevB.76.104429
|
|
|
“Structural and magnetic properties of the colossal magnetoresistance perovskite La0.85Ca0.15MnO3”. Lobanov MV, Balagurov AM, Pomjakushin VJ, Fischer P, Gutmann M, Abakumov AM, D'yachenko OG, Antipov EV, Lebedev OI, Van Tendeloo G, Physical review : B : condensed matter and materials physics 61, 8941 (2000). http://doi.org/10.1103/PhysRevB.61.8941
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 47
DOI: 10.1103/PhysRevB.61.8941
|
|
|
“Structural changes in fluorinated T{'} and T* phases”. Hadermann J, Abakumov AM, Lebedev OI, Antipov EV, Van Tendeloo G, , 193 (2000)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Structural features, oxygen and fluorine doping in Cu-based superconductors”. Antipov EV, Putilin SN, Shpanchenko RV, Alyoshin VA, Rozova MG, Abakumov AM, Mikhailova DA, Balagurov AM, Lebedev O, Van Tendeloo G, Physica: C : superconductivity
T2 –, International Conference on Materials and Mechanisms of, Superconductivity –, High Temperature Superconductors V, Feb. 28-Mar. 04, 1997, Beijing, Peoples R. China 282, 61 (1997). http://doi.org/10.1016/S0921-4534(97)00210-4
Abstract: The variation of structures and superconducting properties by changing extra oxygen or fluorine atoms concentration in Hg-based Cu mixed oxides and YBa2Cu3O6+delta was studied. The data obtained by NPD study of Hg-1201 can be considered as an evidence of the conventional oxygen doping mechanism with 2 delta holes per (CuO2) layer. The extra oxygen atom was found to be located in the middle of the Hg mesh only. Different formal charges of oxygen and fluorine inserted into reduced 123 structure results in its distinct variations. The fluorine incorporation into strongly reduced YBa2Cu3O6+delta causes a significant structural rearrangement and the formation of a new compound with a composition close to YBa2Cu3O6F2 (tetragonal alpha = 3.87 Angstrom and c approximate to 13 Angstrom), which structure was deduced from the combined results of X-ray diffraction, electron diffraction and high resolution electron microscopy. Fluorination treatment by XeF2 of nonsuperconducting 123 samples causes an appearance of bulk superconductivity with T-c up to 94K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 10
DOI: 10.1016/S0921-4534(97)00210-4
|
|
|
“Structural study of the new complex oxides Ba5-ySryR2-xAl2Zr1+xO13+x/2 (R=Gd-Lu, Y, Sc)”. Shpanchenko RV, Abakumov AM, Antipov EV, Nistor L, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 118, 180 (1995). http://doi.org/10.1006/jssc.1995.1329
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 8
DOI: 10.1006/jssc.1995.1329
|
|
|
“Structural transformation in fluorinated LaACuGaO5 (A=Ca, Sr) brownmillerites”. Hadermann J, Van Tendeloo G, Abakumov AM, Pavlyuk BP, Rozova MG, Antipov EV, International journal of inorganic materials 2, 493 (2000). http://doi.org/10.1016/S1466-6049(00)00072-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 13
DOI: 10.1016/S1466-6049(00)00072-6
|
|
|
“Structural transformations in the fluorinated T* phase”. Hadermann J, Abakumov AM, Lebedev OI, Van Tendeloo G, Rozova MG, Shpanchenko RV, Pavljuk BP, Kopnin EM, Antipov EV, Journal of solid state chemistry 147, 647 (1999). http://doi.org/10.1006/jssc.1999.8438
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.1999.8438
|
|
|
“Structure and high-temperature properties of the (Sr,Ca,Y)(Co,Mn)O3-y perovskites –, perspective cathode materials for IT-SOFC”. Napolsky PS, Drozhzhin OA, Istomin SY, Kazakov SM, Antipov EV, Galeeva AV, Gippius AA, Svensson G, Abakumov AM, Van Tendeloo G, Journal of solid state chemistry 192, 186 (2012). http://doi.org/10.1016/j.jssc.2012.03.056
Abstract: Oxygen deficient perovskites Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75, were prepared by using the citrate route at 1373-1573 K for 48 h. The cubic Pm-3m perovskite structure for x=0.5 was confirmed by electron diffraction study and refined using neutron powder diffraction (NPD) data. For x=0.75, the superstructure corresponding to a=root 2 x a(per), b=2 x a(per), c=root 2 x a(per) (a(0)b(-)b(-) tilt system, space group Imma) was revealed by electron diffraction. The solid solution Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= x <= 0.6 and compound Ca0.75Y0.25Mn0.85Co0.15O2.92 were prepared in air at 1573 K for 48 h. The crystal structure of Ca0.75Y0.25Mn0.85Co0.15O2.92 was refined using NPD data (S.G. Pnma, a=5.36595(4), b=7.5091(6), c=5.2992(4) angstrom, R-p=0.057, R-wp=0.056, chi(2)=4.26). High-temperature thermal expansion properties of the prepared compounds were studied in air using both dilatometry and high-temperature X-ray powder diffraction data (HTXRPD). They expanding non-linearly at 298-1073 K due to the loss of oxygen at high temperatures. Calculated average thermal expansion coefficients (TECs) for Sr0.75Y0.25Co1-xMnxO3-y, x=0.5, 0.75 and Ca0.75Y0.25Mn0.85Co0.15O2.92(1) are 15.5, 15.1, and 13.8 ppm K-1, respectively. Anisotropy of the thermal expansion along different unit cell axes was observed for Sr0.15Ca0.6Y0.25Co0.25Mn0.75O3-y, and Ca0.75Y0.25Mn0.85Co0.15O2.92. Conductivity of Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75 increases with the temperature reaching 110 S/cm for x=0.5 and 44 S/cm for x=0.75 at 1173 K. Samples of Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= y <= 0.6 were found to be n-type conductors at room temperature with the similar temperature dependence of the conductivity and demonstrated the increase of the sigma value from similar to 1 to similar to 50 S/cm as the temperature increases from 300 to 1173 K. Their conductivity is described in terms of the small polaron charge transport with the activation energy (E-p) increasing from 340 to 430 meV with an increase of the calcium content from x=0 to x=0.6. (C) 2012 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2012.03.056
|
|
|
“Structure and magnetic properties of a new anion-deficient perovskite Pb2Ba2BiFe4ScO13 with crystallographic shear structure”. Batuk M, Tyablikov OA, Tsirlin AA, Kazakov SM, Rozova MG, Pokholok KV, Filimonov DS, Antipov EV, Abakumov AM, Hadermann J, Materials research bulletin 48, 3459 (2013). http://doi.org/10.1016/j.materresbull.2013.05.028
Abstract: Pb2Ba2BiFe4ScO13, a new n = 5 member of the oxygen-deficient perovskite-based A(n)B(n)O(3n-2) homologous series, was synthesized using a solid-state method. The crystal structure of Pb2Ba2BiFe4ScO13 was investigated by a combination of synchrotron X-ray powder diffraction, electron diffraction, high-angle annular dark-field scanning transmission electron microscopy and Mossbauer spectroscopy. At 900 K, it crystallizes in the Ammm space group with the unit cell parameters a = 5.8459(1) angstrom, b = 4.0426(1) angstrom, and c=27.3435(1) angstrom. In the Pb2Ba2BiFe4ScO13 structure, quasi-two-dimensional perovskite blocks are periodically interleaved with 1/2[1 1 0] ((1) over bar 0 1)(p) crystallographic shear (CS) planes. At the CS planes, the corner-sharing FeO6 octahedra are transformed into chains of edge-sharing FeO5 distorted tetragonal pyramids. B-positions of the perovskite blocks between the CS planes are jointly occupied by Fe3+ and Sc3+. The chains of the FeO5 pyramids and (Fe,Sc)O-6 octahedra delimit six-sided tunnels that are occupied by double columns of cations with a lone electron pair (Pb2+). The remaining A-cations (Bi3+, Ba2+) occupy positions in the perovskite block. According to the magnetic susceptibility measurements, Pb2Ba2BiFe4ScO13 is antiferromagnetically ordered below T-N approximate to 350 K. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 2
DOI: 10.1016/j.materresbull.2013.05.028
|
|
|
“Structure determination of YBCO fluorinated phases by HREM”. Van Tendeloo G, Lebedev OI, Shpanchenko RV, Antipov EV, Journal of electron microscopy 1, 23 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.9
|
|
|
“Structure of Y123 and Y247 fluorinated phases by HREM”. Lebedev OI, Van Tendeloo G, Abakumov AM, Shpanchenko RV, Rozova MG, Antipov EV, Electron microscopy: vol. 3 , 297 (1998)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Superspace description, crystal structures, and electric conductiof the Ba4In6-xMgxO13-x/2 solid solutions”. Abakumov AM, Rossell MD, Gutnikova OY, Drozhzhin OA, Leonova LS, Dobrovolsky YA, Istomin SY, Van Tendeloo G, Antipov EV, Chemistry of materials 20, 4457 (2008). http://doi.org/10.1021/cm8004216
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 15
DOI: 10.1021/cm8004216
|
|
|
“Suppression of modulations in fluorinated Bi-2201 phases”. Hadermann J, Khasanova NR, Van Tendeloo G, Abakumov AM, Rozova MG, Alekseeva AM, Antipov EV, Journal of solid state chemistry 156, 445 (2001). http://doi.org/10.1006/jssc.2000.9020
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.2000.9020
|
|
|
“Suppression of superconductivity in Hg-1223 and Hg-1234 by partial replacement of Hg by carbon”. Kopnin EM, Antipov EV, Capponi JJ, Bordet P, Chaillout C, de Brion S, Marezio M, Bobylev AP, Van Tendeloo G, Physica: C : superconductivity 243, 222 (1995). http://doi.org/10.1016/0921-4534(95)00010-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 22
DOI: 10.1016/0921-4534(95)00010-0
|
|
|
“Synthesis and characterization of new phases: Sr3.75K1.75Bi3O12 and Sr3.1Na2.9Bi3O12”. Pshirkov JS, Kazakov SM, Abakumov AM, Putilin SN, Antipov EV, Bougerol-Chaillout C, Lebedev OI, Van Tendeloo G, Journal of solid state chemistry 152, 492 (2000). http://doi.org/10.1006/jssc.2000.8718
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1006/jssc.2000.8718
|
|
|
“Synthesis and characterization of oxygen-deficient oxides BaCo1-xYxO3-y' x = 0.15, 0.25 and 0.33, with the perovskite structure”. Lomakov MV, Istomin SY, Abakumov AM, Van Tendeloo G, Antipov EV, Solid state ionics 179, 1885 (2008). http://doi.org/10.1016/j.ssi.2008.05.004
Abstract: Oxygen-deficient complex cobalt oxides BaCo1 − xYxO3 − y, = 0.15, 0.25 and 0.33, with a cubic perovskite structure have been synthesized in air at 1100 °C using a citrate route. Cation composition of the compounds was confirmed by energy-dispersed X-ray (EDX) microanalysis while oxygen content was determined by iodometric titration. An electron diffraction (ED) study of the x = 0.25 and 0.33 compositions show the presence of a diffuse intensity, indicating possible short-range ordering of the B cations. It was found that the treatment of BaCo0.75Y0.25O2.55 in a humid atmosphere leads to the absorption of water vapour at the first stage. Oxygen permeation studies of the ceramic membranes of BaCo0.75Y0.25O2.55 and BaCo0.67Y0.33O2.55 with variable thickness showed high oxygen fluxes of 0.170.32 µmol/cm2/s at 950 °C.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.354
Times cited: 9
DOI: 10.1016/j.ssi.2008.05.004
|
|
|
“Synthesis and crystal structure of a new complex oxyfluoride La0.813Sr0.187Cu(o,F)3-\delta”. Abakumov AM, Hadermann J, Rozova MG, Pavljuk BP, Antipov EV, Lebedev OI, Van Tendeloo G, Journal of solid state cemistry 149, 189 (2000). http://doi.org/10.1006/jssc.1999.8521
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.1999.8521
|
|
|
“Synthesis and crystal structure of new titanyl phosphate Sr2TiO(PO4)2”. Shpanchenko RV, Tsirlin AA, Hadermann J, Antipov EV, Russian chemical bulletin 57, 552 (2008). http://doi.org/10.1007/s11172-008-0085-9
Abstract: New strontium titanyl phosphate Sr2TiO(PO4)2 (1) was synthesized and characterized by X-ray powder diffraction, electron diffraction, high-resolution electron microscopy, and band structure calculations. Titanyl phosphate 1 is isostructural with vanadyl phosphate Sr2VO(PO4)2 and has a layered structure. The titanium atoms are shifted from the centers of the TiO6 octahedra and form short (1.74 Å) titanyl bonds. The structure of 1 is an unusual example of the disordered orientation of the chains formed by TiO6 octahedra in complex titanium phosphates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 2
DOI: 10.1007/s11172-008-0085-9
|
|
|
“Synthesis and crystal structure of novel layered manganese oxide Ca2MnGaO5+\delta”. Abakumov AM, Rozova MG, Pavlyuk BP, Lobanov MV, Antipov EV, Lebedev OI, Van Tendeloo G, Sheptyakov DV, Balagurov AM, Bourée F, Journal of solid state chemistry 158, 100 (2001). http://doi.org/10.1006/jssc.2000.9105
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 48
DOI: 10.1006/jssc.2000.9105
|
|
|
“Synthesis and crystal structure of the new complex oxide Ca7Mn2.14Ga5.86O17.93”. Kalyuzhnaya AS, Abakumov AM, Rozova MG, d' Hondt H, Hadermann J, Antipov EV, Russian chemical bulletin 59, 706 (2010). http://doi.org/10.1007/s11172-010-0150-z
Abstract: The complex oxide Ca7Mn2.14Ga5.86O17.93 was synthesized by the solid-state reaction in a sealed evacuated quartz tube at 1000 °C. Its crystal structure was determined by electron diffraction and X-ray powder diffraction. The structure can be represented as a tetrahedral framework, viz., the polyanion [(Mn0.285Ga0.715)15O29.86]19- stabilized by the incorporated cation [Ca14GaO6]19+. The polycation consists of the GaO6 octahedra surrounded by the Ca atoms, which are arranged to form a cube capped at all places. The tetrahedral framework is partially disordered due to the presence of tetrahedra with two possible orientations in the positions (0, 0, 0) and (x, x, x) with x ≈ 0.15 and 0.17. The relationship between the Ca7Mn2.14Ga5.86O17.93 structures and related ordered phases with the symmetry F23, as well as the influence of the oxygen content on the ordering in the tetrahedral framework, are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 1
DOI: 10.1007/s11172-010-0150-z
|
|
|
“Synthesis and crystal structure of the novel Pb5Sb2MnO11 compound”. Abakumov AM, Rozova MG, Chizhov PS, Antipov EV, Hadermann J, Van Tendeloo G, Journal of solid state chemistry 177, 2855 (2004). http://doi.org/10.1016/j.jssc.2004.04.047
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 3
DOI: 10.1016/j.jssc.2004.04.047
|
|
|
“Synthesis and crystal structure of the palladium oxides NaPd3O4, Na2PdO3 and K3Pd2O4”. Panin RV, Khasanova NR, Abakumov AM, Antipov EV, Van Tendeloo G, Schnelle W, Journal of solid state chemistry 180, 1566 (2007). http://doi.org/10.1016/j.jssc.2007.03.005
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 24
DOI: 10.1016/j.jssc.2007.03.005
|
|
|
“Synthesis and crystal structure of the Sr2MnGa(O,F)6 oxyfluorides”. Alekseeva AM, Abakumov AM, Rozova MG, Antipov EV, Hadermann J, Journal of solid state chemistry 177, 731 (2004). http://doi.org/10.1016/j.jssc.2003.09.002
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 23
DOI: 10.1016/j.jssc.2003.09.002
|
|
|
“Synthesis and investigation of novel Mn-based oxyfluoride Sr2Mn2O5-xF1+x”. Lobanov MV, Abakumov AM, Sidorova AV, Rozova MG, D'yachenko OG, Antipov EV, Hadermann J, Van Tendeloo G, Solid state sciences 4, 19 (2002). http://doi.org/10.1016/S1293-2558(01)01209-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 21
DOI: 10.1016/S1293-2558(01)01209-2
|
|